Polyurethane elastomers having improved green strength and demold time and polyoxyalkylene polyols suitable for their preparation
Assignee: Lyondell Chemical Technology LP
•
Filing: 1995-06-15
•
Granted: 1997-09-23
•
Expires: 2015-06-15
Abstract
Abstract Elastomers exhibiting decreased demold times and improved green strength are prepared by reacting a di- or polyisocyanate with a monodisperse polyoxypropylene diol having ultra-low unsaturation, and preferably prepared by the double metal cyanide.t-butyl alcohol catalyzed polymerization of propylene oxide. Further improved demold times and elevated elastomer physical properties are made possible by the use of multidisperse polyoxyalkylene polyether polyol blends having an overall unsaturation of less than 0.010 meq/g and a polydispersity of about 1.4 or greater.
Inventors
- 👤 Gary L. Allen
- 👤 Nigel Barksby
- 👤 Stephen D. Seneker
- 👤 Usama E. Younes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:47
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G65/00; C08G65/02; C08G65/26; C08G65/2642; C08G65/2645; C08G65/2663; C07; C07C; C07C271/00; C07C271/06; C07C271/08; C08G18/08; C08G18/10; C08G18/12; C08G18/4804; C08G18/4808; C08G18/4825; C08G18/4833; C08G18/4837; C08G18/4841; C08G18/4866; C08G18/67; C08L; C08L71/00; C08L71/02; C08G2110/00; C08G2110/0008; C08G2110/0041; C08G2110/0066; C08G2110/0083; C08G2410/00
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
120 words
A method for the improvement of green strength and demold time of polyurethane elastomers prepared by the reaction of an isocyanate component with a polyoxyalkylene polyol and one or more chain extenders, comprising: selecting as said polyoxyalkylene polyol a polyoxyalkylene polyol component having an unsaturation of less than 0.010 meq/g, a polydispersity of 1.4 or greater, and comprising a polyoxypropylene polyol component having an unsaturation of less than 0.010 meq/g, said polyoxyalkylene polyol component having an average equivalent weight of from 1000 Da to about 8000 Da; wherein when said polyoxypropylene polyol component comprises a blend of individual polyoxypropylene polyols, each of said individual polyoxypropylene polyols is an essentially monodisperse polyoxypropylene polyol with an unsaturation of less than 0.015 meq/g.
Claim 2
Independent Claim
120 words
A method for the improvement of green strength and demold time of polyurethane elastomers prepared by the reaction of an isocyanate component with a polyoxyalkylene polyol and one or more chain extenders, comprising: selecting as said polyoxyalkylene polyol a polyoxyalkylene polyol component having an unsaturation of less than 0.010 meq/g, a polydispersity of 1.4 or greater, and comprising a polyoxypropylene polyol component having an unsaturation of less than 0.010 meq/g, said polyoxyalkylene polyol component having an average equivalent weight of from 1000 Da to about 8000 Da; wherein when said polyoxypropylene polyol component comprises a blend of individual polyoxypropylene polyols, each of said individual polyoxypropylene polyols is an essentially monodisperse polyoxypropylene polyol with an unsaturation of less than 0.015 meq/g.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein each of said individual polyoxypropylene polyols has an equivalent weight of from about 400 Da to about 10,000 Da.
Claim 4
Dependent Claim
30 words
The method of claim 1 wherein said polyoxyalkylene polyol component is a blend, and at least one of said individual polyoxypropylene polyols in said blend is a polyoxypropylene/polyoxyethylene copolymer polyol.
Claim 5
Dependent Claim
34 words
The method of claim 3 wherein the oxyethylene moieties of said polyoxypropylene/polyoxyethylene polyol are present as a cap in an amount up to about 30 weight percent based on the weight of the polyol.
Claim 6
Dependent Claim
35 words
The method of claim 1 wherein said polyoxyalkylene polyol is a polyoxypropylene/polyoxyethylene polyol containing random, internal oxyethylene moieties in an amount of up to about 1 weight percent based on the weight of the polyol.
Claim 7
Dependent Claim
45 words
The method of claim 5 wherein said polyoxypropylene/polyoxyethylene polyol with random internal oxyethylene moieties further comprises up to about 25 weight percent oxyethylene moieties present as a cap, wherein said weight percent of oxyethylene moieties is based on the total weight of said polyoxypropylene/polyoxyethylene polyol.
Claim 8
Dependent Claim
18 words
The method of claim 1 wherein said polyoxypropylene polyol component has an unsaturation of less than 0.007 meq/g.
Claim 9
Dependent Claim
24 words
The method of claim 1 wherein each of said individual polyoxypropylene polyols is a polyoxypropylene diol having an unsaturation of less than 0.007 meq/g.
Claim 10
Dependent Claim
116 words
A polyurethane elastomer exhibiting a demold time of 60 minutes or less, said elastomer comprising the reaction product of: a) an isocyanate-terminated prepolymer prepared by reacting an excess of di- or polyisocyanate with a polyoxyalkylene polyol component comprising one or more individual polyoxyalkylene diols comprising oxypropylene moieties in major part, each of said individual polyoxyalkylene diols having an unsaturation of less than 0.010 meq/g and an equivalent weight of from 400 Da to 8000 Da, said polyoxyalkylene polyol component having a polydispersity of about 1.4 or greater; with b) a hydroxyl functional chain extender or mixture thereof having a molecular weight below about 300 Da, at an isocyanate index of from about 70 to about 130.
Claim 11
Dependent Claim
116 words
A polyurethane elastomer exhibiting a demold time of 60 minutes or less, said elastomer comprising the reaction product of: a) an isocyanate-terminated prepolymer prepared by reacting an excess of di- or polyisocyanate with a polyoxyalkylene polyol component comprising one or more individual polyoxyalkylene diols comprising oxypropylene moieties in major part, each of said individual polyoxyalkylene diols having an unsaturation of less than 0.010 meq/g and an equivalent weight of from 400 Da to 8000 Da, said polyoxyalkylene polyol component having a polydispersity of about 1.4 or greater; with b) a hydroxyl functional chain extender or mixture thereof having a molecular weight below about 300 Da, at an isocyanate index of from about 70 to about 130.
Claim 12
Dependent Claim
48 words
The polyurethane elastomer of claim 9 wherein said chain extender is an aliphatic glycol selected from the group consisting of ethylene glycol, diethylene glycol, triethylene glycol, 1,2- and 1,3-propane diol, 2-methyl-1,3-propanediol, dipropylene glycol, 1,2- and 1,4-butanediol, neopentyl glycol, 2,2,4-trimethylpentane-1,5-diol, 1,6-hexanediol, 1,4-cyclohexanediol, 1,4-cyclohexanedimethanol, hydroquinone bis(2-hydroxyethyl) ether, and mixtures thereof.
Claim 13
Dependent Claim
49 words
The polyurethane of claim 10 wherein said elastomer comprises the reaction product of said isocyanate-terminated prepolymer (a) and a second isocyanate-terminated prepolymer prepared by reacting a di- or polyisocyanate with a polyoxypropylene polyol having a nominal functionality greater than 2 and an unsaturation of less than about 0.010 meq/g.
Claim 14
Dependent Claim
14 words
The polyurethane elastomer of claim 11 wherein said polyoxypropylene polyol is a polyoxypropylene triol.
Claim 15
Dependent Claim
12 words
The polyurethane elastomer of claim 9 wherein said chain extender is 1,4-butanediol.
Claim 16
Dependent Claim
72 words
A polyurethane elastomer exhibiting a demold time of 60 minutes or less, said elastomer comprising the reaction product of: a) a prepolymer prepared by the reaction of an excess of di- or polyisocyanate with a monodisperse polyoxypropylene diol having a molecular weight of from 1000 Da to about 20,000 Da, a polydispersity of about 1.20 or less, and an unsaturation of less than about 0.008 meq/g; with b) a glycol chain extender.
Claim 17
Dependent Claim
72 words
A polyurethane elastomer exhibiting a demold time of 60 minutes or less, said elastomer comprising the reaction product of: a) a prepolymer prepared by the reaction of an excess of di- or polyisocyanate with a monodisperse polyoxypropylene diol having a molecular weight of from 1000 Da to about 20,000 Da, a polydispersity of about 1.20 or less, and an unsaturation of less than about 0.008 meq/g; with b) a glycol chain extender.
Claim 18
Dependent Claim
45 words
The polyurethane elastomer of claim 14 wherein said prepolymer has an isocyanate group content of from 3 to 12 weight percent based on the weight of the prepolymer and said glycol chain extender is selected from the group consisting of 1,4-butanediol, 1,6-hexanediol, and mixtures thereof.
Claim 19
Dependent Claim
22 words
The polyurethane elastomer of claim 14 wherein the tan delta of said elastomer is less than 0.10 when measured at 20° C.
Claim 20
Dependent Claim
15 words
The polyurethane elastomer of claim 16 wherein said tan delta is less than about 0.08.
Claim 21
Dependent Claim
15 words
The elastomer of claim 14 which is further the reaction product of a polymer polyol.
Claim 22
Dependent Claim
40 words
A diol-extended polyurethane elastomer having a tan delta of less than 0.10 when measured at 20° C., said diol-extended polyurethane elastomer prepared from at least one polyol component comprising a polyoxypropylene diol having an unsaturation of less than 0.010 meq/g.
Claim 23
Dependent Claim
40 words
A diol-extended polyurethane elastomer having a tan delta of less than 0.10 when measured at 20° C., said diol-extended polyurethane elastomer prepared from at least one polyol component comprising a polyoxypropylene diol having an unsaturation of less than 0.010 meq/g.
References Cited (Backward Citations)
US4239879A
Cited
US5300535A
Cited
US5124425A
Cited
US5100922A
Cited
US5106874A
Cited
US5100997A
Cited
US5116931A
Cited
US5185420A
Cited
US5096993A
Cited
US5158922A
Cited
US5496496A
Cited
US5470813A
Cited
US5589431A
Cited
US5482908A
Cited
US5545601A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-09-22 | 2001-03-24 | 2001-09-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-09-22 | 2005-03-24 | 2005-09-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-09-22 | 2009-03-24 | 2009-09-23 | $7700.00 | Window Closed / Lapsed |