Method for producing semiconductor device
Assignee: Semiconductor Energy Laboratory Co Ltd
•
Filing: 1995-06-29
•
Granted: 1998-12-01
•
Expires: 2015-06-29
Abstract
Abstract A metal element density is lowered in a crystalline silicon film obtained by four hour treatment at about 550° C. by using a catalyst metal which accelerates crystallization. At the same time, a crystalline silicon film can be obtained which has a high crystallinity. For this purpose, extremely oxide film 13 is formed on an amorphous silicon film formed on this glass substrate in the beginning. An aqueous solution of acetate added with 10 to 200 ppm (need adjustment) of catalyst element like nickel or the like is dripped. This state is held for a predetermined time. Then the spin drying is performed by using a spinner. The film is crystallized by four hour treatment at 550° C. Then a localized nickel component is removed by the fluoric acid treatment. Further, the crystalline silicon film is obtained by laser light irradiation. Then a crystalline silicon film is obtained having a low density of metal element and a small defect density by four hour heat treatment at 550° C.
Inventors
- 👤 Hisashi Ohtani
- 👤 Takeshi Fukunaga
- 👤 Akiharu Miyanaga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 10:51
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/38; H10P14/3802; H10P14/3808; H10P14/3816; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3806
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
84 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; disposing a catalyst material in contact with said semiconductor film, said catalyst material being capable of promoting crystallization of said semiconductor film; heating said semiconductor film provided with said catalyst material so that said semiconductor film is crystallized throughout its thickness; removing said catalyst material from said semiconductor film after said heating step; and then irradiating said semiconductor film with laser light or intense light.
Claim 2
Independent Claim
84 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; disposing a catalyst material in contact with said semiconductor film, said catalyst material being capable of promoting crystallization of said semiconductor film; heating said semiconductor film provided with said catalyst material so that said semiconductor film is crystallized throughout its thickness; removing said catalyst material from said semiconductor film after said heating step; and then irradiating said semiconductor film with laser light or intense light.
Claim 3
Dependent Claim
33 words
A method according to claim 1 wherein said catalyst material includes at least one selected from the group consisting of Fe, Co, Ni, Ru, Rh, Pd, Os, Ir, Pt, Cu, Ag and Au.
Claim 4
Dependent Claim
26 words
A method according to claim 1 wherein said catalyst material removing step comprises a process of etching said semiconductor film using an etchant containing hydrofluoric acid.
Claim 5
Dependent Claim
27 words
A method according to claim 3 wherein said catalyst material is removed from portions where said catalyst material is contained at a higher concentration than other portions.
Claim 6
Dependent Claim
25 words
A method according to claim 1 wherein said catalyst material comprises an invasive type atom which diffuses into said semiconductor film during said heating process.
Claim 7
Independent Claim
99 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; disposing a catalyst material in contact with said semiconductor film, said catalyst material being capable of promoting crystallization of said semiconductor film; heating said semiconductor film provided with said catalyst material so that said semiconductor film is crystallized throughout its thickness; removing said catalyst material from said semiconductor film after the step of heating; heating said semiconductor film after said removing step; and then patterning said semiconductor film in order to form an active layer of a thin film transistor.
Claim 8
Independent Claim
99 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; disposing a catalyst material in contact with said semiconductor film, said catalyst material being capable of promoting crystallization of said semiconductor film; heating said semiconductor film provided with said catalyst material so that said semiconductor film is crystallized throughout its thickness; removing said catalyst material from said semiconductor film after the step of heating; heating said semiconductor film after said removing step; and then patterning said semiconductor film in order to form an active layer of a thin film transistor.
Claim 9
Dependent Claim
33 words
A method according to claim 6 wherein said catalyst material includes at least one selected from the group consisting of Fe, Co, Ni, Ru, Rh, Pd, Os, Ir, Pt, Cu, Ag and Au.
Claim 10
Dependent Claim
26 words
A method according to claim 6 wherein said catalyst material removing step comprises a process of etching said semiconductor film using an etchant containing hydrofluoric acid.
Claim 11
Dependent Claim
27 words
A method according to claim 8 wherein said catalyst material is removed from portions where said catalyst material is contained at a higher concentration than other portions.
Claim 12
Independent Claim
113 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; disposing a catalyst material in contact with said semiconductor film, said catalyst material being capable of promoting crystallization of said semiconductor film; heating said semiconductor film provided with said catalyst material so that said semiconductor film is crystallized throughout its thickness; removing said catalyst material from said semiconductor film after the heating step; irradiating said semiconductor film with laser light or intense light after the step of removing; heating said semiconductor film after said removing step; and then patterning said semiconductor film in order to form an active layer of a thin film transistor.
Claim 13
Independent Claim
113 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; disposing a catalyst material in contact with said semiconductor film, said catalyst material being capable of promoting crystallization of said semiconductor film; heating said semiconductor film provided with said catalyst material so that said semiconductor film is crystallized throughout its thickness; removing said catalyst material from said semiconductor film after the heating step; irradiating said semiconductor film with laser light or intense light after the step of removing; heating said semiconductor film after said removing step; and then patterning said semiconductor film in order to form an active layer of a thin film transistor.
Claim 14
Dependent Claim
33 words
A method according to claim 10 wherein said catalyst material includes at least one selected from the group consisting of Fe, Co, Ni, Ru, Rh, Pd, Os, Ir, Pt, Cu, Ag and Au.
Claim 15
Dependent Claim
26 words
A method according to claim 10 wherein said catalyst material removing step comprises a process of etching said semiconductor film using an etchant containing hydrofluoric acid.
Claim 16
Dependent Claim
27 words
A method according to claim 12 wherein said catalyst material is removed from portions where said catalyst material is contained at a higher concentration than other portions.
Claim 17
Independent Claim
89 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; introducing a metal element being capable of promoting crystallization of silicon into said semiconductor film; heating said semiconductor film introduced with said metal element so that said semiconductor film is crystallized throughout its thickness; removing said metal element from said crystallized semiconductor film; and then irradiating said crystallized semiconductor film with laser light or intense light, wherein said heating step and said irradiating step are repeated at least two times.
Claim 18
Independent Claim
89 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; introducing a metal element being capable of promoting crystallization of silicon into said semiconductor film; heating said semiconductor film introduced with said metal element so that said semiconductor film is crystallized throughout its thickness; removing said metal element from said crystallized semiconductor film; and then irradiating said crystallized semiconductor film with laser light or intense light, wherein said heating step and said irradiating step are repeated at least two times.
Claim 19
Independent Claim
109 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; disposing a catalyst material in contact with said semiconductor film, said catalyst material being capable of promoting crystallization of said semiconductor film; heating said semiconductor film provided with said catalyst material in order to crystallize said semiconductor film throughout its thickness; removing said catalyst material from said semiconductor film after the step of crystallizing; and then irradiating said semiconductor film with laser light or intense light, wherein said laser light or said intense light is irradiated a plurality of times, and an energy density in said light is gradually increased.
Claim 20
Independent Claim
109 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; disposing a catalyst material in contact with said semiconductor film, said catalyst material being capable of promoting crystallization of said semiconductor film; heating said semiconductor film provided with said catalyst material in order to crystallize said semiconductor film throughout its thickness; removing said catalyst material from said semiconductor film after the step of crystallizing; and then irradiating said semiconductor film with laser light or intense light, wherein said laser light or said intense light is irradiated a plurality of times, and an energy density in said light is gradually increased.
Claim 21
Dependent Claim
24 words
A method according to claim 15 wherein said laser light or intense light is irradiated in an atmosphere including oxygen or in an air.
Claim 22
Independent Claim
109 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; disposing a catalyst material in contact with said semiconductor film, said catalyst material being capable of promoting crystallization of said semiconductor film; heating said semiconductor film provided with said catalyst material to obtain a crystalline semiconductor film crystallized throughout its thickness after the disposing step; removing the catalyst material from the crystalline semiconductor film after said heating step; and irradiating the crystalline semiconductor film with laser light or intense light after the removing step, wherein said step of heating is performed at 450° to 600° C. for about four hours.
Claim 23
Independent Claim
109 words
A method for producing a semiconductor device comprising the steps of: forming a semiconductor film on an insulating surface; disposing a catalyst material in contact with said semiconductor film, said catalyst material being capable of promoting crystallization of said semiconductor film; heating said semiconductor film provided with said catalyst material to obtain a crystalline semiconductor film crystallized throughout its thickness after the disposing step; removing the catalyst material from the crystalline semiconductor film after said heating step; and irradiating the crystalline semiconductor film with laser light or intense light after the removing step, wherein said step of heating is performed at 450° to 600° C. for about four hours.
Claim 24
Dependent Claim
33 words
A method according to claim 17 wherein said catalyst material includes at least one selected from the group consisting of Fe, Co, Ni, Ru, Rh, Pd, Os, Ir, Pt, Cu, Ag and Au.
Claim 25
Dependent Claim
24 words
A method according to claim 17 wherein said removing step comprises a step of etching said semiconductor film using an etchant containing hydrofluoric acid.
References Cited (Backward Citations)
US5147826A
Cited
US5219786A
Cited
US5608232A
Cited
US5275851A
Cited
US5426064A
Cited
US5366926A
Cited
US5550070A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-11-30 | 2002-06-01 | 2002-12-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-11-30 | 2006-06-01 | 2006-12-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-11-30 | 2010-06-01 | 2010-12-01 | $7700.00 | Window Closed / Lapsed |