US5620907A — Method for making a heterojunction bipolar transi…

Claim 1

Independent Claim 273 words

A method for forming a heterojunction bipolar transistor, comprising: a) forming a substantially single-crystalline silicon collector region of a first conductivity type within a window defined in a layer of dielectric material; b) over the collector region and over at least a portion of the dielectric layer adjacent the collector region, forming a silicon nucleation layer by non-selective rapid thermal epitaxy and then forming a silicon-germanium alloy layer of a second conductivity type opposite to the first conductivity type by non-selective rapid thermal epitaxy, such that each resulting layer has a part to be referred to as intrinsic that overlies the collector region and a part to be referred to as extrinsic that overlies the dielectric layer, and such that each resulting layer is substantially epitaxial in the intrinsic part thereof and substantially polycrystalline in the extrinsic part thereof; c) over the alloy layer, forming a silicon emitter layer of the first conductivity type by non-selective rapid thermal epitaxy, such that the resulting emitter layer comprises a substantially epitaxial part that overlies the collector region and a substantially polycrystalline part that overlies the dielectric layer, said parts to be respectively referred to as intrinsic and extrinsic parts of said emitter layer; and d) implanting dopant species of the second conductivity type into the extrinsic parts of at least the alloy layer and the emitter layer while substantially excluding said species from the intrinsic parts of the alloy layer and emitter layer, wherein e) the implanting step leads to a doping level of the second conductivity type in both the extrinsic part of the alloy layer and the extrinsic part of the emitter layer.

Claim 2

Independent Claim 273 words

A method for forming a heterojunction bipolar transistor, comprising: a) forming a substantially single-crystalline silicon collector region of a first conductivity type within a window defined in a layer of dielectric material; b) over the collector region and over at least a portion of the dielectric layer adjacent the collector region, forming a silicon nucleation layer by non-selective rapid thermal epitaxy and then forming a silicon-germanium alloy layer of a second conductivity type opposite to the first conductivity type by non-selective rapid thermal epitaxy, such that each resulting layer has a part to be referred to as intrinsic that overlies the collector region and a part to be referred to as extrinsic that overlies the dielectric layer, and such that each resulting layer is substantially epitaxial in the intrinsic part thereof and substantially polycrystalline in the extrinsic part thereof; c) over the alloy layer, forming a silicon emitter layer of the first conductivity type by non-selective rapid thermal epitaxy, such that the resulting emitter layer comprises a substantially epitaxial part that overlies the collector region and a substantially polycrystalline part that overlies the dielectric layer, said parts to be respectively referred to as intrinsic and extrinsic parts of said emitter layer; and d) implanting dopant species of the second conductivity type into the extrinsic parts of at least the alloy layer and the emitter layer while substantially excluding said species from the intrinsic parts of the alloy layer and emitter layer, wherein e) the implanting step leads to a doping level of the second conductivity type in both the extrinsic part of the alloy layer and the extrinsic part of the emitter layer.

Claim 3

Dependent Claim 15 words

The method of claim 1, wherein the collector region is formed by selective epitaxial growth.

Claim 4

Dependent Claim 68 words

The method of claim 1, further comprising, before the implanting step, forming a dielectric spacer that at least partially overlies the intrinsic part of the emitter layer and partially overhangs the extrinsic part of said layer, such that during the implanting step, the dopant species are substantially excluded by the spacer from stopping within the intrinsic parts of the emitter layer, the alloy layer, and the nucleation layer.

Claim 5

Dependent Claim 47 words

The method of claim 3, further comprising, after the implanting step, performing an annealing step such that a substantial concentration of dopant species implanted in at least the emitter layer and the nucleation layer is laterally diffused toward the intrinsic parts of said emitter and nucleation layers.

Claim 6

Dependent Claim 52 words

The method of claim 4, wherein said annealing step is carried out such that said substantial concentration of dopant species implanted in the emitter layer and the nucleation layer is laterally diffused into the intrinsic part of each said emitter and nucleation layers to a depth of about 500 Å or less.

Claim 7

Dependent Claim 52 words

The method of claim 4, wherein said annealing step is carried out such that said substantial concentration of dopant species implanted in the emitter layer and the nucleation layer is laterally diffused into the intrinsic part of each said emitter and nucleation layers to a depth of about 200 Å or less.

Claim 8

Dependent Claim 32 words

The method of claim 4, wherein said annealing step is carried out at a temperature low enough to preclude substantial out-diffusion of second-conductivity-type dopant from the intrinsic part of the alloy layer.

Claim 9

Dependent Claim 47 words

The method of claim 4, wherein the alloy layer is doped in situ with boron as it is formed, and said annealing step is carried out at a temperature low enough to preclude substantial out-diffusion of said in-situ-doped boron from the intrinsic part of the alloy layer.

Claim 10

Dependent Claim 18 words

The method of claim 7, wherein the annealing temperature lies in the range 650° C. to 850° C.

Claim 11

Dependent Claim 48 words

The method of claim 3, wherein the alloy layer is doped in-situ with boron as it is formed; the implanted dopant species comprise boron; and the method further comprises forming an emitter contact layer by depositing in-situ arsenic-doped polycrystalline silicon on the intrinsic part of the emitter layer.

Claim 12

Dependent Claim 81 words

The method of claim 9, further comprising forming self-aligned titanium disilicide layers on the extrinsic part of the emitter layer and on the emitter contact layer, wherein: said titanium-disilicide-forming step comprises annealing at one or more annealing temperatures; and said annealing temperature or temperatures are selected to be great enough to activate the boron implanted in the extrinsic part of the alloy layer, but low enough to precludc substantial diffusion of in-situ-doped boron from the intrinsic part of the alloy layer.

Claim 13

Dependent Claim 39 words

The method of claim 3, wherein the spacer-forming step results in an overhang by the spacer of the extrinsic part of the emitter layer by at least a distance characteristic of the lateral straggle of the implanted dopant species.

Claim 14

Dependent Claim 42 words

The method of claim 3, wherein the spacer-forming step results in an overhang by the spacer of the extrinsic part of the emitter layer by a distance that is not less than about 150 nm, and not more than about 400 nm.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	2000-04-14	2000-10-14	2001-04-15	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	2004-04-14	2004-10-14	2005-04-15	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2008-04-14	2008-10-14	2009-04-15	$7700.00	Window Closed / Lapsed

Method for making a heterojunction bipolar transistor

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag