Method to form a capacitor having multiple pillars for advanced DRAMS
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1996-01-11
•
Granted: 1997-07-22
•
Expires: 2016-01-11
Abstract
Abstract A method of fabricating a capacitor having multiple pillars is presented. The invention uses an oxidized hemispherical grain silicon (HSG-Si) layer as a masking layer, in a series of masking steps, to form pillarets on a storage electrode. The method begins by forming a storage electrode having a connection to an active area on the substrate. Next, a cap insulation layer and a cap polysilicon layer are formed over the storage electrode. The cap polysilicon layer has grains and has grain boundaries between the grains. The cap polysilicon layer is oxidized thus forming a thicker oxide layer at the grain boundaries. The oxide layer is dry etched exposing the cap polysilicon layer and leaves a grain boundary oxide covering the grain boundaries. Next, the exposed cap polysilicon layer is etched using the grain boundary oxide as a mask forming a plurality of cap polysilicon layer pillarets. The grain boundary oxide is then removed. Then the cap insulation layer is etched using the cap polysilicon layer pillarets as a mask forming cap oxide pillarets. The cap polysilicon layer pillarets are then removed. The storage electrode node is dry etched using the cap oxide pillarets as a mask forming storage electrode pillarets. The cap oxide pillarets are removed. A capacitor dielectric layer and top plate electrode are formed over the storage electrode pillarets and the storage electrode to complete the capacitor.
Inventors
- 👤 Shye-Lin Wu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:57
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10B12/033; H10B12/30; H10B12/31; H10B12/318; H10D; H10D1/00; H10D1/60; H10D1/68; H10D1/692; H10D1/711; H10D1/712; H10D1/716; Y; Y10; Y10S; Y10S438/00; Y10S438/911
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
333 words
A method of fabricating a memory device having a multiple pillar-shaped capacitor on a substrate, said substrate having a conductive word line and a transistor, said transistor having a source, a drain, and a transfer gate; the method comprises the steps of: sequentially forming a first planarization layer and a first silicon nitride layer over a substrate surface; etching a node contact hole through said first silicon nitride layer and said first planarization layer to expose said source; forming a first polysilicon layer on said first silicon nitride layer and filling said node contact hole thereby making an electrical connection to said source; depositing a cap insulation layer covering said first polysilicon layer, forming a cap polysilicon layer over said cap insulation layer; said cap polysilicon layer having grains and having grain boundaries between said grains; oxidizing said cap polysilicon layer to form a thermal oxide layer over said cap polysilicon layer, said thermal oxide layer growing thicker at said grain boundaries; etching back said thermal oxide layer exposing portions of said cap polysilicon layer and leaving thermal oxide islands covering said grain boundaries; etching the exposed portions of said cap polysilicon layer using said thermal oxide islands as a mask forming a plurality of cap polysilicon layer pillarets; removing said thermal oxide islands; etching said cap insulation layer using said cap polysilicon layer pillarets as a mask forming cap insulation layer pillarets; removing said cap polysilicon layer pillarets; etching said first polysilicon layer using said cap insulation layer piIlarets as a mask forming storage electrode pillarets; removing said cap insulation layer pillarets; forming a hemispherical grain polysilicon (HSG-Si) layer over said storage electrode piilarets and said first polysilicon layer; patterning said first polysilicon layer and said a hemispherical grain polysilicon (HSG-Si) layer to form a storage electrode; forming a capacitor dielectric layer over said storage electrode pillarets and said storage electrode; and forming a top plate electrode over said capacitor dielectric layer thereby forming said memory device having said multi-pillar shape capacitor.
Claim 2
Independent Claim
333 words
A method of fabricating a memory device having a multiple pillar-shaped capacitor on a substrate, said substrate having a conductive word line and a transistor, said transistor having a source, a drain, and a transfer gate; the method comprises the steps of: sequentially forming a first planarization layer and a first silicon nitride layer over a substrate surface; etching a node contact hole through said first silicon nitride layer and said first planarization layer to expose said source; forming a first polysilicon layer on said first silicon nitride layer and filling said node contact hole thereby making an electrical connection to said source; depositing a cap insulation layer covering said first polysilicon layer, forming a cap polysilicon layer over said cap insulation layer; said cap polysilicon layer having grains and having grain boundaries between said grains; oxidizing said cap polysilicon layer to form a thermal oxide layer over said cap polysilicon layer, said thermal oxide layer growing thicker at said grain boundaries; etching back said thermal oxide layer exposing portions of said cap polysilicon layer and leaving thermal oxide islands covering said grain boundaries; etching the exposed portions of said cap polysilicon layer using said thermal oxide islands as a mask forming a plurality of cap polysilicon layer pillarets; removing said thermal oxide islands; etching said cap insulation layer using said cap polysilicon layer pillarets as a mask forming cap insulation layer pillarets; removing said cap polysilicon layer pillarets; etching said first polysilicon layer using said cap insulation layer piIlarets as a mask forming storage electrode pillarets; removing said cap insulation layer pillarets; forming a hemispherical grain polysilicon (HSG-Si) layer over said storage electrode piilarets and said first polysilicon layer; patterning said first polysilicon layer and said a hemispherical grain polysilicon (HSG-Si) layer to form a storage electrode; forming a capacitor dielectric layer over said storage electrode pillarets and said storage electrode; and forming a top plate electrode over said capacitor dielectric layer thereby forming said memory device having said multi-pillar shape capacitor.
Claim 3
Dependent Claim
39 words
The method of claim 1 wherein said first planarization layer is composed of a material selected from the group consisting of silicon oxide and borophosphosilicate glass, and has a thickness in a range between about 500 to 10,000 Å.
Claim 4
Dependent Claim
52 words
The method of claim 1 wherein said first planarization layer comprises a first silicon oxide layer and a bottom borophosphosilicate glass (BPSG) layer, said first silicon oxide layer is formed by a chemical vapor deposition process using tetraethylorthosilicate and has a thickness in a range of between about 500 and 5000 Å.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein said cap insulation layer has a thickness in a range of between about 300 and 3000 Å.
Claim 6
Dependent Claim
45 words
The method of claim 1 wherein said cap polysilicon layer is formed of amorphous silicon having a thickness in a range of between about 300 and 3000 Å and a p-type impurity doping in a range of between about 1E19 and 5E21 atoms/cm 3 .
Claim 7
Dependent Claim
65 words
The method of claim 1 wherein said cap polysilicon layer is formed of amorphous silicon by a decomposition of silane SiH 4 in a hot wall vertical LPCVD reactor, at a pressure of between about 80 to 200 mtorr and a temperature of between about 500° to 560° C. to produce hemispherical shaped grains (HSG) having a diameter of between about 200 to 1500 Å.
Claim 8
Dependent Claim
77 words
The method of claim 1 wherein said cap polysilicon layer is formed by depositing a polysilicon layer by a decomposition of silane (SiH 4 ) in a hot wall LPCVD reactor, at a pressure of between about 150 to 500 mtorr and a temperature of between about 600° to 630° C. to produce hemispherical shaped grains (HSG) having a diameter of between about 500 to 1500 Å followed by a doping with POCl 3 at 900° C.
Claim 9
Dependent Claim
43 words
The method of claim 1 wherein said thermal oxide layer has a thickness at the grain bounties in the a of between about 300 and 1500 Å and a thickness over said grains in a range of between about 100 and 500 Å.
Claim 10
Dependent Claim
44 words
The method of claim 1 wherein said thermal oxide layer is formed in a wet oxidation process with a temperature in a range of between about 750° and 950° C. and at a pressure in a range of between about 1 and 760 torr.
Claim 11
Dependent Claim
25 words
The method of claim 1 wherein said etching back of said thermal oxide layer is performed with CF 4 , CHF 3 and Ar reactants.
Claim 12
Dependent Claim
37 words
The method of claim 1 wherein said thermal oxide islands have a thickness in a range of between about 100 and 1500 Å and have a diameter in a range of between about 100 and 1500 Å.
Claim 13
Dependent Claim
25 words
The method of claim 1 wherein said etching of said exposed cap polysilicon layer is performed with an etch using Cl 2 and HBr reactants.
Claim 14
Dependent Claim
32 words
The method of claim 3 wherein said first polysilicon layer is formed by depositing a amorphous silicon layer over said first silicon nitride layer, and becomes said polysilicon layer by heat processing.
Claim 15
Dependent Claim
44 words
The method of claim 1 wherein said capacitor dielectric is composed of a material selected from the group consisting of ONO, silicon nitride, Ta 2 O 5 , and silicon oxide, and has a thickness in a range between about 20 to 300 Å.
Claim 16
Dependent Claim
42 words
The method of claim 1 wherein said top plate electrode is formed of doped polysilicon having a thickness in the range between about 500 to 3000 Å and an impurity concentration in a range between about 5E19 to 5E21 atoms/cm 3 .
Claim 17
Dependent Claim
54 words
The method of claim 1 which further includes forming a top insulation layer over said top plate electrode, said top insulation layer is formed of a material selected from the group consisting of silicon nitride, borophosphosilicate glass and tetraethylorthosilicate (TEOS) and has a thickness in a range of between about 500 and 8000 Å.
Claim 18
Independent Claim
314 words
A method of fabricating a capacitor having multiple pillars on a substrate having an active area, the method comprising the steps of: sequentially forming a first planarization layer and a first silicon nitride layer over a substrate surface; etching a node contact hole through said first silicon nitride layer and said first planarization layer exposing said active area; forming a first polysilicon layer on said first silicon nitride layer and in said node contact hole thereby making an electrical connection to said active area; forming a cap insulation layer covering said first polysilicon layer; forming a cap polysilicon layer over said cap insulation layer, said cap polysilicon layer having grains and having grain boundaries between said grains; oxidizing said cap polysilicon layer to form a thermal oxide layer over said cap polysilicon layer, said thermal oxide layer growing thicker at said grain boundaries; etching back said thermal oxide layer exposing portions of said cap polysilicon layer and leaving thermal oxide islands covering said grain boundaries and etching back said exposed portions of said cap polysilicon layer to form cap polysilicon layer pillarets and removing said thermal oxide islands; etching said cap insulation layer using said cap polysilicon layer pillarets as a mask forming cap insulation layer pillarets; removing said cap polysilicon layer pillarets; etching said first polysilicon layer using said cap insulation layer pillarets as a mask forming storage electrode pillarets; removing said cap insulation layer pillarets; forming a hemispherical grain polysilicon (HSG-Si) layer over said storage electrode pillarets and said first polysilicon layer; patterning said first polysilicon layer and said a hemispherical grain polysilicon (HSG-Si) layer to form a storage electrode; forming a capacitor dielectric layer over said storage electrode pillarets and said storage electrode; and forming a top plate electrode over said capacitor dielectric layer thereby forming said capacitor having multi-pillars and forming a top insulation layer over said top plate electrode.
Claim 19
Independent Claim
314 words
A method of fabricating a capacitor having multiple pillars on a substrate having an active area, the method comprising the steps of: sequentially forming a first planarization layer and a first silicon nitride layer over a substrate surface; etching a node contact hole through said first silicon nitride layer and said first planarization layer exposing said active area; forming a first polysilicon layer on said first silicon nitride layer and in said node contact hole thereby making an electrical connection to said active area; forming a cap insulation layer covering said first polysilicon layer; forming a cap polysilicon layer over said cap insulation layer, said cap polysilicon layer having grains and having grain boundaries between said grains; oxidizing said cap polysilicon layer to form a thermal oxide layer over said cap polysilicon layer, said thermal oxide layer growing thicker at said grain boundaries; etching back said thermal oxide layer exposing portions of said cap polysilicon layer and leaving thermal oxide islands covering said grain boundaries and etching back said exposed portions of said cap polysilicon layer to form cap polysilicon layer pillarets and removing said thermal oxide islands; etching said cap insulation layer using said cap polysilicon layer pillarets as a mask forming cap insulation layer pillarets; removing said cap polysilicon layer pillarets; etching said first polysilicon layer using said cap insulation layer pillarets as a mask forming storage electrode pillarets; removing said cap insulation layer pillarets; forming a hemispherical grain polysilicon (HSG-Si) layer over said storage electrode pillarets and said first polysilicon layer; patterning said first polysilicon layer and said a hemispherical grain polysilicon (HSG-Si) layer to form a storage electrode; forming a capacitor dielectric layer over said storage electrode pillarets and said storage electrode; and forming a top plate electrode over said capacitor dielectric layer thereby forming said capacitor having multi-pillars and forming a top insulation layer over said top plate electrode.
Claim 20
Dependent Claim
39 words
The method of claim 17 wherein said first planarization layer is composed of a material selected from the group consisting of silicon oxide and borophosphosilicate glass, and has a thickness in a range between about 500 to 10,000 Å.
Claim 21
Dependent Claim
52 words
The method of claim 17 wherein said first planarization layer comprises a first silicon oxide layer and a bottom borophosphosilicate glass (BPSG) layer, said first silicon oxide layer is formed by a chemical vapor deposition process using Tetraethylorthosilicate and has a thickness in a range of between about 500 and 5000 Å.
Claim 22
Dependent Claim
23 words
The method of claim 17 wherein said cap insulation layer has a thickness in a range of between about 300 and 3000 Å.
Claim 23
Dependent Claim
45 words
The method of claim 17 wherein said cap polysilicon layer is formed of amorphous silicon having a thickness in a range of between about 300 and 3000 Å and a p-type impurity doping in a range of between about 1E19 and 5E21 atoms/cm 3 .
Claim 24
Dependent Claim
66 words
The method of claim 17 wherein said cap polysilicon layer is formed of amorphous silicon by a decomposition of silane (SiH 4 ) in a hot wall vertical LPCVD reactor, at a pressure of between about 80 to 200 mtorr and a temperature of between about 500° to 560° C. to produce hemispherical shaped grains (HSG) having a diameter of between about 200 to 1500 Å.
Claim 25
Dependent Claim
103 words
The method of claim 17 wherein said cap polysilicon layer and the thermal oxide layer are formed by depositing a polysilicon layer by a decomposition of silane SiH 4 in a hot wall LPCVD reactor, at a pressure of between about 150 to 500 mtorr and a temperature of between about 600° to 630° C. to produce hemispherical shaped grains (HSG) having a diameter of between about 500 to 1500 Å followed by a doping with POCl 3 at 900° C. and an oxidation thereby forming said thermal oxide layer having a thickness in a range of between about 300 and 1500 Å.
Claim 26
Dependent Claim
43 words
The method of claim 17 wherein said thermal oxide layer has a thickness at the grain boundaries in a range of between about 300 and 1500 Å and a thickness over said grains in a range of between about 100 and 500 Å.
Claim 27
Dependent Claim
37 words
The method of claim 17 wherein said thermal oxide islands have a thickness in a range of between about 100 and 1500 Å and have a diameter in a range of between about 100 and 1500 Å.
Claim 28
Dependent Claim
26 words
The method of claim 17 wherein said etching back of said exposed cap polysilicon layer is performed with an etch using Cl 2 and HBr reactants.
Claim 29
Dependent Claim
32 words
The method of claim 19 wherein said first polysilicon layer is formed by depositing a amorphous silicon layer over said first silicon nitride layer, and becomes said polysilicon layer by heat processing.
Claim 30
Dependent Claim
44 words
The method of claim 17 wherein said capacitor dielectric is composed of a material selected from the group consisting of ONO, silicon nitride, Ta 2 O 5 , and silicon oxide, and has a thickness in a range between about 20 to 300 Å.
Claim 31
Dependent Claim
53 words
The method of claim 17 which includes forming a top insulation layer over said top plate electrode, said top insulation layer is formed of a material selected from the group consisting of silicon nitride, borophosphosilicate glass and Tetraethylorthosilicate (TEOS) and has a thickness in a range of between about 500 and 8000 Å.
References Cited (Backward Citations)
US5304828A
Cited
US5164881A
Cited
US5256587A
Cited
US5227322A
Cited
US5342800A
Cited
US5302540A
Cited
US5358888A
Cited
US5204280A
Cited
US5254503A
Cited
US5338700A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-07-21 | 2001-01-20 | 2001-07-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-07-21 | 2005-01-20 | 2005-07-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-07-21 | 2009-01-20 | 2009-07-22 | $7700.00 | Window Closed / Lapsed |