Bronze glass composition
Assignee: Vitro SAB de CV
•
Filing: 1995-04-03
•
Granted: 1996-10-15
•
Expires: 2015-04-03
Abstract
Abstract The present invention provides a glass composition having a bronze color and a luminous (visible) transmittance of 70% or greater. The base glass is a soda-lime-silica composition and iron and selenium are added as colorants. In one particular embodiment of the invention, a bronze colored glass with a luminous transmittance (C.I.E. illuminant A) of 70% and higher at a thickness of 4.1 millimeters may be attained by using as colorants: 0.4 to 0.6 wt. % Fe2O3, 0.09 to 0.17 wt. % FeO and 3 to 11 PPM Se. In addition, it is preferred that the total solar energy transmittance be no greater than 60%.
Inventors
- 👤 John F. Krumwiede
- 👤 Larry J. Shelestak
- 👤 Anthony V. Longobardo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:15
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/04; C03C3/062; C03C3/07; C03C3/076; C03C3/083; C03C3/085; C03C3/087; C03C4/00; C03C4/02; C03C4/08; C03C4/085
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
133 words
A bronze colored glass composition having a base glass portion comprising, in percent by weight: ______________________________________
SiO.sub.2 66 to 75
Na.sub.2 O 10 to 20
CaO 5 to 15
MgO 0 to 5
Al.sub.2 O.sub.3
0 to 5
K.sub.2 O 0 to 5
______________________________________ and a colorant portion consisting essentially of: ______________________________________
Fe.sub.2 O.sub.3 (total iron)
about 0.4 to 0.6 percent by weight
FeO about 0.09 to 0.17 percent by weight
Se about 3 to 11 PPM
______________________________________ the glass having a luminous transmittance of about 70% or greater and a color characterized by a dominant wavelength in the range of about 540 to 567.2 nanometers at a thickness of 4.1 millimeters and a monochromatic transmittance which on the average decreases from the shorter wavelengths to the longer wavelengths in the visible spectrum.
Claim 2
Dependent Claim
133 words
A bronze colored glass composition having a base glass portion comprising, in percent by weight: ______________________________________
SiO.sub.2 66 to 75
Na.sub.2 O 10 to 20
CaO 5 to 15
MgO 0 to 5
Al.sub.2 O.sub.3
0 to 5
K.sub.2 O 0 to 5
______________________________________ and a colorant portion consisting essentially of: ______________________________________
Fe.sub.2 O.sub.3 (total iron)
about 0.4 to 0.6 percent by weight
FeO about 0.09 to 0.17 percent by weight
Se about 3 to 11 PPM
______________________________________ the glass having a luminous transmittance of about 70% or greater and a color characterized by a dominant wavelength in the range of about 540 to 567.2 nanometers at a thickness of 4.1 millimeters and a monochromatic transmittance which on the average decreases from the shorter wavelengths to the longer wavelengths in the visible spectrum.
Claim 3
Dependent Claim
42 words
The composition as in claim 1 wherein the Fe 2 O 3 (total iron) concentration is from 0.45 to 0.53 wt. %, the FeO concentration is from 0.1 to 0.15 wt. % and the Se concentration is from 5 to 10 PPM.
Claim 4
Dependent Claim
42 words
The composition as in claim 1 wherein the Fe 2 O 3 (total iron) concentration is from 0.52 to 0.6 wt. %, the FeO concentration is from 0.14 to 0.16 wt. % and the Se concentration is from 4 to 8 PPM.
Claim 5
Dependent Claim
12 words
The composition as in claim 1 further including additional ultraviolet absorbing material.
Claim 6
Dependent Claim
44 words
The composition as in claim 4 wherein said ultraviolet absorbing material is an oxide of a material selected from a group consisting essentially of cerium, vanadium, titanium and molybdenum and combination thereof in an amount up to 2.0 wt. % of the glass composition.
Claim 7
Dependent Claim
20 words
The composition as in claim 5 wherein said TiO 2 is in an amount from 0.1 to 1.0 wt. %.
Claim 8
Dependent Claim
20 words
The composition as in claim 6 wherein said TiO 2 is in an amount from 0.2 to 0.5 wt. %.
Claim 9
Dependent Claim
59 words
The composition as in claim 1 wherein the glass has an average monochromatic transmittance value within the visible spectrum over a first wavelength range below said wavelength corresponding to said maximum monochromatic transmittance, which is up to 10% greater than an average monochromatic transmittance value over a second wavelength range above said wavelength corresponding to said maximum monochromatic transmittance.
Claim 10
Dependent Claim
35 words
The composition as in claim 8 wherein said average monochromatic transmittance over said first range is between 65 and 71% and said average monochromatic transmittance over said second range is between 60 and 66 percent.
Claim 11
Dependent Claim
12 words
A glass sheet made from the composition as recited in claim 1.
Claim 12
Dependent Claim
18 words
The glass sheet as in claim 10 wherein the sheet has a thickness between 1.8 to 6 millimeters.
Claim 13
Dependent Claim
21 words
The glass sheet as in claim 10 wherein the glass has a total solar energy transmittance of no greater than 60%.
Claim 14
Dependent Claim
31 words
The glass sheet as in claim 12 wherein the Fe 2 O 3 concentration is at least 0.5 wt. %, and the total solar energy transmittance is no greater than 55%.
Claim 15
Dependent Claim
25 words
The composition as in claim 1 wherein the glass color is characterized by a dominant wavelength in the range of about 540 to 565 nanometers.
Claim 16
Dependent Claim
136 words
A bronze colored glass composition having a base glass portion comprising, in percent by weight: ______________________________________
SiO.sub.2 66 to 75
Na.sub.2 O 10 to 20
CaO 5 to 15
MgO 0 to 5
Al.sub.2 O.sub.3
0 to 5
K.sub.2 O 0 to 5
______________________________________ and a colorant portion consisting essentially of: ______________________________________
Fe.sub.2 O.sub.3 (total iron)
about 0.4 to 0.6 percent by weight
FeO about 0.1 to 0.17 percent by weight
Se about 3 to 11 PPM
CoO 0 to about 5 PPM
NiO 0 to about 50 PPM
Cr.sub.2 O.sub.3
0 to about 50 PPM
______________________________________ wherein the glass has a luminous transmittance of about 70% or greater and the color of the glass is characterized by a dominant wavelength in the range of about 540 to 567.2 nanometers at a thickness of 4.1 millimeters.
Claim 17
Dependent Claim
136 words
A bronze colored glass composition having a base glass portion comprising, in percent by weight: ______________________________________
SiO.sub.2 66 to 75
Na.sub.2 O 10 to 20
CaO 5 to 15
MgO 0 to 5
Al.sub.2 O.sub.3
0 to 5
K.sub.2 O 0 to 5
______________________________________ and a colorant portion consisting essentially of: ______________________________________
Fe.sub.2 O.sub.3 (total iron)
about 0.4 to 0.6 percent by weight
FeO about 0.1 to 0.17 percent by weight
Se about 3 to 11 PPM
CoO 0 to about 5 PPM
NiO 0 to about 50 PPM
Cr.sub.2 O.sub.3
0 to about 50 PPM
______________________________________ wherein the glass has a luminous transmittance of about 70% or greater and the color of the glass is characterized by a dominant wavelength in the range of about 540 to 567.2 nanometers at a thickness of 4.1 millimeters.
Claim 18
Dependent Claim
33 words
The composition as in claim 15 wherein the color of the glass is characterized by a dominant wavelength in the range of about 540 to 565 nanometers at a thickness of 4.1 millimeters.
Claim 19
Dependent Claim
30 words
The composition as in claim 16 wherein the glass has a monochromatic transmittance which on the average decreases from the shorter wavelengths to the longer wavelengths in the visible spectrum.
Claim 20
Dependent Claim
26 words
The composition as in claim 16 wherein the glass has a total solar energy transmittance of no greater than 60% at a thickness of 4.1 millimeters.
Claim 21
Dependent Claim
12 words
The composition as in claim 18 further including additional ultraviolet absorbing material.
References Cited (Backward Citations)
CA735187A
Cited
US1957279A
Cited
US2524719A
Cited
US2688565A
Cited
US2860059A
Cited
US2892726A
Cited
USRE25312E
Cited
US3294556A
Cited
US3296004A
Cited
US3411934A
Cited
US3300323A
Cited
US3294561A
Cited
US3498806A
Cited
US3660061A
Cited
US3628932A
Cited
US3723142A
Cited
US4104076A
Cited
FR2082647A5
Cited
GB1331492A
Cited
US4129434A
Cited
US3967040A
Cited
FR2270215A1
Cited
US4101705A
Cited
US4190452A
Cited
FR2331527A1
Cited
US4308319A
Cited
US4336303A
Cited
US4339541A
Cited
US4294881A
Cited
US4719126A
Cited
US4719127A
Cited
US4521454A
Cited
US4971843A
Cited
US4617206A
Cited
GB2162835A
Cited
US4866010A
Cited
US4728353A
Cited
US4798616A
Cited
US4792536A
Cited
EP0297404B1
Cited
US4873206A
Cited
US5023210A
Cited
WO1991007356A1
Cited
WO1991011402A1
Cited
EP0452207A1
Cited
US5030593A
Cited
US5070048A
Cited
FR2672587A1
Cited
US5318931A
Cited
EP0536049A1
Cited
US5264400A
Cited
FR2682372A1
Cited
EP0561337A1
Cited
US5380685A
Cited
FR2690437A1
Cited
US5278108A
Cited
EP0619274A1
Cited
US5308805A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-10-15 | 2000-04-15 | 2000-10-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-10-15 | 2004-04-15 | 2004-10-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-10-15 | 2008-04-15 | 2008-10-15 | $7700.00 | Window Closed / Lapsed |