Multilayer oxide coatings
Assignee: Northwestern University
•
Filing: 1996-12-12
•
Granted: 1998-08-04
•
Expires: 2016-12-12
Abstract
Abstract A method and apparatus for monitoring and controlling deposition of metal, insulating compounds or other compounds on a substrate by sputtering techniques includes maintaining pulsed, constant, direct current power to the target, sensing the voltage of the target material used in the process, simultaneously rapidly sensing the partial pressure of the reactive gas, and simultaneously biasing the substrate to activate the reactive gas or otherwise energizing the reactive gas in the vicinity of the substrate. Low temperature coating (eg., below 550 DEG C.) of compounds such as alumina is effected by introduction of an extra energy source such as a radio frequency coil to the sputtering system to enhance the ionization potential of the positive ions. The asymmetric direct current pulsed magnetron power source is coupled to the cathode, as well as the substrate to be coated. An apparatus for practicing the invention is also disclosed and examples of various oxide coatings using the method of the invention are disclosed. A multilayer coating of nanometer scale layers of yttrium oxide and zirconium oxide having increased hardness is disclosed.
Inventors
- 👤 William D. Sproul
- 👤 Scott A. Barnett
- 👤 Anthony Lefkow
- 👤 Ming-Show Wong
- 👤 Phillip Yashar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 11:36
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/0021; C23C14/02; C23C14/024; C23C14/025; C23C14/06; C23C14/08; C23C14/081; C23C14/083; C23C14/22; C23C14/50; C23C14/505; C23C28/00; C23C28/04; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/24983; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
43 words
A substrate coating comprising: alternating layers of yttrium oxide and zirconium oxide, each layer in the range of about 1 to 5 nanometers and forming a coating having a thickness greater than about 1 micrometer, said coating layers having a cubic crystalline structure.
Claim 2
Dependent Claim
43 words
A substrate coating comprising: alternating layers of yttrium oxide and zirconium oxide, each layer in the range of about 1 to 5 nanometers and forming a coating having a thickness greater than about 1 micrometer, said coating layers having a cubic crystalline structure.
Claim 3
Dependent Claim
15 words
The protective coating of claim 1 having a thickness of at least about 3 micrometers.
Claim 4
Dependent Claim
14 words
The protective coating of claim 1 wherein the individual layers have approximately equal thickness.
Claim 5
Dependent Claim
23 words
The protective coating of claim 1 wherein the thickness of the zirconium layer is about 3 times the thickness of the yttrium layer.
Claim 6
Dependent Claim
44 words
A substrate coating comprising, in combination: alternating metallic oxide layers, each layer having a thickness in the range of about 1 to 10 nanometers and cubic or pseudomorphic cubic structure in the combination, said layers forming a coating of at least about 1 micrometer.
Claim 7
Dependent Claim
44 words
A substrate coating comprising, in combination: alternating metallic oxide layers, each layer having a thickness in the range of about 1 to 10 nanometers and cubic or pseudomorphic cubic structure in the combination, said layers forming a coating of at least about 1 micrometer.
Claim 8
Dependent Claim
48 words
An article having an oxide coating comprising, in combination: a substrate, a coating of alternating metal oxide layers, each layer having a thickness in the range of about 1 to 10 nanometers, a cubic or pseudomorphic cubic structure and a coating thickness of greater than about 1 micrometer.
Claim 9
Dependent Claim
48 words
An article having an oxide coating comprising, in combination: a substrate, a coating of alternating metal oxide layers, each layer having a thickness in the range of about 1 to 10 nanometers, a cubic or pseudomorphic cubic structure and a coating thickness of greater than about 1 micrometer.
Claim 10
Dependent Claim
15 words
The article of claim 6 wherein the metal oxides are yttrium oxide and zirconium oxide.
Claim 11
Dependent Claim
17 words
The article of claim 6 wherein each layer has a thickness of about 1 to 5 nanometers.
Claim 12
Dependent Claim
58 words
An article having an oxide coating comprising, in combination: a substrate, a coating of alternating metal oxide layers, each layer having a crystalline structure, each layer having a thickness in the range of about 1 to 5 nanometers, said coating having a thickness of at least about 1 micrometer, each of said layers having a substantially stoichiometric composition.
Claim 13
Dependent Claim
58 words
An article having an oxide coating comprising, in combination: a substrate, a coating of alternating metal oxide layers, each layer having a crystalline structure, each layer having a thickness in the range of about 1 to 5 nanometers, said coating having a thickness of at least about 1 micrometer, each of said layers having a substantially stoichiometric composition.
Claim 14
Dependent Claim
14 words
The article of claim 9 wherein the crystalline structure is cubic or pseudomorphic cubic.
Claim 15
Dependent Claim
15 words
The article of claim 9 wherein the alternating layers comprise yttrium oxide and zirconium oxide.
Claim 16
Dependent Claim
26 words
The article of claim 11 wherein the hardness of the coating is at least 50% greater than the hardness of separate layers of the oxide material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-08-03 | 2002-02-02 | 2002-08-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-08-03 | 2006-02-02 | 2006-08-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-08-03 | 2010-02-02 | 2010-08-04 | $7700.00 | Window Closed / Lapsed |