Self-aligned opaque regions for attenuating phase-shifting masks
Assignee: Bell Semiconductor LLC
•
Filing: 1994-12-30
•
Granted: 1996-12-31
•
Expires: 2014-12-30
Abstract
Abstract An attenuating phase-shifting optical lithographic mask is fabricated, in a specific embodiment of the invention, by first depositing a uniformly thick molybdenum silicide layer on a top planar surface of quartz. The molybdenum silicide layer has a thickness sufficient for acting as an attenuating (partially transparent) layer in a phase-shifting mask. A uniformly thick chromium layer is deposited on the molybdenum silicide layer. The chromium layer has a thickness sufficient for acting as an opaque layer in the phase-shifting mask. Next, the chromium layer is patterned by dry or wet etching, while the chromium is selectively masked with a patterned resist layer. Then the molybdenum silicide is patterned by dry or wet etching, using the patterned chromium layer as a protective layer, whereby a composite layer of molybdenum silicide and chromium is formed having mutually separated composite stripes. Any remaining resist is removed. Next the top and sidewall surfaces of some, but not others, of these mutually separated stripes are coated with a second patterned resist layer. Finally, the chromium layer, but not the molybdenum silicide layer, is removed from the others of the mutually separated composite stripes.
Inventors
- 👤 John J. DeMarco
- 👤 Taeho Kook
- 👤 Robert L. Kostelak, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:33
CPC Classifications
G; G03; G03F; G03F1/00; G03F1/26; G03F1/32; G03F1/68; G03F1/76; G03F1/80
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
282 words
A method of making an optical lithographic mask comprising the steps of: (a) providing a substrate having a top surface upon which is located a first layer, the first layer being partially transparent to optical radiation of a wavelength λ; (b) depositing a second layer chemically different from the first layer on the top surface of the first layer, the second layer being sufficiently thick so as to be, in combination with the first layer, opaque to the optical radiation of the wavelength λ; (c) forming a first patterned resist layer on the top surface of the second layer; (d) etching the first and second layers, using the first patterned resist layer as a protective layer against etching of the second layer and using the first patterned resist layer or the resulting patterned second material layer as a protective mask against etching the first layer, whereby a first patterned opaque layer is formed having spaced-apart areas each having a top surface bounded by at least one sidewall; (e) forming a second patterned resist layer that coats the entire top surfaces of, and the entire spaces between, at least some, but not all, of the spaced-apart areas; and (f) etching only the patterned second layer using the second patterned resist layer as a protective mask against etching the patterned second layer, while using exposed portions of the first patterned opaque layer as a protective mask against etching the patterned first layer, whereby a second patterned opaque layer and a patterned partially transparent layer are formed, the second patterned opaque layer having a first pattern that includes at least an alignment indicator that is self-aligned with a second pattern of the partially transparent layer.
Claim 2
Independent Claim
282 words
A method of making an optical lithographic mask comprising the steps of: (a) providing a substrate having a top surface upon which is located a first layer, the first layer being partially transparent to optical radiation of a wavelength λ; (b) depositing a second layer chemically different from the first layer on the top surface of the first layer, the second layer being sufficiently thick so as to be, in combination with the first layer, opaque to the optical radiation of the wavelength λ; (c) forming a first patterned resist layer on the top surface of the second layer; (d) etching the first and second layers, using the first patterned resist layer as a protective layer against etching of the second layer and using the first patterned resist layer or the resulting patterned second material layer as a protective mask against etching the first layer, whereby a first patterned opaque layer is formed having spaced-apart areas each having a top surface bounded by at least one sidewall; (e) forming a second patterned resist layer that coats the entire top surfaces of, and the entire spaces between, at least some, but not all, of the spaced-apart areas; and (f) etching only the patterned second layer using the second patterned resist layer as a protective mask against etching the patterned second layer, while using exposed portions of the first patterned opaque layer as a protective mask against etching the patterned first layer, whereby a second patterned opaque layer and a patterned partially transparent layer are formed, the second patterned opaque layer having a first pattern that includes at least an alignment indicator that is self-aligned with a second pattern of the partially transparent layer.
Claim 3
Dependent Claim
34 words
The method of claim 1 in which during step (e) the second patterned resist layer coats only a portion of the top surface of at least one, but not all, of the spaced-apart areas.
Claim 4
Dependent Claim
109 words
A photolithographic method including the steps of: (a) forming the mask in accordance with the steps of claim 2; (b) directing optical radiation of the wavelength λ onto the mask, and focusing resulting optical radiation propagating through the mask onto a second photoresist layer located on a major surface of a wafer or onto a layer of substance located on the major surface of the wafer; (c) developing the second photoresist layer, whereby an edge feature is formed therein; and (d) forming a feature at the major surface of the wafer or in the layer of substance, respectively, in accordance with the edge feature in the second photoresist layer.
Claim 5
Dependent Claim
31 words
The method of claim 1 in which during step (e) the second patterned resist layer coats only a portion of the space between at least one pair of the spaced-apart areas.
Claim 6
Dependent Claim
109 words
A photolithographic method including the steps of: (a) forming the mask in accordance with the steps of claim 4; (b) directing optical radiation of the wavelength λ onto the mask, and focusing resulting optical radiation propagating through the mask onto a second photoresist layer located on a major surface of a wafer or onto a layer of substance located on the major surface of the wafer; (c) developing the second photoresist layer, whereby an edge feature is formed therein; and (d) forming a feature at the major surface of the wafer or in the layer of substance, respectively, in accordance with the edge feature in the second photoresist layer.
Claim 7
Dependent Claim
13 words
The method of claim 1 followed by stripping the second patterned resist layer.
Claim 8
Dependent Claim
61 words
The method of claim 6 in which step (c) is performed by the steps of: etching substantially only the second layer using the first patterned resist layer as a first protective mask against the etching, followed by removing the first patterned resist layer, followed by etching only the first layer using the resulting patterned second layer as a second protective mask.
Claim 9
Dependent Claim
109 words
A photolithographic method including the steps of: (a) forming the mask in accordance with the steps of claim 7; (b) directing optical radiation of the wavelength λ onto the mask, and focusing resulting optical radiation propagating through the mask onto a second photoresist layer located on a major surface of a wafer or onto a layer of substance located on the major surface of the wafer; (c) developing the second photoresist layer, whereby an edge feature is formed therein; and (d) forming a feature at the major surface of the wafer or in the layer of substance, respectively, in accordance with the edge feature in the second photoresist layer.
Claim 10
Dependent Claim
109 words
A photolithographic method including the steps of: (a) forming the mask in accordance with the steps of claim 6; (b) directing optical radiation of the wavelength λ onto the mask, and focusing resulting optical radiation propagating through the mask onto a second photoresist layer located on a major surface of a wafer or onto a layer of substance located on the major surface of the wafer; (c) developing the second photoresist layer, whereby an edge feature is formed therein; and (d) forming a feature at the major surface of the wafer or in the layer of substance, respectively, in accordance with the edge feature in the second photoresist layer.
Claim 11
Dependent Claim
49 words
The method of claim 1 in which step (a) is performed by the steps of: forming a first resist layer of substantially uniform thickness on the top surface of the second layer; exposing the first resist to a first pattern of actinic radiation; and developing the first resist layer.
Claim 12
Dependent Claim
61 words
The method of claim 10 in which step (c) is performed by the steps of: etching substantially only the second layer using the first patterned resist layer as a first protective mask against the etching, followed by removing the first patterned resist layer, followed by etching only the first layer using the resulting patterned second layer as a second protective mask.
Claim 13
Dependent Claim
109 words
A photolithographic method including the steps of: (a) forming the mask in accordance with the steps of claim 11; (b) directing optical radiation of the wavelength λ onto the mask, and focusing resulting optical radiation propagating through the mask onto a second photoresist layer located on a major surface of a wafer or onto a layer of substance located on the major surface of the wafer; (c) developing the second photoresist layer, whereby an edge feature is formed therein; and (d) forming a feature at the major surface of the wafer or in the layer of substance, respectively, in accordance with the edge feature in the second photoresist layer.
Claim 14
Dependent Claim
109 words
A photolithographic method including the steps of: (a) forming the mask in accordance with the steps of claim 10; (b) directing optical radiation of the wavelength λ onto the mask, and focusing resulting optical radiation propagating through the mask onto a second photoresist layer located on a major surface of a wafer or onto a layer of substance located on the major surface of the wafer; (c) developing the second photoresist layer, whereby an edge feature is formed therein; and (d) forming a feature at the major surface of the wafer or in the layer of substance, respectively, in accordance with the edge feature in the second photoresist layer.
Claim 15
Dependent Claim
61 words
The method of claim 1 in which step (c) is performed by the steps of: etching substantially only the second layer using the first patterned resist layer as a first protective mask against the etching, followed by removing the first patterned resist layer, followed by etching only the first layer using the resulting patterned second layer as a second protective mask.
Claim 16
Dependent Claim
16 words
The method of claim 14 followed by the step of stripping the second patterned resist layer.
Claim 17
Dependent Claim
109 words
A photolithographic method including the steps of: (a) forming the mask in accordance with the steps of claim 15; (b) directing optical radiation of the wavelength λ onto the mask, and focusing resulting optical radiation propagating through the mask onto a second photoresist layer located on a major surface of a wafer or onto a layer of substance located on the major surface of the wafer; (c) developing the second photoresist layer, whereby an edge feature is formed therein; and (d) forming a feature at the major surface of the wafer or in the layer of substance, respectively, in accordance with the edge feature in the second photoresist layer.
Claim 18
Dependent Claim
109 words
A photolithographic method including the steps of: (a) forming the mask in accordance with the steps of claim 14; (b) directing optical radiation of the wavelength λ onto the mask, and focusing resulting optical radiation propagating through the mask onto a second photoresist layer located on a major surface of a wafer or onto a layer of substance located on the major surface of the wafer; (c) developing the second photoresist layer, whereby an edge feature is formed therein; and (d) forming a feature at the major surface of the wafer or in the layer of substance, respectively, in accordance with the edge feature in the second photoresist layer.
Claim 19
Dependent Claim
109 words
A photolithographic method including the steps of: (a) forming the mask in accordance with the steps of claim 1; (b) directing optical radiation of the wavelength λ onto the mask, and focusing resulting optical radiation propagating through the mask onto a third photoresist layer located on a major surface of a wafer or onto a layer of substance located on the major surface of the wafer; (c) developing the third photoresist layer, whereby an edge feature is formed therein; and (d) forming a feature at the major surface of the wafer or in the layer of substance, respectively, in accordance with the edge feature in the second photoresist layer.
References Cited (Backward Citations)
US5362591A
Cited
US5405721A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-12-31 | 2000-07-01 | 2000-12-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-12-31 | 2004-07-01 | 2004-12-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-12-31 | 2008-07-01 | 2008-12-31 | $7700.00 | Window Closed / Lapsed |