Stress released VLSI structure by void formation
Assignee: United Microelectronics Corp
•
Filing: 1996-05-29
•
Granted: 1998-02-10
•
Expires: 2016-05-29
Abstract
Abstract A new method of forming controlled voids within the intermetal dielectric and within the passivation layer of an integrated circuit is achieved. A first layer of patterned metallization is provided over semiconductor device structures in and on a semiconductor substrate. An intermetal dielectric layer is deposited overlying the first patterned metal layer wherein the thickness of the intermetal dielectric layer is large enough so as to cause the formation of voids within the intermetal dielectric and wherein said voids are completely covered by said intermetal dielectric. A second layer of metallization is deposited over the intermetal dielectric and patterned. A passivation layer is deposited overlying the second patterned metal layer. The thickness of the passivation layer is large enough so as to cause the formation of voids within the passivation layer wherein said voids are completely covered by said passivation layer. The thermal stresses are released by the voids within the intermetal dielectric and within the passivation layer of the integrated circuit.
Inventors
- 👤 Water Lur
- 👤 Jenn-Tarng Lin
- 👤 Her-Song Liaw
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:51
CPC Classifications
H; H10; H10W; H10W74/00; H10W74/10; H10W74/131; H10W74/137; H10W20/00; H10W20/40; H10W20/45; H10W20/48; Y; Y10; Y10S; Y10S438/00; Y10S438/958
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
147 words
The method of forming stress releasing voids in the intermetal dielectric of an integrated circuit comprising: providing at least a first patterned metal layer having openings between metal lines over semiconductor device structures in and on a semiconductor substrate; depositing a silicon oxide and/or nitride intermetal dielectric layer overlying said first patterned metal layer wherein the deposition conditions and the thickness of said intermetal dielectric layer cause the formation of voids within said intermetal dielectric layer above openings between metal lines and entirely above the adjacent upper surfaces of said metal lines, wherein said voids are completely covered by said intermetal dielectric layer and wherein said voids are permanently placed upon formation; and depositing a second metal layer over said intermetal dielectric layer wherein thermal stresses experienced by said integrated circuit after said second metal layer is deposited are reduced by said voids within said intermetal dielectric.
Claim 2
Independent Claim
147 words
The method of forming stress releasing voids in the intermetal dielectric of an integrated circuit comprising: providing at least a first patterned metal layer having openings between metal lines over semiconductor device structures in and on a semiconductor substrate; depositing a silicon oxide and/or nitride intermetal dielectric layer overlying said first patterned metal layer wherein the deposition conditions and the thickness of said intermetal dielectric layer cause the formation of voids within said intermetal dielectric layer above openings between metal lines and entirely above the adjacent upper surfaces of said metal lines, wherein said voids are completely covered by said intermetal dielectric layer and wherein said voids are permanently placed upon formation; and depositing a second metal layer over said intermetal dielectric layer wherein thermal stresses experienced by said integrated circuit after said second metal layer is deposited are reduced by said voids within said intermetal dielectric.
Claim 3
Dependent Claim
45 words
The method of claim 1 wherein said openings in said metal layer are between about 0.3 to 1.5 microns and said intermetal dielectric layer is chemical vapor deposited silicon oxide to a thickness of between about 3,000 to 10,000 Angstroms wherein said voids are formed.
Claim 4
Dependent Claim
32 words
The method of claim 2 wherein said voids are formed by the deposition of said intermetal dielectric layer with suitable step coverage to the size of between about 0.05 to 1.3 microns.
Claim 5
Dependent Claim
26 words
The method of claim 1 wherein said intermetal dielectric layer is chemical vapor deposited silicon nitride to a thickness of between about 3,000 to 10,000 Angstroms.
Claim 6
Dependent Claim
40 words
The method of claim 1 wherein said openings in said metal layer are between about 0.3 to 1.5 microns and said intermetal dielectric layer is chemical vapor deposited silicon oxynitride to a thickness of between about 3,000 to 10,000 Angstroms.
Claim 7
Dependent Claim
55 words
The method of claim 1 wherein said openings in said metal layer are between about 0.3 to 1.5 microns and said intermetal dielectric layer is composed of one or more than one layer of chemical vapor deposited silicon oxide, silicon nitride, and silicon oxynitride to a total thickness of between about 3,000 to 10,000 Angstroms.
Claim 8
Dependent Claim
55 words
The method of claim 1 wherein said openings in said metal layer are between about 0.3 to 1.5 microns and said intermetal dielectric layer is composed of one or more than one layer of physical vapor deposited silicon oxide, silicon nitride, and silicon oxynitride to a total thickness of between about 3,000 to 10,000 Angstroms.
Claim 9
Dependent Claim
40 words
The method of claim 1 wherein said thermal stresses experienced by said substrate in the presence of voids are smaller that the thermal stresses experienced by said substrate in the absence of voids by two to three orders of magnitude.
Claim 10
Independent Claim
170 words
The method of forming stress releasing voids in the passivation layer of an integrated circuit comprising: providing a plurality of patterned metallization layers over semiconductor device structures in and on a semiconductor substrate wherein topmost of said patterned metallization layers has openings between metal lines; depositing a silicon oxide and/or nitride passivation layer overlying said topmost patterned metallization layer wherein the deposition conditions and the thickness of said passivation layer cause the formation of voids within said passivation layer and extending vertically above said openings between said metal lines and above adjacent upper surfaces of said wiring lines and extending vertically over at least half of the thickness of said passivation layer between said adjacent upper surfaces of said wiring lines and an upper surface of said passivation layer, wherein said voids are completely covered by said intermetal dielectric and wherein said voids are permanently placed upon formation; and completing fabrication of said integrated circuit wherein thermal stresses experienced by said substrate are reduced by voids within said passivation layer.
Claim 11
Independent Claim
170 words
The method of forming stress releasing voids in the passivation layer of an integrated circuit comprising: providing a plurality of patterned metallization layers over semiconductor device structures in and on a semiconductor substrate wherein topmost of said patterned metallization layers has openings between metal lines; depositing a silicon oxide and/or nitride passivation layer overlying said topmost patterned metallization layer wherein the deposition conditions and the thickness of said passivation layer cause the formation of voids within said passivation layer and extending vertically above said openings between said metal lines and above adjacent upper surfaces of said wiring lines and extending vertically over at least half of the thickness of said passivation layer between said adjacent upper surfaces of said wiring lines and an upper surface of said passivation layer, wherein said voids are completely covered by said intermetal dielectric and wherein said voids are permanently placed upon formation; and completing fabrication of said integrated circuit wherein thermal stresses experienced by said substrate are reduced by voids within said passivation layer.
Claim 12
Dependent Claim
45 words
The method of claim 9 said openings in said patterned metallization layer are between about 0.5 to 3.0 microns and wherein said passivation layer is chemical vapor deposited silicon oxide to a thickness of between about 3,000 to 30,000 Angstroms wherein said voids are formed.
Claim 13
Dependent Claim
31 words
The method of claim 10 wherein said voids are formed by the deposition of said passivation layer with suitable step coverage to the size of between about 0.05 to 2.8 microns.
Claim 14
Dependent Claim
40 words
The method of claim 9 wherein said openings in said patterned metallization layer are between about 0.5 to 3.0 microns and said passivation layer is chemical vapor deposited silicon nitride to a thickness of between about 3,000 to 30,000 Angstroms.
Claim 15
Dependent Claim
40 words
The method of claim 9 wherein said openings in said patterned metallization layer are between about 0.5 to 3.0 microns and said passivation layer is chemical vapor deposited silicon oxynitride to a thickness of between about 3,000 to 30,000 Angstroms.
Claim 16
Dependent Claim
55 words
The method of claim 9 wherein said openings in said patterned metallization layer are between about 0.5 to 3.0 microns and wherein said passivation layer is composed of one or more than one layer of chemical vapor deposited silicon oxide, silicon nitride, and silicon oxynitride to a thickness of between about 3,000 to 30,000 Angstroms.
Claim 17
Dependent Claim
55 words
The method of claim 9 wherein said openings in said patterned metallization layer are between about 0.5 to 3.0 microns and wherein said passivation layer is composed of one or more than one layer of physical vapor deposited silicon oxide, silicon nitride, and silicon oxynitride to a thickness of between about 3,000 to 30,000 Angstroms.
Claim 18
Dependent Claim
23 words
A method according to claim 1 wherein said voids are formed above said openings and above the top surface of said metal lines.
Claim 19
Dependent Claim
72 words
A method according to claim 1 wherein said step coverage is within the range defined by the following formula: minimum step coverage is equal to twice the minimum thickness of said intermetal dielectric layer divided by the spacing between said metal lines; and maximum step coverage is equal to the difference between said spacing between said metal lines and the minimum size of said voids divided by said spacing between metal lines.
Claim 20
Dependent Claim
23 words
A method according to claim 9 wherein said voids are formed above said openings and above the top surface of said metal lines.
Claim 21
Dependent Claim
72 words
A method according to claim 9 wherein said step coverage is within the range defined by the following formula: minimum step coverage is equal to twice the minimum thickness of said intermetal dielectric layer divided by the spacing between said metal lines; and maximum step coverage is equal to the difference between said spacing between said metal lines and the minimum size of said voids divided by said spacing between metal lines.
References Cited (Backward Citations)
JPS63111651A
Cited
JPS63232447A
Cited
US5099304A
Cited
US5119164A
Cited
US5192715A
Cited
US5217926A
Cited
US5290358A
Cited
US5278103A
Cited
US5310700A
Cited
US5545919A
Cited
US5517062A
Cited
US5407860A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-02-09 | 2001-08-11 | 2002-02-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-02-09 | 2005-08-11 | 2006-02-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-02-09 | 2009-08-11 | 2010-02-10 | $7700.00 | Window Closed / Lapsed |