Wear resisting copper base alloy
Assignee: Toyota Motor Corp
•
Filing: 1990-03-09
•
Granted: 1992-04-14
•
Expires: 2010-03-09
Abstract
Abstract A copper base alloy exhibits improved wear resistance particularly at elevated temperatures, which consists essentially of, in percent by weight, 10-40% of Ni, 1-7% of Si, 0.5-5% of B, 1-20% of Cr, and the balance of Cu, wherein particles of at least one of chromium boride and chromium silicide having a size of about 0.1 to about 50 μm are evenly dispersed in a copper-nickel base matrix. The alloy may further contain W, Mo or Fe and/or a high-melting carbide such as WC and TaC.
Inventors
- 👤 Kazuhiko Mori
- 👤 Soya Takagi
- 👤 Minoru Kawasaki
- 👤 Shinji Kato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 02:18
CPC Classifications
C; C22; C22C; C22C9/00; C22C9/06; B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/30; B23K35/302; B23K35/32; B23K35/327; C22C1/00; C22C1/04; C22C1/05; C22C1/059; C22C32/00; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12903
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
158 words
A composite article comprising a dispersion-strengthened, copper-base alloy having improved heat resistance and wear resistance and a metallic substrate onto which said alloy is deposited, said alloy consisting essentially of, in weight percent; 10 to 40% nickel, 1 to 7% silicon, 0.5 to 5% boron, 1 to 20% chromium, and balance copper, with said deposited alloy having prealloyed particles of at least one of chromium boride and chromium silicide having a particle size of about 0.1 to 50 microns evenly dispersed in a copper-nickel base matrix of said deposited alloy, said alloy being deposited in the form of powder on said metallic substrate and then applying to said alloy powder high density heat energy to rapidly form a melt of said alloy powder and fuse said melt to said metallic substrate and thereafter rapidly quenching said melt to solidify said alloy thereof and form a solidified deposit of said alloy on said metallic substrate and crystallize said particles.
Claim 2
Dependent Claim
158 words
A composite article comprising a dispersion-strengthened, copper-base alloy having improved heat resistance and wear resistance and a metallic substrate onto which said alloy is deposited, said alloy consisting essentially of, in weight percent; 10 to 40% nickel, 1 to 7% silicon, 0.5 to 5% boron, 1 to 20% chromium, and balance copper, with said deposited alloy having prealloyed particles of at least one of chromium boride and chromium silicide having a particle size of about 0.1 to 50 microns evenly dispersed in a copper-nickel base matrix of said deposited alloy, said alloy being deposited in the form of powder on said metallic substrate and then applying to said alloy powder high density heat energy to rapidly form a melt of said alloy powder and fuse said melt to said metallic substrate and thereafter rapidly quenching said melt to solidify said alloy thereof and form a solidified deposit of said alloy on said metallic substrate and crystallize said particles.
Claim 3
Dependent Claim
35 words
The composite article of claim 1 wherein said copper-base alloy further includes at least one metal selected from the group consisting of 0.1 to 5% tungsten, 0.1 to 5% molybdenum, and 1 to 20% iron.
Claim 4
Dependent Claim
28 words
The composite article of claim 1 wherein said copper-base alloy further includes 1 to 20% of a high melting temperature carbide evenly dispersed in said copper-nickel base matrix.
Claim 5
Dependent Claim
52 words
The composite article of claim 1 wherein said copper-base alloy further includes at least one metal selected from the group consisting of 0.1 to 5% tungsten, 0.1 to 5% molybdenum, and 1 to 20% iron, and 1 to 20% of a high melting temperature carbide evenly dispersed in said copper-nickel base matrix.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-04-14 | 1995-10-14 | 1996-04-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-04-14 | 1999-10-14 | 2000-04-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-04-14 | 2003-10-14 | 2004-04-14 | $7700.00 | Window Closed / Lapsed |