Method for forming fine titanium nitride film and method for fabricating semiconductor element using the same
Assignee: SK Hynix Inc
•
Filing: 1995-05-22
•
Granted: 1997-02-18
•
Expires: 2015-05-22
Abstract
Abstract A method for forming a fine titanium nitride film and a method for fabricating a semiconductor element using this method. The method for forming a fine titanium nitride film includes the steps of depositing a titanium nitride film on a semiconductor substrate such as with a reactive sputtering method, introducing oxygen into the columnar structured grain boundaries of the titanium nitride film such as by exposing the titanium nitride film to atmosphere, depositing a titanium film on the titanium nitride film having oxygen stuffed therein, converting the titanium film into a fine titanium nitride film by subjecting the titanium film to two times of a heat treatment process. In case a COB DRAM element bit line is formed of tungsten, the fine titanium nitride film and the underlying oxygen-stuffed titanium nitride film, serving as barriers for preventing high temperature diffusion of the tungsten, allow a tungsten bit line having excellent contact and barrier properties. In case the fine titanium nitride film is used as an MOS transistor gate, a gate which can satisfy the thermal stability of a polysilicon as well as the low resistivity of a silicide may be obtained.
Inventors
- 👤 Jeong S. Byun
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 07:38
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/047; H10W20/048; H10B; H10B12/00; H10B12/01; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/01312; H10D64/01318; H10W20/033
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
84 words
A method for forming a titanium nitride film comprising the steps of: forming an oxide film on a semiconductor substrate; forming a first titanium nitride film having grain boundaries on the oxide film; introducing oxygen into the grain boundaries of the first titanium nitride film, wherein the oxygen is introduced into the grain boundaries by exposing the first titanium nitride film to atmosphere; forming a titanium film on the first titanium nitride film; and convening the titanium film into a second titanium nitride film.
Claim 2
Independent Claim
84 words
A method for forming a titanium nitride film comprising the steps of: forming an oxide film on a semiconductor substrate; forming a first titanium nitride film having grain boundaries on the oxide film; introducing oxygen into the grain boundaries of the first titanium nitride film, wherein the oxygen is introduced into the grain boundaries by exposing the first titanium nitride film to atmosphere; forming a titanium film on the first titanium nitride film; and convening the titanium film into a second titanium nitride film.
Claim 3
Dependent Claim
26 words
The method of claim 1, wherein the step of converting the titanium film to the second titanium nitride film comprises thermal annealing of the titanium film.
Claim 4
Dependent Claim
24 words
The method of claim 1, wherein the first titanium nitride film has columnar structured grain boundaries and is formed by a reactive sputtering method.
Claim 5
Dependent Claim
30 words
The method of claim 1, wherein the titanium film is subjected to one to three times of thermal annealing to convert the titanium film into the second titanium nitride film.
Claim 6
Dependent Claim
28 words
The method of claim 4, wherein the thermal annealing is performed at about 500° C. for about 40 seconds and at about 800° C. for about 30 seconds.
Claim 7
Dependent Claim
30 words
The method of claim 1, wherein the step of converting the titanium film into the second titanium nitride film comprises thermal annealing under an N 2 or NH 3 atmosphere.
Claim 8
Dependent Claim
25 words
The method of claim 1, wherein, the step for convening the titanium film into the second titanium nitride film comprises nitridation of the titanium film.
Claim 9
Dependent Claim
21 words
The method of claim 7, wherein the amount of nitrogen atoms contained in the converted titanium film is below about 40%.
Claim 10
Dependent Claim
18 words
The method of claim 1, wherein the thickness of the titanium film is about 200 to 2000 Å.
Claim 11
Dependent Claim
18 words
The method of claim 1, wherein the thickness of the titanium film is about 50 to 500 Å.
Claim 12
Dependent Claim
29 words
The method of claim 1, wherein the first titanium nitride film under the titanium film serves as a barrier for inhibiting reaction of the titanium film with the substrate.
Claim 13
Independent Claim
136 words
A method for fabricating a semiconductor element comprising the steps of: forming a gate oxide film on a semiconductor substrate of a first conductivity type; forming a polysilicon film on the gate oxide film; forming a first titanium nitride film having grain boundaries on the polysilicon film; introducing oxygen into the grain boundaries of the first titanium nitride film, wherein the oxygen is introduced into the grain boundaries by exposing the first titanium nitride film to atmosphere; forming a titanium film on the first titanium nitride film; converting the titanium film into a second titanium nitride film; forming a gate by patterning the first titanium nitride film and the second titanium nitride film; and forming impurity regions in the substrate by injecting second conductivity type impurities into the substrate with the gate used as a mask.
Claim 14
Independent Claim
136 words
A method for fabricating a semiconductor element comprising the steps of: forming a gate oxide film on a semiconductor substrate of a first conductivity type; forming a polysilicon film on the gate oxide film; forming a first titanium nitride film having grain boundaries on the polysilicon film; introducing oxygen into the grain boundaries of the first titanium nitride film, wherein the oxygen is introduced into the grain boundaries by exposing the first titanium nitride film to atmosphere; forming a titanium film on the first titanium nitride film; converting the titanium film into a second titanium nitride film; forming a gate by patterning the first titanium nitride film and the second titanium nitride film; and forming impurity regions in the substrate by injecting second conductivity type impurities into the substrate with the gate used as a mask.
Claim 15
Dependent Claim
26 words
The method of claim 12, wherein the step of converting the titanium film into the second titanium nitride film comprises thermal annealing of the titanium film.
Claim 16
Independent Claim
210 words
A method for fabricating a semiconductor element comprising the steps of: forming a second conductivity type impurity region in a first conductivity type semiconductor substrate; forming an insulation film on the semiconductor substrate; forming a contact hole to the impurity region by removing a portion of the insulation film on the impurity region; forming a first titanium film having grain boundaries on the insulation film and the impurity region and introducing oxygen into the grain boundaries of the first titanium film, wherein the oxygen is introduced into the grain boundaries by exposing the first titanium nitride film to atmosphere; forming a first titanium nitride film having grain boundaries on the first titanium film and introducing oxygen into the grain boundaries of the first titanium nitride film; forming a second titanium film on the first titanium nitride film; converting the second titanium film into a second titanium nitride film by thermal annealing the second titanium film; forming a bit line metal layer on the second titanium nitride film; forming a bit line contacting the impurity region through the contact hole by patterning the first titanium film, the first titanium nitride film, the second titanium nitride film, and the bit line metal layer; and forming a capacitor extending over the bit line.
Claim 17
Independent Claim
210 words
A method for fabricating a semiconductor element comprising the steps of: forming a second conductivity type impurity region in a first conductivity type semiconductor substrate; forming an insulation film on the semiconductor substrate; forming a contact hole to the impurity region by removing a portion of the insulation film on the impurity region; forming a first titanium film having grain boundaries on the insulation film and the impurity region and introducing oxygen into the grain boundaries of the first titanium film, wherein the oxygen is introduced into the grain boundaries by exposing the first titanium nitride film to atmosphere; forming a first titanium nitride film having grain boundaries on the first titanium film and introducing oxygen into the grain boundaries of the first titanium nitride film; forming a second titanium film on the first titanium nitride film; converting the second titanium film into a second titanium nitride film by thermal annealing the second titanium film; forming a bit line metal layer on the second titanium nitride film; forming a bit line contacting the impurity region through the contact hole by patterning the first titanium film, the first titanium nitride film, the second titanium nitride film, and the bit line metal layer; and forming a capacitor extending over the bit line.
Claim 18
Dependent Claim
32 words
The method of claim 14, wherein the impurity region comprises silicon, and wherein the impurity region and the titanium film react during the thermal annealing step to form a titanium silicide film.
Claim 19
Dependent Claim
13 words
The method of claim 14, wherein the bit line metal layer comprises tungsten.
Claim 20
Dependent Claim
19 words
The method of claim 14, wherein the bit line metal layer is deposited with a chemical vapor deposition method.
References Cited (Backward Citations)
US4887146A
Cited
US4990997A
Cited
US5162262A
Cited
US5236868A
Cited
US5164333A
Cited
US5420070A
Cited
US5378660A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-02-18 | 2000-08-19 | 2001-02-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-02-18 | 2004-08-19 | 2005-02-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-02-18 | 2008-08-19 | 2009-02-18 | $7700.00 | Window Closed / Lapsed |