Abstract
Abstract PCT No. PCT/GB94/01654 Sec. 371 Date Aug. 22, 1996 Sec. 102(e) Date Aug. 22, 1996 PCT Filed Jul. 29, 1994 PCT Pub. No. WO95/04168 PCT Pub. Date Feb. 9, 1995A method of depositing a Group IIIA metal layer of high purity on a substrate comprises pyrolyzing contacting the substrate with a tritertiary butyl compound of the Group IIIA metal and pyrolyzing the compound to leave the Group IIIA metal deposited on the substrate. The method of the invention may be used on any suitable substrate, such as silicon or polyimide. The method of the invention may be used for the growth of Group IIIA/silicon alloys as well as for depositing semi-conducting III-V alloys such as, for example, AlGaAs, AlInAs and AlSb.
Inventors
- 👤 Anthony Copland Jones
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:37
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/02; C23C18/08; C23C18/10; C22; C22C; C22C21/00; C23C16/00; C23C16/06; C23C16/18; C23C16/20
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
51 words
A method of depositing an aluminum or indium film on a substrate comprising the steps of contacting the substrate with an aluminum or indium precursor and treating the precursor to decompose leaving the aluminum or indium deposited in the substrate, wherein the precursor is the tritertiarybutyl compound of aluminum or indium.
Claim 2
Independent Claim
51 words
A method of depositing an aluminum or indium film on a substrate comprising the steps of contacting the substrate with an aluminum or indium precursor and treating the precursor to decompose leaving the aluminum or indium deposited in the substrate, wherein the precursor is the tritertiarybutyl compound of aluminum or indium.
Claim 3
Dependent Claim
25 words
A method as claimed in claim 1, wherein the precursor is delivered to the substrate as a vapour phase and is pyrolyzed on the substrate.
Claim 4
Dependent Claim
26 words
A method as claimed in claim 1, wherein the precursor is in liquid form and the substrate is coated therewith before heating to pyrolyze the precursor.
Claim 5
Dependent Claim
35 words
A method as claimed in claim 1, wherein said contacting step comprises coating the substrate with the precursor, and wherein said treating step comprises heating the coated substrate to pyrolyze the coating onto the substrate.
Claim 6
Dependent Claim
29 words
A method as claimed in claim 4, wherein said heating step is effective to heat the substrate to a temperature of between about 150° C. and about 300° C.
Claim 7
Dependent Claim
14 words
A method as claimed in claim 1, wherein the substrate is silicon or polyamide.
Claim 8
Dependent Claim
29 words
A method as claimed in claim 1, wherein an aluminium/silicon or indium/silicon alloy is formed by treatment of the precursor with a silicon precursor also deposited on the substrate.
Claim 9
Dependent Claim
15 words
A method as claimed in claim 7, wherein the silicon precursor is SiH 4 .
Claim 10
Dependent Claim
34 words
A method as claimed in claim 1, wherein said treating step produces a Group III/V alloy by treatment of the aluminium or indium precursor with a Group V precursor also deposited on the substrate.
Claim 11
Dependent Claim
18 words
A method as claimed in claim 9, wherein the alloy produced is selected from AlGaAs, AlInAs and Alsb.
Claim 12
Dependent Claim
51 words
A composition of matter comprising a substrate having an aluminium or indium layer deposited thereon by contacting the substrate with an aluminium or indium precursor and treating the precursor to decompose leaving the aluminium or indium deposited on the substrate, wherein the precursor is the tritertiarybutyl compound of aluminium or indium.
Claim 13
Dependent Claim
51 words
A composition of matter comprising a substrate having an aluminium or indium layer deposited thereon by contacting the substrate with an aluminium or indium precursor and treating the precursor to decompose leaving the aluminium or indium deposited on the substrate, wherein the precursor is the tritertiarybutyl compound of aluminium or indium.
References Cited (Backward Citations)
GB1320098A
Cited
US4328261A
Cited
US4923717A
Cited
US5151305A
Cited
US5376409A
Cited
US5376409B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-01-25 | 2002-07-27 | 2003-01-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-01-25 | 2006-07-27 | 2007-01-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-01-25 | 2010-07-27 | 2011-01-26 | $7700.00 | Window Closed / Lapsed |