Method of manufacturing a polysilicon resistor having uniform resistance
Assignee: Vanguard International Semiconductor Corp
•
Filing: 1996-07-18
•
Granted: 1998-03-17
•
Expires: 2016-07-18
Abstract
Abstract A method of manufacturing a polysilicon resistor which has a uniform high resistance includes a thermal process to increase the hydrogen concentration uniformity in the polysilicon resistor. The thermal step increases the diffusion of the hydrogen into and out of the third polysilicon, thereby helping to equalize the hydrogen concentration within the polysilicon resistor. The more uniform hydrogen concentration causes the resistance of the polysilicon resistor to be more uniform.
Inventors
- 👤 Shen-Wen Cheng
- 👤 Chun-Lin Cheng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:58
CPC Classifications
H; H10; H10B; H10B10/00; H10B10/15
Claims Analysis
Total Claims: 48
Claim 1
Independent Claim
87 words
A method of fabricating a polysilicon resistor on semiconductor substrate, said method comprising: forming a polysilicon layer above said semiconductor substrate; forming a first dielectric layer above said polysilicon layer; forming a conductive layer above said first dielectric layer; forming a second dielectric layer (intermetal dielectric layer; IMD) above said conductive layer; providing a nitrogen gas and hydrogen gas atmosphere for said semiconductor substrate, said polysilicon layer and said dielectric layer; and heating said polysilicon layer, wherein uniformity of hydrogen concentration in said polysilicon layer is increased.
Claim 2
Independent Claim
87 words
A method of fabricating a polysilicon resistor on semiconductor substrate, said method comprising: forming a polysilicon layer above said semiconductor substrate; forming a first dielectric layer above said polysilicon layer; forming a conductive layer above said first dielectric layer; forming a second dielectric layer (intermetal dielectric layer; IMD) above said conductive layer; providing a nitrogen gas and hydrogen gas atmosphere for said semiconductor substrate, said polysilicon layer and said dielectric layer; and heating said polysilicon layer, wherein uniformity of hydrogen concentration in said polysilicon layer is increased.
Claim 3
Dependent Claim
27 words
The method of claim 1 wherein said heating said polysilicon layer comprises heating said polysilicon layer to a temperature of about 400°-450° C. for about 30-60 minutes.
Claim 4
Dependent Claim
28 words
The method of claim 2 wherein said polysilicon layer is patterned and etched to form a load resistor for a metal oxide semiconductor field effect transistor (MOSFET) inverter.
Claim 5
Dependent Claim
18 words
The method of claim 3 wherein said MOSFET inverter is used to implement a static random access memory.
Claim 6
Independent Claim
220 words
A method of forming a polysilicon resistor in a SRAM memory cell, said method comprising: forming a silicon dioxide layer on a semiconductor substrate having impurity regions formed therein; forming a buried contact in said substrate; forming a first polysilicon layer on said silicon dioxide layer and on said substrate; forming a metal silicide layer on said first polysilicon layer; etching said silicon dioxide layer, said first polysilicon layer and said metal silicide layer to form a gate structure aligned between two impurity regions in said semiconductor substrate; forming a first dielectric layer over said gate structure, said substrate and said metal silicide layer; anisotropically etching said first dielectric layer to form a side wall spacer adjacent to said gate structure; forming a second dielectric layer on said gate structure, said substrate and said metal silicide layer; forming a contact hole in said second dielectric layer, whereby a portion of said metal silicide layer is exposed; forming a second polysilicon layer on said second dielectric layer and along the surface of said contact hole; patterning a photoresist on said second polysilicon layer and etching said second polysilicon layer to form a polysilicon load resistor; forming a third dielectric layer on said second dielectric layer, on said second polysilicon layer; and forming a fourth dielectric layer on said third dielectric layer.
Claim 7
Independent Claim
220 words
A method of forming a polysilicon resistor in a SRAM memory cell, said method comprising: forming a silicon dioxide layer on a semiconductor substrate having impurity regions formed therein; forming a buried contact in said substrate; forming a first polysilicon layer on said silicon dioxide layer and on said substrate; forming a metal silicide layer on said first polysilicon layer; etching said silicon dioxide layer, said first polysilicon layer and said metal silicide layer to form a gate structure aligned between two impurity regions in said semiconductor substrate; forming a first dielectric layer over said gate structure, said substrate and said metal silicide layer; anisotropically etching said first dielectric layer to form a side wall spacer adjacent to said gate structure; forming a second dielectric layer on said gate structure, said substrate and said metal silicide layer; forming a contact hole in said second dielectric layer, whereby a portion of said metal silicide layer is exposed; forming a second polysilicon layer on said second dielectric layer and along the surface of said contact hole; patterning a photoresist on said second polysilicon layer and etching said second polysilicon layer to form a polysilicon load resistor; forming a third dielectric layer on said second dielectric layer, on said second polysilicon layer; and forming a fourth dielectric layer on said third dielectric layer.
Claim 8
Dependent Claim
173 words
The method of claim 5, further comprising: patterning a photoresist on said fourth dielectric layer and etching said fourth dielectric layer, said third dielectric layer and said second dielectric layer to form a contact hole through said fourth dielectric layer, said third dielectric layer and said second dielectric layer to said substrate; forming a metal plug in said contact hole; forming a first conductive layer on said fourth dielectric layer and on said metal plug; forming a first inter metal dielectric layer on said first metal layer; forming a spin on glass (SOG) layer on said first inter metal dielectric layer; forming a second inter metal dielectric layer on said SOG layer; thermally treating said semiconductor substrate and layers formed thereon, wherein diffusion of hydrogen into and out of said second load resistor is increased, whereby uniformity of hydrogen concentration within said load resistor is increased. forming a second conductive layer on said second inter metal dielectric layer; and patterning a photoresist on said second conductive layer and etching said second conductive layer.
Claim 9
Dependent Claim
22 words
The method of claim 6, further comprising forming a third polysilicon layer on said silicon dioxide layer before forming said buried contact.
Claim 10
Dependent Claim
17 words
The method of claim 6, further comprising performing an annealing process after said contact hole is formed.
Claim 11
Dependent Claim
28 words
The method of claim 8, wherein said annealing is performed in a nitrogen gas ambient for about 30 minutes and at a temperature range of about 600°-800° C.
Claim 12
Dependent Claim
20 words
The method of claim 6, wherein said first polysilicon layer is formed to have a thickness of about 1000 angstroms.
Claim 13
Dependent Claim
15 words
The method of claim 10, further comprising ion implanting said first polysilicon layer with phosphorus.
Claim 14
Dependent Claim
23 words
The method of claim 11, wherein said ion implanting comprises implanting about 5E13-5E16 phosphorus atoms/cm 2 with an energy of about 30-50 KeV.
Claim 15
Dependent Claim
20 words
The method of claim 12, wherein said third polysilicon layer comprises doped polysilicon having a thickness of about 500 angstroms.
Claim 16
Dependent Claim
22 words
The method of claim 5, wherein said metal silicide layer comprises a tungsten silicide layer having a thickness of about 1000-1500 angstroms.
Claim 17
Dependent Claim
13 words
The method of claim 5, wherein said first dielectric layer comprises tetraethylorthosilicate (TEOS).
Claim 18
Dependent Claim
20 words
The method of claim 15, wherein said first dielectric layer is formed to have a thickness of about 1000-2000 angstroms.
Claim 19
Dependent Claim
12 words
The method of claim 5, wherein said second dielectric layer comprises TEOS.
Claim 20
Dependent Claim
20 words
The method of claim 10, wherein said second dielectric layer is formed to have a thickness of about 1000-2000 angstroms.
Claim 21
Dependent Claim
12 words
The method of claim 5, wherein said third dielectric layer comprises TEOS.
Claim 22
Dependent Claim
20 words
The method of claim 14, wherein said third dielectric layer is formed to have a thickness of about 1000-2000 angstroms.
Claim 23
Dependent Claim
14 words
The method of claim 5, wherein said fourth dielectric layer comprises borophosphosilicate glass (BPSG).
Claim 24
Dependent Claim
20 words
The method of claim 21, wherein said fourth dielectric layer is formed to have a thickness of about 4500 angstroms.
Claim 25
Dependent Claim
20 words
The method of claim 5, wherein said second polysilicon layer is formed to have a thickness of about 500-600 angstroms.
Claim 26
Dependent Claim
14 words
The method of claim 5, wherein said second polysilicon layer is doped with arsenic.
Claim 27
Dependent Claim
14 words
The method of claim 5, wherein said second polysilicon layer is doped with phosphorus.
Claim 28
Dependent Claim
27 words
The method of claim 25, wherein said second polysilicon layer is doped with a dosage of about 5E13-8E13 atoms/cm 2 with an energy of about 30-50 KeV.
Claim 29
Dependent Claim
42 words
The method of claim 6, wherein said thermally treating said substrate and layers deposited thereon comprises heating said substrate and said layers deposited thereon in a nitrogen gas with hydrogen gas ambient for about 30-60 minutes at temperature of about 400°-450° C.
Claim 30
Independent Claim
393 words
A method of fabricating a polysilicon load resistor in SRAM memory cell, said method comprising the step of: forming a silicon dioxide layer on a semiconductor substrate; forming a first polysilicon layer on said silicon dioxide layer; forming a buried contact by using dry etching process; forming a second polysilicon layer on said first polysilicon layer and on said substrate; forming a silicide layer on said second polysilicon layer; etching said silicon dioxide layer, said first polysilicon layer, said second polysilicon layer and said silicide layer to form a gate structure; forming a first tetraethylorthosilicate (TEOS) layer over said gate structure, said substrate and said silicide layer; anisotropically etching said first TEOS layer to form a side wall spacer adjacent to said gate structure; forming a second TEOS layer on said gate structure, said substrate and said silicide layer; forming a contact hole in said second TEOS layer and to expose a portion of said silicide layer; forming a third polysilicon layer on said second TEOS layer and along the surface of said contact hole; patterning a photoresist on said third polysilicon layer and etching said third polysilicon layer to form polysilicon load resistor; forming a third TEOS layer on said second dielectric layer and on said third polysilicon layer; forming a borophosphosilicate glass (BPSG) layer on said third TEOS layer; patterning a photoresist on said BPSG layer and etching said BPSG layer, said third TEOS layer and said second TEOS layer to form a contact hole through said BPSG layer, said third TEOS layer and said second TEOS layer to said substrate; performing a contact anneal; forming a first metal layer on said BPSG layer, wherein said contact hole is filled with said first metal layer; forming a metal plug by etching said first metal layer; forming a second metal layer on said BPSG layer and on said metal plug; forming a first inter metal dielectric layer on said second metal layer; forming a spin on glass (SOG) layer on said first inter metal dielectric layer; forming a second inter metal dielectric layer on said SOG layer; thermally treating the third polysilicon layer, wherein the third polysilicon layer has a hydrogen concentration with increased uniformity. forming a third metal layer on said first inter metal dielectric layer; and patterning a photoresist on said third metal layer and etching said third metal layer.
Claim 31
Independent Claim
393 words
A method of fabricating a polysilicon load resistor in SRAM memory cell, said method comprising the step of: forming a silicon dioxide layer on a semiconductor substrate; forming a first polysilicon layer on said silicon dioxide layer; forming a buried contact by using dry etching process; forming a second polysilicon layer on said first polysilicon layer and on said substrate; forming a silicide layer on said second polysilicon layer; etching said silicon dioxide layer, said first polysilicon layer, said second polysilicon layer and said silicide layer to form a gate structure; forming a first tetraethylorthosilicate (TEOS) layer over said gate structure, said substrate and said silicide layer; anisotropically etching said first TEOS layer to form a side wall spacer adjacent to said gate structure; forming a second TEOS layer on said gate structure, said substrate and said silicide layer; forming a contact hole in said second TEOS layer and to expose a portion of said silicide layer; forming a third polysilicon layer on said second TEOS layer and along the surface of said contact hole; patterning a photoresist on said third polysilicon layer and etching said third polysilicon layer to form polysilicon load resistor; forming a third TEOS layer on said second dielectric layer and on said third polysilicon layer; forming a borophosphosilicate glass (BPSG) layer on said third TEOS layer; patterning a photoresist on said BPSG layer and etching said BPSG layer, said third TEOS layer and said second TEOS layer to form a contact hole through said BPSG layer, said third TEOS layer and said second TEOS layer to said substrate; performing a contact anneal; forming a first metal layer on said BPSG layer, wherein said contact hole is filled with said first metal layer; forming a metal plug by etching said first metal layer; forming a second metal layer on said BPSG layer and on said metal plug; forming a first inter metal dielectric layer on said second metal layer; forming a spin on glass (SOG) layer on said first inter metal dielectric layer; forming a second inter metal dielectric layer on said SOG layer; thermally treating the third polysilicon layer, wherein the third polysilicon layer has a hydrogen concentration with increased uniformity. forming a third metal layer on said first inter metal dielectric layer; and patterning a photoresist on said third metal layer and etching said third metal layer.
Claim 32
Dependent Claim
26 words
The method of claim 28, wherein said contact annealing is performed in N ambient about 30 minutes, at a temperature between a range about 600°-800° C.
Claim 33
Dependent Claim
20 words
The method of claim 28, wherein said first polysilicon layer is doped polysilicon, having a thickness of about 500 angstroms.
Claim 34
Dependent Claim
20 words
The method of claim 28, wherein said second polysilicon layer is formed to have a thickness of about 1000 angstroms.
Claim 35
Dependent Claim
14 words
The method of claim 31, wherein said first polysilicon layer is implanted by phosphorus.
Claim 36
Dependent Claim
26 words
The method of claim 32, wherein said implantation has a dosage of about 5E13-5E16 atoms/cm 2 , the energy of said implantation is about 30-50 KeV.
Claim 37
Dependent Claim
19 words
The method of claim 28, wherein said silicide layer comprises tungsten silicide having a thickness of about 1000-1500 angstroms.
Claim 38
Dependent Claim
20 words
The method of claim 28, wherein said first TEOS layer is formed to have a thickness of about 1000-2000 angstroms.
Claim 39
Dependent Claim
20 words
The method of claim 28, wherein said second TEOS layer is formed to have a thickness of about 1000-2000 angstroms.
Claim 40
Dependent Claim
20 words
The method of claim 28, wherein said third TEOS layer is formed to have a thickness of about 1000-2000 angstroms.
Claim 41
Dependent Claim
19 words
The method of claim 28, wherein said BPSG layer is formed to have a thickness of about 4500 angstroms.
Claim 42
Dependent Claim
20 words
The method of claim 28, wherein said third polysilicon layer is formed to have a thickness of about 500-600 angstroms.
Claim 43
Dependent Claim
14 words
The method of claim 39, wherein said second polysilicon layer is doped with arsenic.
Claim 44
Dependent Claim
26 words
The method of claim 40, wherein the dosage of said implantation is between 5E13-8E13 atoms/cm 2 , the energy of said implantation is about 30-50 KeV.
Claim 45
Dependent Claim
25 words
The method of claim 28, wherein said thermal process is performed in N 2 with H 2 ambient about 30 minutes, at temperature 400°-450° C.
Claim 46
Dependent Claim
14 words
The method of claim 39 wherein said second polysilicon layer is doped with phosphorus.
Claim 47
Dependent Claim
36 words
The method of claim 28, wherein said first metal layer is composed of Ti/TiN composition layer, the thickness of said Ti layer is about 400-800 angstrom, the thickness of said TiN layer is about 800-1200 angstroms.
Claim 48
Dependent Claim
36 words
The method of claim 28, wherein said second metal layer is composed of AlSiCu/Ti composition layer, the thickness of said AlSiCu layer is about 4000-5000 angstrom, the thickness of said Ti layer is about 300-500 angstroms.
References Cited (Backward Citations)
US4475964A
Cited
US5461000A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-03-16 | 2001-09-15 | 2002-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-03-16 | 2005-09-15 | 2006-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-03-16 | 2009-09-15 | 2010-03-17 | $7700.00 | Window Closed / Lapsed |