Method for forming interconnections and conductors for high density integrated circuits
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1996-01-16
•
Granted: 1998-01-20
•
Expires: 2016-01-16
Abstract
Abstract The present invention provides a method of manufacturing miniature interconnect for semiconductor devices. The method uses a configuration of spacers and etch barriers (silicon nitride cap layers) to form self aligned source and drain contacts. Antireflective silicon nitride cap layers and highly selective etches are used define smaller interconnect openings. First spacers are formed on the gate electrodes. Later, the second spacers are formed the sidewalls of a storage electrode hole formed in insulation layers over the gate electrodes. The inventive self-aligning process, which uses the two set of spacers, allows a wide processing window for contact etching to form the contact hole and permit a small contact hole aspect ratio. The method reduces the masking steps by defining both the source and drain contacts in the same masking step.
Inventors
- 👤 Erik S. Jeng
- 👤 Ing-Ruey Liaw
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 05:03
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10B12/033
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
225 words
A method of fabricating an interconnect on a semiconductor substrate having a device area and spaced isolation regions formed therein; comprising the steps of: a) providing spaced gate electrodes on said device area and conductive structures on said isolation regions; said gate electrodes and conductive structures having a top surface formed of a first isolation cap layer composed of an anti reflective silicon nitride film; said gate electrodes and conductive structures having sidewalls; b) forming first isolation spacers composed of silicon nitride on the sidewalls of said gate electrodes and on the sidewalls of said conductive structures; c) forming a top isolation layer covering said first isolation cap layer over said gate electrodes; d) forming sequentially a first polysilicon layer, a dielectric layer, and a second isolation cap layer, over the substrate surface; e) forming a first opening having first sidewalls by masking and selectively etching said second isolation layer and said dielectric layer between said gate electrode and said conductive structure; and etching upper portions of said first polysilicon layer between said gate electrode and said conductive structure thereby forming a bottom node plug; f) forming second isolation spacers on said first sidewalls of said first opening; and g) forming a top node plug filling said first opening and forming a contact to said bottom node plug thereby forming said interconnect to said substrate.
Claim 2
Independent Claim
225 words
A method of fabricating an interconnect on a semiconductor substrate having a device area and spaced isolation regions formed therein; comprising the steps of: a) providing spaced gate electrodes on said device area and conductive structures on said isolation regions; said gate electrodes and conductive structures having a top surface formed of a first isolation cap layer composed of an anti reflective silicon nitride film; said gate electrodes and conductive structures having sidewalls; b) forming first isolation spacers composed of silicon nitride on the sidewalls of said gate electrodes and on the sidewalls of said conductive structures; c) forming a top isolation layer covering said first isolation cap layer over said gate electrodes; d) forming sequentially a first polysilicon layer, a dielectric layer, and a second isolation cap layer, over the substrate surface; e) forming a first opening having first sidewalls by masking and selectively etching said second isolation layer and said dielectric layer between said gate electrode and said conductive structure; and etching upper portions of said first polysilicon layer between said gate electrode and said conductive structure thereby forming a bottom node plug; f) forming second isolation spacers on said first sidewalls of said first opening; and g) forming a top node plug filling said first opening and forming a contact to said bottom node plug thereby forming said interconnect to said substrate.
Claim 3
Dependent Claim
30 words
The method of claim 1 which further includes forming a capacitor dielectric layer and a top electrode layer over said interconnect thereby forming a capacitor and completing a memory cell.
Claim 4
Dependent Claim
137 words
The method of claim 1 wherein said gate electrode and said conductive structure comprise: (1) a gate oxide layer, (2) a conductive layer, (3) a gate insulation layer, and (4) a first isolation cap layer; said first isolation cap layer is formed of silicon nitride having an anti-reflective coating formed by a low pressure chemical vapor deposition (LPCVD) process by reacting an excess of dichlorosilane with ammonia with a ratio in the range of between about 2.0 and 4.0, and at a pressure in the range of between about 100 and 500 mTorr, and at a temperature in the range of between about 750° and 850° C., and said first isolation cap layer having a thickness in the range of between about 200 and 2000 Å and an extinction coefficient (k) in range of 0.3 to 0.5.
Claim 5
Dependent Claim
59 words
The method of claim 1 wherein said first isolation cap layer is formed of a silicon oxide layer over a silicon nitride layer; and said silicon nitride layer having a thickness in the range of between about 400 and 2000 Å and the silicon oxide layer has a thickness in the range of between about 200 and 1000 Å.
Claim 6
Dependent Claim
29 words
The method of claim 1 wherein said first isolation spacers are formed of silicon nitride and have a thickness in the range of between about 200 and 2000 Å.
Claim 7
Dependent Claim
41 words
The method of claim 1 wherein the distance between said gate electrodes is in the range of between about 0.25 and 0.4 μm and the distance between said first isolation spacers in the range of between about 0.2 and 0.35 μm.
Claim 8
Dependent Claim
28 words
The method of claim 1 wherein said top isolation layer has a thickness in the range of between about 1000 and 5500 Åand is composed of borophosphosilicate glass.
Claim 9
Dependent Claim
23 words
The method of claim 1 wherein said first polysilicon layer has a thickness in the range of between about 1000 and 6000 Å.
Claim 10
Dependent Claim
27 words
The method of claim 1 wherein said dielectric layer has a thickness in the range of between about 500 and 2000 and is formed of silicon oxide.
Claim 11
Dependent Claim
63 words
The method of claim 1 wherein said second isolation cap layer is formed of silicon nitride having an anti-reflective coating formed by a LPCVD process by reacting an excess of dichlorosilane with ammonia and the first isolation layer has a thickness in the range of between about 600 and 1800 Å. and an extinction coefficient (k) in range of about 0.3 to 0.5.
Claim 12
Dependent Claim
215 words
The method of claim 1 wherein said selective etching used to etch said second isolation cap layer is a highly selective silicon nitride etch; said highly selective etch having a main etch step and an over etch step; said main etch step performed with a pressure in the range of between about 280 and 320 mtorr and a power in the range of between about 250 and 300 watts, and a gap in the range of between about 0.7 and 0.9 cm, and a SF 6 flow in the range of between about 60 and 80 sccm, and a CHF 3 flow in the range of between about 9 and 11 sccm, and a He flow in the range of between about 240 and 260 sccm; and said over etch step performed with a pressure in the range of between about 725 and 775 mtorr and a power in the range of between about 180 and 200 watts, and a gap in the range of between about 0.9 and 1.1 cm, and a SF 6 flow in the range of between about 110 and 130 sccm, and a CHF 3 flow in the range of between about 9 and 11 sccm, and a He flow in the range of between about 18 and 22 sccm.
Claim 13
Dependent Claim
15 words
The method of claim 1 wherein said second isolation spacers are formed of borophosphosilicate glass.
Claim 14
Independent Claim
345 words
A method of fabricating a capacitor on a semiconductor substrate having a device area and spaced isolation regions formed therein; comprising the steps of: a) forming a gate oxide layer over said substrate and said isolation regions; b) forming a first conductive layer over said gate oxide layer; c) forming a gate dielectric layer over said first conductive layer; d) forming a first isolation cap layer over said gate dielectric layer; said first isolation cap layer formed of anti-reflective silicon nitride; e) patterning said gate oxide layer, said first conductive layer, gate dielectric layer, and said first isolation cap layer to form spaced gate electrodes over said device area and conductive structures over said isolation regions; f) forming first isolation spacers on the sidewalls of said gate electrodes and on the sidewalls of said conductive structures; said first isolation spacers formed of silicon nitride; g) implanting impurity ions into said substrate surface using said gate electrodes and said isolation spacers as a mask forming sources and drains; h) forming a top isolation layer covering the first isolation cap layer over said gate electrodes; said top isolation layer composed of silicon oxide; i) forming sequentially a first polysilicon layer, a dielectric layer, and a second isolation cap layer over the resulting structure; said second isolation cap layer composed of anti reflective silicon nitride; j) forming a first opening having first sidewalls by masking and selectively etching said second isolation cap layer and said dielectric layer over said source; and etching upper portions of said first polysilicon layer over said source forming a bottom node plug; and forming a drain contact to said drain, k) forming second isolation spacers on said first sidewalls of said first opening; said second isolation spacers formed of silicon oxide; and l) forming a top node plug filling said first opening and forming an electrical contact to said bottom node plug thereby forming a interconnect to said source; and m) forming a capacitor dielectric layer and a top electrode layer over said interconnect thereby forming a capacitor and completing a memory cell.
Claim 15
Independent Claim
345 words
A method of fabricating a capacitor on a semiconductor substrate having a device area and spaced isolation regions formed therein; comprising the steps of: a) forming a gate oxide layer over said substrate and said isolation regions; b) forming a first conductive layer over said gate oxide layer; c) forming a gate dielectric layer over said first conductive layer; d) forming a first isolation cap layer over said gate dielectric layer; said first isolation cap layer formed of anti-reflective silicon nitride; e) patterning said gate oxide layer, said first conductive layer, gate dielectric layer, and said first isolation cap layer to form spaced gate electrodes over said device area and conductive structures over said isolation regions; f) forming first isolation spacers on the sidewalls of said gate electrodes and on the sidewalls of said conductive structures; said first isolation spacers formed of silicon nitride; g) implanting impurity ions into said substrate surface using said gate electrodes and said isolation spacers as a mask forming sources and drains; h) forming a top isolation layer covering the first isolation cap layer over said gate electrodes; said top isolation layer composed of silicon oxide; i) forming sequentially a first polysilicon layer, a dielectric layer, and a second isolation cap layer over the resulting structure; said second isolation cap layer composed of anti reflective silicon nitride; j) forming a first opening having first sidewalls by masking and selectively etching said second isolation cap layer and said dielectric layer over said source; and etching upper portions of said first polysilicon layer over said source forming a bottom node plug; and forming a drain contact to said drain, k) forming second isolation spacers on said first sidewalls of said first opening; said second isolation spacers formed of silicon oxide; and l) forming a top node plug filling said first opening and forming an electrical contact to said bottom node plug thereby forming a interconnect to said source; and m) forming a capacitor dielectric layer and a top electrode layer over said interconnect thereby forming a capacitor and completing a memory cell.
Claim 16
Dependent Claim
105 words
The method of claim 13 wherein said first isolation cap layer is formed of antireflective silicon nitride formed by a low pressure chemical vapor deposition (LPCVD) process by reacting an excess of dichlorosilane with ammonia with a ratio in the range of between about 2 and 4 and at a pressure in the range of between about 100 and 500 mTorr and at a temperature in the range of between about 750° and 850° C., and said first isolation cap layer has a thickness in the range of between about 200 and 2000 Å and an extinction coefficient (k) in range of 0.3 to 0.5.
Claim 17
Dependent Claim
29 words
The method of claim 13 wherein said first isolation spacers are formed of silicon nitride and have a thickness in the range of between about 200 and 2000 Å.
Claim 18
Dependent Claim
29 words
The method of claim 13 wherein said top isolation layer has a thickness in the range of between about 1000 and 5500 Å and is composed of borophosphosilicate glass.
Claim 19
Dependent Claim
35 words
The method of claim 13 wherein said dielectric layer has a thickness in the range of between about 500 and 2000 and is formed by a silicon oxide using a LPCVD process with Tetraethylorthosilicate (TEOS).
Claim 20
Dependent Claim
62 words
The method of claim 13 wherein said second isolation cap layer is formed of silicon nitride having an anti-reflective coating formed by a LPCVD process by reacting an excess of dichlorosilane with ammonia and the first isolation layer has a thickness in the range of between about 600 and 1800 Å and an extinction coefficient (k) in range of 0.3 to 0.5.
Claim 21
Dependent Claim
213 words
The method of claim 13 wherein said selective etching used to etch said second isolation cap layer is a highly selective silicon nitride etch; said highly selective etch having a main etch step and an over etch step; said main etch performed with a pressure in the range of between about 280 and 320 mtorr and a power in the range of between about 250 and 300 watts, and a gap in the range of between about 0.7 and 0.9 cm, and a SF 6 flow in the range of between about 60 and 80 sccm, and a CHF 3 flow in the range of between about 9 and 11 sccm, and a He flow in the range of between about 240 and 260 sccm; said over etch step performed with a pressure in the range of between about 725 and 775 mtorr and a power in the range of between about 180 and 200 watts, and a gap in the range of between about 0.9 and 1.1 cm, and a SF 6 flow in the range of between about 110 and 130 sccm, and a CHF 3 flow in the range of between about 9 and 11 sccm, and a He flow in the range of between about 18 and 22 sccm.
Claim 22
Independent Claim
545 words
A method of fabricating an interconnect on a semiconductor substrate having a device area and spaced isolation regions formed therein; comprising the steps of: a) forming a gate oxide layer over said substrate and said isolation regions; b) forming a first conductive layer over said gate oxide layer; c) forming a gate dielectric layer over said first conductive layer; said gate dielectric layer composed of silicon oxide; d) forming a first isolation cap layer over said gate dielectric layer; said first isolation cap layer formed of an anti-reflective silicon nitride coating; e) patterning said gate oxide layer, said first conductive layer, gate dielectric layer, and said first isolation cap layer to form spaced gate electrodes over said device area and conductive structures over said isolation regions; f) forming first isolation spacers composed of silicon nitride on the sidewalls of said gate electrodes and on the sidewalls of said conductive structures by forming a first isolation layer over the substrate surface and anisotrophically etching said first isolation layer using a highly selective silicon nitride etch; said highly selective etch having a main etch step and a over etch step; said main etch step performed with a pressure in the range of between about 280 and 320 mtorr and a power in the range of between about 250 and 300 watts, and a gap in the range of between about 0.7 and 0.9 cm, and a SF 6 flow in the range of between about 60 and 80 sccm, and a CHF 3 flow in the range of between about 9 and 11 sccm, and a He flow in the range of between about 240 and 260 sccm; said over etch step performed with a pressure in the range of between about 725 and 775 mtorr and a power in the range of between about 180 and 200 watts, and a gap in the range of between about 0.9 and 1.1 cm, and a SF 6 flow in the range of between about 110 and 130 sccm, and a CHF 3 flow in the range of between about 9 and 11 sccm, and a He flow in the range of between about 18 and 22 sccm; g) implanting impurity ions into said substrate surface using said gate electrodes and said isolation spacers as a mask forming highly doped sources and drains; h) forming a top isolation layer covering the first isolation cap layer over said gate electrodes; said top isolation layer formed of silicon oxide; i) forming sequentially a first polysilicon layer, a dielectric layer, and a second isolation cap layer, over the resulting structure; said second isolation cap layer formed of an anti-reflective silicon nitride coating; j) forming a first opening having first sidewalls by masking and selectively etching said second isolation cap layer and said dielectric layer, over said source; and etching upper portion of said first polysilicon layer over said source forming a bottom node plug; and forming a drain contact to said highly doped drain, k) forming second isolation spacers on said first sidewalls of said first opening; said second isolation spacers formed of borophosphosilicate glass; and l) forming a top node plug filling said first opening and forming a contact to said bottom node plug thereby forming a interconnect to said source.
Claim 23
Independent Claim
545 words
A method of fabricating an interconnect on a semiconductor substrate having a device area and spaced isolation regions formed therein; comprising the steps of: a) forming a gate oxide layer over said substrate and said isolation regions; b) forming a first conductive layer over said gate oxide layer; c) forming a gate dielectric layer over said first conductive layer; said gate dielectric layer composed of silicon oxide; d) forming a first isolation cap layer over said gate dielectric layer; said first isolation cap layer formed of an anti-reflective silicon nitride coating; e) patterning said gate oxide layer, said first conductive layer, gate dielectric layer, and said first isolation cap layer to form spaced gate electrodes over said device area and conductive structures over said isolation regions; f) forming first isolation spacers composed of silicon nitride on the sidewalls of said gate electrodes and on the sidewalls of said conductive structures by forming a first isolation layer over the substrate surface and anisotrophically etching said first isolation layer using a highly selective silicon nitride etch; said highly selective etch having a main etch step and a over etch step; said main etch step performed with a pressure in the range of between about 280 and 320 mtorr and a power in the range of between about 250 and 300 watts, and a gap in the range of between about 0.7 and 0.9 cm, and a SF 6 flow in the range of between about 60 and 80 sccm, and a CHF 3 flow in the range of between about 9 and 11 sccm, and a He flow in the range of between about 240 and 260 sccm; said over etch step performed with a pressure in the range of between about 725 and 775 mtorr and a power in the range of between about 180 and 200 watts, and a gap in the range of between about 0.9 and 1.1 cm, and a SF 6 flow in the range of between about 110 and 130 sccm, and a CHF 3 flow in the range of between about 9 and 11 sccm, and a He flow in the range of between about 18 and 22 sccm; g) implanting impurity ions into said substrate surface using said gate electrodes and said isolation spacers as a mask forming highly doped sources and drains; h) forming a top isolation layer covering the first isolation cap layer over said gate electrodes; said top isolation layer formed of silicon oxide; i) forming sequentially a first polysilicon layer, a dielectric layer, and a second isolation cap layer, over the resulting structure; said second isolation cap layer formed of an anti-reflective silicon nitride coating; j) forming a first opening having first sidewalls by masking and selectively etching said second isolation cap layer and said dielectric layer, over said source; and etching upper portion of said first polysilicon layer over said source forming a bottom node plug; and forming a drain contact to said highly doped drain, k) forming second isolation spacers on said first sidewalls of said first opening; said second isolation spacers formed of borophosphosilicate glass; and l) forming a top node plug filling said first opening and forming a contact to said bottom node plug thereby forming a interconnect to said source.
Claim 24
Dependent Claim
30 words
The method of claim 20 which further includes forming a capacitor dielectric layer and a top electrode layer over said interconnect thereby forming a capacitor and completing a memory cell.
Claim 25
Dependent Claim
108 words
The method of claim 20 wherein said first isolation cap layer and second isolation cap layer are formed of silicon nitride having an anti-reflective coating formed by a LPCVD process by reacting an excess of dichlorosilane with ammonia with a ratio in the range of between about 2 and 4 and at a pressure in the range of between about 100 and 500 mTorr and at a temperature in the range of between about 750° and 850° C., and said first isolation cap layer has a thickness in the range of between about 200 and 2000 Å. and an extinction coefficient (k) in range of 0.3 to 0.5.
Claim 26
Dependent Claim
41 words
The method of claim 20 wherein the distance between said gate electrodes is in the range of between about 0.25 and 0.4 μm and the distance between said first isolation spacers in the range of between about 0.2 and 0.35 μm.
Claim 27
Dependent Claim
29 words
The method of claim 20 wherein said top isolation layer has a thickness in the range of between about 1000 and 5500 Å and is composed of borophosphosilicate glass.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-01-19 | 2001-07-21 | 2002-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-01-19 | 2005-07-21 | 2006-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-01-19 | 2009-07-21 | 2010-01-20 | $7700.00 | Window Closed / Lapsed |