Use of materials comprising microbubbles as acoustical barriers
Assignee: 3M Co
•
Filing: 1995-08-03
•
Granted: 1997-08-19
•
Expires: 2015-08-03
Abstract
Abstract A method of using a material as an acoustical barrier in an ambient medium. The material comprises microbubbles having average outer diameters of 5 to 150 microns, bound together at their contact points. The material is characterized by either a porosity of 20 to 60 percent, or by voids between the microbubbles which have characteristic diameter within an order of magnitude of the viscous skin depth of the ambient medium, as calculated at 1 kHz; an air flow resistivity of 0.5×10 4 to 4×10 7 mks rayls/meter, and an attenuation of sound comparable to mass law performance. The microbubbles can be sintered into direct contact with each other, or one of many types of binder material can be used to support the microbubbles within a composite material. The method may be practiced in an acoustical system comprising a sound source and the material, such as by placing a muffler comprising the material substantially in a direct path of a fluid; and also in applications requiring high specific stiffness and flexural strength.
Inventors
- 👤 Leland R. Whitney
- 👤 Michael W. Dolezal
- 👤 Ronald W. Gerdes
- 👤 Gary N. Harvieux
- 👤 Charles A. Marttila
- 👤 Joseph G. Mandell
- 👤 Thomas J. Scanlan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:48
CPC Classifications
H; H04; H04R; H04R1/00; H04R1/02; H04R1/023; E; E04; E04B; E04B1/00; E04B1/62; E04B1/74; E04B1/82; E04B1/8218; E04B1/84; E04B1/86; F; F01; F01N; F01N1/00; F01N1/08; F01N1/082; F01N1/10; F01N1/24; F02; F02M; F02M35/00; F02M35/12; F02M35/1272; F02M35/1277; G; G10; G10K; G10K11/00; G10K11/18; G10K11/20; E04B2001/8457; E04B2001/8461; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249955; Y10T428/249956; Y10T428/249958; Y10T428/249967; Y10T428/249978; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2996; Y10T428/31504
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
125 words
A self-supporting acoustical barrier material for use within an ambient medium having a viscous skin depth, comprising microbubbles having average outer diameters of 5 to 150 microns bound together at their contact points; characterized by the microbubbles having between themselves voids which have a characteristic diameter within an order of magnitude of the viscous skin depth of the ambient medium, as calculated at 1 kHz, an air flow resistivity for the barrier material of 0.5×10 4 to 4×10 7 mks rayl/meter, and an attenuation of sound by the material comparable to mass law performance; and further characterized by a specific stiffness of 1×10 6 to 8×10 6 psi/lb-in 3 , and a flexural strength of 200 to 500 psi as measured by ASTM Standard C293-79.
Claim 2
Dependent Claim
125 words
A self-supporting acoustical barrier material for use within an ambient medium having a viscous skin depth, comprising microbubbles having average outer diameters of 5 to 150 microns bound together at their contact points; characterized by the microbubbles having between themselves voids which have a characteristic diameter within an order of magnitude of the viscous skin depth of the ambient medium, as calculated at 1 kHz, an air flow resistivity for the barrier material of 0.5×10 4 to 4×10 7 mks rayl/meter, and an attenuation of sound by the material comparable to mass law performance; and further characterized by a specific stiffness of 1×10 6 to 8×10 6 psi/lb-in 3 , and a flexural strength of 200 to 500 psi as measured by ASTM Standard C293-79.
Claim 3
Dependent Claim
21 words
The self-supporting acoustical barrier material of claim 1, in the form of a panel having a portion of an interlocking joint.
Claim 4
Dependent Claim
94 words
A self-supporting acoustical barrier material, comprising microbubbles having average outer diameters of 5 to 150 microns bound together at their contact points; characterized by a porosity for the barrier material of 20 to 60 percent, an air flow resistivity for the barrier material of 0.5×10 4 to 4×10 7 mks rayl/meter, and an attenuation of sound by the material comparable to mass law performance; further characterized by a specific stiffness of 1×10 6 to 8×10 6 psi/lb-in 3 , and a flexural strength of 200 to 500 psi as measured by ASTM Standard C293-79.
Claim 5
Dependent Claim
94 words
A self-supporting acoustical barrier material, comprising microbubbles having average outer diameters of 5 to 150 microns bound together at their contact points; characterized by a porosity for the barrier material of 20 to 60 percent, an air flow resistivity for the barrier material of 0.5×10 4 to 4×10 7 mks rayl/meter, and an attenuation of sound by the material comparable to mass law performance; further characterized by a specific stiffness of 1×10 6 to 8×10 6 psi/lb-in 3 , and a flexural strength of 200 to 500 psi as measured by ASTM Standard C293-79.
Claim 6
Dependent Claim
21 words
The self-supporting acoustical barrier material of claim 3, in the form of a panel having a portion of an interlocking joint.
Claim 7
Dependent Claim
89 words
A muffler comprising: a porous acoustical barrier material, which allows gases to pass through, comprising microbubbles having average outer diameters of 5 to 150 microns bound together at their contact points; the barrier material characterized by a porosity of 20 to 60 percent and an air flow resistivity of 0.5×10 4 to 4×10 7 mks rayls/meter; wherein the acoustical barrier material is characterized by a specific stiffness of 1×10 6 to 8×10 6 psi/lb-in 3 ; and wherein said barrier material exhibits sound attenuation comparable to mass law performance.
Claim 8
Dependent Claim
89 words
A muffler comprising: a porous acoustical barrier material, which allows gases to pass through, comprising microbubbles having average outer diameters of 5 to 150 microns bound together at their contact points; the barrier material characterized by a porosity of 20 to 60 percent and an air flow resistivity of 0.5×10 4 to 4×10 7 mks rayls/meter; wherein the acoustical barrier material is characterized by a specific stiffness of 1×10 6 to 8×10 6 psi/lb-in 3 ; and wherein said barrier material exhibits sound attenuation comparable to mass law performance.
Claim 9
Dependent Claim
12 words
The muffler of claim 5 wherein said microbubbles are hollow glass microbubbles.
Claim 10
Dependent Claim
16 words
The muffler of claim 6 wherein said microbubbles have average outer diameters of approximately 70 microns.
Claim 11
Dependent Claim
18 words
The muffler of claim 6 wherein said microbubbles are bound together at their contact points by a binder.
Claim 12
Dependent Claim
20 words
The muffler of claim 8 wherein said binder is selected from the group consisting of ceramic, elastomeric and polymeric materials.
Claim 13
Dependent Claim
22 words
The muffler of claim 5 wherein the muffler comprises chambers within the muffler that increase the exposed surface of acoustical barrier material.
Claim 14
Dependent Claim
25 words
The muffler of claim 5 wherein the acoustical barrier material has a flexural strength of 200 to 500 psi as measured by ASTM Standard C293-79.
Claim 15
Dependent Claim
85 words
A loudspeaker enclosure comprising: a porous acoustical barrier material comprising microbubbles having average outer diameters of 5 to 150 microns bound together at their contact points; the barrier material characterized by a porosity of 20 to 60 percent and an air flow resistivity of 0.5×10 4 to 4×10 7 mks rayls/meter; wherein the acoustical barrier material is characterized by a specific stiffness of 1×10 6 to 8×10 6 psi/lb-in 3 ; and wherein said barrier material exhibits attenuation of sound comparable to mass law performance.
Claim 16
Dependent Claim
85 words
A loudspeaker enclosure comprising: a porous acoustical barrier material comprising microbubbles having average outer diameters of 5 to 150 microns bound together at their contact points; the barrier material characterized by a porosity of 20 to 60 percent and an air flow resistivity of 0.5×10 4 to 4×10 7 mks rayls/meter; wherein the acoustical barrier material is characterized by a specific stiffness of 1×10 6 to 8×10 6 psi/lb-in 3 ; and wherein said barrier material exhibits attenuation of sound comparable to mass law performance.
Claim 17
Dependent Claim
19 words
The loudspeaker enclosure of claim 12 wherein said microbubbles are bound together at their contact points by a binder.
Claim 18
Dependent Claim
21 words
The loudspeaker enclosure of claim 13 wherein said binder is selected from the group consisting of ceramic, elastomeric and polymeric materials.
Claim 19
Dependent Claim
26 words
The loudspeaker enclosure of claim 12 wherein the acoustical barrier material has a flexural strength of 200 to 500 psi as measured by ASTM Standard C293-79.
Claim 20
Dependent Claim
90 words
A headphone having ear enclosures, the ear enclosures comprising: a porous acoustical barrier material comprising microbubbles having average outer diameters of 5 to 150 microns bound together at their contact points; the barrier material characterized by a porosity of 20 to 60 percent and an air flow resistivity of 0.5×10 4 to 4×10 7 mks rayls/meter; wherein the acoustical barrier material is characterized by a specific stiffness of 1×10 6 to 8×10 6 psi/lb-in 3 ; and wherein said barrier material exhibits attenuation of sound comparable to mass law performance.
Claim 21
Dependent Claim
90 words
A headphone having ear enclosures, the ear enclosures comprising: a porous acoustical barrier material comprising microbubbles having average outer diameters of 5 to 150 microns bound together at their contact points; the barrier material characterized by a porosity of 20 to 60 percent and an air flow resistivity of 0.5×10 4 to 4×10 7 mks rayls/meter; wherein the acoustical barrier material is characterized by a specific stiffness of 1×10 6 to 8×10 6 psi/lb-in 3 ; and wherein said barrier material exhibits attenuation of sound comparable to mass law performance.
Claim 22
Dependent Claim
18 words
The headphone of claim 16 wherein said microbubbles are bound together at their contact points by a binder.
Claim 23
Dependent Claim
20 words
The headphone of claim 17 wherein said binder is selected from the group consisting of ceramic, elastomeric and polymeric materials.
Claim 24
Dependent Claim
25 words
The headphone of claim 16 wherein the acoustical barrier material has a flexural strength of 200 to 500 psi as measured by ASTM Standard C293-79.
References Cited (Backward Citations)
US2720276A
Cited
US2806509A
Cited
US2985411A
Cited
US3132956A
Cited
US3608010A
Cited
US3898063A
Cited
US3989534A
Cited
US4079162A
Cited
US4146112A
Cited
US4238641A
Cited
US4528652A
Cited
US4463049A
Cited
US4465159A
Cited
US4816618A
Cited
US4528305A
Cited
US4548863A
Cited
US4788230A
Cited
FR2649356A1
Cited
US5187461A
Cited
US5504281A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-08-18 | 2001-02-17 | 2001-08-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-08-18 | 2005-02-17 | 2005-08-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-08-18 | 2009-02-17 | 2009-08-19 | $7700.00 | Window Closed / Lapsed |