Rechargeable positive electrodes
Assignee: Polyplus Battery Co Inc
•
Filing: 1996-07-26
•
Granted: 1997-11-11
•
Expires: 2016-07-26
Abstract
Abstract Disclosed are positive electrodes containing active-sulfur-based composite electrodes. The cells include active-sulfur, an electronic conductor, and an ionic conductor. These materials are provided in a manner allowing at least about 10% of the active-sulfur to be available for electrochemical reaction. Also disclosed are methods for fabricating active-sulfur-based composite electrodes. The method begins with a step of combining the electrode components in a slurry. Next, the slurry is homogenized such that the electrode components are well mixed and free of agglomerates. Thereafter, before the electrode components have settled or separated to any significant degree, the slurry is coated on a substrate to form a thin film. Finally, the coated film is dried to form the electrode in such a manner that the electrode components do not significantly redistribute.
Inventors
- 👤 May-Ying Chu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 13:19
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/05; H01M10/052; C; C07; C07C; C07C227/00; C07C227/30; C07C227/32; H01M10/056; H01M10/0564; H01M10/0565; H01M10/0566; H01M10/0569; H01M10/36; H01M4/00; H01M4/02; H01M4/04; H01M4/0402; H01M4/0404; H01M4/0409; H01M4/0411; H01M4/0416; H01M4/043; H01M4/0435; H01M4/0438; H01M4/045; H01M4/13; H01M4/36; H01M4/38; H01M4/381; H01M4/382; H01M4/58; H01M4/581; H01M4/5815; H01M4/62; H01M4/624; H01M4/626; H01M10/39; H01M10/3909; H01M10/42; H01M10/44; H01M2004/026; H01M2004/028; H01M2300/00; H01M2300/0017; H01M2300/0065; H01M2300/0085; H01M4/60; H01M4/621; H01M4/625; H01M50/00; H01M50/40; H01M50/46; H01M6/00; H01M6/14; H01M6/16; H01M6/162; H01M6/164; H01M6/168; H01M6/18; H01M6/181; H01M6/188; H01M6/40; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02T; Y02T10/00; Y02T10/60; Y02T10/70
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
143 words
A method of preventing damage from overcharge, the method comprising the following steps: (a) providing a metal-sulfur cell having a first cell voltage which it attains when fully charged but not overcharged, the cell including a metal negative electrode and a sulfur positive electrode which positive electrode includes i) active-sulfur; ii) an electronic conductor mixed with the active-sulfur so that electrons can move between the active-sulfur and the electronic conductor; and iii) an ionic conductor mixed with the active-sulfur so that ions can move between the ionic conductor and the active-sulfur; and (b) charging said metal-sulfur cell to a level beyond the normal charge capacity while the cell maintains an overcharge cell voltage that is not substantially higher than the first cell voltage, wherein the sulfur positive electrode has between about 10% and about 100% of the active-sulfur is available for electrochemical reaction.
Claim 2
Independent Claim
143 words
A method of preventing damage from overcharge, the method comprising the following steps: (a) providing a metal-sulfur cell having a first cell voltage which it attains when fully charged but not overcharged, the cell including a metal negative electrode and a sulfur positive electrode which positive electrode includes i) active-sulfur; ii) an electronic conductor mixed with the active-sulfur so that electrons can move between the active-sulfur and the electronic conductor; and iii) an ionic conductor mixed with the active-sulfur so that ions can move between the ionic conductor and the active-sulfur; and (b) charging said metal-sulfur cell to a level beyond the normal charge capacity while the cell maintains an overcharge cell voltage that is not substantially higher than the first cell voltage, wherein the sulfur positive electrode has between about 10% and about 100% of the active-sulfur is available for electrochemical reaction.
Claim 3
Dependent Claim
23 words
The method of claim 1, wherein the overcharge cell voltage is not more than about 4 volts greater than the first cell voltage.
Claim 4
Dependent Claim
23 words
The method of claim 1, wherein the overcharge cell voltage is not more than about 2 volts greater than the first cell voltage.
Claim 5
Dependent Claim
23 words
The method of claim 1, wherein the overcharge cell voltage is not more than about 1 volt greater than the first cell voltage.
Claim 6
Dependent Claim
22 words
The method of claim 1 wherein the sulfur positive electrode is operated between about -40 degrees Celsius and about 180 degrees Celsius.
Claim 7
Dependent Claim
22 words
The method of claim 1 wherein the sulfur positive electrode contains, between about 20% by weight to about 80% by weight, active-sulfur.
Claim 8
Dependent Claim
40 words
The method of claim 1 wherein the electronic conductor is selected from the group consisting of carbon black, compounds with conjugated carbon-carbon or carbon-nitrogen double bonds, electronically conductive polymers, polyaniline compounds, polythiophene compounds, polyacetylene compounds, polypyrrole compounds, and combinations thereof.
Claim 9
Dependent Claim
23 words
The method of claim 1 wherein the sulfur positive electrode contains, between about 5% by weight to about 40% by weight, electronic conductor.
Claim 10
Dependent Claim
33 words
The method of claim 1 wherein the sulfur positive electrode contains between about 15% by weight and 75% by weight, ionic conductor, and wherein the ionic conductor is a solid or a gel.
Claim 11
Dependent Claim
29 words
The method of claim 9 wherein the ionic conductor is selected from the group consisting essentially of polymeric electrolytes, ceramic electrolytes, glass electrolytes, beta alumina compounds, and combinations thereof.
Claim 12
Dependent Claim
47 words
The method of claim 9 wherein the ionic conductor comprises an electrolyte salt that form a complex with compounds selected from the group consisting of polyether compounds, polyimine compounds, polythioether compounds, polyphosphazene compounds, polyalkylene oxide compounds, polyethylene oxide compounds, and amorphous polyethylene oxide compounds, and combinations thereof.
Claim 13
Dependent Claim
25 words
The method of claim 1 wherein the metal electrode is selected from the group consisting of lithium metal, lithium alloys, sodium metal, and sodium alloys.
Claim 14
Dependent Claim
18 words
The method of claim 12 wherein the metal electrode is a lithium electrode or a lithium alloy electrode.
References Cited (Backward Citations)
US3404035A
Cited
US3413150A
Cited
US3532543A
Cited
US3907591A
Cited
US3915743A
Cited
US3953231A
Cited
US4143214A
Cited
US4410609A
Cited
US4469761A
Cited
GB2137406A
Cited
US4644911A
Cited
US4833048A
Cited
US4917974A
Cited
US5162175A
Cited
EP0602984A2
Cited
GB2273603A
Cited
JPH06275313A
Cited
US5529860A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-11-10 | 2001-05-12 | 2001-11-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-11-10 | 2005-05-12 | 2005-11-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-11-10 | 2009-05-12 | 2009-11-11 | $7700.00 | Window Closed / Lapsed |