Method for making improved shallow trench isolation with dielectric studs for semiconductor integrated circuits
Assignee: Vanguard International Semiconductor Corp
•
Filing: 1997-08-18
•
Granted: 1998-09-01
•
Expires: 2017-08-18
Abstract
Abstract A method is achieved for making improved shallow trench isolation (STI) regions surrounding and electrically isolating device areas on a substrate using dielectric studs, spin-on-glass (SOG), and an isotropic wet etchback. The method consists of forming trenches in a silicon substrate using a pad oxide and silicon nitride mask. A thermal oxide is grown in the silicon trenches and a CVD silicon oxide is deposited and chemical/mechanically polished back to the silicon nitride masking layer to form dielectric studs (or plugs) in the silicon trenches that extend above the silicon substrate surface. The silicon nitride is removed in hot phosphoric acid, and a thin SOG is deposited to form disposable sidewall spacers on the raised studs. The thin SOG and the pad oxide are wet etched in HF acid to the device areas while isotropically etching back the disposable SOG sidewall spacers and dielectric studs to form shallow trench isolation regions having a raised convex surface. This eliminates dishing in the STI (concave STI) that results in undesirable variation in FET threshold voltage (V th ). The gradual convex profile also minimizes the polysilicon residue problem when anisotropically etching the gate electrodes over the device areas. The use of SOG with wet etchback is more cost effective than the conventional CVD oxide deposition and plasma etchback process.
Inventors
- 👤 Horng-Huei Tseng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:10
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/0148; H10W10/10; H10W10/17; Y; Y10; Y10S; Y10S148/00; Y10S148/05
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
230 words
A method for fabricating raised shallow trench isolation regions in a semiconductor substrate comprising the steps of: forming a pad oxide layer composed of silicon oxide on said substrate; depositing a silicon nitride layer on said pad oxide layer; forming openings in said silicon nitride layer and said pad oxide layer surrounding device areas using a photoresist mask and anisotropic plasma etching; removing said photoresist mask; forming trenches by selectively anisotropic plasma etching said silicon substrate in said openings while leaving portions of said silicon nitride layer over said device areas; forming a liner oxide by thermal oxidation on exposed surfaces of said trenches in said substrate; forming a channel-stop implant in said trenches; depositing a conformal chemical vapor deposited gap-fill silicon oxide to fill said trenches; chemical/mechanically polishing back said gap-fill silicon oxide to said silicon nitride layer; removing said silicon nitride layer over said device areas, thereby forming raised dielectric studs in said trenches extending above said substrate surface; depositing a spin-on glass by spin coating thereby forming disposable spin-on glass spacers on said raised dielectric studs; curing said spin-on glass by thermal annealing; wet etching back said spin-on glass and said pad oxide to said device areas and concurrently etching back said raised dielectric studs and said spin-on glass spacers thereby completing said shallow trench isolation regions having a convex raised surface relative to said substrate surface.
Claim 2
Independent Claim
230 words
A method for fabricating raised shallow trench isolation regions in a semiconductor substrate comprising the steps of: forming a pad oxide layer composed of silicon oxide on said substrate; depositing a silicon nitride layer on said pad oxide layer; forming openings in said silicon nitride layer and said pad oxide layer surrounding device areas using a photoresist mask and anisotropic plasma etching; removing said photoresist mask; forming trenches by selectively anisotropic plasma etching said silicon substrate in said openings while leaving portions of said silicon nitride layer over said device areas; forming a liner oxide by thermal oxidation on exposed surfaces of said trenches in said substrate; forming a channel-stop implant in said trenches; depositing a conformal chemical vapor deposited gap-fill silicon oxide to fill said trenches; chemical/mechanically polishing back said gap-fill silicon oxide to said silicon nitride layer; removing said silicon nitride layer over said device areas, thereby forming raised dielectric studs in said trenches extending above said substrate surface; depositing a spin-on glass by spin coating thereby forming disposable spin-on glass spacers on said raised dielectric studs; curing said spin-on glass by thermal annealing; wet etching back said spin-on glass and said pad oxide to said device areas and concurrently etching back said raised dielectric studs and said spin-on glass spacers thereby completing said shallow trench isolation regions having a convex raised surface relative to said substrate surface.
Claim 3
Dependent Claim
20 words
The method of claim 1, wherein said pad oxide layer has a thickness of between about 200 and 300 Angstroms.
Claim 4
Dependent Claim
20 words
The method of claim 1, wherein said silicon nitride layer has a thickness of between about 1500 and 3000 Angstroms.
Claim 5
Dependent Claim
23 words
The method of claim 1, wherein said trenches are etched to a depth of between about 3000 and 6000 Angstroms in said substrate.
Claim 6
Dependent Claim
21 words
The method of claim 1, wherein said liner oxide is grown to a thickness of between about 50 and 300 Angstroms.
Claim 7
Dependent Claim
24 words
The method of claim 1, wherein said channel-stop implant species is boron at a dose sufficient to provide electrical isolation between said device areas.
Claim 8
Dependent Claim
23 words
The method of claim 1, wherein said gap-fill silicon oxide is deposited to a thickness at least one-half the width of said trenches.
Claim 9
Dependent Claim
18 words
The method of claim 1, wherein said silicon nitride layer is removed in a hot phosphoric acid etch.
Claim 10
Dependent Claim
24 words
The method of claim 1, wherein said raised dielectric studs extend above said substrate surface by about the thickness of said silicon nitride layer.
Claim 11
Dependent Claim
37 words
The method of claim 1, wherein said spin-on glass is deposited to a thickness of between about 200 and 1000 Angstroms over said device areas, while forming a thicker layer on sidewalls of said raised dielectric studs.
Claim 12
Dependent Claim
28 words
The method of claim 1, wherein said curing of said spin-on glass is carried out at a temperature in the range of between about 200° and 500° C.
Claim 13
Dependent Claim
28 words
The method of claim 1, wherein said wet etching back of said spin-on glass and said pad oxide is carried out in a dilute solution of hydrofluoric acid.
Claim 14
Independent Claim
269 words
A method for fabricating raised shallow trench isolation regions in a semiconductor substrate, and gate electrodes for field effect transistors comprising the steps of: forming a pad oxide layer composed of silicon oxide on said substrate; depositing a silicon nitride layer on said pad oxide layer; forming openings in said silicon nitride layer and said pad oxide layer surrounding device areas using a photoresist mask and anisotropic plasma etching; removing said photoresist mask; forming trenches by selectively anisotropic plasma etching said silicon substrate in said openings while leaving portions of said silicon nitride layer over said device areas; forming a liner oxide by thermal oxidation on exposed surfaces of said trenches in said substrate; forming a channel-stop implant in said trenches; depositing a conformal chemical vapor deposited gap-fill silicon oxide to fill said trenches; chemical/mechanically polishing back said gap-fill silicon oxide to said silicon nitride layer; removing said silicon nitride layer over said device areas, thereby forming raised dielectric studs in said trenches extending above said substrate surface; depositing a spin-on glass by spin coating thereby forming disposable spin-on glass spacers on said raised dielectric studs; curing said spin-on glass by thermal annealing; wet etching back said spin-on glass and said pad oxide to said device areas and concurrently etching back said raised dielectric studs and said spin-on glass spacers thereby forming said shallow trench isolation regions having a convex raised surface relative to said substrate surface; forming a gate oxide by thermal oxidation on said device areas; depositing a polysilicon layer on said substrate; patterning said polysilicon layer and completing said gate electrodes for said field effect transistors.
Claim 15
Independent Claim
269 words
A method for fabricating raised shallow trench isolation regions in a semiconductor substrate, and gate electrodes for field effect transistors comprising the steps of: forming a pad oxide layer composed of silicon oxide on said substrate; depositing a silicon nitride layer on said pad oxide layer; forming openings in said silicon nitride layer and said pad oxide layer surrounding device areas using a photoresist mask and anisotropic plasma etching; removing said photoresist mask; forming trenches by selectively anisotropic plasma etching said silicon substrate in said openings while leaving portions of said silicon nitride layer over said device areas; forming a liner oxide by thermal oxidation on exposed surfaces of said trenches in said substrate; forming a channel-stop implant in said trenches; depositing a conformal chemical vapor deposited gap-fill silicon oxide to fill said trenches; chemical/mechanically polishing back said gap-fill silicon oxide to said silicon nitride layer; removing said silicon nitride layer over said device areas, thereby forming raised dielectric studs in said trenches extending above said substrate surface; depositing a spin-on glass by spin coating thereby forming disposable spin-on glass spacers on said raised dielectric studs; curing said spin-on glass by thermal annealing; wet etching back said spin-on glass and said pad oxide to said device areas and concurrently etching back said raised dielectric studs and said spin-on glass spacers thereby forming said shallow trench isolation regions having a convex raised surface relative to said substrate surface; forming a gate oxide by thermal oxidation on said device areas; depositing a polysilicon layer on said substrate; patterning said polysilicon layer and completing said gate electrodes for said field effect transistors.
Claim 16
Dependent Claim
20 words
The method of claim 13, wherein said pad oxide layer has a thickness of between about 200 and 300 Angstroms.
Claim 17
Dependent Claim
20 words
The method of claim 13, wherein said silicon nitride layer has a thickness of between about 1500 and 3000 Angstroms.
Claim 18
Dependent Claim
23 words
The method of claim 13, wherein said trenches are etched to a depth of between about 3000 and 6000 Angstroms in said substrate.
Claim 19
Dependent Claim
21 words
The method of claim 13, wherein said liner oxide is grown to a thickness of between about 50 and 300 Angstroms.
Claim 20
Dependent Claim
24 words
The method of claim 13, wherein said channel-stop implant species is boron at a dose sufficient to provide electrical isolation between said device areas.
Claim 21
Dependent Claim
23 words
The method of claim 13, wherein said gap-fill silicon oxide is deposited to a thickness at least one-half the width of said trenches.
Claim 22
Dependent Claim
18 words
The method of claim 13, wherein said silicon nitride layer is removed in a hot phosphoric acid etch.
Claim 23
Dependent Claim
24 words
The method of claim 13, wherein said raised dielectric studs extend above said substrate surface by about the thickness of said silicon nitride layer.
Claim 24
Dependent Claim
37 words
The method of claim 13, wherein said spin-on glass is deposited to a thickness of between about 200 and 1000 Angstroms over said device areas, while forming a thicker layer on sidewalls of said raised dielectric studs.
Claim 25
Dependent Claim
28 words
The method of claim 13, wherein said curing of said spin-on glass is carried out at a temperature in the range of between about 200° and 500° C.
Claim 26
Dependent Claim
28 words
The method of claim 13, wherein said wet etching back of said spin-on glass and said pad oxide is carried out in a dilute solution of hydrofluoric acid.
Claim 27
Dependent Claim
21 words
The method of claim 13, wherein said gate oxide is grown to a thickness of between about 50 and 200 Angstroms.
Claim 28
Dependent Claim
25 words
The method of claim 13, wherein said polysilicon layer is deposited to a thickness of between about 1000 and 3500 Angstroms and is conductively doped.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-08-31 | 2002-03-02 | 2002-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-08-31 | 2006-03-02 | 2006-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-08-31 | 2010-03-02 | 2010-09-01 | $7700.00 | Window Closed / Lapsed |