US5366926A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Low temperature process for laser dehydrogenation and crystallization of amorphous silicon
Assignee: Thomson Licensing SAS
•
Filing: 1993-06-07
•
Granted: 1994-11-22
•
Expires: 2013-06-07
Abstract
Abstract A low temperature process for dehydrogenating amorphous silicon using lasers. Dehydrogenation occurs by irradiating one or more areas of a hydrogenated amorphous silicon layer with laser beam pulses at a relatively low energy density. After the multiple laser pulse irradiation at a relatively low energy density, the laser energy density is increased and multiple irradiation at a higher energy density is performed. If after the multiple irradiation at the higher energy density the amorphous silicon hydrogen content is still too high, dehydrogenation proceeds by multiple irradiations at a yet higher energy density. The irradiation at the various energy densities can result in the formation of polysilicon due to melting of the amorphous silicon layer. As irradiation may be selectively applied to the amorphous silicon, an integral amorphous silicon-polysilicon structure may be formed.
Inventors
- 👤 Ping Mei
- 👤 James B. Boyce
- 👤 Richard I. Johnson
- 👤 Michael G. Hack
- 👤 Rene A. Lujan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:24
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/29; H10P14/2901; H10P14/2922; H10P14/32; H10P14/3202; H10P14/3238; H10P14/3241; H10P14/3242; H10P14/3244; H10P14/3251; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3451; H10P14/3452; H10P14/3454; H10P14/3456; H10P14/38; H10P14/3802; H10P14/3808; H10P14/381; H10P14/3816; H10P14/382; Y; Y10; Y10S; Y10S148/00; Y10S148/09; Y10S148/093
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
80 words
A method of removing hydrogen from a hydrogenated amorphous silicon structure having a surface melt threshold and a melt through threshold, said method comprising the steps, in the sequence set forth, of: irradiating an area of the hydrogenated amorphous silicon structure with a plurality of laser beam pulses at a first energy density; and irradiating said area with a plurality of laser beam pulses at a second energy density, said second energy density being greater than said first energy density.
Claim 2
Independent Claim
80 words
A method of removing hydrogen from a hydrogenated amorphous silicon structure having a surface melt threshold and a melt through threshold, said method comprising the steps, in the sequence set forth, of: irradiating an area of the hydrogenated amorphous silicon structure with a plurality of laser beam pulses at a first energy density; and irradiating said area with a plurality of laser beam pulses at a second energy density, said second energy density being greater than said first energy density.
Claim 3
Dependent Claim
44 words
The method according to claim 1, further including the step of irradiating said area with a plurality of laser beam pulses at a third energy density after irradiation at said second energy density, said third energy density being greater than said second energy density.
Claim 4
Dependent Claim
23 words
The method according to claim 2, wherein said first energy density is above the surface melt threshold and below the melt through threshold.
Claim 5
Dependent Claim
17 words
The method according to claim 3, wherein said third energy density is above the melt through threshold.
Claim 6
Dependent Claim
23 words
The method according to claim 1, wherein said first energy density is above the surface melt threshold and below the melt through threshold.
Claim 7
Dependent Claim
17 words
The method according to claim 5, wherein said second energy density is above the melt through threshold.
Claim 8
Independent Claim
102 words
A method of producing polycrystallized silicon from hydrogenated amorphous silicon having a surface melt threshold and a melt through threshold, said method comprising the steps, in the sequence set forth, of: irradiating an area of the hydrogenated amorphous silicon structure with a plurality of laser beam pulses at a first energy density; irradiating said area with a plurality of laser beam pulses at a second energy density, said second energy density being greater than said first energy density; and irradiating said area with laser beam pulses at a third energy density, said third energy density being greater than said second energy density.
Claim 9
Independent Claim
102 words
A method of producing polycrystallized silicon from hydrogenated amorphous silicon having a surface melt threshold and a melt through threshold, said method comprising the steps, in the sequence set forth, of: irradiating an area of the hydrogenated amorphous silicon structure with a plurality of laser beam pulses at a first energy density; irradiating said area with a plurality of laser beam pulses at a second energy density, said second energy density being greater than said first energy density; and irradiating said area with laser beam pulses at a third energy density, said third energy density being greater than said second energy density.
Claim 10
Dependent Claim
23 words
The method according to claim 7, wherein said first energy density is above the surface melt threshold and below the melt through threshold.
Claim 11
Dependent Claim
17 words
The method according to claim 8, wherein said third energy density is above the melt through threshold.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-11-21 | 1998-05-23 | 1998-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-11-21 | 2002-05-23 | 2002-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-11-21 | 2006-05-23 | 2006-11-22 | $7700.00 | Window Closed / Lapsed |