Method of making a flash memory cell
Assignee: GlobalFoundries Singapore Pte Ltd
•
Filing: 1996-05-28
•
Granted: 1997-04-15
•
Expires: 2016-05-28
Abstract
Abstract A flash memory EEPROM transistor is formed on a surface of a semiconductor substrate. In portions of the substrate, at the surface thereof, a doped source region and a doped drain region are formed with a channel region therebetween. A tunnel silicon oxide dielectric layer is formed over the semiconductor substrate aside from the source region. Above the source region is formed a gate oxide layer which is thicker than the tunnel oxide layer. Above a portion of the tunnel oxide dielectric layer, over the channel region and above a portion of the gate oxide layer is formed a stacked-gate structure for the transistor comprising a floating gate layer, an interelectrode dielectric layer, and a control gate layer. The source region is located on one side of the stacked gate structure with one edge of the source region overlapping the gate structure. The drain region which is located on the other side of the stacked gate structure with one edge thereof overlapping the gate structure.
Inventors
- 👤 Hsiao-Lun Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:59
CPC Classifications
H; H10; H10B; H10B41/00; H10D; H10D30/00; H10D30/60; H10D30/68; H10D30/681; H10D30/683
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
161 words
A method of forming a flash memory EEPROM transistor comprising the steps in the sequence as follows: forming on a surface of a semiconductor substrate a sacrificial silicon oxide layer over a semiconductor substrate, forming a doped source region in the surface of said substrate, stripping said sacrificial silicon oxide layer from said semiconductor substrate, forming a dielectric layer over said substrate including a gate oxide layer over said source region and a tunnelling dielectric layer over said substrate aside from said source region, forming a stacked-gate structure for said transistor said stacked-gate structure overlapping one edge of said doped source region, said stacked-gate structure comprising a floating gate layer, an interelectrode dielectric layer, and a control gate layer, and forming at another side of said stacked gate structure opposite from said one side of said stacked gate structure a doped drain region in the surface of said substrate with one edge of said doped drain region overlapping said gate structure.
Claim 2
Independent Claim
161 words
A method of forming a flash memory EEPROM transistor comprising the steps in the sequence as follows: forming on a surface of a semiconductor substrate a sacrificial silicon oxide layer over a semiconductor substrate, forming a doped source region in the surface of said substrate, stripping said sacrificial silicon oxide layer from said semiconductor substrate, forming a dielectric layer over said substrate including a gate oxide layer over said source region and a tunnelling dielectric layer over said substrate aside from said source region, forming a stacked-gate structure for said transistor said stacked-gate structure overlapping one edge of said doped source region, said stacked-gate structure comprising a floating gate layer, an interelectrode dielectric layer, and a control gate layer, and forming at another side of said stacked gate structure opposite from said one side of said stacked gate structure a doped drain region in the surface of said substrate with one edge of said doped drain region overlapping said gate structure.
Claim 3
Dependent Claim
29 words
A method in accordance with claim 1 wherein said gate oxide layer between said floating gate and said source region has a thickness between about 100Å and about 400Å.
Claim 4
Dependent Claim
22 words
A method in accordance with claim 1 wherein the said tunneling dielectric layer has a thickness between about 60Å and about 130Å.
Claim 5
Dependent Claim
22 words
A method in accordance with claim 2 wherein the said tunneling dielectric layer has a thickness between about 60Å and about 130Å.
Claim 6
Dependent Claim
44 words
A method in accordance with claim 1 wherein said doped source region is formed by ion implanting with an energy from about 25 keV to about 180 keV with an N+ dopant concentration from about 1E14 atoms/cm 2 to about 9E15 atoms/cm 2 .
Claim 7
Dependent Claim
50 words
A method in accordance with claim 1 wherein after formation of said stacked-gate structure said doped source and drain region are ion implanted with an energy from about 25 keV to about 180 keV with an N+ dopant dose from about 1E15 atoms/cm 2 to about 1E16 atoms/cm 2 .
Claim 8
Dependent Claim
50 words
A method in accordance with claim 5 wherein after formation of said stacked-gate structure said doped source and drain region are ion implanted with an energy from about 25 keV to about 180 keV with an N+ dopant dose from about 1E15 atoms/cm 2 to about 1E16 atoms/cm 2 .
Claim 9
Dependent Claim
40 words
A method in accordance with claim 1 wherein said tunneling dielectric layer comprises a tunnel oxide layer providing an overlap dielectric thickness between said floating gate and said drain region which has a thickness between about 60Å and about 130Å.
Claim 10
Dependent Claim
186 words
A method in accordance with claim 1 wherein said stacked-gate structure for said transistor is formed by deposition of blanket layers as follows: forming said floating gate layer by low pressure chemical vapor deposition of polysilicon material with a thickness from about 1,200Å to about 4,000Å, doping said floating gate layer by a method selected from the group consisting of diffusion with POCl 3 and ion implanting with phosphorus dopant at an energy from about 25 keV to about 180 keV with a dose from about 2E14 atoms/cm 2 to about 9E15 atoms/cm 2 , forming an interelectrode dielectric layer selected from the group consisting of silicon oxide or Oxide/Nitride/Oxide, and forming said control gate layer with a thickness from about 3,500Å to about 4,700Å of a material selected from the group consisting of tungsten polycide and polysilicon formed by low pressure chemical vapor deposition of polysilicon material and doping said control gate layer by a ion implanting with phosphorus dopant at an energy from about 25 keV to about 180 keV with a dose from about 2E14 atoms/cm 2 to about 9E15 atoms/cm 2 .
Claim 11
Dependent Claim
29 words
A method in accordance with claim 9 wherein said gate oxide layer between said floating gate and said source region has a thickness between about 100Å and about 400Å.
Claim 12
Dependent Claim
22 words
A method in accordance with claim 9 wherein the said tunneling dielectric layer has a thickness between about 60Å and about 130Å.
Claim 13
Dependent Claim
22 words
A method in accordance with claim 10 wherein the said tunneling dielectric layer has a thickness between about 60Å and about 130Å.
Claim 14
Dependent Claim
44 words
A method in accordance with claim 9 wherein said doped source region is formed by ion implanting with an energy from about 25 keV to about 180 keV with an N+ dopant dose from about 1E14 atoms/cm 2 to about 9E15 atoms/cm 2 .
Claim 15
Dependent Claim
50 words
A method in accordance with claim 9 wherein after formation of said stacked-gate structure said doped source and drain region are ion implanted with an energy from about 25 keV to about 180 keV with an N+ dopant dose from about 1E15 atoms/cm 2 to about 1E16 atoms/cm 2 .
Claim 16
Dependent Claim
50 words
A method in accordance with claim 13 wherein after formation of said stacked-gate structure said doped source and drain region are ion implanted with an energy from about 25 keV to about 180 keV with an N+ dopant dose from about 1E15 atoms/cm 2 to about 1E16 atoms/cm 2 .
Claim 17
Dependent Claim
40 words
A method in accordance with claim 9 wherein said tunneling dielectric layer comprises a tunnel oxide layer providing an overlap dielectric thickness between said floating gate and said drain region which has a thickness between about 60Å and about 130Å.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-04-14 | 2000-10-14 | 2001-04-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-04-14 | 2004-10-14 | 2005-04-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-04-14 | 2008-10-14 | 2009-04-15 | $7700.00 | Window Closed / Lapsed |