Method for fabricating metallization patterns on an electronic substrate
Assignee: Motorola Solutions Inc
•
Filing: 1995-08-21
•
Granted: 1997-01-07
•
Expires: 2015-08-21
Abstract
Abstract One method for fabricating solderable pads (406) onto a substrate (220) for direct chip attachment uses a multilayer metallization coating (500). The coating has a bottom layer (202) of indium-tin oxide, with an intermediate layer (204) of copper and a top layer (206) of indium-tin oxide. A masking layer (208) is deposited on the active display area (402) of the substrate, leaving the bonding pads uncovered. The revealed bonding pads are then plasma etched, using the polyimide as an etch resist, and the top layer of ITO is selectively removed to reveal the underlying copper layer. The exposed copper layer (204) is then plated with a solderable metal to the desired thickness to form bonding pads that may be used with direct chip attachment schemes.
Inventors
- 👤 Douglas H. Weisman
- 👤 Thomas J. Swirbel
- 👤 John K. Arledge
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:24
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/243; H03; H03H; H03H3/00; H03H3/007; H03H3/08; H10; H10W; H10W70/00; H10W70/01; H10W70/05; G; G02; G02F; G02F1/00; G02F1/01; G02F1/13; G02F1/133; G02F1/1333; G02F1/1345; H05K2201/00; H05K2201/03; H05K2201/032; H05K2201/0326; H05K2203/00; H05K2203/03; H05K2203/0384; H05K2203/09; H05K2203/095; H05K3/02; H05K3/06; H05K3/061; H05K3/062; H05K3/064
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
149 words
A method for providing thin film metallization areas having varying thicknesses on an electronic substrate, comprising the steps of: providing a substrate having a multilayer metal coating disposed on an upper surface thereof, the coating comprising a first aluminum layer on the substrate surface, a second titanium layer on top of the first layer, and a third aluminum layer on top of the second layer; forming first and second metallization patterns in the multilayer metal coating by etching portions of the multilayer metal coating in a single step to reveal portions of the substrate upper surface; applying a photoresist layer over the substrate sufficient to cover the first metallization pattern and to reveal the second metallization pattern; chemically etching the revealed second metallization pattern to remove only the third aluminum layer, thereby exposing the underlying second titanium layer; and removing the photoresist layer after removing the third aluminum layer.
Claim 2
Independent Claim
149 words
A method for providing thin film metallization areas having varying thicknesses on an electronic substrate, comprising the steps of: providing a substrate having a multilayer metal coating disposed on an upper surface thereof, the coating comprising a first aluminum layer on the substrate surface, a second titanium layer on top of the first layer, and a third aluminum layer on top of the second layer; forming first and second metallization patterns in the multilayer metal coating by etching portions of the multilayer metal coating in a single step to reveal portions of the substrate upper surface; applying a photoresist layer over the substrate sufficient to cover the first metallization pattern and to reveal the second metallization pattern; chemically etching the revealed second metallization pattern to remove only the third aluminum layer, thereby exposing the underlying second titanium layer; and removing the photoresist layer after removing the third aluminum layer.
Claim 3
Dependent Claim
21 words
The method as described in claim 1, wherein the step of forming comprises defining the patterns by photolithography and chemical etching.
Claim 4
Dependent Claim
21 words
The method as described in claim 1, wherein the step of chemically etching is performed by plasma etching or wet etching.
Claim 5
Dependent Claim
56 words
The method as described in claim 1, wherein the step of providing comprises providing a first aluminum layer having a thickness of between 100 and 2000 Angstroms, providing a second titanium layer having a thickness of between 50 and 500 Angstroms, and providing a third aluminum layer having a thickness of between 100 and 10,000 Angstroms.
Claim 6
Dependent Claim
34 words
The method as described in claim 1, wherein the first metallization pattern is a reflector element of a surface acoustic wave (SAW), and the second metallization pattern is a transducer element of the SAW.
Claim 7
Independent Claim
164 words
A method for providing solderable metallization areas on a liquid crystal display substrate, comprising the steps of: providing a liquid crystal display substrate having a multilayer metal coating disposed on an upper surface thereof, the coating comprising a first layer of indium-tin-oxide on the substrate surface, a second metal layer on top of the first layer, and a third layer of indium-tin-oxide on top of the second metal layer; forming a display electrode pattern and a bonding pad pattern in the multilayer metal coating by etching portions of the multilayer metal coating to reveal portions of the substrate upper surface; applying a polyimide layer on the liquid crystal display substrate in a manner sufficient to cover the display electrode pattern and to reveal the bonding pad pattern; selectively etching the revealed bonding pad pattern to remove only the third layer of indium-tin-oxide, thereby exposing the underlying second metal layer; and depositing a fourth layer, comprising a solderable metal, on the exposed second metal layer.
Claim 8
Independent Claim
164 words
A method for providing solderable metallization areas on a liquid crystal display substrate, comprising the steps of: providing a liquid crystal display substrate having a multilayer metal coating disposed on an upper surface thereof, the coating comprising a first layer of indium-tin-oxide on the substrate surface, a second metal layer on top of the first layer, and a third layer of indium-tin-oxide on top of the second metal layer; forming a display electrode pattern and a bonding pad pattern in the multilayer metal coating by etching portions of the multilayer metal coating to reveal portions of the substrate upper surface; applying a polyimide layer on the liquid crystal display substrate in a manner sufficient to cover the display electrode pattern and to reveal the bonding pad pattern; selectively etching the revealed bonding pad pattern to remove only the third layer of indium-tin-oxide, thereby exposing the underlying second metal layer; and depositing a fourth layer, comprising a solderable metal, on the exposed second metal layer.
Claim 9
Dependent Claim
21 words
The method as described in claim 6, wherein the step of forming comprises defining the patterns by photolithography and chemical etching.
Claim 10
Dependent Claim
32 words
The method as described in claim 6, wherein the second metal layer comprises one or more materials selected from the group consisting of Cu, Ag, Au, Ni, Al, Cr, Ti and Sn.
Claim 11
Dependent Claim
28 words
The method as described in claim 6, wherein the step of providing comprises providing a first layer of indium-tin-oxide having a thickness of between 100 and 1000 Angstroms.
Claim 12
Dependent Claim
27 words
The method as described in claim 6, wherein the step of providing comprises providing a second metal layer having a thickness of between 50 and 100 Angstroms.
Claim 13
Dependent Claim
28 words
The method as described in claim 6, wherein the step of providing comprises providing a third layer of indium-tin-oxide having a thickness of between 100 and 10,000 Angstroms.
Claim 14
Dependent Claim
23 words
The method as described in claim 6, wherein the step of selectively etching the revealed bonding pad pattern is performed by plasma etching.
Claim 15
Dependent Claim
23 words
The method as described in claim 6, wherein the step of electively etching the revealed bonding pad pattern is performed by sputter etching.
Claim 16
Dependent Claim
23 words
The method as described in claim 6, wherein the step of forming comprises etching all three of the layers in a single step.
Claim 17
Dependent Claim
19 words
The method as described in claim 6, wherein the step of forming comprises etching each of the layers individually.
Claim 18
Dependent Claim
20 words
The method as described in claim 6, wherein the step of depositing a fourth layer is performed by electroless plating.
Claim 19
Dependent Claim
19 words
The method as described in claim 6, wherein the step of depositing a fourth layer is performed by electroplating.
Claim 20
Independent Claim
172 words
A method for providing solderable metallization areas on a liquid crystal display substrate, comprising the steps of: providing a liquid crystal display substrate having a multilayer metal coating disposed on an upper surface thereof, the coating comprising a first layer of indium-tin-oxide on the substrate surface, a second layer of copper on top of the first layer, and a third layer of indium-tin-oxide on top of the second copper layer; forming a display electrode pattern and a bonding pad pattern in the multilayer metal coating by chemically etching portions of the multilayer metal coating in a single step to reveal portions of the substrate upper surface; applying a polyimide layer on the liquid crystal display substrate in a manner sufficient to cover the display electrode pattern and to reveal the bonding pad pattern; plasma etching the revealed bonding pad pattern to remove only the third layer of indium-tin-oxide, thereby exposing the underlying second layer of copper; and depositing a fourth layer, comprising a solderable metal, on the exposed second layer of copper.
Claim 21
Independent Claim
172 words
A method for providing solderable metallization areas on a liquid crystal display substrate, comprising the steps of: providing a liquid crystal display substrate having a multilayer metal coating disposed on an upper surface thereof, the coating comprising a first layer of indium-tin-oxide on the substrate surface, a second layer of copper on top of the first layer, and a third layer of indium-tin-oxide on top of the second copper layer; forming a display electrode pattern and a bonding pad pattern in the multilayer metal coating by chemically etching portions of the multilayer metal coating in a single step to reveal portions of the substrate upper surface; applying a polyimide layer on the liquid crystal display substrate in a manner sufficient to cover the display electrode pattern and to reveal the bonding pad pattern; plasma etching the revealed bonding pad pattern to remove only the third layer of indium-tin-oxide, thereby exposing the underlying second layer of copper; and depositing a fourth layer, comprising a solderable metal, on the exposed second layer of copper.
Claim 22
Dependent Claim
18 words
The method as described in claim 18, wherein the step of forming comprises defining the patterns by photolithography.
Claim 23
Dependent Claim
59 words
The method as described in claim 18, wherein the step of providing comprises providing a first layer of indium-tin-oxide having a thickness of between 100 and 1000 Angstroms, providing a second layer of copper having a thickness of between 50 and 100 Angstroms, and providing a third layer of indium-tin-oxide having a thickness of between 100 and 10,000 Angstroms.
Claim 24
Dependent Claim
24 words
The method as described in claim 18, wherein the step of depositing a fourth layer is performed by brush plating, electroplating and electroless plating.
Claim 25
Dependent Claim
19 words
The method as described in claim 18, wherein the step of depositing a fourth layer is performed by electroplating.
Claim 26
Independent Claim
176 words
A method for providing solderable metallization areas on a liquid crystal display substrate, comprising the steps of: providing a liquid crystal display substrate having a multilayer metal coating disposed on an upper surface thereof, the coating comprising a first layer of indium-tin-oxide on the substrate surface, a second layer of copper on top of the first layer, and a third layer of indium-tin-oxide on top of the second copper layer; forming a display electrode pattern and a bonding pad pattern in the multilayer metal coating by chemically etching portions of the multilayer metal coating in a single step to reveal portions of the substrate upper surface; applying a polyimide layer on the liquid crystal display substrate in a manner sufficient to cover the display electrode pattern and to reveal the bonding pad pattern; curing the polyimide layer; plasma etching the revealed bonding pad pattern to remove only the third layer of indium-tin-oxide, thereby exposing the underlying second layer of copper; and depositing a fourth layer, comprising a solderable metal, on the exposed second layer of copper.
Claim 27
Independent Claim
176 words
A method for providing solderable metallization areas on a liquid crystal display substrate, comprising the steps of: providing a liquid crystal display substrate having a multilayer metal coating disposed on an upper surface thereof, the coating comprising a first layer of indium-tin-oxide on the substrate surface, a second layer of copper on top of the first layer, and a third layer of indium-tin-oxide on top of the second copper layer; forming a display electrode pattern and a bonding pad pattern in the multilayer metal coating by chemically etching portions of the multilayer metal coating in a single step to reveal portions of the substrate upper surface; applying a polyimide layer on the liquid crystal display substrate in a manner sufficient to cover the display electrode pattern and to reveal the bonding pad pattern; curing the polyimide layer; plasma etching the revealed bonding pad pattern to remove only the third layer of indium-tin-oxide, thereby exposing the underlying second layer of copper; and depositing a fourth layer, comprising a solderable metal, on the exposed second layer of copper.
Claim 28
Dependent Claim
28 words
The method as described in claim 23, further comprising a step of buffing the polyimide layer to provide a preferential orientation on a surface of the polyimide layer.
Claim 29
Independent Claim
173 words
A method for providing a thin film surface acoustic wave (SAW) filter having varying thicknesses on an electronic substrate, comprising the steps of: providing a substrate having a multilayer metal coating disposed on an upper surface thereof, the coating comprising a first aluminum layer having a thickness of between 100 and 2000 Angstroms on the substrate surface, a titanium layer having a thickness of between 50 and 500 Angstroms on top of the first aluminum layer, and a second aluminum layer having a thickness of between 100 and 10,000 Angstroms on top of the titanium layer; forming a reflector element of the SAW and a transducer element of the SAW in the multilayer metal coating by etching through all layers of the multilayer metal coating in a single step to reveal portions of the substrate upper surface; applying a photoresist layer to mask the reflector element and reveal the transducer element; etching the revealed transducer element to remove only the second aluminum layer, exposing the underlying titanium layer; and removing the photoresist layer.
Claim 30
Independent Claim
173 words
A method for providing a thin film surface acoustic wave (SAW) filter having varying thicknesses on an electronic substrate, comprising the steps of: providing a substrate having a multilayer metal coating disposed on an upper surface thereof, the coating comprising a first aluminum layer having a thickness of between 100 and 2000 Angstroms on the substrate surface, a titanium layer having a thickness of between 50 and 500 Angstroms on top of the first aluminum layer, and a second aluminum layer having a thickness of between 100 and 10,000 Angstroms on top of the titanium layer; forming a reflector element of the SAW and a transducer element of the SAW in the multilayer metal coating by etching through all layers of the multilayer metal coating in a single step to reveal portions of the substrate upper surface; applying a photoresist layer to mask the reflector element and reveal the transducer element; etching the revealed transducer element to remove only the second aluminum layer, exposing the underlying titanium layer; and removing the photoresist layer.
References Cited (Backward Citations)
US4358748A
Cited
US4495026A
Cited
JPS62238647A
Cited
US4684436A
Cited
US4925524A
Cited
US4917466A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-01-07 | 2000-07-08 | 2001-01-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-01-07 | 2004-07-08 | 2005-01-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-01-07 | 2008-07-08 | 2009-01-07 | $7700.00 | Window Closed / Lapsed |