Pressure-sensitive adhesive material

Claim 2

A tape or sheet form pressure-sensitive adhesive material which comprises a substrate which is obtained by curing a curable resin composition comprising: (A) an organic elastomeric polymer which is liquid at room temperature and has, in a molecule, at least one silicon-containing group to the silicon atom of which at least one hydroxyl group or hydrolyzable group is bonded and which is cross linkable through formation of a siloxane bond, (B) a curing catalyst and (C) optionally a tackifier resin and a pressure-sensitive adhesive layer comprising an acrylic adhesive laminated on said substrate.

Claim 3

A tape or sheet form pressure-sensitive adhesive material according to claim 1, wherein the organic elastomeric polymer (A) comprises, as a backbone chain, a polyether comprising repeating units of the formula: --R--O-- in which R is a divalent organic group.

Claim 4

A tape or sheet form pressure-sensitive adhesive material according to claim 2, wherein the polyether contains a least 50% by weight of the repeating units --R--O--.

Claim 5

A tape or sheet form pressure sensitive adhesive material according to claim 3, wherein the polyether is polypropylene oxide.

Claim 6

A tape or sheet form pressure-sensitive adhesive material according to claim 1, wherein the silicon-containing group is a group of the formula: ##STR22## wherein X is a hydroxyl or a hydrolyzable group, provided that when two or more X groups are present, they may be the same or different; R 1 is a monovalent hydrocarbon group having 1 to 20 carbon atoms or a triorganosiloxy group of the formula: R.sub.3.sup.2 Si--O-- in which R 2 is a monovalent hydrocarbon group having 1 to 20 carbon atoms, provided that the three R 2 groups may be the same or different and that when two or more R 1 groups are present, they may be the same or different; a is 0, 1, 2 or 3; b is 0, 1 or 2; m is 0 or an integer of 1 to 18, provided that the sum of a and mb is at least 1; and provided that when m is two or more, the ##STR23## groups may be the same or different.

Claim 7

A tape or sheet form pressure-sensitive adhesive material according to claim 5, wherein the silicon-containing group is the group of the formula: ##STR24## wherein c is 1, 2 or 3.

Claim 8

A tape or sheet form pressure-sensitive adhesive material according to claim 1, wherein the hydrolyzable group is selected from the group consisting of a hydrogen atom, a halogen atom, an alkoxyl group, an acyloxy group, a ketoximate group, an amino group, an amide group, an aminoxy group, a mercapto group, and an alkenyloxy group.

Claim 9

A tape or sheet form pressure-sensitive adhesive material according to claim 7, wherein the hydrolyzable group is an alkoxy group having 1 to 8 carbon atoms.

Claim 10

A tape or sheet form pressure-sensitive adhesive material according to claim 2, wherein R is a divalent alkylene group.

Claim 11

A tape or sheet form pressure-sensitive adhesive material according to claim 3, wherein the polyether contains at least 70% by weight of the repeating units --R--O--.

Claim 12

A tape or sheet form pressure-sensitive adhesive material according to claim 3, wherein the polyether contains at least 90% by weight of the repeating units --R--O--.

Claim 13

A tape or sheet form pressure-sensitive adhesive material according to claim 1, wherein polymer (A) has a number average molecular weight of about 500 to 50,000 and after curing has a modulus of elasticity of 1×10 8 dyne/cm 2 or less.

Claim 14

A tape or sheet form pressure-sensitive adhesive material according to claim 1, wherein the curing catalyst (B) is used in an amount of 0.1 to 10 parts by weight per 100 parts by weight of the organic elastomeric polymer (A) and the tackifier resin (C) is used in an amount of 10 to 140 parts by weight per 100 parts of the organic elastomeric polymer (A).

Claim 15

A tape or sheet form pressure-sensitive adhesive material according to claim 1, wherein a pressure-sensitive adhesive layer is laminated on both sides of the substrate.

Claim 16

A tape or sheet form pressure-sensitive adhesive material according to claim 1, wherein the pressure-sensitive adhesive layer has a thickness of from 5 micrometers to 1 millimeter and the thickness of the substrate is 10 micrometers to 3 millimeters.

Claim 17

A tape or sheet form pressure-sensitive adhesive material according to claim 1, wherein the curable resin composition further comprises one or more of a silicon-containing compound, a solvent, plasticizer, or a filler.

Claim 18

A tape or sheet form pressure-sensitive adhesive material which comprises a substrate which is obtained by curing a curable resin composition comprising: (A) an organic elastomeric polymer which is liquid at room temperature and has, in a molecule, at least one silicon-containing group to the silicon atom of which at least one hydroxyl group or hydrolyzable group is bonded and which is cross linkable through formation of a siloxane bond, wherein the organic elastomeric polymer (A) comprises, as a backbone chain, a polyether comprising repeating units of the formula: --R--O-- in which R is a divalent polypropylene oxide organic group, and wherein the silicon-containing group is the group of the formula: ##STR25## wherein X is a hydroxyl or a hydrolyzable group, provided that when two or more X groups are present, they may be the same or different; R 1 is a monovalent hydrocarbon group having 1 to 20 carbon atoms or a triorganosiloxy group of the formula: R.sub.3.sup.2 Si--O-- in which R 2 is a monovalent hydrocarbon group having 1 to 20 carbon atoms, provided that the three R 2 groups may be the same or different and that when two or more R 1 groups are present, they may be the same or different; wherein X and R 1 are the same as defined above and "c" is 1, 2 or 3. (B) a curing catalyst and (C) optionally a tackifier resin and a pressure-sensitive adhesive layer comprising an acrylic adhesive laminated on said substrate.

Claim 19

A tape or sheet form pressure-sensitive adhesive material which comprises a substrate which is obtained by curing a curable resin composition comprising: (A) an organic elastomeric polymer which is liquid at room temperature and has, in a molecule, at least one silicon-containing group to the silicon atom of which at least one hydroxyl group or hydrolyzable group is bonded and which is cross linkable through formation of a siloxane bond, wherein the organic elastomeric polymer (A) comprises, as a backbone chain, a polyether comprising repeating units of the formula: --R--O-- in which R is a divalent polypropylene oxide organic group, and wherein the silicon-containing group is the group of the formula: ##STR25## wherein X is a hydroxyl or a hydrolyzable group, provided that when two or more X groups are present, they may be the same or different; R 1 is a monovalent hydrocarbon group having 1 to 20 carbon atoms or a triorganosiloxy group of the formula: R.sub.3.sup.2 Si--O-- in which R 2 is a monovalent hydrocarbon group having 1 to 20 carbon atoms, provided that the three R 2 groups may be the same or different and that when two or more R 1 groups are present, they may be the same or different; wherein X and R 1 are the same as defined above and "c" is 1, 2 or 3. (B) a curing catalyst and (C) optionally a tackifier resin and a pressure-sensitive adhesive layer comprising an acrylic adhesive laminated on said substrate.

Claim 20

A tape or sheet form pressure-sensitive adhesive material according to claim 17, wherein a pressure-sensitive adhesive layer is laminated on both sides of the substrate.