Abstract
Abstract A method for making multilevel electrical interconnections having a planar intermetal dielectric (IMD) with low dielectric constant k and good thermal conductivity was achieved. The method involves patterning an electrically conductive layer to form metal lines on which is deposited an anisotropic plasma oxide (APO) resulting in a thin oxide on the sidewalls of the metal lines and a much thicker oxide on top of the lines. A low dielectric constant (k) polymer is deposited and the polymer and APO are chem/mech polished back to the top of the metal lines. A fluorine-doped silicon oxide (FSG) is deposited, and via holes are etched to provide electrical connections for the next level of interconnections. The APO provides wider openings between metal lines filled with the low k dielectric polymer thereby reducing the RC time delay of the circuit. The thick top APO provides more processing latitude for polishing back the APO and low k polymer. The FSG provides a lower dielectric constant k for further reducing the RC delay and a better thermal conductivity constant K for minimizing the Joule heating when the circuit is powered up. The process can be repeated several times to form a planar multilevel interconnection for completing wiring on the integrated circuit.
Inventors
- 👤 Lai-Juh Chen
- 👤 Chien-Mei Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:53
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/68; H10P14/683; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10P14/6342; H10P14/66; H10P14/662; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; H10P14/6922; H10P14/6924; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/074; H10W20/077; H10W20/40; H10W20/45; H10W20/48
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
189 words
A method for fabricating multilevel metal interconnections having low dielectric constant insulators on a substrate comprising the steps of: a. providing a semiconductor substrate having semiconductor devices having contacts protected by a barrier layer; b. depositing a first conductive layer for-contacting regions of said devices; c. patterning said first conductive layer to form interconnections for said devices; d. depositing an anisotropic plasma oxide over said patterned first conductive layer, said anisotropic plasma oxide being thicker on the top surface than on the sidewalls of said patterned conductive layer; e. depositing a low dielectric constant insulator on said anisotropic plasma oxide; f. planarizing said low dielectric constant insulator down to and further planarizing into said anisotropic plasma oxide by chemical/mechanical polishing to said top surface of said patterned first conductive layer; g. depositing a fluorine-doped oxide on said low dielectric insulator on said patterned first conductive layer; h. forming via holes in said fluorine-doped oxide to said patterned first conductive layer; i. depositing a second conductive layer on said fluorine-doped oxide and in said via holes; j. patterning said second conductive layer to form a second level of metal interconnections.
Claim 2
Independent Claim
189 words
A method for fabricating multilevel metal interconnections having low dielectric constant insulators on a substrate comprising the steps of: a. providing a semiconductor substrate having semiconductor devices having contacts protected by a barrier layer; b. depositing a first conductive layer for-contacting regions of said devices; c. patterning said first conductive layer to form interconnections for said devices; d. depositing an anisotropic plasma oxide over said patterned first conductive layer, said anisotropic plasma oxide being thicker on the top surface than on the sidewalls of said patterned conductive layer; e. depositing a low dielectric constant insulator on said anisotropic plasma oxide; f. planarizing said low dielectric constant insulator down to and further planarizing into said anisotropic plasma oxide by chemical/mechanical polishing to said top surface of said patterned first conductive layer; g. depositing a fluorine-doped oxide on said low dielectric insulator on said patterned first conductive layer; h. forming via holes in said fluorine-doped oxide to said patterned first conductive layer; i. depositing a second conductive layer on said fluorine-doped oxide and in said via holes; j. patterning said second conductive layer to form a second level of metal interconnections.
Claim 3
Dependent Claim
24 words
The method of claim 1, wherein said barrier layer is composed of titanium/titanium nitride and prevents aluminum from penetrating said devices having said contacts.
Claim 4
Dependent Claim
11 words
The method of claim 1, wherein said conductive layer is aluminum.
Claim 5
Dependent Claim
35 words
The method of claim 1, wherein said anisotropic plasma oxide is a silicon oxide deposited by plasma-enhanced chemical vapor deposition at a temperature of between about 375° and 425° C. using tetraethosiloxane (TEOS) and oxygen.
Claim 6
Dependent Claim
54 words
The method of claim 1, wherein said anisotropic plasma oxide is deposited to a thickness of between about 1000 and 5000 Angstroms on top surface of said patterned conductive layer, resulting in a respective thickness of said anisotropic oxide on the sidewalls of said patterned conductive layer of between about 170 and 850 Angstroms.
Claim 7
Dependent Claim
26 words
The method of claim 1, wherein said low dielectric constant insulating layer is an organic material having a dielectric constant of between about 1.9 and 3.7.
Claim 8
Dependent Claim
33 words
The method of claim 6, wherein said organic material is comprised of a polymer selected from a group consisting of polyimide, polysilsequioxane, benzocyclobutene (BCB), parylene N, fluorinated polyimide, parylene F, and amorphous Teflon.
Claim 9
Dependent Claim
27 words
The method of claim 1, wherein said low dielectric constant insulating layer is deposited to a thickness sufficient to fill the openings in said patterned conductive layer.
Claim 10
Dependent Claim
28 words
The method of claim 1, wherein said fluorine-doped oxide is a silicon oxide deposited by chemical vapor deposition to a thickness of between about 2000 and 10000 Angstroms.
Claim 11
Dependent Claim
31 words
The method of claim 1, wherein said fluorine-doped oxide has a fluorine concentration of between about 2 and 8 atomic percent and a dielectric constant of between about 3.8 and 3.1.
Claim 12
Independent Claim
184 words
A method for fabricating multilevel metal interconnections having low dielectric constant insulators on a substrate comprising the steps of: a. providing a semiconductor substrate having semiconductor devices having contacts protected by a barrier layer; b. depositing a conductive layer for contacting regions of said devices; c. patterning said conductive layer to form interconnections for said devices; d. depositing an anisotropic plasma oxide over said patterned conductive layer, said anisotropic plasma oxide being thicker on the top surface than on the sidewalls of said patterned conductive layer; e. depositing a low dielectric constant insulator on said anisotropic plasma oxide; f. planarizing said low dielectric constant insulator down to and further planarizing into said anisotropic plasma oxide by chemical/mechanical polishing to said top surface of said patterned conductive layer; g. depositing a fluorine-doped oxide on said low dielectric insulator on said patterned conductive layer; h. forming via holes in said fluorine-doped oxide to said patterned conductive layer; i. performing elements b. through h. n times, where n is the number of said patterned conductive layers required to complete said multilevel metal interconnections on an integrated circuit.
Claim 13
Independent Claim
184 words
A method for fabricating multilevel metal interconnections having low dielectric constant insulators on a substrate comprising the steps of: a. providing a semiconductor substrate having semiconductor devices having contacts protected by a barrier layer; b. depositing a conductive layer for contacting regions of said devices; c. patterning said conductive layer to form interconnections for said devices; d. depositing an anisotropic plasma oxide over said patterned conductive layer, said anisotropic plasma oxide being thicker on the top surface than on the sidewalls of said patterned conductive layer; e. depositing a low dielectric constant insulator on said anisotropic plasma oxide; f. planarizing said low dielectric constant insulator down to and further planarizing into said anisotropic plasma oxide by chemical/mechanical polishing to said top surface of said patterned conductive layer; g. depositing a fluorine-doped oxide on said low dielectric insulator on said patterned conductive layer; h. forming via holes in said fluorine-doped oxide to said patterned conductive layer; i. performing elements b. through h. n times, where n is the number of said patterned conductive layers required to complete said multilevel metal interconnections on an integrated circuit.
Claim 14
Dependent Claim
24 words
The method of claim 11, wherein said barrier layer is composed of titanium/titanium nitride and prevents aluminum from penetrating said devices having said contacts.
Claim 15
Dependent Claim
11 words
The method of claim 11, wherein said conductive layer is aluminum.
Claim 16
Dependent Claim
36 words
The method of claim 11, wherein said anisotropic plasma oxide is a silicon oxide deposited by plasma enhanced chemical vapor deposition at a temperature of between about 375° and 425° C. using tetraethosiloxane (TEOS) and oxygen.
Claim 17
Dependent Claim
54 words
The method of claim 11, wherein said anisotropic plasma oxide is deposited to a thickness of between about 1000 and 5000 Angstroms on top surface of said patterned conductive layer, resulting in a respective thickness of said anisotropic oxide on the sidewalls of said patterned conductive layer of between about 170 and 850 Angstroms.
Claim 18
Dependent Claim
26 words
The method of claim 11, wherein said low dielectric constant insulating layer is an organic material having a dielectric constant of between about 1.9 and 3.7.
Claim 19
Dependent Claim
33 words
The method of claim 16, wherein said organic material is comprised of a polymer selected from a group consisting of polyimide, polysilsequioxane, benzocyclobutene (BCB), parylene N, fluorinated polyimide, parylene F, and amorphous Teflon.
Claim 20
Dependent Claim
27 words
The method of claim 11, wherein said low dielectric constant insulating layer is deposited to a thickness sufficient to fill the openings in said patterned conductive layer.
Claim 21
Dependent Claim
28 words
The method of claim 11, wherein said fluorine-doped oxide is a silicon oxide deposited by chemical vapor deposition to a thickness of between about 2000 and 10000 Angstroms.
Claim 22
Dependent Claim
31 words
The method of claim 11, wherein said fluorine-doped oxide has a fluorine concentration of between about 2 and 8 atomic percent and a dielectric constant of between about 3.8 and 3.1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-01-11 | 2002-07-13 | 2003-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-01-11 | 2006-07-13 | 2007-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-01-11 | 2010-07-13 | 2011-01-12 | $7700.00 | Window Closed / Lapsed |