Method for fabricating transistors using crystalline silicon devices on glass
Assignee: Lawrence Livermore National Security LLC
•
Filing: 1995-01-17
•
Granted: 1997-09-02
•
Expires: 2015-01-17
Abstract
Abstract A method for fabricating transistors using single-crystal silicon devices on glass. This method overcomes the potential damage that may be caused to the device during high voltage bonding and employs a metal layer which may be incorporated as part of the transistor. This is accomplished such that when the bonding of the silicon wafer or substrate to the glass substrate is performed, the voltage and current pass through areas where transistors will not be fabricated. After removal of the silicon substrate, further metal may be deposited to form electrical contact or add functionality to the devices. By this method both single and gate-all-around devices may be formed.
Inventors
- 👤 Anthony M. McCarthy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 13:12
CPC Classifications
H; H10; H10D; H10D10/00; H10D10/01; H10D10/041; H10D10/311; H10D30/00; H10D30/01; H10D30/021; H10D30/031; H10D30/0321; H10D30/0323; H10D30/60; H10D30/67; H10D30/6704; H10D30/6723; H10D30/6729; H10D30/673; H10D30/6733; H10D30/6734; H10D30/6735; H10D30/674; H10D30/6741; H10D30/6743; H10D30/6744; H10P; H10P50/00; H10P50/60; H10P50/64; H10P50/642; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10P90/1914; H10W; H10W10/00; H10W10/01; H10W10/061; H10W10/10; H10W10/181; Y; Y10; Y10S; Y10S438/00; Y10S438/97
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
129 words
A method for fabricating microelectronic devices using crystalline silicon on glass, comprising: forming at least one etch stop layer on a silicon substrate; forming at least one layer of silicon on the etch stop layer; providing the layer of silicon with at least one patterned doped and activated region therein; forming an oxide layer over at least the doped and activated region; forming a layer of conductive material over the oxide layer and exposed areas of the silicon layer; forming an amorphous silicon containing layer over the conductive material layer; bonding the amorphous silicon layer to a glass substrate; removing the silicon substrate; removing the etch stop layer; forming at least one island in the at least one silicon layer; and patterning the oxide and the conductive material layer.
Claim 2
Independent Claim
129 words
A method for fabricating microelectronic devices using crystalline silicon on glass, comprising: forming at least one etch stop layer on a silicon substrate; forming at least one layer of silicon on the etch stop layer; providing the layer of silicon with at least one patterned doped and activated region therein; forming an oxide layer over at least the doped and activated region; forming a layer of conductive material over the oxide layer and exposed areas of the silicon layer; forming an amorphous silicon containing layer over the conductive material layer; bonding the amorphous silicon layer to a glass substrate; removing the silicon substrate; removing the etch stop layer; forming at least one island in the at least one silicon layer; and patterning the oxide and the conductive material layer.
Claim 3
Dependent Claim
29 words
The method of claim 1, additionally including forming an oxide layer on at least one area of the silicon layer, and forming a metal layer on the oxide layer.
Claim 4
Dependent Claim
33 words
The method of claim 1, additionally including patterning and etching the layers on the glass substrate to form a desired configuration prior to forming the metal layer on the doped and activated area.
Claim 5
Dependent Claim
50 words
The method of claim 1, wherein the etch stop layer is composed of material selected from the group of silicon-germanium, silicon-lead, silicon-tin and boron doped silicon-germanium-lead, and boron doped silicon-germanium-tin; and wherein said layer of conductive material is composed of material selected from the group of aluminum, titanium, and polysilicon.
Claim 6
Dependent Claim
26 words
The method of claim 1, wherein the amorphous silicon layer is composed of a material selected from the group consisting of silicon, silicon nitride, silicon dioxide.
Claim 7
Dependent Claim
20 words
The method of claim 1, wherein the amorphous silicon layer is a material selected from α-Si, α-SiN, α-SiON, and α-SiO.
Claim 8
Dependent Claim
25 words
The method of claim 1, wherein the bonding is carried out by anodic bonding at a temperature of 300°-700° C. and voltage of 0.5-5000 volts.
Claim 9
Dependent Claim
72 words
The method of claim 1, additionally including forming at least one additional etch stop layer on the first formed layer of silicon, and forming at least one additional layer of silicon on each etch stop layer, whereby there is at least an etch stop layer, a layer of silicon, an etch stop layer, and a layer of silicon, and wherein the last formed layer of silicon is of a device quality type.
Claim 10
Dependent Claim
19 words
The method of claim 8, wherein the layer of conductive material is composed of material which includes a metal.
Claim 11
Dependent Claim
36 words
The method of claim 8, wherein each of said etch stop layers may be composed of material selected from the group consisting of boron doped silicon, silicon-germanium, silicon-lead, silicon-tin and boron doped silicon-germanium, silicon-lead and silicon-tin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-09-01 | 2001-03-03 | 2001-09-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-09-01 | 2005-03-03 | 2005-09-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-09-01 | 2009-03-03 | 2009-09-02 | $7700.00 | Window Closed / Lapsed |