Coating composition having anti-reflective, and anti-fogging properties

Claim 2

A coating composition which imparts anti-reflection and anti-fogging properties to a substrate having a surface coated therewith, the coating composition comprising: (a) inorganic metal oxide particles; and (b) a silane, or a siloxane oligomer which is formed by the partial or complete hydrolysis and condensation of said silane, wherein said silane or siloxane oligomer comprises at least one hydrophilic anionic group selected from the group consisting of --OSO 2 O - , --SO 2 O - , --CO 2 - , (--O) 2 P(O)O - , --P(O)(O - ) 2 , --OP(O)(O - ) 2 , --P(O - ) 2 and --OP(O - ) 2 ; and wherein the coating composition when coated on at least one side of a light transmissive substrate and dried: 1) exhibits a drop diameter of at least about 4 mm when tested in accordance with the Wetting Test; and 2) provides said substrate with a percent transmission at 550 nm which is at least 3 percent greater than that of the uncoated substrate.

Claim 3

The coating composition of claim 1 wherein the silane or siloxane oligomer has the general formula: ##STR13## wherein: Q is selected from the group consisting of hydroxyl, alkyl groups containing from 1 to about 4 carbon atoms, and alkoxy groups containing from 1 to about 4 carbon atoms; J is selected from cations derived from the group consisting of hydrogen, alkali metals and organic cations of strong bases having an average molecular weight of less than about 150 and a pKa of greater than about 11; X is an organic linking group; Z is selected from the group consisting of --OSO 2 O - , --SO 2 O - , --CO 2 - , (--O) 2 P(O)O - , --P(O)(O - ) 2 , --OP(O)(O - ) 2 , --P(O - ) 2 and --OP(O - ) 2 ; Y is selected from cations derived from the group consisting of hydrogen, alkali metals, alkali earth metals, organic cations of weak bases having an average molecular weight of less than about 200 and a pKa of about 8 to 11, organic cations of strong bases having an average molecular weight of less than about 150 and a pKa of greater than about 11, substituted and unsubstituted guanidines, and quaternary ammonium cations; provided that J is hydrogen when Y is selected from cations derived from hydrogen, alkaline earth metals or said weak organic bases; r is equal to the valence of Y and is 1 to 3; h is 1 or 2; and i is 1 or 2; and t is 1 to 3.

Claim 4

The coating composition of claim 1 wherein the silane is an organosilanol or organosilanolate.

Claim 5

The coating composition of claim 3 wherein the silane is a sulfonate-organosilanol or sulfonate organosilanolate.

Claim 6

The coating composition of claim 2 wherein Z is --SO 2 O - , --P(O)(O - ) 2 or --CO 2 - .

Claim 7

The coating composition of claim 2 wherein X is selected from the group consisting of alkylene groups, cycloalkylene groups, hydroxy-substituted alkylene groups, hydroxy-substituted mono-oxa alkylene groups, divalent hydrocarbon groups having mono-oxa backbone substitution, divalent hydrocarbon groups having mono-thia backbone substitution, divalent hydrocarbon groups having monooxa-thia backbone substitution, divalent hydrocarbon groups having dioxa-thia backbone substitution, arylene groups, arylalkylene groups, alkylarylene groups, and alkylarylene groups; wherein any of said groups comprising X are unsubstituted or independently substituted in available positions by nitrogen, oxygen or sulfur atoms, and wherein X comprises from about 1 to 20 carbon atoms.

Claim 8

The coating composition of claim 6 wherein X is selected from the group consisting of alkylene groups, hydroxy-substituted alkylene groups and hydroxy-substituted mono-oxa alkylene groups.

Claim 9

The coating composition of claim 2 wherein Y is sodium, potassium or lithium.

Claim 10

The coating composition of claim 2 wherein Y is selected from the group consisting of HN + (CH 2 CH 2 CH 2 OH) 3 and H 2 N + (CH 2 CH 2 OH) 2 .

Claim 11

The coating composition of claim 2 wherein Y is selected from the group consisting of N + (CH 3 ) 4 , N + (CH 2 CH 3 ) 4 and N + H 4 .

Claim 12

The coating composition of claim 3 wherein the organosilanol or organosilanolate comprises 30 percent by weight oxygen.

Claim 13

The coating composition of claim 3 wherein the organosilanol or organosilanolate comprises no more than 15 percent by weight silicon.

Claim 14

The coating composition of claim 1 wherein the inorganic metal oxide is selected from the group consisting of aluminum oxide, tin oxide, titanium oxide, antimony oxide, silica, zirconium oxide and mixtures thereof.

Claim 15

A coating composition according to claim 1 wherein the inorganic metal oxide comprises silica.

Claim 16

A coating composition according to claim 1 wherein the inorganic metal oxide is provided as a colloidal solution of inorganic metal oxide particles.

Claim 17

The coating composition of claim 14 wherein the silane is an organo-silanolate-sulfonate salt, an organo-silanate-carboxylate salt, or an organo-silanolate-phosphonate salt.

Claim 18

The coating composition of claim 1 wherein the silane or siloxane oligomer is present in the coating composition in a concentration of 5 to 50 percent by weight of the metal oxide.

Claim 19

The coating composition of claim 16 wherein the silane or siloxane oligomer is present in the coating composition in a concentration of 10 to 30 percent by weight of the metal oxide.

Claim 20

The coating composition of claim 1 further comprising: a surfactant comprised of at least one hydrophobic group and at least one hydrophilic anionic group, wherein: (i) the hydrophilic anionic group comprises an anion selected from the group consisting of --OSO 2 O - , --SO 2 O - , --CO 2 - , (--O) 2 P(O)O - , --OP(O)(O - ) 2 , --P(O) (O - ) 2 , --P(O - ) 2 , --OP(O - ) 2 , (--SO 2 ) 2 N - , --SO 2 N(R) - , (--SO 2 ) 2 C - H, and --N + (R) 2 (CH 2 ) x L', wherein R is hydrogen, an alkyl group which is unsubstituted or substituted with atoms independently selected from the group consisting of oxygen, nitrogen and sulfur, or an alkylene carboxyl group, which alkyl or alkylene carboxyl group comprises about 1 to 10 carbon atoms; x is 1 to 4; and L' is selected from the group consisting of --OSO 2 O - , --SO 2 O - , (--O) 2 P(O)O - , --OP(O)(O - ) 2 , --P(O)(O - ) 2 and --CO 2 - ; and wherein each anionic group is associated with or covalently bound to at least one cation, which cation is selected from the group consisting of H + , Na + , K + , Li + , Ca +2 , Mg +2 , Sr +3 , Al +3 , and R"A + , wherein R" is R or R' wherein R is hydrogen or an alkyl or cycloalkyl group of about 1 to 10 carbon atoms, and R' is covalently bonded to the surfactant molecule and is an alkyl bridging group of 1 to 10 carbon atoms, and A + is N + R 3 , a guanidinium ion optionally substituted with oxygen, nitrogen or sulfur atoms, or N + B wherein B comprises 3 to 7 atoms selected from the group consisting of carbon, nitrogen, sulfur and oxygen atoms which complete the nitrogen containing heterocyclic ring; and wherein any R or R' group may be unsubstituted or substituted with atoms independently selected from the group consisting of oxygen, nitrogen and sulfur; the cation selected such that the net change of the surfactant molecule is neutral; and (ii) wherein the hydrophobic group comprises a hydrocarbon chain comprising at least 4 carbon atoms, or a perfluorinated radical comprising at least 3 carbon atoms.

Claim 21

The coating composition of claim 19 wherein the surfactant has the general formula: [(R).sub.a L.sup.-c ].sub.d (M.sup.+b).sub.c wherein: R is selected from the group consisting of a perfluorinated alkyl or cycloalkyl group of about 3 to 18 perfluorinated carbon atoms; a polyethoxylated perfluoroalkyl or perfluorocycloalkyl substituted alcohol comprising about 3 to 18 perfluorinated carbon atoms and about 0 to 30 non-fluorinated carbon atoms; a perfluoroalkyl substituted alkyl or alkenyl group of about 3 to 18 perfluorinated atoms and about 0 to 30 non-fluorinated carbon atoms, which alkyl or alkenyl group is unsubstituted or comprises oxygen, nitrogen or sulfur atoms within or substituted upon the alkyl or alkenyl chain; an alkyl or alkenyl group of about 4 to 36 carbon atoms, which alkyl or alkenyl group is unsubstituted or comprises oxygen, nitrogen or sulfur atoms within or substituted upon the alkyl or alkenyl chain; an aralkyl group of about 7 to 36 carbon atoms, which aralkyl group is unsubstituted or independently substituted in available positions by oxygen, nitrogen or sulfur atoms; and a polyethoxylated or polypropoxylated alkyl or aralkyl group of about 7 to 36 carbon atoms; L is selected from the group consisting of sulfate, sulfonate, phosphate, phosphonate, sulfonimide, sulfonamide, carboxylate, phosphonite, phosphite and disulfonylmethide groups, and amphoteric alkyl forms thereof; provided that when L is a carboxylate, the surfactant molecule further comprises an additional polar heteroatom or substituent no further than four atoms removed from the carboxylate group, wherein said polar substituent is selected from the group consisting of ether, amide, alcohol, carboxyl, ester, thioester, urea, and urethane groups, and combinations thereof; M is selected from the group consisting of hydrogen, sodium, potassium, lithium, ammonium, calcium, magnesium, strontium aluminum and R"A wherein R" is R or R', wherein R is hydrogen or an alkyl or cycloalkyl group of about 1 to 10 carbon atoms and R' is covalently bonded to the surfactant molecule and is an alkyl bridging group of about 1 to 10 carbon atoms which is unsubstituted or substituted in available positions with oxygen, nitrogen or sulfur atoms; and A is selected from the group consisting of N + R 3 ; a guanidinium ion optionally substituted with oxygen, nitrogen or sulfur atoms; or a heterocyclic N + B wherein B comprises 3 to 7 atoms selected from the group consisting .of carbon, nitrogen, sulfur and oxygen atoms which complete the nitrogen containing heterocyclic ring; a and c are independently 1 or 2; b and d are independently 1, 2 or 3; and e is equal to (c times d)/b, or 0.

Claim 22

The coating composition of claim 19 wherein the hydrophobic group of the surfactant comprises a perfluorinated radical comprising at least 3 carbon atoms.

Claim 23

The coating composition of claim 21 wherein the anionic group of the surfactant is associated with at least one cation selected from lithium, sodium or potassium.

Claim 24

The coating composition of claim 1 further comprising a silane coupling agent capable of covalently bonding the metal oxide to the surfactant or substrate.

Claim 25

The coating composition of claim 23 wherein the silane coupling agent has the general formula: ##STR14## wherein: R 5 is a divalent hydrocarbon bridging group of about 1 to 20 carbon atoms, optionally including in the backbone 1 to 5 moieties selected from the group consisting of --O--, --C(O)--, --S--, --SO 2 -- and --NR 6 -- groups, and optionally substituted on the backbone by --OH, --SH, or --NR 2 6 , wherein R 6 is hydrogen, acetyl, or a hydrocarbon group of 1 to 6 carbon atoms; X is --OR 8 where R 8 is an alkyl, aryl, heteroaryl or aralkyl group of 1 to 8 carbon atoms, or --N═C(R 9 ) 2 , wherein R 9 is independently an alkyl, aryl or aralkyl group of 1 to 8 carbon atoms; R 7 is independently an alkyl, aryl, aralkyl or alkoxy group of 1 to 8 carbon atoms which is unsubstituted or independently substituted in available positions by oxygen, nitrogen and/or sulfur atoms; f is 0, 1, or 2; g is 2 or 3; and Q is a reactive functional group having one moiety selected from the group consisting of amino; hydroxyl; mercaptan; oxirane; chloro-, iodo-, and bromo-alkyl; aziridine; cyclic carboxylic anhydride; acrylate; methacrylate; acrylamide, azide, and isocyanato groups.

Claim 26

A coating composition according to claim 23 wherein the silane coupling agent has the formula (Q).sub.f --R.sup.5 --Si(OR.sup.8).sub.3 wherein: (Q) f is a primary or secondary epoxy or amino group.

Claim 27

A coating composition according to claim 23 wherein the silane coupling agent comprises about 0.1 to 20 percent by weight of the inorganic metal oxide.

Claim 28

A coating composition according to claim 1 further comprising a wetting agent.

Claim 29

An article comprising a substrate having a surface and a layer of a coating composition according to claim 1 on at least one surface of the substrate which coating composition has been dried.

Claim 30

An article according to claim 28 wherein the surface is plastic or glass.

Claim 31

An article according to claim 28 wherein the substrate is transparent or translucent to visible light incident thereon.

Claim 32

An article according to claim 28 wherein the substrate is selected from the group consisting of polyester, polycarbonate, allyldiglycolcarbonate, polyacrylates, polystyrene, polysulfone, polyethersulfone, cellulose acetate butyrate, glass, blends and laminates thereof.

Claim 33

An article according to claim 28 wherein the layer of the coating composition has a thickness in the range of about 500 to 2500 Å.

Claim 34

An article according to claim 28 wherein the layer of the coating composition provides a continuous network of inorganic metal oxide particles.

Claim 35

An eye shield comprising a substrate which is transparent or translucent to visible light coated with (a) a porous inorganic metal oxide network of uniform average thickness which provides anti-reflection properties to the substrate; and (b) a silane, or a siloxane oligomer which is formed by the partial or complete hydrolysis and condensation of said silane, wherein said silane or siloxane oligomer comprises at least one hydrophilic anionic group selected from the group consisting of --OSO 2 O - , --SO 2 O - , --CO 2 - , (--O) 2 P(O)O - , --P(O)(O - ) 2 , --OP(O)(O - ) 2 , --P(O - ) 2 and --OP(O - ) 2 ; which coated substrate exhibits 1) a drop diameter of at least 4 mm when tested in accordance with the Wetting Test described herein; and 2) a percent transmission at 550 nm which is at least 3 percent greater than that of the uncoated substrate.

Claim 36

An eye shield comprising a substrate which is transparent or translucent to visible light coated with (a) a porous inorganic metal oxide network of uniform average thickness which provides anti-reflection properties to the substrate; and (b) a silane, or a siloxane oligomer which is formed by the partial or complete hydrolysis and condensation of said silane, wherein said silane or siloxane oligomer comprises at least one hydrophilic anionic group selected from the group consisting of --OSO 2 O - , --SO 2 O - , --CO 2 - , (--O) 2 P(O)O - , --P(O)(O - ) 2 , --OP(O)(O - ) 2 , --P(O - ) 2 and --OP(O - ) 2 ; which coated substrate exhibits 1) a drop diameter of at least 4 mm when tested in accordance with the Wetting Test described herein; and 2) a percent transmission at 550 nm which is at least 3 percent greater than that of the uncoated substrate.

Claim 37

A surgical mask comprising a face mask and an eye shield according to claim 34.

Claim 38

The article of claim 28 wherein the article is packaged within a material which protects the article from environmental exposure.

Claim 39

The article of claim 36 wherein the packaging material is selected from the group consisting of paper, polyester, high density polyethylene and polystyrene.