Film containing oriented dye, method of manufacturing the same, and polarizer and liquid crystal display unit utilizing the same
Assignee: Sumitomo Chemical Co Ltd
•
Filing: 1995-02-13
•
Granted: 1998-05-12
•
Expires: 2015-02-13
Abstract
Abstract Films containing oriented dye, methods of manufacturing such films, and polarizers and liquid crystal display devices utilizing the films are disclosed. The film contains at least one dichroic dye which is uniaxially oriented. A film has a thickness of not less than 1 nanometer and not greater than 5 micrometer and contains the dichroic dye of not less than 1 percent by weight and not greater than 100 percent by weight. The film has a peak of absorption at 400 nm through 800 nm and a dichroic ratio of not less than 25 at the peak of absorption. The film may include a micro-pattern having a minimum width in a film plane of not less than 1 micrometer and not greater than 200 micrometer. In such a case, the dichroic dye has a dichroic ratio of not less than 10 at the peak of absorption. A method of manufacturing such a film according to the invention includes the step of forming a dye-containing film on a substrate having a fluororesin alignment layer on the surface thereof. The dye-containing film includes at least one dichroic dye or a mixture of at least one dichroic dye and at least one polymer compound. In subsequent steps, the dye-containing film may be stripped off from the substrate and transferred to another substrate.
Inventors
- 👤 Alejandro Andreatta
- 👤 Shuji Doi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 15:14
CPC Classifications
G; G02; G02B; G02B5/00; G02B5/30; G02B5/3025; G02B5/3033; G02F; G02F1/00; G02F1/01; G02F1/13; G02F1/133; G02F1/1333; G02F1/1335; G02F1/133528; G02F1/133538
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
72 words
A uniaxially oriented film of a film-forming material comprising at least 1% by weight dichroic dye, said dye having a wavelength of peak absorbance of from 400 to 800 nanometers, the film having a thickness of from 1 nanometer to 5 micrometers, having a dichroic ratio of not less than 25 at the wavelength of peak absorbance and having been formed by deposit of the film-forming material upon a fluororesin alignment layer.
Claim 2
Dependent Claim
72 words
A uniaxially oriented film of a film-forming material comprising at least 1% by weight dichroic dye, said dye having a wavelength of peak absorbance of from 400 to 800 nanometers, the film having a thickness of from 1 nanometer to 5 micrometers, having a dichroic ratio of not less than 25 at the wavelength of peak absorbance and having been formed by deposit of the film-forming material upon a fluororesin alignment layer.
Claim 3
Dependent Claim
12 words
The uniaxially oriented film of claim 1 consisting essentially of dichroic dye.
Claim 4
Dependent Claim
21 words
The uniaxially oriented film of claim 1 comprising an admixture of binder polymer and at least 1% by weight dichroic dye.
Claim 5
Dependent Claim
19 words
The uniaxially oriented film of claim 1 wherein the dye has an aspect ratio of not less than 2.
Claim 6
Dependent Claim
11 words
The film of claim 1 wherein the fluroresin is PTFE polytetrafluorethylene.
Claim 7
Dependent Claim
18 words
A polarizer comprising a transparent support having a planar surface carrying a uniaxially oriented film of claim 1.
Claim 8
Dependent Claim
12 words
The polarizer of claim 6 wherein the support is a polymer film.
Claim 9
Dependent Claim
12 words
The polarizer of claim 6 wherein the support is a glass plate.
Claim 10
Dependent Claim
12 words
The polarizer of claim 6 wherein the support is a transparent electrode.
Claim 11
Dependent Claim
85 words
A liquid crystal display device comprising a liquid crystal cell containing a pair of separated transparent substrates having electrodes thereon and a nematic liquid crystal layer positioned between the substrates, the nematic liquid crystal layer having a positive dielectric anisotropy and a helical axis aligned vertically to the substrates and oriented substantially horizontally with a twist angle of from 90 to 270 degrees when no voltage is applied and a polarizer of claim 6 positioned adjacent to a transparent electrode of the liquid crystal cell.
Claim 12
Dependent Claim
13 words
The display device of claim 10 wherein the polarizer is outside the cell.
Claim 13
Dependent Claim
22 words
The display device of claim 10 wherein the polarizer is inside the cell between the liquid crystal layer and a transparent electrode.
Claim 14
Dependent Claim
86 words
A body of micro-patterned dye-containing film of a film-forming material comprising at least 1% by weight uniaxially oriented dichroic dye, said dye having a wavelength of peak absorbance of from 400 to 800 nanometers, the film having a thickness of from 1 nanometer to 5 micrometers, having a dichroic ratio of not less than 10 at the wavelength of peak absorbance, a micropattern width of from 1 to 200 micrometers and having been formed by deposit of the film-forming material upon a micropatterned fluororesin alignment layer.
Claim 15
Dependent Claim
86 words
A body of micro-patterned dye-containing film of a film-forming material comprising at least 1% by weight uniaxially oriented dichroic dye, said dye having a wavelength of peak absorbance of from 400 to 800 nanometers, the film having a thickness of from 1 nanometer to 5 micrometers, having a dichroic ratio of not less than 10 at the wavelength of peak absorbance, a micropattern width of from 1 to 200 micrometers and having been formed by deposit of the film-forming material upon a micropatterned fluororesin alignment layer.
Claim 16
Dependent Claim
14 words
The body of micro-patterned dye-containing film of claim 13 consisting essentially of dichroic dye.
Claim 17
Dependent Claim
23 words
The body of micro-patterned dye-containing film of claim 13 comprising an admixture of binder polymer and at least 1% by weight dichroic dye.
Claim 18
Dependent Claim
21 words
The body of micro-patterned dye-containing film of claim 13 wherein the dye has an aspect ratio of not less than 2.
Claim 19
Dependent Claim
22 words
A micropolarizer comprising a transparent support having a planar surface carrying a body of micro-patterned dye-containing uniaxially oriented film of claim 13.
Claim 20
Dependent Claim
12 words
The micropolarizer of claim 17 wherein the support is a polymer film.
Claim 21
Dependent Claim
12 words
The micropolarizer of claim 17 wherein the support is a glass plate.
Claim 22
Dependent Claim
12 words
The micropolarizer of claim 17 wherein the support is a transparent electrode.
Claim 23
Dependent Claim
85 words
A liquid crystal display device comprising a liquid crystal cell containing a pair of separated transparent substrates having electrodes thereon and a nematic liquid crystal layer positioned between the substrates, the nematic liquid crystal layer having a positive dielectric anisotropy and a helical axis aligned vertically to the substrates and oriented substantially horizontally with a twist angle of from 90 to 270 degrees when no voltage is applied and a micropolarizer of claim 17 positioned adjacent to a transparent electrode of the liquid crystal cell.
Claim 24
Dependent Claim
13 words
The display device of claim 21 wherein the polarizer is outside the cell.
Claim 25
Dependent Claim
22 words
The display device of claim 21 wherein the polarizer is inside the cell between the liquid crystal layer and a transparent electrode.
Claim 26
Dependent Claim
58 words
A uniaxially oriented film comprising at least 1% by weight dichroic dye and having a thickness of from 1 nanometer to 5 micrometers, a wavelength of peak absorbance of from 400 to 800 nanometers, and a dichroic ratio of not less than 25 at the wavelength of peak absorbance formed on and present upon a fluororesin alignment layer.
Claim 27
Dependent Claim
58 words
A uniaxially oriented film comprising at least 1% by weight dichroic dye and having a thickness of from 1 nanometer to 5 micrometers, a wavelength of peak absorbance of from 400 to 800 nanometers, and a dichroic ratio of not less than 25 at the wavelength of peak absorbance formed on and present upon a fluororesin alignment layer.
Claim 28
Dependent Claim
78 words
A body of micro-patterned dye-containing film comprising at least 1% by weight uniaxially oriented dichroic dye and having a thickness of from 1 nanometer to 5 micrometers, a wavelength of peak absorbance of from 400 to 800 nanometers, and a dichroic ratio of not less than 10 at the wavelength of peak absorbance, said micropattern having a length and width in the film plane with the width being from 1 to 200 micrometers on a fluororesin alignment layer.
Claim 29
Dependent Claim
78 words
A body of micro-patterned dye-containing film comprising at least 1% by weight uniaxially oriented dichroic dye and having a thickness of from 1 nanometer to 5 micrometers, a wavelength of peak absorbance of from 400 to 800 nanometers, and a dichroic ratio of not less than 10 at the wavelength of peak absorbance, said micropattern having a length and width in the film plane with the width being from 1 to 200 micrometers on a fluororesin alignment layer.
Claim 30
Independent Claim
99 words
A method for manufacturing a uniaxially-oriented, light polarizing film, the method comprising the steps of a) obtaining a solid fluororesin alignment layer having a thickness of from about 1 nanometer through about 2 micrometers, and b) forming a film from a film-forming material comprising at least 1% by weight dichroic dye and having a thickness of from 1 nanometer to 5 micrometers, a wavelength of peak absorbance of from 400 to 800 nanometers on said fluororesin alignment layer, thereby yielding a uniaxially oriented film having a dichroic ratio of not less than 25 at the wavelength of peak absorbance.
Claim 31
Independent Claim
99 words
A method for manufacturing a uniaxially-oriented, light polarizing film, the method comprising the steps of a) obtaining a solid fluororesin alignment layer having a thickness of from about 1 nanometer through about 2 micrometers, and b) forming a film from a film-forming material comprising at least 1% by weight dichroic dye and having a thickness of from 1 nanometer to 5 micrometers, a wavelength of peak absorbance of from 400 to 800 nanometers on said fluororesin alignment layer, thereby yielding a uniaxially oriented film having a dichroic ratio of not less than 25 at the wavelength of peak absorbance.
Claim 32
Dependent Claim
14 words
The method of claim 26 wherein the film-forming material additionally comprises a film-forming polymer.
Claim 33
Dependent Claim
27 words
The method of claim 26 comprising the additional steps of c) stripping the film from the alignment layer and d) applying the film to a supporting substrate.
Claim 34
Independent Claim
123 words
A method for manufacturing a body of micro-patterned dye-containing film comprising a) obtaining a solid fluororesin alignment layer having a thickness of from about 1 nanometer through about 2 micrometers and a defined width in the film plane of from 1 to 200 micrometers, and b) forming a film of a film-forming material comprising at least 1% by weight uniaxially oriented dichroic dye and having a thickness of from 1 nanometer to 5 micrometers, a wavelength of peak absorbance of from 400 to 800 nanometers on said fluororesin alignment layer thereby yielding a body of uniaxially oriented film having a defined width of from 1 to 200 micrometers and a dichroic ratio of not less than 10 at the wavelength of peak absorbance.
Claim 35
Independent Claim
123 words
A method for manufacturing a body of micro-patterned dye-containing film comprising a) obtaining a solid fluororesin alignment layer having a thickness of from about 1 nanometer through about 2 micrometers and a defined width in the film plane of from 1 to 200 micrometers, and b) forming a film of a film-forming material comprising at least 1% by weight uniaxially oriented dichroic dye and having a thickness of from 1 nanometer to 5 micrometers, a wavelength of peak absorbance of from 400 to 800 nanometers on said fluororesin alignment layer thereby yielding a body of uniaxially oriented film having a defined width of from 1 to 200 micrometers and a dichroic ratio of not less than 10 at the wavelength of peak absorbance.
Claim 36
Dependent Claim
27 words
The method of claim 29 comprising the additional steps of c) stripping the film from the alignment layer and d) applying the film to a supporting substrate.
References Cited (Backward Citations)
US3205775A
Cited
US3650625A
Cited
US4193287A
Cited
US4684434A
Cited
US4698121A
Cited
US5004324A
Cited
US4838658A
Cited
US5176786A
Cited
JPH02160697A
Cited
US5024850A
Cited
US5180470A
Cited
US5284779A
Cited
US5235449A
Cited
US5327285A
Cited
US5340504A
Cited
EP0562587A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-05-11 | 2001-11-10 | 2002-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-05-11 | 2005-11-10 | 2006-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-05-11 | 2009-11-10 | 2010-05-12 | $7700.00 | Window Closed / Lapsed |