Method for fabricating dimensionally accurate pieces by laser sintering
Assignee: ELECTRO OPTICAL SYSTEMS FINLAND Oy
•
Filing: 1995-09-20
•
Granted: 1998-03-24
•
Expires: 2015-09-20
Abstract
Abstract The invention relates to a method for the fabrication of dimensionally accurate metal pieces by sintering a material which, before the sintering, consists of a blend of three pulverous ingredients, of which the first ingredient is in the main an iron-group metal, the second ingredient is in the main copper and phosphorus, and the third ingredient is an alloy of copper and some other metal. The shape of the piece is produced by layer-by-layer freeform selected area laser sintering, wherein a layer of the said powder blend is spread on a base, those regions of the layer which correspond to this cross-sectional surface of the piece are heated by a laser beam to the sintering temperature. Thereafter further successive powder layers are spread one on top of another, and in each layer in turn those areas which correspond to the cross-sectional surface of the piece in that layer are laser sintered. The sintering takes place in a gas atmosphere which contains a chemical compound of some iron-group metal, the compound decomposing at the sintering temperature, in which case the iron-group metal will deposit into those cross-sectional areas of the piece being sintered at a given time.
Inventors
- 👤 Olli Juhani Nyrhila
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:16
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/10; B22F3/1003; B22F3/1007; B22F10/00; B22F10/20; B22F10/28; B22F10/30; B22F10/32; B22F10/38; B33; B33Y; B33Y10/00; B33Y50/00; B33Y50/02; B33Y70/00; B33Y70/10; B22F10/80; B22F10/85; B22F2201/00; B22F2201/40; B22F2998/00; B22F2999/00; Y; Y02; Y02P; Y02P10/00; Y02P10/25
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
226 words
A method for the fabrication of dimensionally accurate metal pieces by sintering a material which, before the sintering, consists of a blend of at least three pulverous ingredients, the first ingredient being an iron-group metal, the second ingredient being copper and phosphorus, and the third ingredient being an alloy of copper and at least one other metal, this powder blend of ingredients containing the third ingredient in the largest amount and both the first ingredient and the second ingredient in smaller amounts, characterized by the following combination: the shape of the piece is effected by layer-by-layer freeform selected area laser sintering, wherein a layer of the said powder blend is spread onto a base, those regions of the layer which correspond to this cross-sectional surface of the piece are heated to the sintering temperature by a laser beam, step by step, whereafter successive powder layers are spread one on top of another, in each of which those areas which correspond to the cross-sectional surface of the piece according to the layer concerned are laser sintered, and that the sintering is carried out in a gas atmosphere which contains a chemical compound, at least of an iron-group metal, which decomposes at the said sintering temperature, the iron-group metal depositing onto those areas of the cross-sectional surfaces of the piece which are being sintered at a given time.
Claim 2
Independent Claim
226 words
A method for the fabrication of dimensionally accurate metal pieces by sintering a material which, before the sintering, consists of a blend of at least three pulverous ingredients, the first ingredient being an iron-group metal, the second ingredient being copper and phosphorus, and the third ingredient being an alloy of copper and at least one other metal, this powder blend of ingredients containing the third ingredient in the largest amount and both the first ingredient and the second ingredient in smaller amounts, characterized by the following combination: the shape of the piece is effected by layer-by-layer freeform selected area laser sintering, wherein a layer of the said powder blend is spread onto a base, those regions of the layer which correspond to this cross-sectional surface of the piece are heated to the sintering temperature by a laser beam, step by step, whereafter successive powder layers are spread one on top of another, in each of which those areas which correspond to the cross-sectional surface of the piece according to the layer concerned are laser sintered, and that the sintering is carried out in a gas atmosphere which contains a chemical compound, at least of an iron-group metal, which decomposes at the said sintering temperature, the iron-group metal depositing onto those areas of the cross-sectional surfaces of the piece which are being sintered at a given time.
Claim 3
Dependent Claim
70 words
A method according to claim 1, characterized in that the said chemical compound of an iron-group metal is metal carbonyl, hydride, chloride, fluoride, iodide or bromide, or some other pyrolytically decomposing metal compound, and that the iron-group metal in the said chemical compound is preferably the same metal, or any one of the metals, as is present in the first ingredient of the powder blend, or alternatively some other metal.
Claim 4
Dependent Claim
91 words
A method according to claim 1 or 2, characterized in that the first ingredient is at least nickel and the average particle size of the first ingredient is at minimum 50 μm and at maximum 250 μm, preferably in the order of 100 μm, that the third ingredient is bronze and/or brass having an average particle size at maximum 50 μm and preferably at maximum30 μm, and that the second ingredient is copper phosphide having an average particle size at maximum equal to the average particle size of the first ingredient.
Claim 5
Dependent Claim
88 words
A method according to claim 1 or 2, characterized in that for the said powder blend there are mixed the third ingredient in an amount of approx. 60-75% by weight, the second ingredient in an amount of approx. 5-30% by weight, and the first ingredient in an amount of approx. 10-30% by weight, that the said gas atmosphere consists either of a gaseous compound of an iron-group metal and possibly other metal compounds, or of an iron-group metal compound and possibly other metal compounds in a carrier gas.
Claim 6
Dependent Claim
91 words
A method according to claim 1 or 2, characterized in that the powder blend is heated by the laser beam in its target areas to a temperature which is higher than the melting point of the second ingredient, that this temperature deviates by at maximum 100° C., preferably by at maximum 50° C., and typically by at maximum 30° C., in either direction from the melting point of the third ingredient, and that the said temperature produced by the laser beam is at maximum 950° C., preferably at maximum 900° C.
Claim 7
Dependent Claim
100 words
A method according to claim 1 or 2, characterized in that the decomposition of the iron-group metal compound present in the gas atmosphere elsewhere than in the laser-heated and thus sintering regions is prevented by cooling the base and/or by maintaining the temperature of the gas atmosphere in the area of the powder blend layers at a predetermined temperature, and that in those regions in which no sintering takes place the powder blend on the base is maintained at a temperature below 150° C., preferably at a temperature below 80° C., and typically at a temperature at maximum 40° C.
Claim 8
Dependent Claim
34 words
A method according to claim 6, characterized in that the temperature of the gas atmosphere is set at a predetermined value by means of gas circulation and/or gas exchange and/or cooling of the gas.
Claim 9
Dependent Claim
43 words
A method according to claim 1 or 2, characterized in that the first ingredient is a mixture of iron-group metals, and that in the first ingredient the said iron-group metal or mixture of iron-group metals additionally contains other metallic and/or nonmetallic alloying elements.
Claim 10
Dependent Claim
68 words
A method according to claim 1 or 2, characterized in that the gas atmosphere additionally comprises a chemical compound of a metal contained in the third ingredient, the chemical compound also decomposing at the sintering temperature, in which case the said metal or metals and/or non-metals and/or compounds will deposit into those areas of the cross-sectional surfaces of the piece which are being sintered at a given time.
Claim 11
Dependent Claim
113 words
A method according to claim 1, characterized in that the power and target area of the said laser are directed, in the layer-by-layer sintering of a powder blend and at the same time in the depositing of metal out from the gas phase, by computer or by numeric control, in which case the design for the piece has been sectioned into cross-sectional regions of the piece, corresponding to the thicknesses of the powder layers used, the regions together making up the form of the piece, these cross-sectional regions are stored in the memory for the said laser control, and the said control is implemented in accordance with these data stored in the memory.
References Cited (Backward Citations)
US4853514A
Cited
US5316580A
Cited
US4938816A
Cited
US5155324A
Cited
US5104748A
Cited
GB2220421A
Cited
US5637175A
Cited
WO1990011855A1
Cited
US5156697A
Cited
US5431967A
Cited
WO1991009149A1
Cited
WO1992010343A1
Cited
US5393613A
Cited
US5314003A
Cited
US5510066A
Cited
US5352405A
Cited
US5622769A
Cited
US5616423A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-03-23 | 2001-09-22 | 2002-03-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-03-23 | 2005-09-22 | 2006-03-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-03-23 | 2009-09-22 | 2010-03-24 | $7700.00 | Window Closed / Lapsed |