Synthesis of microporous ceramics
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1994-05-24
•
Granted: 1997-07-01
•
Expires: 2014-05-24
Abstract
Abstract The present invention provides for microporous ceramic materials having a surface area in excess of 70 m2/gm and an open microporous cell structure wherein the micropores have a mean width of less than 20 Angstroms and wherein said microporous structure comprises a volume of greater than about 0.03 cm3/gm of the ceramic. The invention also provides for a preceramic composite intermediate composition comprising a mixture of a ceramic precursor and finely divided silicon carbide or silicon nitride, whose pyrolysis product in inert atmosphere or in an ammonia atmosphere at temperatures of up to less than about 1100 DEG C. gives rise to the microporous ceramics of the invention. Also provided is a process for the preparation of the microporous ceramics of the invention involving pyrolysis of the ceramic intermediate under controlled conditions of heating up to temperatures of less than 1100 DEG C. to form a microporous ceramic product.
Inventors
- 👤 John Pickett Dismukes
- 👤 Jack Wayne Johnson
- 👤 Edward William Corcoran, Jr.
- 👤 Joseph Vallone
- 👤 James J. Pizzulli, Jr.
- 👤 Michael P. Anderson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:48
CPC Classifications
C; C04; C04B; C04B38/00; C04B38/0022
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
206 words
A process for preparing a microporous ceramic product having a surface area in excess of 70 m 2 /gm and a volume of open-pore micropores having a mean diameter of less than 20 Angstroms, and a volume of greater than about 0.03 cm 3 /gm, comprising: a. forming an intimate mixture comprising from greater than 30 up to about 99 parts by weight of a ceramic precursor oligomer or polymer having a number average molecular weight in the range of from about 200 to about 100,000 g/mole and from about 1 to less than 70 parts by weight of ceramic particles selected from the group consisting of silicon carbide, silicon nitride, silicon-carbide-nitride and mixtures thereof, said particles having a mean particle size or mean diameter of less than about 10 microns; b. gradually heating said mixture in the presence of an inert gas or ammonia gas and in sequential stages with hold times at intermediate temperatures to a maximum temperature in the range of from about 400° C. up to less than 1100° C. and over a period of total combined heating and hold time of from about 5 to about 50 hours to form a microporous ceramic product; and c. cooling said microporous ceramic product.
Claim 2
Dependent Claim
206 words
A process for preparing a microporous ceramic product having a surface area in excess of 70 m 2 /gm and a volume of open-pore micropores having a mean diameter of less than 20 Angstroms, and a volume of greater than about 0.03 cm 3 /gm, comprising: a. forming an intimate mixture comprising from greater than 30 up to about 99 parts by weight of a ceramic precursor oligomer or polymer having a number average molecular weight in the range of from about 200 to about 100,000 g/mole and from about 1 to less than 70 parts by weight of ceramic particles selected from the group consisting of silicon carbide, silicon nitride, silicon-carbide-nitride and mixtures thereof, said particles having a mean particle size or mean diameter of less than about 10 microns; b. gradually heating said mixture in the presence of an inert gas or ammonia gas and in sequential stages with hold times at intermediate temperatures to a maximum temperature in the range of from about 400° C. up to less than 1100° C. and over a period of total combined heating and hold time of from about 5 to about 50 hours to form a microporous ceramic product; and c. cooling said microporous ceramic product.
Claim 3
Dependent Claim
32 words
The process of claim 1 wherein said ceramic precursor is selected from the group consisting of polysilazanes, polycarbosilazanes, perhydropolysilizanes, polycarbosilanes, vinylic polysilanes, amine boranes, polyphenylborazanes, carboranesiloxanes, polysilastyrenes, polytitanocarbosilanes, polyalazanes and mixtures thereof.
Claim 4
Dependent Claim
12 words
The process of claim 2 wherein said ceramic precursor is a polysilazane.
Claim 5
Dependent Claim
36 words
The process of claim 1 wherein said mixture contains from about 52 to about 70 parts by weight of said ceramic precursor and from about 30 to about 48 parts by weight of said ceramic particles.
Claim 6
Dependent Claim
32 words
The process of claim 1 wherein said microporous ceramic product has a surface area in excess of 100 m 2 /gm and a micropore volume of greater than 0.05 cm 3 /gm.
Claim 7
Dependent Claim
22 words
The process of claim 1 wherein said microporous ceramic product has a surface area in excess of about 150 m 2 /gm.
Claim 8
Dependent Claim
33 words
The process of claim 1 wherein said microporous ceramic product has a surface area in excess of about 200 m 2 /gm and a micropore volume of greater than 0.08 cm 3 /gm.
Claim 9
Dependent Claim
26 words
The process of claim 1 wherein said mixture is heated to a maximum temperature in the range of from about 500° C. to about 850° C.
Claim 10
Dependent Claim
26 words
The process of claim 8 wherein said mixture is heated to a maximum temperature in the range of from about 550° C. to about 750° C.
Claim 11
Dependent Claim
22 words
The process of claim 1 wherein said gas is an inert gas selected from the group consisting of nitrogen, argon and helium.
Claim 12
Dependent Claim
10 words
The process of claim 1 wherein said gas is ammonia.
Claim 13
Dependent Claim
27 words
The process of claim 1 wherein said heating step includes a holding step of a period of from about 0.5 to 5 hours at approximately 200°±25° C.
Claim 14
Dependent Claim
24 words
The process of claim 12 wherein said heating step includes a holding period of from about 0.5 to 5 hours at approximately 300°±25° C.
Claim 15
Dependent Claim
24 words
The process of claim 13 wherein said heating step includes a holding period of from about 0.5 to 5 hours at approximately 500°±25° C.
Claim 16
Dependent Claim
24 words
The process of claim 14 wherein said heating step includes a holding period of from about 0.5 to 5 hours at approximately 700°±25° C.
Claim 17
Dependent Claim
5 words
The product of claim 1.
Claim 18
Dependent Claim
19 words
The microporous ceramic product of claim 16 having a surface area in excess of about 100 m 2 /gm.
Claim 19
Dependent Claim
31 words
The microporous ceramic product of claim 17 having a surface area in excess of about 200 m 2 /gm and a micropore volume of greater than about 0.08 cm 3 /gm.
References Cited (Backward Citations)
EP0200326A1
Cited
US4833107A
Cited
US4937304A
Cited
US4950381A
Cited
US4835207A
Cited
US4891340A
Cited
EP0331424A1
Cited
US5006492A
Cited
EP0376183A1
Cited
EP0389084A2
Cited
US4942145A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-06-30 | 2000-12-30 | 2001-07-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-06-30 | 2004-12-30 | 2005-07-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-06-30 | 2008-12-30 | 2009-07-01 | $7700.00 | Window Closed / Lapsed |