Dual damascene process using single photoresist process
Assignee: Industrial Technology Research Institute
•
Filing: 1997-10-14
•
Granted: 1999-03-02
•
Expires: 2017-10-14
Abstract
Abstract A simplified method is disclosed for forming dual damascene patterns using a single photoresist process. A substrate is provided with a tri-layer of insulation formed thereon. A layer of photoresist is formed on the substrate and is imaged with a hole pattern by exposure through a dark field mask. Hole is formed in the photoresist by a wet etch. As a key step, the photoresist is next subjected to post-exposure bake such that the sensitivity of the photoresist is still retained. The same photoresist layer is then exposed for the second time for aligned line patterning using a "clear-field" mask. The line patterned region is cross-linked by performing pre-silylation bake, which region in turn is not affected by the subsequent silylation process that forms a silicon rich mask in the field surrounding the hole and line patterns. The vertical hole is transferred into the middle layer of the underlying composite layer by dry etching. Twine pattern which is next formed in the same photoresist layer is transferred into the top layer of the composite layer while at the same time the hole pattern is transferred to the bottom layer. Having thus formed the vertical hole interconnect and line trench into the insulation layer, metal is deposited into the dual damascene pattern. Any excess metal on the surface of the insulating layer is then removed by any number of ways including chemical-mechanical polishing, thereby planarizing the surface and readying it for the next semiconductor process.
Inventors
- 👤 Chang-Ming Dai
- 👤 Jammy Chin-Ming Huang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:40
CPC Classifications
H; H10; H10P; H10P76/00; H10P76/20; H10P76/204; H10P76/2041; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/081; H10W20/084; H10W20/088; H10W20/0882
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
316 words
A method of forming a dual damascene pattern employing a single photoresist layer comprising the steps of: providing a substrate having a composite layer of insulation deposited thereon whereby said composite layer comprises a first layer of dielectric separated from a second layer of dielectric by an intervening intermediate layer of dielectric; forming a layer of photoresist on said composite layer of dielectric insulation; hole patterning said layer of photoresist by exposing said photoresist using a dark field photo mask; post-exposure baking of said layer of photoresist; performing a wet development of said layer of photoresist; line patterning said layer of photoresist by exposing said photoresist using a clear field photo mask; performing a pre-silylation bake of said layer of photoresist; treating a surface portion of said layer of photoresist with a silylation process thereby forming a silylated layer of silylation regions in said layer of photoresist; etching said second layer of dielectric underlying said layer of photoresist using said silylated layer of said layer of photoresist as a mask thereby transferring said hole pattern in said layer of photoresist into said second layer of dielectric; etching said intermediate layer of dielectric underlying said second layer of dielectric using said silylated layer of said layer of photoresist as a mask thereby transferring said hole pattern in said layer of photoresist into said intermediate layer of dielectric; etching said layer of photoresist to form said line pattern adjacent to said silylated layer in said layer of photoresist; etching said composite layer of insulation thereby transferring said line pattern in said layer of photoresist into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form a contact hole; removing said layer of photoresist; and depositing metal into said trench and said hole to form a dual damascene structure.
Claim 2
Independent Claim
316 words
A method of forming a dual damascene pattern employing a single photoresist layer comprising the steps of: providing a substrate having a composite layer of insulation deposited thereon whereby said composite layer comprises a first layer of dielectric separated from a second layer of dielectric by an intervening intermediate layer of dielectric; forming a layer of photoresist on said composite layer of dielectric insulation; hole patterning said layer of photoresist by exposing said photoresist using a dark field photo mask; post-exposure baking of said layer of photoresist; performing a wet development of said layer of photoresist; line patterning said layer of photoresist by exposing said photoresist using a clear field photo mask; performing a pre-silylation bake of said layer of photoresist; treating a surface portion of said layer of photoresist with a silylation process thereby forming a silylated layer of silylation regions in said layer of photoresist; etching said second layer of dielectric underlying said layer of photoresist using said silylated layer of said layer of photoresist as a mask thereby transferring said hole pattern in said layer of photoresist into said second layer of dielectric; etching said intermediate layer of dielectric underlying said second layer of dielectric using said silylated layer of said layer of photoresist as a mask thereby transferring said hole pattern in said layer of photoresist into said intermediate layer of dielectric; etching said layer of photoresist to form said line pattern adjacent to said silylated layer in said layer of photoresist; etching said composite layer of insulation thereby transferring said line pattern in said layer of photoresist into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form a contact hole; removing said layer of photoresist; and depositing metal into said trench and said hole to form a dual damascene structure.
Claim 3
Dependent Claim
19 words
The method of claim 1, wherein said composite layer of insulation is planarized by means of chemical-mechanical polishing (CMP).
Claim 4
Dependent Claim
29 words
The method of claim 1, wherein said first layer of dielectric of said composite layer is phosphosilicate glass (PSG) having a thickness between about 0.3 to 0.7 micrometers (μm).
Claim 5
Dependent Claim
39 words
The method of claim 3, wherein said hole patterning is accomplished by decomposing said PAG component in light exposed field areas adjacent to said hole pattern in said layer of photoresist exposed by said exposing through said photo mask.
Claim 6
Dependent Claim
39 words
The method of claim 3, wherein said line patterning is accomplished by decomposing said PAG component in light exposed field areas adjacent to said hole pattern in said layer of photoresist exposed by said exposing through said photo mask.
Claim 7
Dependent Claim
25 words
The method of claim 1, wherein said intermediate layer of dielectric is silicon nitride (SiN) having a thickness between about 500 to 2000 angstroms (Å).
Claim 8
Dependent Claim
29 words
The method of claim 1, wherein said second layer of dielectric of said composite layer is phosphosilicate glass (PSG) having a thickness between about 0.3 to 0.7 micrometers (μm).
Claim 9
Dependent Claim
19 words
The method of claim 1, wherein said layer of photoresist has a thickness between about 0.50 to 0.90 μm.
Claim 10
Dependent Claim
24 words
The method of claim 1, wherein said layer of photoresist is a positive chemical amplification resist (CAR) having a photo acid generator (PAG) component.
Claim 11
Dependent Claim
25 words
The method of claim 1, wherein said post-exposure baking of said layer of photoresist is accomplished at a temperature between about 80° to 100° C.
Claim 12
Dependent Claim
34 words
The method of claim 1, wherein said wet development of said layer of photoresist is accomplished with a recipe comprising stream puddle with developer TMAH at 2.38%, for a about 45 to 70 seconds.
Claim 13
Dependent Claim
20 words
The method of claim 1, wherein said pre-silylation bake is performed at a temperature between about 130° to 180° C.
Claim 14
Dependent Claim
23 words
The method of claim 1, wherein said silylation process is performed with tetra-methyl-di-silazane (TMDS) at a temperature between about 140° to 210° C.
Claim 15
Dependent Claim
18 words
The method of claim 1, wherein said silylated layer has a thickness between about 1,000 to 4,000 Å.
Claim 16
Dependent Claim
81 words
The method of claim 1, wherein said etching said second layer of dielectric underlying said layer of photoresist using said silylated layer of said layer of photoresist as a mask thereby transferring said hole pattern in said layer of photoresist into said second layer of dielectric is accomplished in a HDP etcher with etch recipe comprising Ar, CHF 3 , C 4 F 8 at flow rates between about 50 to 150, 10 to 150 and 0 to 20 sccm, respectively.
Claim 17
Dependent Claim
83 words
The method of claim 1, wherein said etching said intermediate layer of dielectric underlying said second layer of dielectric using said silylated layer of said layer of photoresist as a mask thereby transferring said hole pattern in said layer of photoresist into said intermediate layer of dielectric is accomplished in a HDP nitride etcher with etch recipe comprising Ar, CHF 3 , C 4 F 8 at flow rates between about 50 to 150, 10 to 150 and 0 to 20 sccm, respectively.
Claim 18
Dependent Claim
67 words
The method of claim 1, wherein said etching said layer of photoresist to form said line pattern adjacent to said silylated layer in said layer of photoresist is accomplished in a resist HDP etcher with etch recipe comprising O 2 , He, SO 2 and CF 4 at flow rates between about 10 to 250, 40 to 80, 10 to 80 and 0 to 50 sccm, respectively.
Claim 19
Dependent Claim
92 words
The method of claim 1, wherein etching said composite layer of insulation thereby transferring said line pattern in said layer of photoresist into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form a contact hole is accomplished in an oxide HDP etcher with etch recipe comprising Ar, CHF 3 , C 4 F 8 at flow rates between about 50 to 150, 10 to 150 and 0 to 20 sccm, respectively.
Claim 20
Dependent Claim
37 words
The method of claim 1, wherein said removing said layer of photoresist is accomplished with oxygen plasma ashing followed by wet strip using H 2 SO 4 , H 2 O 2 and NH 4 OH solutions.
Claim 21
Dependent Claim
20 words
The method of claim 1, wherein said metal deposited to form a dual damascene structure is copper or aluminum-copper alloy.
Claim 22
Independent Claim
209 words
A method of forming a dual damascene pattern employing a single photoresist layer comprising the steps of: providing a substrate having a composite layer of insulation deposited thereon whereby said composite layer comprises a top layer of dielectric separated from a bottom layer of dielectric by an intervening intermediate layer of dielectric; forming a layer of photoresist on said composite layer; hole patterning said first layer of photoresist; post-exposure baking of said layer of photoresist; superimposing a line patterning on said hole patterning in said layer of photoresist; performing a pre-silylation bake of said layer of photoresist; silylating said layer of photoresist to form a silylated mask comprising said hole pattern; transferring said hole pattern in said silylated layer into said intermediate layer of said composite layer of insulation by etching; forming line pattern in said layer of photoresist by etching; transferring said line pattern in said layer of photoresist into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form a interconnect hole; removing said layer of photoresist; and depositing metal into said trench and said hole to form a dual damascene structure and planarizing said composite layer.
Claim 23
Independent Claim
209 words
A method of forming a dual damascene pattern employing a single photoresist layer comprising the steps of: providing a substrate having a composite layer of insulation deposited thereon whereby said composite layer comprises a top layer of dielectric separated from a bottom layer of dielectric by an intervening intermediate layer of dielectric; forming a layer of photoresist on said composite layer; hole patterning said first layer of photoresist; post-exposure baking of said layer of photoresist; superimposing a line patterning on said hole patterning in said layer of photoresist; performing a pre-silylation bake of said layer of photoresist; silylating said layer of photoresist to form a silylated mask comprising said hole pattern; transferring said hole pattern in said silylated layer into said intermediate layer of said composite layer of insulation by etching; forming line pattern in said layer of photoresist by etching; transferring said line pattern in said layer of photoresist into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form a interconnect hole; removing said layer of photoresist; and depositing metal into said trench and said hole to form a dual damascene structure and planarizing said composite layer.
Claim 24
Dependent Claim
28 words
The method of claim 21, wherein said intermediate layer of said composite layer of insulation is silicon nitride with a thickness between about 500 to 2000 angstroms (Å).
Claim 25
Dependent Claim
23 words
The method of claim 21, wherein said layer of photoresist is P-type chemical amplification resist (CAR) having a photo acid generator (PAG) agent.
Claim 26
Dependent Claim
25 words
The method of claim 21, wherein said post-exposure baking of said layer of photoresist is accomplished at a temperature between about 80° to 100° C.
Claim 27
Dependent Claim
20 words
The method of claim 21, wherein said pre-silylation bake is performed at a temperature between about 130° to 180° C.
Claim 28
Dependent Claim
22 words
The method of claim 21, wherein said silylating is accomplished with tetra-methyl-di-silazane (TMDS) at a temperature between about 140° to 210° C.
Claim 29
Dependent Claim
18 words
The method of claim 21, wherein said silylated mask has a thickness between about 1000 to 4000 Å.
Claim 30
Dependent Claim
86 words
The method of claim 21, wherein said transferring said line pattern in said layer of photoresist into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form a interconnect hole is accomplished in an oxide HDP etcher with etch recipe comprising Ar, CHF 3 , C 4 F 8 at flow rates between about 50 to 150, 10 to 150 and 0 to 20 sccm, respectively.
Claim 31
Dependent Claim
20 words
The method of claim 21, wherein said metal deposited to form a dual damascene structure is copper or aluminum-copper alloy.
References Cited (Backward Citations)
US5427649A
Cited
US5529953A
Cited
US5614765A
Cited
US5705430A
Cited
US5795823A
Cited
US5602053A
Cited
US5814557A
Cited
US5726100A
Cited
US5783485A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-03-01 | 2002-08-31 | 2003-03-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-03-01 | 2006-08-31 | 2007-03-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-03-01 | 2010-08-31 | 2011-03-02 | $7700.00 | Window Closed / Lapsed |