Method of making EEPROM cell structure
Assignee: STMicroelectronics lnc USA
•
Filing: 1997-07-31
•
Granted: 1999-03-23
•
Expires: 2017-07-31
Abstract
Abstract A memory cell for an EEPROM memory is fabricated to provide increased oxide thickness at the edge of the tunnel oxide and under the edges of the polysilicon capacitor plate in order to improve the dielectric integrity of the capacitor structure. In one embodiment using a silicided polysilicon process, the oxide is made thicker at the edge of the tunnel oxide by reoxidizing the silicon at the corner of the polysilicon capacitor plate and the underlying substrate surface by exposing the device to a short duration oxidation step after having deposited a 200 Å to 500 Å thick porous oxide over the device to protect the silicide from excessivie exposure to the oxidizing ambient. In another embodiment the tunnel oxide is grown in a window in the gate oxide layer, which is about four times thicker than the tunnel oxide, so that the gate oxide completely surrounds the tunnel oxide, and the polysilicon capacitor plate extends beyond the edge of the tunnel oxide terminating at a point above the gate oxide.
Inventors
- 👤 Tsiu Chiu Chan
- 👤 Pervez H. Sagarwala
- 👤 Loi Nguyen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:56
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0411; H10D30/60; H10D30/68; H10D30/681; H10D30/683; H10D30/6891; H10B; H10B69/00
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
253 words
A process for providing improved dielectric integrity at the edge of an oxide insulating layer in circuit element of a semiconductor integrated circuit device, comprising the steps: providing a substrate having an upper surface region defining a first conductive portion of the circuit element; forming the oxide insulating layer on the upper surface region of the substrate, the oxide insulating layer having an interior portion of a uniform thickness and an oxide edge portion of a thickness greater than the uniform thickness, at least the oxide edge portion overlying the first conductive portion of the substrate, forming a polysilicon layer on the oxide insulating layer overlying the interior portion and the oxide edge portion; forming a tantalum silicide layer atop the polysilicon layer to provide a composite silicided polysilicon layer, the ratio of silicon to tantalum in the tantalum silicide layer being at least about 2.6, the silicided polysilicon layer having a conductive edge portion juxtaposed above the oxide edge portion, the silicided polysilicon layer defining a second conductive portion of the circuit element, the conductive edge portion having a lower corner defined by the bottom and side surfaces of the conductive edge portion; forming a sidewall oxide spacer abutting the oxide edge portion and the conductive edge portion; whereby the lower corner of the conductive edge portion is insulated from the underlying conductive upper surface region of the substrate and is spaced therefrom by an intervening oxide thickness greater than the uniform thickness of the interior portion of the oxide insulating layer.
Claim 2
Dependent Claim
253 words
A process for providing improved dielectric integrity at the edge of an oxide insulating layer in circuit element of a semiconductor integrated circuit device, comprising the steps: providing a substrate having an upper surface region defining a first conductive portion of the circuit element; forming the oxide insulating layer on the upper surface region of the substrate, the oxide insulating layer having an interior portion of a uniform thickness and an oxide edge portion of a thickness greater than the uniform thickness, at least the oxide edge portion overlying the first conductive portion of the substrate, forming a polysilicon layer on the oxide insulating layer overlying the interior portion and the oxide edge portion; forming a tantalum silicide layer atop the polysilicon layer to provide a composite silicided polysilicon layer, the ratio of silicon to tantalum in the tantalum silicide layer being at least about 2.6, the silicided polysilicon layer having a conductive edge portion juxtaposed above the oxide edge portion, the silicided polysilicon layer defining a second conductive portion of the circuit element, the conductive edge portion having a lower corner defined by the bottom and side surfaces of the conductive edge portion; forming a sidewall oxide spacer abutting the oxide edge portion and the conductive edge portion; whereby the lower corner of the conductive edge portion is insulated from the underlying conductive upper surface region of the substrate and is spaced therefrom by an intervening oxide thickness greater than the uniform thickness of the interior portion of the oxide insulating layer.
Claim 3
Dependent Claim
17 words
The process of claim 1 wherein the circuit element is a capacitor of an EEPROM memory cell.
Claim 4
Dependent Claim
60 words
The process of claim 1 wherein the oxide edge portion is formed by oxidizing the polysilicon layer in the vicinity of its lower corner and the upper surface region of the substrate juxtaposed beneath the polysilicon lower corner, the oxidizing step being preceded by the deposition of a porous oxide layer as a protective layer over the silicided polysilicon layer.
Claim 5
Dependent Claim
47 words
The process of claim 1 wherein the oxide edge portion is a shelf of oxide several times thicker than the uniform thickness interior portion, the shelf being a portion of an oxide layer grown in a step preceding a step in which the interior portion is grown.
Claim 6
Dependent Claim
170 words
A process for making an integrated circuit device comprising the steps: providing a semiconductor substrate having an upper surface for defining circuit elements; forming isolated active areas on the substrate; growing an oxide layer for use at least in part as a capacitor dielectric; depositing a polysilicon layer on the device and atop the dielectric oxide layer; depositing a silicide layer atop the polysilicon layer to form a composite silicided polysilicon layer; selectively etching portions of the silicided polysilicon layer to define a pattern and incident thereto cutting through edge portions of the dielectric oxide layer, the edge portions being substantially vertically aligned with edge portions of the silicided polysilicon layer and defining a lower polysilicon corner meeting a dielectric oxide upper corner at the aligned edge portions; depositing a porous oxide layer; exposing the device to an oxidizing ambient for a short duration to oxidize the silicon beneath the porous oxide layer including silicon at the lower polysilicon corner and silicon on the opposed upper surface of the substrate.
Claim 7
Dependent Claim
170 words
A process for making an integrated circuit device comprising the steps: providing a semiconductor substrate having an upper surface for defining circuit elements; forming isolated active areas on the substrate; growing an oxide layer for use at least in part as a capacitor dielectric; depositing a polysilicon layer on the device and atop the dielectric oxide layer; depositing a silicide layer atop the polysilicon layer to form a composite silicided polysilicon layer; selectively etching portions of the silicided polysilicon layer to define a pattern and incident thereto cutting through edge portions of the dielectric oxide layer, the edge portions being substantially vertically aligned with edge portions of the silicided polysilicon layer and defining a lower polysilicon corner meeting a dielectric oxide upper corner at the aligned edge portions; depositing a porous oxide layer; exposing the device to an oxidizing ambient for a short duration to oxidize the silicon beneath the porous oxide layer including silicon at the lower polysilicon corner and silicon on the opposed upper surface of the substrate.
Claim 8
Dependent Claim
13 words
The process of claim 5 wherein the metal silicide layer is tantalum silicide.
Claim 9
Dependent Claim
24 words
The process of claim 6 wherein the tantalum silicide has a silicon to tantalum ratio in the range from about 2.5 to about 2.7.
Claim 10
Dependent Claim
18 words
The process of claim 7 wherein the tantalum silicide has a silicon to tantalum ratio of about 2.6.
Claim 11
Dependent Claim
23 words
The process of claim 5 wherein the porous oxide layer is deposited to a thickness of about 200 Å to about 500 Å.
Claim 12
Dependent Claim
21 words
The process of claim 9 wherein the porous oxide layer is deposited at a temperature between 400° C. and 500° C.
Claim 13
Dependent Claim
39 words
The process of claim 9 wherein the duration of the step of exposing the device to an oxidizing ambient for a short duration is just long enough to grow about 200 Å of oxide on bare, lightly-doped monitor wafers.
Claim 14
Dependent Claim
249 words
A process for making an integrated circuit device having a plurality of nonvolatile memory cells arranged in rows and columns, a cell site being defined at each intersection of a row and a column, comprising the steps: providing a semiconductor substrate of a first conductivity type; forming a thick oxide layer on an upper surface of the substrate in a pattern to define active areas between edges of the thick oxide layer; at each cell site introducing a dopant into a selected portion of an active area to define a first capacitor plate of a second conductivity type extending to a depth below the surface of the substrate; growing a thin oxide layer in the active areas and atop the first capacitor plates; etching a window through the thin oxide layer above each first capacitor plate; growing an ultrathin tunnel oxide layer in each window; forming a conductive layer on the device overlying the oxide layers; and selectively removing portions of the conductive layer leaving portions in place at each cell site to define a second capacitor plate overlying the corresponding first capacitor plate, the second capacitor plate completely covering the ultrathin tunnel oxide layer and extending laterally beyond the edges of the ultrathin tunnel oxide layer to define a shoulder overlying the thin oxide layer, the shoulder completely surrounding the ultrathin tunnel oxide layer; whereby a tunneling capacitor is defined at each cell site by the first and second capacitor plates and the ultrathin tunnel oxide layer therebetween.
Claim 15
Dependent Claim
249 words
A process for making an integrated circuit device having a plurality of nonvolatile memory cells arranged in rows and columns, a cell site being defined at each intersection of a row and a column, comprising the steps: providing a semiconductor substrate of a first conductivity type; forming a thick oxide layer on an upper surface of the substrate in a pattern to define active areas between edges of the thick oxide layer; at each cell site introducing a dopant into a selected portion of an active area to define a first capacitor plate of a second conductivity type extending to a depth below the surface of the substrate; growing a thin oxide layer in the active areas and atop the first capacitor plates; etching a window through the thin oxide layer above each first capacitor plate; growing an ultrathin tunnel oxide layer in each window; forming a conductive layer on the device overlying the oxide layers; and selectively removing portions of the conductive layer leaving portions in place at each cell site to define a second capacitor plate overlying the corresponding first capacitor plate, the second capacitor plate completely covering the ultrathin tunnel oxide layer and extending laterally beyond the edges of the ultrathin tunnel oxide layer to define a shoulder overlying the thin oxide layer, the shoulder completely surrounding the ultrathin tunnel oxide layer; whereby a tunneling capacitor is defined at each cell site by the first and second capacitor plates and the ultrathin tunnel oxide layer therebetween.
Claim 16
Dependent Claim
119 words
The process of claim 12 wherein the conductive layer is a silicided polysilicon layer formed by: depositing a polysilicon layer atop the oxide layers; depositing a tantalum silicide layer onto the polysilicon layer forming the silicided polysilicon layer; anisotrophically etching a pattern through the silicided polysilicon layer and underlying thin oxide layer to expose active area portions; and introducing dopants of the second conductivity type into the exposed portions of the active areas to define transistor source and drain regions; a floating gate transistor being formed at each cell site, the floating gate of the floating -)ate transistor and the second capacitor plate of the tunneling capacitor being extensions from a common unitary portion of the silicided polysilicon layer.
Claim 17
Dependent Claim
54 words
The process of claim 13 wherein the anisotropically etching step etches the thin oxide layer to form a substantially annular shelf of the thin oxide layer conforming to the shape of shoulder of the second capacitor plate, the inner edges of the annular shelf abutting the peripheral edges of the ultrathin tunnel oxide layer.
Claim 18
Dependent Claim
19 words
The process of claim 13 wherein the ultrathin tunnel oxide is grown to be less than 100 Å thick.
Claim 19
Dependent Claim
34 words
The process of claim 15 wherein the ultrathin tunnel oxide is about 65 Å to 70 Å thick and the thin oxide layer is about four times the thickness of the ultrathin tunnel oxide.
Claim 20
Dependent Claim
19 words
The process of claim 12 wherein the first conductivity type is P-type and the second conductivity type is N-type.
Claim 21
Dependent Claim
16 words
The process of claim 12 wherein the thick oxide layer is a LOCOS field oxide layer.
Claim 22
Dependent Claim
17 words
The process of claim 12 wherein the depth of the first capacitor plate is about 0.4 microns.
Claim 23
Dependent Claim
51 words
The process of claim 12 wherein the selective removal of the conductive layer is performed by an anisotropic etching step that defines the edges of the second capacitor plate and cuts through the thin oxide layer to define an annular shelf of thin oxide that surrounds the ultrathin tunnel oxide layer.
Claim 24
Dependent Claim
55 words
The process of claim 20 wherein the anisotropic etching step is followed by an oxide deposition step for forming sidewall oxide spacers at edges of the second capacitor plate, the sidewall oxide spacers having inner edges abutting the vertically aligned edges of the capacitor plate and thin oxide layer cut by the anisotropic etching step.
References Cited (Backward Citations)
US4553314A
Cited
US4553314B1
Cited
US4203158A
Cited
US4203158B1
Cited
US4505027A
Cited
US4640844A
Cited
US5395778A
Cited
US5550072A
Cited
US5576233A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-03-22 | 2002-09-21 | 2003-03-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-03-22 | 2006-09-21 | 2007-03-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-03-22 | 2010-09-21 | 2011-03-23 | $7700.00 | Window Closed / Lapsed |