Composite bump structure and methods of fabrication
Assignee: Industrial Technology Research Institute
•
Filing: 1995-07-26
•
Granted: 1998-01-13
•
Expires: 2015-07-26
Abstract
Abstract A composite bump structure and methods of forming the composite bump structure. The composite bump structure comprises a polymer body of relatively low Young's Modulus compared to metals covered by a conductive metal coating formed at the input/output pads of an integrated circuit element or substrate. The composite bump is formed using material deposition, lithography, and etching techniques. A layer of soldering metal can be formed on the composite bumps if this is desired for subsequent processing. A base metal pad covering the integrated circuit element input/output pad can be used to provide added flexibility in location of the composite bump. The composite bump can be formed directly on the input/output pad or on the base metal pad.
Inventors
- 👤 Shyh-Ming Chang
- 👤 Yu-Chi Lee
- 👤 Jwo-huei Jou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:35
CPC Classifications
H; H10; H10W; H10W72/00; H10W72/20; H10W72/01; H10W72/012; H10W72/01231; H10W72/01251; H10W72/221; H10W72/222; H10W72/223; H10W72/231; H10W72/234; H10W72/241; H10W72/242; H10W72/245; H10W72/251; H10W72/253; H10W72/255; H10W72/90; H10W72/921; H10W72/923; H10W72/951; H10W72/952
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
96 words
A method of forming composite bumps, comprising the steps of: providing an integrated circuit element or substrate with input/output pads on the top surface of said integrated circuit element or substrate; forming a dielectric layer over the top surface of said integrated circuit element or substrate and over said input/output pads having contact openings directly over said input/output pads wherein said contact openings expose at least a part of each said input/output pad; and forming composite bumps on said input/output pads wherein each said composite bump comprises a polymer body covered by a conductive metal coating.
Claim 2
Independent Claim
96 words
A method of forming composite bumps, comprising the steps of: providing an integrated circuit element or substrate with input/output pads on the top surface of said integrated circuit element or substrate; forming a dielectric layer over the top surface of said integrated circuit element or substrate and over said input/output pads having contact openings directly over said input/output pads wherein said contact openings expose at least a part of each said input/output pad; and forming composite bumps on said input/output pads wherein each said composite bump comprises a polymer body covered by a conductive metal coating.
Claim 3
Dependent Claim
164 words
The method of claim 1 wherein forming said composite bumps comprises the steps of: forming a polymer layer on the top surface of said dielectric layer covering said input/output pads; forming a first photoresist mask on the top surface of said polymer layer directly over said input/output pads; etching away said polymer layer not protected by said first photoresist mask thereby forming a plurality of said polymer bodies; stripping said first photoresist mask; forming a second photoresist mask on the top surface of said integrated circuit element or substrate, except those areas of said integrated circuit element or substrate covered by said polymer bodies; forming a conductive metal layer over the top surface of said second photoresist mask and over said polymer bumps; and removing said second photoresist mask thereby removing said conductive metal layer on the top surface of said second photoresist mask and leaving said conductive metal layer on said polymer bodies thereby forming said conductive metal coating and said composite bumps.
Claim 4
Dependent Claim
140 words
The method of claim 1 wherein forming said composite bumps comprises the steps of: forming a photosensitive polymer layer on the top surface of said dielectric layer covering said input/output pads; exposing and developing a pattern on said photosensitive polymer so as to leave photosensitive polymer directly over said input/output pads only thereby forming a plurality of said polymer bodies; forming a photoresist mask on the top surface of said dielectric layer so that said polymer bodies are not covered by said photoresist mask; forming a conductive metal layer over the top surface of said photoresist mask and said polymer bodies; and removing said photoresist mask thereby removing said conductive metal layer on the top surface of said photoresist mask and leaving said conductive metal layer on said polymer bodies thereby forming said conductive metal coating and said composite bumps.
Claim 5
Dependent Claim
165 words
The method of claim 1 wherein forming said composite bumps comprises the steps of: forming a first photoresist mask over the top surface of said dielectric layer except those areas directly over said input/output pads; forming a polymer layer on the top surface of said first photoresist mask and those areas of said input/output pads not covered by said first photoresist mask; removing said first photoresist mask thereby removing said polymer on the top surface of said first photoresist mask and leaving polymer over said input/output pads thereby forming a plurality of said polymer bodies; forming a conductive metal layer on the top surface of said dielectric layer and said polymer bodies; forming a second photoresist mask on the top surface of said conductive metal layer directly over said polymer bodies; and etching away said conductive metal layer not covered by said second photoresist mask thereby leaving a conductive metal layer over said polymer bodies and forming said conductive metal coating and said composite bumps.
Claim 6
Independent Claim
132 words
A method of forming composite bumps, comprising the steps of: providing an integrated circuit element or substrate with input/output pads on the top surface of said integrated circuit element or substrate; forming a dielectric layer over the top surface of said integrated circuit element or substrate having contact openings directly over said input/output pads, wherein said contact openings expose at least a part of each said input/output pad; forming a base metal layer over said dielectric layer covering said input/output pads; forming composite bumps on said base metal layer, wherein each said composite bump comprises a polymer body covered by a conductive metal coating; and removing part or all of that part of said base metal layer which is not covered by said composite bumps and does not cover said/input output pads.
Claim 7
Independent Claim
132 words
A method of forming composite bumps, comprising the steps of: providing an integrated circuit element or substrate with input/output pads on the top surface of said integrated circuit element or substrate; forming a dielectric layer over the top surface of said integrated circuit element or substrate having contact openings directly over said input/output pads, wherein said contact openings expose at least a part of each said input/output pad; forming a base metal layer over said dielectric layer covering said input/output pads; forming composite bumps on said base metal layer, wherein each said composite bump comprises a polymer body covered by a conductive metal coating; and removing part or all of that part of said base metal layer which is not covered by said composite bumps and does not cover said/input output pads.
Claim 8
Dependent Claim
217 words
The method of claim 5 wherein forming composite bumps on said base metal layer and removing part or all of that part of said base metal layer which is not covered by said composite bumps and does not cover said input output/pads comprises the steps of: forming a polymer layer on the top surface of said base metal layer; forming a first photoresist mask on the top surface of said polymer layer; etching away said polymer not protected by said first photoresist mask thereby forming a plurality of said polymer bodies; stripping said first photoresist mask; forming a second photoresist mask on the top surface of said base metal layer except those areas of said base metal layer covered by said polymer bodies; forming a conductive metal layer over the top surface of said second photoresist mask and over said polymer bodies; removing said second photoresist mask thereby removing said conductive metal layer on the top surface of said second photoresist mask and leaving said conductive metal layer on said polymer bodies thereby forming said conductive metal coating and said composite bumps; forming a third photoresist mask over said composite bumps and part of said base metal layer; etching away said base metal layer not covered by said third photoresist mask; and removing said third photoresist mask.
Claim 9
Dependent Claim
199 words
The method of claim 5 wherein forming composite bumps on said base metal layer and removing part or all of that part of said base metal layer which is not covered by said composite bumps and does not cover said input output/pads comprises the steps of: forming a photosensitive polymer layer on the top surface of said base metal layer; exposing and developing a pattern on said photosensitive polymer thereby forming a plurality of said polymer bodies; forming a first photoresist mask on the top surface of said base metal layer except those areas of said base metal layer covered by said polymer bodies; forming a conductive metal layer over the top surface of said first photoresist mask and over said polymer bodies; and removing said first photoresist mask thereby removing said conductive metal layer on the top surface of said first photoresist mask and leaving said conductive metal layer on said polymer bodies thereby forming said conductive metal coating and said composite bumps; forming a second photoresist mask over said composite bumps and part of said base metal layer; etching away said base metal layer not covered by said second photoresist mask; and removing said second photoresist mask.
Claim 10
Dependent Claim
206 words
The method of claim 5 wherein forming composite bumps on said base metal layer and removing part or all of that part of said base metal layer which is not covered by said composite bumps and does not cover said input output/pads comprises the steps of: forming a first photoresist mask over the top surface of said base metal layer; forming a polymer layer on the top surface of said first photoresist mask and those areas on the top surface of said base metal layer not covered by said first photoresist mask; removing said first photoresist mask thereby removing said polymer on the top surface of said first photoresist mask thereby forming a plurality of said polymer bodies; forming a conductive metal layer on the top surface of said base metal layer and said polymer bodies; forming a second photoresist mask on the top surface of said conductive metal layer directly over said polymer bodies; etching away said conductive metal layer not covered by said second photoresist mask leaving said conductive metal layer on said polymer bodies thereby forming said conductive metal coating and said composite bumps; etching away said base metal layer not covered by said second photoresist mask; and removing said second photoresist mask.
Claim 11
Dependent Claim
183 words
The method of claim 5 wherein forming composite bumps on said base metal layer and removing part or all of that part of said base metal layer which is not covered by said composite bumps and does not cover said input output/pads comprises the steps of: forming a first photoresist mask over the top surface of said base metal layer; forming a polymer layer on the top surface of said photoresist mask and those areas on the top surface of said base metal layer not covered by said first photoresist mask; forming a conductive metal layer on the top surface of said polymer layer; removing said first photoresist mask thereby removing said polymer and said conductive metal layer on the top surface of said first photoresist mask leaving a plurality of said polymer bodies covered by said conductive metal coating on said base metal layer thereby forming said composite bumps on said base metal layer; forming a second photoresist mask over said composite bumps; etching away said base metal layer not covered by said second photoresist mask; and removing said second photoresist mask.
Claim 12
Independent Claim
192 words
A method of forming composite bumps, comprising the steps of: providing an integrated circuit element or substrate with input/output pads on the top surface of said integrated circuit element or substrate; forming a dielectric layer over the top surface of said integrated circuit element or substrate having contact openings directly over said input/output pads wherein said contact openings expose at least a part of each said input/output pad; forming a first photoresist layer on the top surface of said dielectric layer covering said input/output pads; forming a first photoresist mask in said first photoresist layer having openings over said input/output pads; forming a base metal layer on the top surface of said first photoresist mask, on the top surface of said dielectric layer not covered by said first photoresist mask, and on said input/output pads not covered by said dielectric layer; removing said first photoresist mask thereby removing that part of said base metal layer on the top surface of said first photoresist mask and forming base metal pads; forming composite bumps on said base metal pads wherein each said composite bump comprises a polymer body covered by a conductive metal coating.
Claim 13
Independent Claim
192 words
A method of forming composite bumps, comprising the steps of: providing an integrated circuit element or substrate with input/output pads on the top surface of said integrated circuit element or substrate; forming a dielectric layer over the top surface of said integrated circuit element or substrate having contact openings directly over said input/output pads wherein said contact openings expose at least a part of each said input/output pad; forming a first photoresist layer on the top surface of said dielectric layer covering said input/output pads; forming a first photoresist mask in said first photoresist layer having openings over said input/output pads; forming a base metal layer on the top surface of said first photoresist mask, on the top surface of said dielectric layer not covered by said first photoresist mask, and on said input/output pads not covered by said dielectric layer; removing said first photoresist mask thereby removing that part of said base metal layer on the top surface of said first photoresist mask and forming base metal pads; forming composite bumps on said base metal pads wherein each said composite bump comprises a polymer body covered by a conductive metal coating.
Claim 14
Dependent Claim
139 words
The method of claim 10 wherein forming composite bumps on said base metal pads, comprises the steps of: forming a polymer layer on the top surface of said dielectric layer covering said base metal pads; forming a second photoresist mask on the top surface of said polymer layer directly over said base metal pads; etching away said polymer not protected by said second photoresist mask thereby forming a plurality of said polymer bodies; stripping said second photoresist mask; forming a conductive metal layer on the top surface of said dielectric layer over said polymer bodies; forming a third photoresist mask on the top surface of said conductive metal layer a directly over said polymer bodies; and etching away said conductive metal layer not covered by said third photoresist mask thereby forming said conductive metal coating and said composite bumps.
Claim 15
Dependent Claim
164 words
The method of claim 10 wherein forming composite bumps on said base metal pads comprises the steps of: forming a polymer layer on the top surface of said dielectric layer covering said base metal pads; forming a second photoresist mask on the top surface of said polymer layer directly over said base metal pads; etching away said polymer not protected by said second photoresist mask thereby forming a plurality of said polymer bodies; stripping said second photoresist mask; forming a third photoresist mask over the top surface of said dielectric layer said third photoresist mask having openings at the locations of said polymer bodies; forming a conductive metal layer on the top surface of said third photoresist mask and over said polymer bodies; and removing said third photoresist mask thereby removing said conductive metal layer on the top surface of said third photoresist mask and leaving said conductive metal layer over said polymer bodies thereby forming said conductive metal coating and said composite bumps.
Claim 16
Dependent Claim
131 words
The method of claim 10 wherein forming composite bumps on said base metal pads, comprises the steps of: forming a photosensitive polymer layer on the top surface of said dielectric layer covering said base metal pads; exposing and developing a pattern on said photosensitive polymer so as to leave a plurality of said polymer bodies on said base metal pads; forming a conductive metal layer on the top surface of said dielectric layer and over said polymer bodies; forming a second photoresist mask on the top surface of said conductive metal layer directly over said polymer bodies; and etching away said conductive metal layer not covered by said second photoresist mask thereby leaving a conductive metal layer over said polymer bodies and forming said conductive metal coating and said composite bumps.
Claim 17
Dependent Claim
147 words
The method of claim 10 wherein forming composite bumps on said base metal pads, comprises the steps of: forming a photosensitive polymer layer on the top surface of said dielectric layer covering said base metal pads; exposing and developing a pattern on said photosensitive polymer layer so as to form a plurality of said polymer bodies on said base metal pads; forming a second photoresist mask over the top surface of said dielectric layer said second photoresist mask having openings at the location of said polymer bodies; forming a conductive metal layer on the top surface of said second photoresist mask and over said polymer bodies; and removing said second photoresist mask thereby removing said conductive metal layer on the top surface of said second photoresist mask and leaving said conductive metal layer over said polymer bodies thereby forming said conductive metal coating and said composite bumps.
Claim 18
Dependent Claim
147 words
The method of claim 10 wherein forming composite bumps on said base metal pads, comprises the steps of: forming a polymer layer on the top surface of said base metal layer after forming said base metal layer and before removing said first photoresist mask so that when said first photoresist mask is removed said polymer layer over said first photoresist mask is also removed thereby forming a plurality of said polymer bodies; forming a conductive metal layer on the top surface of said dielectric layer over said polymer bodies; forming a second photoresist mask on the top surface of said conductive metal layer a directly over said polymer bodies; etching away said conductive metal layer not covered by said second photoresist mask leaving a conductive metal layer over said polymer bodies thereby forming said conductive metal coating and said composite bumps; and removing said second photoresist mask.
Claim 19
Dependent Claim
145 words
The method of claim 10 wherein forming composite bumps on said base metal pads, comprises the steps of: forming a polymer layer on the top surface of said base metal layer after forming said base metal layer and before removing said first photoresist mask so that when said first photoresist mask is removed said polymer layer over said first photoresist mask is also removed; and forming a conductive metal layer over the top surface of said polymer layer after forming said polymer layer and before removing said first photoresist mask so that when said first photoresist mask is removed said conductive metal layer over said first photoresist mask is also removed leaving said conductive metal layer on that part of said polymer layer not over said first photoresist mask thereby forming said polymer bodies covered by said conductive metal coating and forming said composite bumps.
Claim 20
Dependent Claim
28 words
The method of claim 1 wherein said conductive metal coating is a layer of chrome about 500 Angstroms thick and a layer of gold about 2000 Angstroms thick.
Claim 21
Dependent Claim
21 words
The method of claim 11 wherein said conductive metal coating includes an adhesion layer, a barrier layer, and a conductor layer.
Claim 22
Dependent Claim
12 words
The method of claim 5 wherein said base metal layer is aluminum.
Claim 23
Dependent Claim
27 words
The method of claim 5 wherein said conductive metal coating is a layer of chrome about 500 Angstroms thick and layer of gold about 2000 Angstroms thick.
Claim 24
Dependent Claim
21 words
The method of claim 5 wherein said conductive metal coating includes an adhesion layer, a barrier layer, and a conductor layer.
Claim 25
Dependent Claim
12 words
The method of claim 10 wherein said base metal layer is aluminum.
Claim 26
Dependent Claim
28 words
The method of claim 10 wherein said conductive metal coating is a layer of chrome about 500 Angstroms thick and a layer of gold about 2000 Angstroms thick.
Claim 27
Dependent Claim
21 words
The method of claim 10 wherein said conductive metal coating includes an adhesion layer, a barrier layer, and a conductor layer.
Claim 28
Dependent Claim
15 words
The method of claim 1 wherein said polymer bodies are formed from polyamic acid polyimide.
Claim 29
Dependent Claim
15 words
The method of claim 5 wherein said polymer bodies are formed from polyamic acid polyimide.
Claim 30
Dependent Claim
15 words
The method of claim 10 wherein said polymer bodies are formed from polyamic acid polyimide.
References Cited (Backward Citations)
US3401126A
Cited
US3625837A
Cited
US3809625A
Cited
US4763829A
Cited
US5134460A
Cited
US4749120A
Cited
US5223454A
Cited
US4963002A
Cited
US4916523A
Cited
US5086558A
Cited
US5393696A
Cited
JPH05144823A
Cited
US5329423A
Cited
US5393697A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-01-12 | 2001-07-14 | 2002-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-01-12 | 2005-07-14 | 2006-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-01-12 | 2009-07-14 | 2010-01-13 | $7700.00 | Window Closed / Lapsed |