Abstract
Abstract The present invention provides a method of manufacturing a sacrificial self aligned sub-atmospheric chemical vapor deposition (SACVD) O3 TEOS layer 50 70 over a trench oxide 40 to protect the trench oxide from excessive subsequent etch steps. The SACVD O3 TEOS layer has a higher deposition rate over the trench oxide layer 40 than over the surrounding non-trench thermally grown pad oxides. The trench oxide is preferably formed using a process of PECVD, LPTEOS, or O3-TEOS. The invention provides two preferred embodiments: (1) a first self aligned sacrificial O3 TEOS oxide layer 50 deposited before the pad oxide etch and (2) a second self aligned sacrificial O3 TEOS oxide layer 70 deposited before the sacrificial implant oxide etch. The invention can be applied in a variety of situations where the trench oxide is exposed to damaging etches.
Inventors
- 👤 Syun-Ming Jang
- 👤 Ying-Ho Chen
- 👤 Chen-Hua Yu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:22
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/0145; H10W10/10; H10W10/17; Y; Y10; Y10S; Y10S148/00; Y10S148/05
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
188 words
A method of fabricating a shallow trench isolation having a protective self-aligned sacrificial O 3 TEOS oxide layer comprising the steps of: a) thermally oxidizing a semiconductor substrate forming pad oxide layer; said substrate having at least an isolation area and an active area; b) depositing a masking layer over said pad oxide layer; c) patterning said masking layer and said pad oxide layer exposing said substrate in said isolation area; d) etching a trench in said substrate using said masking layer and said pad oxide layer as a mask; said trench having sidewalls and a bottom; e) filling said trench with a trench oxide layer; said trench oxide layer having a property where a SACVD O 3 TEOS layer selectively deposits over said trench oxide layer; f) removing said masking layer; g) selectively depositing a first self aligned SACVD O 3 TEOS layer over said trench oxide layer; and h) etching said pad oxide layer and said first self aligned SACVD O 3 TEOS layer and removing said pad oxide layer and removing at least a portion of said first self aligned SACVD O 3 TEOS layer.
Claim 2
Independent Claim
188 words
A method of fabricating a shallow trench isolation having a protective self-aligned sacrificial O 3 TEOS oxide layer comprising the steps of: a) thermally oxidizing a semiconductor substrate forming pad oxide layer; said substrate having at least an isolation area and an active area; b) depositing a masking layer over said pad oxide layer; c) patterning said masking layer and said pad oxide layer exposing said substrate in said isolation area; d) etching a trench in said substrate using said masking layer and said pad oxide layer as a mask; said trench having sidewalls and a bottom; e) filling said trench with a trench oxide layer; said trench oxide layer having a property where a SACVD O 3 TEOS layer selectively deposits over said trench oxide layer; f) removing said masking layer; g) selectively depositing a first self aligned SACVD O 3 TEOS layer over said trench oxide layer; and h) etching said pad oxide layer and said first self aligned SACVD O 3 TEOS layer and removing said pad oxide layer and removing at least a portion of said first self aligned SACVD O 3 TEOS layer.
Claim 3
Dependent Claim
85 words
The method of claim 1 which further includes a) forming an implant sacrificial oxide layer over the substrate surface; b) forming at least a well in said active area in said substrate; c) for selectively depositing a second self aligned SACVD O 3 TEOS layer over said trench oxide layer; d) removing said implant sacrificial oxide layer using an etch and etching at least a portion of said second self aligned SACVD O 3 TEOS layer thereby leaving said trench oxide layer filling said trench.
Claim 4
Dependent Claim
129 words
The method of claim 1 wherein said trench oxide layer is formed by the following steps: a) forming a thermal oxide layer over said sidewalls of said trench; said thermal oxide layer thickness in a range of between about 300 and 400 Å; b) forming a PE SiH 4 thermal oxide layer over said thermal oxide layer; said PE SiH 4 thermal oxide layer thickness in a range of between about 350 and 600 Å; c) treating said PE SiH 4 thermal oxide layer with a N 2 plasma; d) forming a trench oxide layer composed of a O 3 TEOS layer in said trench and over said masking layer; e) chemical-mechanical polish said trench oxide layer so that said trench oxide layer is level with said masking layer.
Claim 5
Dependent Claim
85 words
The method of claim 1 wherein said trench oxide layer is formed using a O 3 TEOS process at a temperature in a range of between about 360° and 400° C. and a pressure in a range of between about 300 and 600 torr and a TetraEthylOrthoSilicate (TEOS) flow of between 1700 and 2300 sccm, and a O 3 in O 2 flow of between 4500 and 5500 sccm with a O 3 in O 2 wt % ratio between 12 and 13 weight %.
Claim 6
Dependent Claim
21 words
The method of claim 1 wherein said trench has a depth in a range of between about 3000 and 5000 Å.
Claim 7
Dependent Claim
35 words
The method of claim 1 wherein said trench oxide layer is composed of an oxide formed by a process selected from the group consisting of LPTEOS, O 3 TEOS and N 2 treated thermal oxide.
Claim 8
Dependent Claim
28 words
The method of claim 1 wherein said first self aligned SACVD O 3 TEOS layer has a thickness in a range of between about 5000 and 7000 Å.
Claim 9
Dependent Claim
43 words
The method of claim 1 wherein said first self aligned SACVD O 3 TEOS layer has a faster deposition rate over said trench oxide layer than over said pad oxide layer 20, with a ratio of between about 5:1 to 7:1 times faster.
Claim 10
Dependent Claim
79 words
The method of claim 1 wherein said first self aligned SACVD O 3 TEOS layer deposited at a pressure between about 400 and 500 torr, at a temperature in a range of between about 360° and 440° C., and a TetraEthylOrthoSilicate (TEOS) flow of between 1700 and 2300 sccm, and a O 3 in O 2 flow of between 4500 and 5500 sccm with a O 3 in O 2 wt % ratio between 12 and 13 weight %.
Claim 11
Dependent Claim
46 words
The method of claim 1 wherein said first self aligned SACVD O 3 TEOS layer is deposited over said Trench oxide layer at a rate between about 1500 and 1900 Å/min and over said pad oxide layer at a rate between about 120 and 160 Å/min.
Claim 12
Independent Claim
312 words
A method of fabricating a shallow trench isolation having a protective self-aligned sacrificial O 3 TEOS oxide comprising the steps of: a) thermally oxidizing a semiconductor substrate forming pad oxide layer; said substrate having at least an isolation area and an active area; b) depositing a masking layer composed of silicon nitride over said pad oxide layer; c) patterning said masking layer and said pad oxide layer exposing said substrate in said isolation area; d) etching a trench in said substrate using said masking layer and said pad oxide layer as a mask; said trench having sidewalls and a bottom; e) forming a thermal oxide layer lining said sidewalls and said bottom of said trench; said thermal oxide layer having a thickness in a range of between about 300 and 400 Å; f) filling said trench with a trench oxide layer; said trench oxide layer having a property where a SACVD O 3 TEOS layer selectively deposits over said trench oxide layer; said trench oxide layer formed by a process selected from the group consisting of PECVD, LPTEOS, and O 3 -TEOS; g) removing said masking layer; h) selectively depositing a first self aligned SACVD O 3 TEOS layer over said Trench oxide layer; said first self aligned SACVD O 3 TEOS layer is deposited at a pressure between about 400 and 500 torr, at a temperature in a range of between about 360° and 440° C., and a TEOS flow of between 1700 and 2300 sccm, and a O 3 in O 2 flow of between 4500 and 5500 sccm with a O 3 in O 2 wt % ratio between 12 and 13 weight %; i) etching said pad oxide layer and said first self aligned SACVD O 3 TEOS layer and removing said pad oxide layer and removing at least a portion of said SACVD O 3 TEOS layer.
Claim 13
Independent Claim
312 words
A method of fabricating a shallow trench isolation having a protective self-aligned sacrificial O 3 TEOS oxide comprising the steps of: a) thermally oxidizing a semiconductor substrate forming pad oxide layer; said substrate having at least an isolation area and an active area; b) depositing a masking layer composed of silicon nitride over said pad oxide layer; c) patterning said masking layer and said pad oxide layer exposing said substrate in said isolation area; d) etching a trench in said substrate using said masking layer and said pad oxide layer as a mask; said trench having sidewalls and a bottom; e) forming a thermal oxide layer lining said sidewalls and said bottom of said trench; said thermal oxide layer having a thickness in a range of between about 300 and 400 Å; f) filling said trench with a trench oxide layer; said trench oxide layer having a property where a SACVD O 3 TEOS layer selectively deposits over said trench oxide layer; said trench oxide layer formed by a process selected from the group consisting of PECVD, LPTEOS, and O 3 -TEOS; g) removing said masking layer; h) selectively depositing a first self aligned SACVD O 3 TEOS layer over said Trench oxide layer; said first self aligned SACVD O 3 TEOS layer is deposited at a pressure between about 400 and 500 torr, at a temperature in a range of between about 360° and 440° C., and a TEOS flow of between 1700 and 2300 sccm, and a O 3 in O 2 flow of between 4500 and 5500 sccm with a O 3 in O 2 wt % ratio between 12 and 13 weight %; i) etching said pad oxide layer and said first self aligned SACVD O 3 TEOS layer and removing said pad oxide layer and removing at least a portion of said SACVD O 3 TEOS layer.
Claim 14
Dependent Claim
85 words
The method of claim 11 which further includes a) forming an implant sacrificial oxide layer over the substrate surface; b) forming at least a well in said active area in said substrate; c) for selectively depositing a second self aligned SACVD O 3 TEOS layer over said trench oxide layer; d) removing said implant sacrificial oxide layer using an etch and etching at least a portion of said second self aligned SACVD O 3 TEOS layer thereby leaving said trench oxide layer filling said trench.
Claim 15
Dependent Claim
128 words
The method of claim 11 wherein said trench oxide layer is formed by the following steps: a) forming a thermal oxide layer over said sidewalls of said trench; said thermal oxide layer thickness in a range of between about 300 and 400 Å; b) forming a PE SiH 4 thermal oxide layer over said thermal oxide layer; said PE SiH 4 thermal oxide layer thickness in a range of between about 350 and 600 Å; c) treating said PE SiH 4 thermal oxide layer with a N 2 plasma; d) forming a trench oxide layer composed of O 3 TEOS layer in said trench and over said masking layer; e) chemical-mechanical polish said trench oxide layer so that said trench oxide layer is level with said masking layer.
Claim 16
Dependent Claim
86 words
The method of claim 11 wherein said trench oxide layer is formed using a O 3 TEOS process at a temperature in a range of between about 360° and 400 ° C. and a pressure in a range of between about 300 and 600 torr and a TetraEthylOrthoSilicate (TEOS) flow of between 1700 and 2300 sccm, and a O 3 in O 2 flow of between 4500 and 5500 sccm with a O 3 in O 2 wt % ratio between 12 and 13 weight %.
Claim 17
Dependent Claim
21 words
The method of claim 11 wherein said trench has a depth in a range of between about 3000 and 5000 Å.
Claim 18
Dependent Claim
28 words
The method of claim 11 wherein said first self aligned SACVD O 3 TEOS layer has a thickness in a range of between about 5000 and 7000 Å.
Claim 19
Dependent Claim
42 words
The method of claim 11 wherein said first self aligned SACVD O 3 TEOS layer has a faster deposition rate over said trench oxide layer than over said pad oxide layer, with a ratio of between about 5:1 to 7:1 times faster.
Claim 20
Dependent Claim
79 words
The method of claim 11 wherein said first self aligned SACVD O 3 TEOS layer deposited at a pressure between about 400 and 500 torr, at a temperature in a range of between about 360° and 440° C., and a TetraEthylOrthoSilicate (TEOS) flow of between 1700 and 2300 sccm, and a O 3 in O 2 flow of between 4500 and 5500 sccm with a O 3 in O 2 wt % ratio between 12 and 13 weight %.
Claim 21
Dependent Claim
45 words
The method of claim 11 wherein said first self aligned SACVD O 3 TEOS layer deposited over said trench oxide layer at a rate between about 1500 and 1900 Å/min and over said pad oxide layer at a rate between about 120 and 160 Å/min.
Claim 22
Independent Claim
208 words
A method of fabricating a shallow trench isolation having a self-aligned sacrificial oxide comprising the steps of: a) thermally oxidizing a semiconductor substrate forming pad oxide layer; said substrate having at least an isolation area and an active area; b) depositing a masking layer composed of silicon nitride over said pad oxide layer; c) patterning said masking layer and said pad oxide layer exposing said substrate in said isolation area; d) etching a trench in said substrate using said masking layer and said pad oxide layer as a mask; said trench having sidewalls and a bottom; e) forming a thermal oxide layer lining said sidewalls and said bottom of said trench; f) filling said trench with a trench oxide layer; g) removing said masking layer; h) removing said pad oxide layer; i) forming an implant sacrificial oxide layer over the substrate surface; j) forming at least a well in said active area in said substrate; k) for selectively depositing a second self aligned SACVD O 3 TEOS layer over said trench oxide layer; l) removing said implant sacrificial oxide layer using an etch and etching at least a portion of said second self aligned SACVD O 3 TEOS layer thereby leaving said trench oxide layer filling said trench.
Claim 23
Independent Claim
208 words
A method of fabricating a shallow trench isolation having a self-aligned sacrificial oxide comprising the steps of: a) thermally oxidizing a semiconductor substrate forming pad oxide layer; said substrate having at least an isolation area and an active area; b) depositing a masking layer composed of silicon nitride over said pad oxide layer; c) patterning said masking layer and said pad oxide layer exposing said substrate in said isolation area; d) etching a trench in said substrate using said masking layer and said pad oxide layer as a mask; said trench having sidewalls and a bottom; e) forming a thermal oxide layer lining said sidewalls and said bottom of said trench; f) filling said trench with a trench oxide layer; g) removing said masking layer; h) removing said pad oxide layer; i) forming an implant sacrificial oxide layer over the substrate surface; j) forming at least a well in said active area in said substrate; k) for selectively depositing a second self aligned SACVD O 3 TEOS layer over said trench oxide layer; l) removing said implant sacrificial oxide layer using an etch and etching at least a portion of said second self aligned SACVD O 3 TEOS layer thereby leaving said trench oxide layer filling said trench.
Claim 24
Dependent Claim
85 words
The method of claim 20 wherein said trench oxide layer is formed using a O 3 TEOS process at a temperature in a range of between about 360° and 400° C. and a pressure in a range of between about 300 and 600 torr and a TetraEthylOrthoSilicate (TEOS) flow of between 1700 and 2000 sccm, and a O 3 in O 2 flow of between 4500 and 5500 sccm with a O 3 in O 2 wt % ratio between 12 and 13 weight %.
Claim 25
Dependent Claim
79 words
The method of claim 20 wherein said second self aligned SACVD O 3 TEOS layer deposited at a pressure between about 400 and 500 torr, at a temperature in a range of between about 360° and 440° C., and a TetraEthylOrthoSilicate (TEOS) flow of between 1700 and 2300 sccm, and a O 3 in O 2 flow of between 4500 and 5500 sccm with a O 3 in O 2 wt % ratio between 12 and 13 weight %.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-03-23 | 2001-09-22 | 2002-03-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-03-23 | 2005-09-22 | 2006-03-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-03-23 | 2009-09-22 | 2010-03-24 | $7700.00 | Window Closed / Lapsed |