Silicon nitride film formation method
Assignee: Mitsubishi Electric Corp
•
Filing: 1995-09-12
•
Granted: 1997-05-13
•
Expires: 2015-09-12
Abstract
Abstract In the formation of a silicon nitride film, dichlorosilane and ammonia are used as source gas and, for example, argon is used as carrier gas. The pressure (total pressure) inside a chamber is set to about 100 to 300 Torr (1.33×10 4 to 4.00×10 4 Pa). The desirable setting is that, for example, dichlorosilane is 60 SCCM, ammonia is 300 SCCM and hydrogen is 20 SLM. When the silicon nitride film is formed under such conditions, improvement in a masking effect of the silicon nitride film for preventing oxidation can be achieved.
Inventors
- 👤 Yutaka Inaba
- 👤 Kiyoteru Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:52
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/34; C23C16/345; H; H10; H10P; H10P14/00; H10P14/60; H10P14/66; H10P14/668; H10P14/6681; H10P14/6682; H10D; H10D1/00; H10D1/60; H10D1/68; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/69; H10P14/694; H10P14/6943; H10P14/69433
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
104 words
A method of forming a silicon nitride film by low pressure chemical vapor deposition, comprising the steps of: (a) introducing a substrate of a silicon film having a silicon oxide film surrounding the silicon film in an upper portion of the substrate into a reaction container; (b) evacuating said reaction container; and (c) introducing a source gas comprising dichlorosilane and ammonia and a carrier gas into said reaction container while maintaining the pressure of gas within said reaction container from 2.00×10 4 Pa to 4.00×10 4 Pa, thereby depositing said silicon nitride film at a thickness of about 58 Å to about 48 Å.
Claim 2
Independent Claim
104 words
A method of forming a silicon nitride film by low pressure chemical vapor deposition, comprising the steps of: (a) introducing a substrate of a silicon film having a silicon oxide film surrounding the silicon film in an upper portion of the substrate into a reaction container; (b) evacuating said reaction container; and (c) introducing a source gas comprising dichlorosilane and ammonia and a carrier gas into said reaction container while maintaining the pressure of gas within said reaction container from 2.00×10 4 Pa to 4.00×10 4 Pa, thereby depositing said silicon nitride film at a thickness of about 58 Å to about 48 Å.
Claim 3
Dependent Claim
32 words
The method of claim 1, wherein the carrier gas and dichlorosilane are introduced into said reaction container at a volume flow ratio of carrier gas to dichlorosilane ranging from 100 to 500.
Claim 4
Dependent Claim
30 words
The method of claim 2, wherein the ammonia and dichlorosilane are introduced into said reaction container at a volume flow ratio of ammonia to dichlorosilane ranging from 3 to 10.
Claim 5
Dependent Claim
36 words
The method of claim 3, wherein the volume flow ratio of said ammonia to said dichlorosilane is achieved by a flow volume of ammonia of 300 SCCM and a flow volume of dichlorosilane of 60 SCCM.
Claim 6
Dependent Claim
22 words
The method of claim 4, wherein said substrate is heated to a temperature within the range of 650° C. to 750° C.
Claim 7
Dependent Claim
25 words
The method of claim 5, wherein said carrier gas is at least one gas selected from the group consisting of hydrogen, nitrogen, helium and argon.
Claim 8
Dependent Claim
39 words
The method of claim 1, further comprising a step of (d) performing a reduction reaction on said substrate which reduces a natural oxide film on said substrate placed into said reaction container after step (b), but before step (c).
Claim 9
Dependent Claim
36 words
The method of claim 7, wherein said step (d) comprises the steps of: (d-1) introducing a reducing gas into said reaction container to remove said natural oxide film on said substrate; and (d-2) heating said substrate.
Claim 10
Dependent Claim
37 words
The method of claim 8, wherein said reducing gas comprises at least one gas selected from the group consisting of silane and disilane and wherein the partial pressure thereof ranges from 1.33×10 -4 to 1.33×10 -2 Pa.
Claim 11
Dependent Claim
25 words
The method of claim 9, wherein said substrate is heated to a temperature within the range of 700° C. to 850° C. in step (d-2).
Claim 12
Dependent Claim
11 words
The method of claim 8, wherein said reducing gas comprises hydrogen.
Claim 13
Dependent Claim
21 words
The method of claim 11, wherein said substrate is heated to a temperature of at least 850° C. in step (d-2).
Claim 14
Independent Claim
158 words
A method of forming a stacked capacitor, comprising the steps of: (a) preparing a substrate of a silicon film having a silicon oxide film surrounding said silicon film in an upper portion of said substrate; (b) coating a silicon nitride film on the silicon oxide film on said silicon film by low pressure chemical vapor deposition; (c) oxidizing a surface of said silicon nitride film to form an oxide film; and (d) providing an electrode on said film, wherein said step (b) comprises the steps of: (b-1) introducing said substrate into a reaction container; (b-2) evacuating said reaction container; and (b-3) introducing a source gas comprising dichlorosilane and ammonia and a carrier gas into said reaction container while maintaining the pressure of gas within the reaction container to within the range of 2.00×10 4 to 4.00×10 4 Pa at which said silicon nitride film is prepared at a thickness ranging from about 58 Å to about 48 Å.
Claim 15
Independent Claim
158 words
A method of forming a stacked capacitor, comprising the steps of: (a) preparing a substrate of a silicon film having a silicon oxide film surrounding said silicon film in an upper portion of said substrate; (b) coating a silicon nitride film on the silicon oxide film on said silicon film by low pressure chemical vapor deposition; (c) oxidizing a surface of said silicon nitride film to form an oxide film; and (d) providing an electrode on said film, wherein said step (b) comprises the steps of: (b-1) introducing said substrate into a reaction container; (b-2) evacuating said reaction container; and (b-3) introducing a source gas comprising dichlorosilane and ammonia and a carrier gas into said reaction container while maintaining the pressure of gas within the reaction container to within the range of 2.00×10 4 to 4.00×10 4 Pa at which said silicon nitride film is prepared at a thickness ranging from about 58 Å to about 48 Å.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-05-12 | 2000-11-11 | 2001-05-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-05-12 | 2004-11-11 | 2005-05-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-05-12 | 2008-11-11 | 2009-05-13 | $7700.00 | Window Closed / Lapsed |