US5596218A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Hot carrier-hard gate oxides by nitrogen implantation before gate oxidation
Assignee: Hewlett Packard Development Co LP
•
Filing: 1993-10-18
•
Granted: 1997-01-21
•
Expires: 2013-10-18
Abstract
Abstract A CMOS device is provided having a high concentration of nitrogen atoms at the SiO 2 /Si interface reducing hot carrier effects associated with operating shorter devices at voltage levels typically used with longer devices. In one embodiment, the process for providing the CMOS device resistant to hot carrier effects makes use of a sacrificial oxide layer through which the nitrogen atoms are implanted and is then removed. Following removal of the sacrificial oxide layer, a gate oxide is grown giving a CMOS device having high nitrogen concentration at the SiO 2 /Si interface. In an alternate embodiment, nitrogen atoms are implanted through the final gate oxide using an implantation energy which does not damage the oxide layer.
Inventors
- 👤 Hamid R. Soleimani
- 👤 Brian Doyle
- 👤 Ara Philipossian
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 15:57
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01332; H10D64/01336; H10D64/01338; H10D64/01344; H10D64/60; H10D64/66; H10D64/68; H10D64/681; H10D64/685; H10D64/693; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0165; H10D84/0181; H10D84/02; H10D84/03; H10D84/038; H10D84/80; H10D84/82; H10D84/83; H10D84/85; H10P30/208; H10P30/225; H10D64/01348
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
134 words
An article comprising: a silicon substrate having a surface layer portion including nitrogen atoms; an oxide layer disposed on the surface layer portion of said silicon substrate and consisting essentially of silicon dioxide and nitrogen atoms and being substantially free of a formation of Si 3 N 4 , with said silicon substrate surface layer portion and said oxide layer in a region having a concentration of nitrogen atoms in a range of at least 5×10 11 /cm 2 to 1×10 12 /cm 2 and occurring about an interface between said silicon substrate surface layer portion and said oxide layer, said region extending substantially from a depth of 1000 angstroms in said silicon substrate to a level in said oxide layer which is ten to twenty percent of the thickness of said oxide layer.
Claim 2
Dependent Claim
134 words
An article comprising: a silicon substrate having a surface layer portion including nitrogen atoms; an oxide layer disposed on the surface layer portion of said silicon substrate and consisting essentially of silicon dioxide and nitrogen atoms and being substantially free of a formation of Si 3 N 4 , with said silicon substrate surface layer portion and said oxide layer in a region having a concentration of nitrogen atoms in a range of at least 5×10 11 /cm 2 to 1×10 12 /cm 2 and occurring about an interface between said silicon substrate surface layer portion and said oxide layer, said region extending substantially from a depth of 1000 angstroms in said silicon substrate to a level in said oxide layer which is ten to twenty percent of the thickness of said oxide layer.
Claim 3
Dependent Claim
18 words
The article of claim 1 wherein said concentration of nitrogen atoms is approximately 7×10 11 /cm 2 .
Claim 4
Dependent Claim
19 words
The article of claim 1 wherein a remaining thickness of said oxide layer is substantially free of nitrogen atoms.
Claim 5
Dependent Claim
320 words
A complementary metal-oxide semiconductor comprising: a silicon substrate, said silicon substrate having a plurality of doped regions disposed therein; a first oxide layer disposed on a surface of said silicon substrate between a first source and drain pair disposed within said silicon substrate and consisting essentially of silicon dioxide and nitrogen atoms diffused throughout and being substantially free of a formation of Si 3 N 4 , said silicon substrate and said first oxide layer having the highest concentration of nitrogen atoms being in a range of at least 5×10 11 /cm 2 to 1×10 12 /cm 2 and occurring in a region encompassing an interface between said silicon substrate and said first oxide layer, said region extending substantially from a depth of 1000 angstroms in said silicon substrate to a level in said first oxide layer which is approximately ten to twenty percent of the thickness of said first oxide layer; a second oxide layer disposed on a surface of said silicon substrate in a region spanning the separation between a second source and drain pair disposed within said silicon substrate and consisting essentially of silicon dioxide and nitrogen atoms diffused throughout and being substantially free of a formation of Si 3 N 4 , said second source and drain pair being further disposed within a well disposed within said silicon substrate and having doped characteristics opposite to said second source and drain pair, said silicon substrate and said second oxide layer having the highest concentration of nitrogen atoms being in a range of approximately 1×10 11 /cm 2 to 1×10 12 /cm 2 and occurring in a second region encompassing an interface between said silicon substrate and said second oxide layer, said region extending substantially from a depth of 1000 angstroms in said silicon substrate to a level in said second oxide layer which is approximately ten to twenty percent of the thickness of said second oxide layer.
Claim 6
Dependent Claim
320 words
A complementary metal-oxide semiconductor comprising: a silicon substrate, said silicon substrate having a plurality of doped regions disposed therein; a first oxide layer disposed on a surface of said silicon substrate between a first source and drain pair disposed within said silicon substrate and consisting essentially of silicon dioxide and nitrogen atoms diffused throughout and being substantially free of a formation of Si 3 N 4 , said silicon substrate and said first oxide layer having the highest concentration of nitrogen atoms being in a range of at least 5×10 11 /cm 2 to 1×10 12 /cm 2 and occurring in a region encompassing an interface between said silicon substrate and said first oxide layer, said region extending substantially from a depth of 1000 angstroms in said silicon substrate to a level in said first oxide layer which is approximately ten to twenty percent of the thickness of said first oxide layer; a second oxide layer disposed on a surface of said silicon substrate in a region spanning the separation between a second source and drain pair disposed within said silicon substrate and consisting essentially of silicon dioxide and nitrogen atoms diffused throughout and being substantially free of a formation of Si 3 N 4 , said second source and drain pair being further disposed within a well disposed within said silicon substrate and having doped characteristics opposite to said second source and drain pair, said silicon substrate and said second oxide layer having the highest concentration of nitrogen atoms being in a range of approximately 1×10 11 /cm 2 to 1×10 12 /cm 2 and occurring in a second region encompassing an interface between said silicon substrate and said second oxide layer, said region extending substantially from a depth of 1000 angstroms in said silicon substrate to a level in said second oxide layer which is approximately ten to twenty percent of the thickness of said second oxide layer.
Claim 7
Dependent Claim
20 words
The complementary metal-oxide semiconductor of claim 4 wherein said concentration of nitrogen atoms is approximately 7×10 11 /cm 2 .
Claim 8
Dependent Claim
46 words
The complementary metal-oxide semiconductor of claim 4 wherein said silicon substrate is a p-type silicon substrate and wherein said first source and drain pair are n-type regions and wherein said second source and drain pair are p-type regions and wherein said well is an n-type well.
Claim 9
Dependent Claim
46 words
The complementary metal-oxide semiconductor of claim 4 wherein said silicon substrate is a n-type silicon substrate and wherein said first source and drain pair are p-type regions and wherein said second source and drain pair are n-type regions and wherein said well is a p-type well.
Claim 10
Dependent Claim
26 words
The complementary metal-oxide semiconductor of claim 4 wherein a remaining thickness of each of said first and second oxide layers is substantially free of nitrogen atoms.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-01-21 | 2000-07-22 | 2001-01-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-01-21 | 2004-07-22 | 2005-01-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-01-21 | 2008-07-22 | 2009-01-21 | $7700.00 | Window Closed / Lapsed |