Foamed cementitious compositions and method of producing same
Assignee: Individual
•
Filing: 1974-08-29
•
Granted: 1976-11-02
•
Expires: 1994-08-29
Abstract
Abstract A cellular product useful for such purposes as fire resistance, thermal insulation, and acoustical sound proofing may be produced from a mineral cement, such as gypsum cement, portland cement, calcium aluminate cement, or magneisa cement, an organic film former such as guar gun, or an inorganic film former such as bentonite, a mixture of nonionic and anionic surfactants, a lightweight aggregate, such as perlite, vermiculite, or hollow silicate spheres, and air in amount substantially in excess of that used in air entrainment of cement, whereby the product has a density which is only a small fraction of the density of the mineral cement and aggregate composition per se.
Inventors
- 👤 Mark Plunguian
- 👤 Charles E. Cornwell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:33
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
108 words
A low density cementitious foamed composition comprising 100 parts by weight of a mineral cement; about 10-50 parts by weight of a filler, selected from the group consisting of an exfoliated lightweight aggregate and hollow silicate spheres; about 1-20 parts by weight of an organic, water-soluble film former selected from the group consisting of guar gum, pregelatinized starch, xanthan gum, and protein colloids; about 0.1-3.0 parts by weight of surface active foaming agents; and at least about 8% by volume, based on the total volume of said components, of air, said cementitious composition having been processed with from about 30 to about 150 parts by weight of water.
Claim 2
Dependent Claim
108 words
A low density cementitious foamed composition comprising 100 parts by weight of a mineral cement; about 10-50 parts by weight of a filler, selected from the group consisting of an exfoliated lightweight aggregate and hollow silicate spheres; about 1-20 parts by weight of an organic, water-soluble film former selected from the group consisting of guar gum, pregelatinized starch, xanthan gum, and protein colloids; about 0.1-3.0 parts by weight of surface active foaming agents; and at least about 8% by volume, based on the total volume of said components, of air, said cementitious composition having been processed with from about 30 to about 150 parts by weight of water.
Claim 3
Dependent Claim
27 words
A composition according to claim 1 wherein said mineral cement is selected from the group consisting of gypsum cement, portland cement, calcium aluminate cement, and magnesia cement.
Claim 4
Dependent Claim
30 words
A composition according to claim 1 wherein said surface active foaming agents are selected from the group consisting of synthetic anionic and nonionic surface active foaming agents and mixtures thereof.
Claim 5
Dependent Claim
28 words
A composition according to claim 1 wherein said mineral cement is gypsum cement, and wherein said composition has a dry density of about 10-30 pounds per cubic foot.
Claim 6
Dependent Claim
27 words
A composition according to claim 1 wherein said mineral cement is portland cement, and said composition has a dry density of about 25-45 pounds per cubic foot.
Claim 7
Independent Claim
113 words
A method for producing a foamed cementitious composition comprising the steps of mixing together about 30-150 parts of water, about 100 parts by weight of a mineral cement, up to about 50 parts by weight of a lightweight mineral aggregate or hollow silicate spheres, about 1-20 parts by weight of an organic water-soluble film former selected from the group consisting of guar gum, pregelatinized starch, xanthan gum, and protein colloids, and 0.1-3.0 parts by weight of a mixture of anionic and nonionic surface active foaming agents, stirring the resulting mixture and incorporation air therein in an amount of at least 8 percent by volume based on the volume of the final foamed composition.
Claim 8
Independent Claim
113 words
A method for producing a foamed cementitious composition comprising the steps of mixing together about 30-150 parts of water, about 100 parts by weight of a mineral cement, up to about 50 parts by weight of a lightweight mineral aggregate or hollow silicate spheres, about 1-20 parts by weight of an organic water-soluble film former selected from the group consisting of guar gum, pregelatinized starch, xanthan gum, and protein colloids, and 0.1-3.0 parts by weight of a mixture of anionic and nonionic surface active foaming agents, stirring the resulting mixture and incorporation air therein in an amount of at least 8 percent by volume based on the volume of the final foamed composition.
Claim 9
Dependent Claim
42 words
A method according to Claim 6 further comprising preparing a dry blend of said cement, said film former, said surface active agents, and said aggregate, thereafter introducing said dry blend gradually with stirring and aerating into water while incorporating said air thereto.
References Cited (Backward Citations)
US3062669A
Cited
US2979415A
Cited
US2921862A
Cited
US2993016A
Cited
US3522069A
Cited
US3615578A
Cited
US3679445A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-02 | 1980-05-03 | 1980-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-02 | 1984-05-03 | 1984-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-02 | 1988-05-03 | 1988-11-02 | $7700.00 | Window Closed / Lapsed |