Method for forming a gold plating electrode, a substrate based on the electrode forming method, and a wire bonding method utilizing this electrode forming method
Assignee: Panasonic Holdings Corp
•
Filing: 1996-02-20
•
Granted: 1998-06-16
•
Expires: 2016-02-20
Abstract
Abstract A circuit pattern 2a, made of copper foil, is arranged on a substrate 1. A nickel-containing barrier metal layer 2b is formed on the.circuit pattern 2a. A gold layer 2c is formed on the barrier metal layer 2b by electroless substitution plating. Then, substrate 1 is heated up to impel nickel contained in the gold layer 2c to move toward a surface zone of the gold layer 2c to deposit nickel compound in the surface zone of the gold layer 2c, thereby enhancing the fineness of a remaining part of the gold layer 2c at at least an inside zone immediately below the surface zone. Then, the surface zone containing the crowded nickel compound is removed off the gold layer 2c so as to expose a purified surface of the inside zone of the gold layer 2c. Therefore, it becomes possible to form an excellent electrode having satisfactory bondability to the wire by using a less amount of gold at low costs.
Inventors
- 👤 Hiroshi Haji
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 17:30
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/244; H10; H10W; H10W70/00; H10W70/01; H10W70/05; H10W70/60; H10W70/62; H10W70/66; H10W72/00; H10W72/01; H10W72/015; H10W72/01571; H10W72/071; H10W72/073; H10W72/07331; H10W72/075; H10W72/07511; H10W72/30; H10W72/351; H10W72/353; H10W72/354; H10W72/50; H10W72/551; H10W72/552; H10W72/5522; H10W72/59; H10W72/851; H10W72/874; H10W72/884; H10W72/90; H10W72/951; H10W72/952; H10W74/00; H10W90/00; H10W90/701; H10W90/731; H10W90/734; H10W90/751; H10W90/754; H10W99/00; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12868; Y10T428/12889; Y10T428/12903; Y10T428/1291; Y10T428/24; Y10T428/24802; Y10T428/24917
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
144 words
A method for forming a gold plating electrode comprising: a step of forming a circuit pattern on a substrate; a step of forming a nickel-containing barrier metal layer at a portion where an electrode of said circuit pattern is formed; a step of forming a gold layer on said barrier metal layer by plating; a step of heating said substrate to cause nickel contained in said gold layer to move toward a surface zone of said gold layer to deposit nickel compound in said surface zone of said gold layer, thereby enhancing the fineness of a remaining part of said gold layer at at least an inside zone immediately below said surface zone; and a step of removing said surface zone containing said nickel compound off said gold layer so as to expose a purified surface of said inside zone of said gold layer.
Claim 2
Independent Claim
144 words
A method for forming a gold plating electrode comprising: a step of forming a circuit pattern on a substrate; a step of forming a nickel-containing barrier metal layer at a portion where an electrode of said circuit pattern is formed; a step of forming a gold layer on said barrier metal layer by plating; a step of heating said substrate to cause nickel contained in said gold layer to move toward a surface zone of said gold layer to deposit nickel compound in said surface zone of said gold layer, thereby enhancing the fineness of a remaining part of said gold layer at at least an inside zone immediately below said surface zone; and a step of removing said surface zone containing said nickel compound off said gold layer so as to expose a purified surface of said inside zone of said gold layer.
Claim 3
Dependent Claim
25 words
The method for forming a gold plating electrode defined by claim 1, wherein said surface zone containing said nickel compound is removed off by etching.
Claim 4
Dependent Claim
31 words
The method for forming a gold plating electrode defined by claim 1, wherein said surface zone containing said nickel compound is removed off by a thickness of 3 to 10 nanometer.
Claim 5
Dependent Claim
30 words
The method for forming a gold plating electrode defined by claim 1, wherein said substrate is heated at a temperature of 150 to 200 centigrade for 5 to 60 minutes.
Claim 6
Dependent Claim
33 words
The method for forming a gold plating electrode defined by claim 1, wherein said gold layer has a thickness of 5 to 100 nanometer when said gold layer is formed by said plating.
Claim 7
Dependent Claim
181 words
A wire bonding method comprising: a step of forming a. circuit pattern. on a substrate, forming a nickel-containing barrier metal layer at a portion where an electrode of said circuit pattern is formed, and forming a gold layer on said barrier metal layer by plating, thereby forming an electrode on said substrate; a step of heating said substrate to cause nickel contained in said gold layer to move toward a surface zone of said gold layer to deposit nickel compound in said surface zone of said gold layer, thereby enhancing the fineness of a remaining part of said gold layer at at least an inside zone immediately below said surface zone; a step of removing said surface zone containing said nickel compound off said gold layer by etching to expose a purified surface of said inside zone of said gold layer; a step of applying an adhesive material on said substrate and die bonding a chip on said adhesive material; and a step of connecting an electrode of said chip to said electrode of said substrate via an electrically conductive wire.
Claim 8
Dependent Claim
181 words
A wire bonding method comprising: a step of forming a. circuit pattern. on a substrate, forming a nickel-containing barrier metal layer at a portion where an electrode of said circuit pattern is formed, and forming a gold layer on said barrier metal layer by plating, thereby forming an electrode on said substrate; a step of heating said substrate to cause nickel contained in said gold layer to move toward a surface zone of said gold layer to deposit nickel compound in said surface zone of said gold layer, thereby enhancing the fineness of a remaining part of said gold layer at at least an inside zone immediately below said surface zone; a step of removing said surface zone containing said nickel compound off said gold layer by etching to expose a purified surface of said inside zone of said gold layer; a step of applying an adhesive material on said substrate and die bonding a chip on said adhesive material; and a step of connecting an electrode of said chip to said electrode of said substrate via an electrically conductive wire.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-06-15 | 2001-12-15 | 2002-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-06-15 | 2005-12-15 | 2006-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-06-15 | 2009-12-15 | 2010-06-16 | $7700.00 | Window Closed / Lapsed |