Preparation of elastomers using high molecular weight polyols or polyamines, said polyols prepared using a double metal cyanide complex catalyst
Assignee: Olin Corp
•
Filing: 1990-05-29
•
Granted: 1992-03-31
•
Expires: 2010-05-29
Abstract
Abstract The present invention relates to a process for preparing polyurethane/polyurea or polyurea elastomers by spray processing or reaction injection molding a reaction mixture comprising an A-side and a B-side, wherein said A-side comprises a polyisocyanate or an isocyanato-terminated polyurethane prepolymer and wherein said B-side comprises a polyol or polyamine plus a chain extender, in order to form a polyurethane/polyurea or polyurea elastomer, said polyol having an equivalent of between about 1,000 and about 20,000, a preferred molecular weight of between about 5,000 and about 30,000 and an end group unsaturation level of no greater than 0.06 milliequivalents per gram of polyol, said polyol being prepared using a double metal cyanide complex catalyst, said polyamine being fabricated by amine-capping said polyol with an amine-containing compound, said chain extender being selected from the group consisting of diol and aromatic diamine chain extenders with the proviso that said B-side contain at least some amount of said polyamine or of said aromatic diamine chain extender.
Inventors
- 👤 John W. Reisch
- 👤 Maurice C. Raes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 20:18
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/4829; C08G18/4866; C08G18/50; C08G18/5021; C08G18/5024; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6674; C08G18/6681; C08G18/6685; C08G65/00; C08G65/02; C08G65/26; C08G65/2642; C08G65/2645; C08G65/2663; C08G2120/00; C08G2150/00; C08G2150/50
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
146 words
A process for preparing polyurethane/polyurea or polyurea elastomers by spray processing or reaction injection molding a reaction mixture comprising an A-side and a B-side, wherein said A-side comprises a polyisocyanate or an isocyanato-terminated polyurethane prepolymer and wherein said B-side comprises a polyol or polyamine plus a chain extender, in order to form a polyurethane/polyurea or polyurea elastomer, said polyol having an equivalent weight of between about 1,000 and about 20,000 and an end group unsaturation level of no greater than 0.06 milli-equivalents per gram of polyol, said polyol being prepared using a double metal cyanide complex catalyst, said polyamine being fabricated by amine-capping said polyol with an amine-containing compound, said chain extender being selected from the group consisting of diol and aromatic diamine chain extenders with the proviso that said B-side contain at least some amount of said polyamine or of said aromatic diamine chain extender.
Claim 2
Dependent Claim
146 words
A process for preparing polyurethane/polyurea or polyurea elastomers by spray processing or reaction injection molding a reaction mixture comprising an A-side and a B-side, wherein said A-side comprises a polyisocyanate or an isocyanato-terminated polyurethane prepolymer and wherein said B-side comprises a polyol or polyamine plus a chain extender, in order to form a polyurethane/polyurea or polyurea elastomer, said polyol having an equivalent weight of between about 1,000 and about 20,000 and an end group unsaturation level of no greater than 0.06 milli-equivalents per gram of polyol, said polyol being prepared using a double metal cyanide complex catalyst, said polyamine being fabricated by amine-capping said polyol with an amine-containing compound, said chain extender being selected from the group consisting of diol and aromatic diamine chain extenders with the proviso that said B-side contain at least some amount of said polyamine or of said aromatic diamine chain extender.
Claim 3
Dependent Claim
28 words
The process of claim 1 wherein said polyol has an equivalent weight of between 1,500 and 5,000 and a molecular weight of between about 3,000 and about 30,000.
Claim 4
Dependent Claim
32 words
The process of claim 1 wherein said A-side or said B-side additionally contains an additive selected from the group consisting of dyes, plasticizers, uv stabilizers, blowing agents, adhesion promoters, fillers and pigments.
Claim 5
Dependent Claim
29 words
The process of claim 3 wherein said additive is employed in an amount of between 0 and about 75 weight percent based upon the total weight of the composition.
Claim 6
Dependent Claim
23 words
The process of claim 1 wherein said polyol has at least two hydroxyl groups and said polyamine has at least two amino groups.
Claim 7
Dependent Claim
38 words
The process of claim 1 wherein said diol is selected from the group consisting of ethylene glycol, butane diol, hexane diol, propylene glycol, bisphenol A, and polyalkylene oxide diols with molecular weights between about 60 and about 500.
Claim 8
Dependent Claim
56 words
The process of claim 1 wherein said aromatic diamine contains at least one alkyl substituent in the ortho-position to a first amino group and two alkyl substituents in the ortho-position to a second amino group or mixtures thereof, preferably with the proviso that at least two of said alkyl substituents contain at least two carbon atoms.
Claim 9
Dependent Claim
26 words
The process of claim 1 wherein said diamine is selected from the group consisting of diethyltoluene diamine, t-butyl toluene diamine, 1-methyl-3,5-diethyl-2,4-diaminobenzene, 1-methyl-3,5-diethyl-2,6-diaminobenzene, 3,5,3',5'-tetraethyl-4,4'-diaminodiphenylmethane, and combinations thereof.
Claim 10
Dependent Claim
46 words
The process of claim 1 wherein said double metal cyanide complex catalyst is a zinc hexacyanometallate of formula: Zn.sub.3 [M(CN).sub.6 ].sub.2.xZnCl.sub.2.yGLYME.zH.sub.2 O wherein M may be Co(III), or Cr(III) or Fe(II) or Fe(III); x, y, and z each have a value of between 0 and 15.
Claim 11
Dependent Claim
87 words
The process of claim 1 wherein said polyisocyanate or isocyanato-terminated polyurethane prepolymer is selected from the group consisting of: diphenylmethane diisocyanate, polymethylene polyphenylisocyanate, naphthylene diisocyanate, paraphenylene diisocyanate, liquid carbodiimide-modified MDI and derivatives thereof, prepolymers of MDI with a mixture of tripropylene glycol (TPG) and dipropylene glycol (DPG), the prepolymers of MDI with 400 to 700 molecular weight diols, prepolymers of MDI with 4,500 to 6,500 molecular weight triols, prepolymers of MDI reacted with the high molecular weight polyols made using double metal cyanide catalysis, and combinations thereof.
Claim 12
Dependent Claim
152 words
A process for making a polyurethane/polyurea or polyurea-containing elastomer which comprises the steps of: (a) fabricating a high molecular weight polyol by reacting an alkylene oxide with a polyhydric initiator to provide a polyol having an equivalent weight of between about 1,000 and about 20,000 and an end group unsaturation level of no greater than 0.06 milliequivalents per gram of polyol, said polyol being prepared using a double metal cyanide complex catalyst, and (b) reacting said high molecular weight polyol and a chain extender with a polyisocyanate or an isocyanto-terminated polyurethane prepolymer using spray processing or reaction injection molding in order to fabricate said polyurethane/polyurea or polyurea-containing elastomer, said chain extender being a diol or aromatic diamine with the proviso that if said chain extender is solely a diol then at least a portion of the polyol from step (a) is amine-capped with an amine-containing compound prior to reaction with the polyisocyanate.
Claim 13
Dependent Claim
152 words
A process for making a polyurethane/polyurea or polyurea-containing elastomer which comprises the steps of: (a) fabricating a high molecular weight polyol by reacting an alkylene oxide with a polyhydric initiator to provide a polyol having an equivalent weight of between about 1,000 and about 20,000 and an end group unsaturation level of no greater than 0.06 milliequivalents per gram of polyol, said polyol being prepared using a double metal cyanide complex catalyst, and (b) reacting said high molecular weight polyol and a chain extender with a polyisocyanate or an isocyanto-terminated polyurethane prepolymer using spray processing or reaction injection molding in order to fabricate said polyurethane/polyurea or polyurea-containing elastomer, said chain extender being a diol or aromatic diamine with the proviso that if said chain extender is solely a diol then at least a portion of the polyol from step (a) is amine-capped with an amine-containing compound prior to reaction with the polyisocyanate.
Claim 14
Dependent Claim
29 words
The process of claim 11 wherein essentially all of the polyol from step (a) is amine-capped with an amine-containing compound prior to reaction with the polyisocyanate of step (b).
Claim 15
Dependent Claim
30 words
The process of claim 11 wherein said polyol has an equivalent weight of between about 1,500 and about 5,000 and a molecular weight of between about 3,000 and about 30,000.
Claim 16
Dependent Claim
34 words
The process of claim 11 wherein step (b) is carried out in the presence of an additive selected from the group consisting of dyes, plasticizers, uv stabilizers, blowing agents, adhesion promoters, fillers and pigments.
Claim 17
Dependent Claim
30 words
The process of claim 14 wherein said compounding ingredient is employed in an amount of between 0 and about 75 weight percent based upon the total weight of the composition.
Claim 18
Dependent Claim
23 words
The process of claim 11 wherein said polyol has at least two hydroxyl groups and said polyamine has at least two amino groups.
Claim 19
Dependent Claim
36 words
The process of claim 11 wherein said diol is selected from the group consisting of ethylene glycol, butane diol, hexane diol, propylene glycol, bisphenol A, and polyalkylene oxide diols with molecular weights between 60 and 500.
Claim 20
Dependent Claim
56 words
The process of claim 11 wherein said aromatic diamine contains at least one alkyl substituent in the ortho-position to a first amino group and two alkyl substituents in the ortho-position to a second amino group or mixtures thereof, preferably with the proviso that at least two of said alkyl substituents contain at least two carbon atoms.
Claim 21
Dependent Claim
26 words
The process of claim 11 wherein said diamine is selected from the group consisting of diethyltoluene diamine, t-butyl toluene diamine, 1-methyl-3,5-diethyl-2,4-diaminobenzene, 1-methyl-3,5-diethyl-2,6-diaminobenzene, 3,5,3',5'-tetraethyl-4,4'-diaminodiphenylmethane, and combinations thereof.
Claim 22
Dependent Claim
46 words
The process of claim 11 wherein said double metal cyanide complex catalyst is a zinc hexacyanometallate of formula: Zn.sub.3 [M(CN).sub.6 ].sub.2.xZnCl.sub.2.yGLYME.zH.sub.2 O wherein M may be Co(III), or Cr(III) or Fe(II) or Fe(III); x, y, and z each have a value of between 0 and 15.
Claim 23
Dependent Claim
87 words
The process of claim 11 wherein said polyisocyanate or isocyanato-terminated polyurethane prepolymer is selected from the group consisting of: diphenylmethane diisocyanate, polymethylene polyphenylisocyanate, naphthylene diisocyanate, paraphenylene diisocyanate, liquid carbodiimide-modified MDI and derivatives thereof, prepolymers of MDI with a mixture of tripropylene glycol (TPG) and dipropylene glycol (DPG), the prepolymers of MDI with 400 to 700 molecular weight diols, prepolymers of MDI with 4,500 to 6,500 molecular weight triols, prepolymers of MDI reacted with the high molecular weight polyols made using double metal cyanide catalysis, and combinations thereof.
Claim 24
Dependent Claim
14 words
The polyurethane/polyurea elastomer or polyurea elastomer product produced by the process of claim 1.
Claim 25
Dependent Claim
14 words
The polyurethane/polyurea elastomer or polyurea elastomer product produced by the process of claim 11.
References Cited (Backward Citations)
US3829505A
Cited
US3654370A
Cited
US3941849A
Cited
US4218543A
Cited
US4335188A
Cited
US4301110A
Cited
US4358547A
Cited
US4472560A
Cited
US4477589A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-31 | 1995-09-30 | 1996-03-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-31 | 1999-09-30 | 2000-03-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-31 | 2003-09-30 | 2004-03-31 | $7700.00 | Window Closed / Lapsed |