Electroless copper plating

Claim 2

A process for electroless copper coating on a substrate, comprising the steps of: cleaning the substrate alkaline cleaning and conditioning for a dwell time of about 4.5 to 5.5 minutes; rinsing with Reverse Osmosis water; preconditioning said substrate in a stannous chloride solution from about 0.75 to about 1.5 minutes; treating with a tin-palladium colloid; postactivating with a solution to remove tin from the tin-palladium colloid from about 2.75 to about 3.25 minutes; and applying electroless copper in solution, which solution has been used less than about one week.

Claim 3

The process as claimed in claim 1 comprising the additional step of: microetching from about 55 to about 65 seconds subsequent to the step of rinsing with reverse osmosis water and prior to the step of preconditioning in a stannous chloride solution.

Claim 4

A process for optimizing an electroless copper coating process so as to maximize overall adhesion and coverage of the electroless copper onto a substrate, wherein the electroless copper coating process comprises the steps of: initial abrasive cleaning the substrate, alcohol rinsing the substrate, immersing the substrate in an alkaline cleaning and conditioning solution, rinsing the substrate with reverse osmosis water, immersing the substrate in a preconditioning solution of stannous chloride, treating the substrate with a tin-palladium colloid, immersing the substrate in a postactivating solution to remove tin from the tin-palladium colloid, and applying electroless copper in solution; the optimizing process comprising the steps of: adjusting the time in which the substrate is in the alkaline cleaning and conditioning solution so as to maximize adhesion and coverage of the resulting electroless copper on a substrate; adjusting the time in which the substrate is in the postactivating solution so as to maximize adhesion and coverage of the resulting electroless copper on a substrate; and adjusting the age of the electroless copper bath so as to maximize adhesion and coverage of the resulting electroless copper on a substrate.

Claim 5

A process for optimizing an electroless copper coating process so as to maximize overall adhesion and coverage of the electroless copper onto a substrate, wherein the electroless copper coating process comprises the steps of: initial abrasive cleaning the substrate, alcohol rinsing the substrate, immersing the substrate in an alkaline cleaning and conditioning solution, rinsing the substrate with reverse osmosis water, immersing the substrate in a preconditioning solution of stannous chloride, treating the substrate with a tin-palladium colloid, immersing the substrate in a postactivating solution to remove tin from the tin-palladium colloid, and applying electroless copper in solution; the optimizing process comprising the steps of: adjusting the time in which the substrate is in the alkaline cleaning and conditioning solution so as to maximize adhesion and coverage of the resulting electroless copper on a substrate; adjusting the time in which the substrate is in the postactivating solution so as to maximize adhesion and coverage of the resulting electroless copper on a substrate; and adjusting the age of the electroless copper bath so as to maximize adhesion and coverage of the resulting electroless copper on a substrate.