Abstract
Abstract Disclosed is a vertically oriented capacitor structure, which is of particular usefulness in MOS DRAM memory modules. The structure has upper and lower polysilicon capacitor plates separated by a dielectric layer, each of the plates and dielectric layers sloping at an angle with of about 80-85 degrees with respect to an underlying silicon substrate. As such, the novel capacitor is formed in a sloped contact opening. The contact area of electrical connection of the lower capacitor plate with an underlying active region has a sufficiently small horizontal cross-section that the contact area will not extend laterally beyond the active region and leakage will not occur. A method for forming the contact opening is disclosed and comprises first, the formation of an active region, preferably located between two insulating bird's beak regions, and covering the active area with a thin layer of oxide etch barrier material. A polysilicon layer is then formed above the oxide etch barrier. The etch is subsequently performed with the use of a diatomic chlorine etchant. Four embodiments are disclosed as variations on the step of etching the polysilicon with the diatomic chlorine etch chemistry.
Inventors
- 👤 David J. Keller
- 👤 Louie Liu
- 👤 Kris K. Brown
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 06:26
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/60; H10D1/68; H10D1/692; H10D1/711; H10D1/716; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10B12/033; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/268; Y; Y10; Y10S; Y10S148/00; Y10S148/014; Y10S438/00; Y10S438/978
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
103 words
A method for forming a contact opening for a semiconductor device, said method comprising the steps of: forming an active region in a semiconductor substrate; forming an oxide etch barrier layer on the semiconductor substrate; providing a polysilicon layer on the oxide etch barrier layer; and etching the contact opening through the polysilicon layer and the oxide etch barrier layer to open a contact on the active region by using an etch chemistry comprising Cl 2 , such that the contact opening etched through the polysilicon layer has a substantially straight sidewall set at a sloping angle with respect to the semiconductor substrate.
Claim 2
Independent Claim
103 words
A method for forming a contact opening for a semiconductor device, said method comprising the steps of: forming an active region in a semiconductor substrate; forming an oxide etch barrier layer on the semiconductor substrate; providing a polysilicon layer on the oxide etch barrier layer; and etching the contact opening through the polysilicon layer and the oxide etch barrier layer to open a contact on the active region by using an etch chemistry comprising Cl 2 , such that the contact opening etched through the polysilicon layer has a substantially straight sidewall set at a sloping angle with respect to the semiconductor substrate.
Claim 3
Dependent Claim
22 words
A method as recited in claim 1, wherein the etch chemistry further comprises a passivating gas mixed with the Cl 2 .
Claim 4
Dependent Claim
15 words
A method as recited in claim 2, wherein the passivating gas comprises N 2 .
Claim 5
Dependent Claim
15 words
A method as recited in claim 2, wherein the passivating gas comprises O 2 .
Claim 6
Dependent Claim
15 words
A method as recited in claim 2, wherein the passivating gas comprises HeO 2 .
Claim 7
Dependent Claim
19 words
A method as recited in claim 1, wherein the etching chemistry is a combination of Cl 2 and HBr.
Claim 8
Dependent Claim
16 words
A method as recited in claim 6, wherein the etch chemistry further comprises a passivating gas.
Claim 9
Dependent Claim
15 words
A method as recited in claim 7, wherein the passivating gas comprises N 2 .
Claim 10
Dependent Claim
15 words
A method as recited in claim 7, wherein the passivating gas comprises O 2 .
Claim 11
Dependent Claim
40 words
A method as recited in claim 7, wherein the etching step is conducted in one step in an etcher in which electrical, magnetic, and pressure parameters are customized to obtain an etch ratio of polysilicon to oxide of about 4:1-100:1.
Claim 12
Dependent Claim
40 words
A method as recited in claim 1, wherein the etching step is conducted in one step in an etcher in which electrical, magnetic, and pressure parameters are customized to obtain an etch ratio of polysilicon to oxide of about 4:1-100:1.
Claim 13
Dependent Claim
134 words
A method as recited in claim 1, wherein the step of etching the contact opening is conducted in a magnetically enhanced reactive ion etcher and comprises: (a) a first step that exposes Cl 2 to the polysilicon layer at a pressure in the range of between about 1 and 100 millitorr, at a power in the range of between about 200 and 700 Watts, and a magnetic field in the range of between about 50 and 100 Gauss; and (b) a second step that exposes Cl 2 and HeO 2 to the polysilicon layer at a pressure in the range of between about 1 and 100 millitorr, at a power in the range of between about 50 and 200 Watts, and a magnetic field in the range of between about 50 and 100 Gauss.
Claim 14
Dependent Claim
22 words
A method as recited in claim 1, wherein the step of etching the contact opening is conducted with a reactive ion etcher.
Claim 15
Dependent Claim
24 words
A method as recited in claim 1, wherein the step of etching the contact opening is conducted with a magnetically enhanced reactive ion etcher.
Claim 16
Dependent Claim
65 words
A method as recited in claim 14, further comprising a passivating gas mixed with the Cl 2 , and wherein the etching step is conducted at a pressure in the range of between about 1 and 100 millitorr, at a power in the range of between about 200 and 700 Watts, and a magnetic field in the range of between about 50 and 100 Gauss.
Claim 17
Dependent Claim
22 words
A method as recited in claim 1, wherein the step of etching the contact opening is conducted with a high density etcher.
Claim 18
Dependent Claim
84 words
A method as recited in claim 16, further comprising a passivating gas mixed with the Cl 2 , and wherein the etching step is conducted at a bias power applied at a bottom portion of a chamber of the high density etcher in the range of between about 10 and 300 Watts, and at a wide range of top power applied to a top portion of the chamber of the high density etcher chamber in the range of between about 100 and 3000 Watts.
Claim 19
Dependent Claim
41 words
A method as recited in claim 1, wherein the semiconductor substrate is formed on a substantially horizontal plane and wherein the sloping angle has a slope in the range of between about 80 and about 85 degrees from the horizontal plane.
Claim 20
Independent Claim
127 words
A method of forming a contact opening for a semiconductor device, said method comprising the steps of: forming an active region in a semiconductor substrate; providing an oxide etch barrier layer on the semiconductor substrate; providing a polysilicon layer above the oxide etch barrier layer; etching the contact opening through the polysilicon layer using a chemical etchant comprising Cl 2 together with a passivating gas such that the contact opening etched thereby has a substantially straight sidewall set at a sloped angle, the slope being in the range of between about 80 and about 85 degrees from the substantially horizontal plane of the semiconductor substrate; and etching through the oxide etch barrier layer using a carbon-containing fluorine chemistry to extend the contact opening to the active region.
Claim 21
Independent Claim
127 words
A method of forming a contact opening for a semiconductor device, said method comprising the steps of: forming an active region in a semiconductor substrate; providing an oxide etch barrier layer on the semiconductor substrate; providing a polysilicon layer above the oxide etch barrier layer; etching the contact opening through the polysilicon layer using a chemical etchant comprising Cl 2 together with a passivating gas such that the contact opening etched thereby has a substantially straight sidewall set at a sloped angle, the slope being in the range of between about 80 and about 85 degrees from the substantially horizontal plane of the semiconductor substrate; and etching through the oxide etch barrier layer using a carbon-containing fluorine chemistry to extend the contact opening to the active region.
Claim 22
Dependent Claim
119 words
A method as recited in claim 19, wherein the etching step is conducted in a magnetically enhanced reactive ion etcher and exposes Cl 2 to the polysilicon layer at a pressure in the range of between about 1 and 100 millitorr, at a power in the range of between about 200 and 700 Watts, and a magnetic field in the range of between about 50 and 100 Gauss, and exposes Cl 2 and HeO 2 to the polysilicon layer at a pressure in the range of between about 1 and 100 millitorr, at a power in the range of between about 50 and 200 Watts, and a magnetic field in the range of between about 50 and 100 Gauss.
Claim 23
Dependent Claim
90 words
A method as recited in claim 19, wherein the etching step is conducted in a high density etcher at a bias power applied at a bottom portion of a chamber of the high density etcher in the range of between about 10 to 300 Watts, at a wide range of top power applied to a top portion of the chamber of the high density etcher chamber in the range of between about 100 and 3000 Watts, and at a pressure in the range of between about 1 and 100 millitorr.
References Cited (Backward Citations)
US5472564A
Cited
US4951175A
Cited
US5354716A
Cited
US5487811A
Cited
US5242536A
Cited
US5256245A
Cited
US5444013A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-07-28 | 2001-01-27 | 2001-07-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-07-28 | 2005-01-27 | 2005-07-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-07-28 | 2009-01-27 | 2009-07-29 | $7700.00 | Window Closed / Lapsed |