Use of polymer spacers for the fabrication of shallow trench isolation regions with rounded top corners
Assignee: INSTITUTE MICROELECTRONICS
•
Filing: 1997-10-20
•
Granted: 1998-09-01
•
Expires: 2017-10-20
Abstract
Abstract A method for forming insulator filled, shallow trench isolation regions, with rounded corners, has been developed. The process features the use of a polymer coated opening, in an insulator layer, used as a mask to define the shallow trench region in silicon. After completion of the shallow trench formation the polymer spacers are removed, exposing a region of unetched semiconductor, that had been protected by the polymer spacers, during the shallow trench dry etching procedure. The sharp corner, at the intersection between the shallow trench and the unetched region of semiconductor, is then converted to a rounded corner, via thermal oxidation of exposed silicon surfaces. The polymer spacers also eliminate the top corner wraparound.
Inventors
- 👤 Bo Yu
- 👤 Qing Hua Zhong
- 👤 Jian Hui Ye
- 👤 Mei Sheng Zhou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:12
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/0145; H10W10/10; H10W10/17; Y; Y10; Y10S; Y10S148/00; Y10S148/05; Y10S148/161; Y10S438/00; Y10S438/978
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
123 words
A method for creating an insulator filled, shallow trench isolation region, in a semiconductor substrate, comprising the steps of: depositing a first insulator layer on said semiconductor substrate; forming an opening in said first insulator layer, exposing said semiconductor substrate; forming polymer spacers on the sides of said opening, creating a polymer coated opening; creating a shallow trench in said semiconductor substrate, in a region exposed in said polymer coated opening; removing said polymer spacers, exposing a region of unetched semiconductor substrate, located between said first insulator layer and said shallow trench; growing a silicon dioxide layer on exposed silicon surfaces of said shallow trench, and on said region of unetched semiconductor substrate; and filling said shallow trench with a second insulator layer.
Claim 2
Independent Claim
123 words
A method for creating an insulator filled, shallow trench isolation region, in a semiconductor substrate, comprising the steps of: depositing a first insulator layer on said semiconductor substrate; forming an opening in said first insulator layer, exposing said semiconductor substrate; forming polymer spacers on the sides of said opening, creating a polymer coated opening; creating a shallow trench in said semiconductor substrate, in a region exposed in said polymer coated opening; removing said polymer spacers, exposing a region of unetched semiconductor substrate, located between said first insulator layer and said shallow trench; growing a silicon dioxide layer on exposed silicon surfaces of said shallow trench, and on said region of unetched semiconductor substrate; and filling said shallow trench with a second insulator layer.
Claim 3
Dependent Claim
44 words
The method of claim 1, wherein said first insulator layer is a composite insulator layer, comprised of an overlying silicon nitride layer, between about 1000 to 2000 Angstroms, in thickness, on an underlying silicon oxide layer, between about 50 to 200 Angstroms, in thickness.
Claim 4
Dependent Claim
48 words
The method of claim 1, wherein said opening, in said first insulator layer, is formed via anisotropic RIE procedures, using CHF 3 --CF 4 --Ar as an etchant for a silicon nitride layer, and using CHF 3 --CF 4 --Ar--CO as an etchant for a silicon oxide layer.
Claim 5
Dependent Claim
36 words
The method of claim 1, wherein said polymer spacers are formed on the sides of said opening, to a thickness between about 200 to 500 Angstroms, via a RIE procedure, using CHF 3 --CF 4 --Ar--CO.
Claim 6
Dependent Claim
66 words
The method of claim 1, wherein said polymer coated opening is used as a mask to create said shallow trench, in said semiconductor substrate, to a depth between about 1500 to 4000 Angstroms, via a RIE procedure, using either HBr--Cl 2 --O 2 , or Cl 2 --O 2 , as an etchant, with the shallow trench shape exhibiting a profile between about 70° to 90°.
Claim 7
Dependent Claim
22 words
The method of claim 1, wherein said unetched region of said semiconductor substrate, is between about 200 to 500 Angstroms, in width.
Claim 8
Dependent Claim
64 words
The method of claim 1, wherein said silicon oxide layer, formed on the exposed silicon surfaces of said shallow trench, and on the surface of said region of unetched semiconductor substrate, is obtained via thermal oxidation, in dry oxygen, or in an oxygen-steam ambient, with HCl, at a temperature between about 850° to 1100° C., to a thickness between about 100 to 200 Angstroms.
Claim 9
Dependent Claim
43 words
The method of claim 1, wherein said second insulator layer, used to fill said shallow trench, is a silicon oxide layer, obtained using LPCVD, APCVD, SACVD, or HPCVD procedures, to a thickness between about 4000 to 7000 Angstroms, using TEOS as a source.
Claim 10
Independent Claim
248 words
A method for forming an insulator filled, shallow trench isolation region, with rounded corners, in a semiconductor substrate, comprising the steps of: depositing a composite insulator layer, on said semiconductor substrate; forming a photoresist shape, with a first opening, on said composite insulator layer; anisotropic etching of said composite insulator layer, using said photoresist shape as a mask, extending said first opening in said photoresist shape, to said composite insulator layer; forming polymer spacers on the sides of said first opening in said photoresist shape, and on the sides of said first opening in said composite insulator layer, creating a polymer coated opening; dry etching of said semiconductor substrate, exposed in polymer coated opening, creating shallow trench regions; removal of said photoresist shape, and of said polymer spacers, exposing a region of unetched semiconductor substrate, between said shallow trench and said composite insulator layer, and exposing a sharp corner at the intersection of said shallow trench and said region of unetched semiconductor substrate; growing a silicon oxide layer on exposed surfaces of said shallow trench, and on the exposed surface of said region of unetched semiconductor substrate, converting said sharp corner, to a rounded corner, at intersection of said shallow trench and said region of unetched semiconductor substrate; depositing an insulator layer on top surface of said composite insulator layer, completely filling shallow trench; and removing said insulator layer from the top surface of said composite insulator layer, resulting in said insulator filled, shallow trench, with rounded corners.
Claim 11
Independent Claim
248 words
A method for forming an insulator filled, shallow trench isolation region, with rounded corners, in a semiconductor substrate, comprising the steps of: depositing a composite insulator layer, on said semiconductor substrate; forming a photoresist shape, with a first opening, on said composite insulator layer; anisotropic etching of said composite insulator layer, using said photoresist shape as a mask, extending said first opening in said photoresist shape, to said composite insulator layer; forming polymer spacers on the sides of said first opening in said photoresist shape, and on the sides of said first opening in said composite insulator layer, creating a polymer coated opening; dry etching of said semiconductor substrate, exposed in polymer coated opening, creating shallow trench regions; removal of said photoresist shape, and of said polymer spacers, exposing a region of unetched semiconductor substrate, between said shallow trench and said composite insulator layer, and exposing a sharp corner at the intersection of said shallow trench and said region of unetched semiconductor substrate; growing a silicon oxide layer on exposed surfaces of said shallow trench, and on the exposed surface of said region of unetched semiconductor substrate, converting said sharp corner, to a rounded corner, at intersection of said shallow trench and said region of unetched semiconductor substrate; depositing an insulator layer on top surface of said composite insulator layer, completely filling shallow trench; and removing said insulator layer from the top surface of said composite insulator layer, resulting in said insulator filled, shallow trench, with rounded corners.
Claim 12
Dependent Claim
42 words
The method of claim 9, wherein said composite insulator layer is comprised of an overlying silicon nitride layer, at a thickness between about 1000 to 2000 Angstroms, and an underlying silicon oxide layer, at a thickness between about 50 to 200 Angstroms.
Claim 13
Dependent Claim
56 words
The method of claim 9, wherein said first opening in said composite insulator layer, is formed via anisotropic RIE procedures, using said photoresist shape as a mask, using CHF 3 --CF 4 --Ar as an etchant for a silicon nitride layer, and using CHF 3 --CF 4 --Ar--CO as an etchant for a silicon oxide layer.
Claim 14
Dependent Claim
38 words
The method of claim 9, wherein said polymer spacers, on the sides of said first opening, are formed to a thickness between about 200 to 500 Angstroms, via an anisotropic RIE procedure, using CHF 3 --CF 4 --Ar--CO.
Claim 15
Dependent Claim
52 words
The method of claim 9, wherein said shallow trench is formed in said semiconductor substrate, to a depth between about 1500 to 4000 Angstroms, via a RIE procedure, using said polymer coated opening as a mask, and using HBr--Cl 2 O 2 , or Cl 2 --O 2 , as an etchant.
Claim 16
Dependent Claim
21 words
The method of claim 9, wherein said region of unetched semiconductor substrate is between about 200 to 500 Angstroms, in width.
Claim 17
Dependent Claim
50 words
The method of claim 9, wherein said rounded corner, at the intersection of said shallow trench and said region of unetched semiconductor substrate, is converted from said sharp corner, via thermal oxidation of exposed silicon surfaces, creating said silicon oxide layer, at a thickness between about 100 to 200 Angstroms.
Claim 18
Dependent Claim
44 words
The method of claim 9, wherein said insulator layer, used to fill said shallow trench, is silicon oxide, deposited using LPCVD, SACVD, APCVD, or HPCVD procedures, to a thickness between about 4000 to 7000 Angstroms, using TEOS, or silane and oxygen, as a source.
References Cited (Backward Citations)
US4855017A
Cited
US4613400A
Cited
US4707218A
Cited
JPS63110746A
Cited
JPH01248523A
Cited
US5084408A
Cited
US5683908A
Cited
US5342481A
Cited
US5719085A
Cited
US5670401A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-08-31 | 2002-03-02 | 2002-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-08-31 | 2006-03-02 | 2006-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-08-31 | 2010-03-02 | 2010-09-01 | $7700.00 | Window Closed / Lapsed |