Neutral bronze glazings
Assignee: Saint Gobain Industries SA
•
Filing: 1975-12-02
•
Granted: 1978-07-18
•
Expires: 1995-12-02
Abstract
Abstract A neutral bronze sheet glass has a dominant wavelength in the vicinity of 575 nm, and a monochromatic transmittance which in the range from about 400 nm to about 550 nm is on the average from about 5 to about 50% lower than in the range from about 550 nm to about 750 nm, and possesses in thicknesses suitable for glazing a luminous transmittance above 70%.
Inventors
- 👤 Klaus Fischer
- 👤 Robert Keul
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 18:10
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/10; B; B32; B32B; B32B17/00; B32B17/06; B32B17/10; B32B17/10005; B32B17/10165; B32B17/10339; C03C3/00; C03C3/04; C03C3/076; C03C3/089; C03C3/091; C03C4/00; C03C4/02; G; G02; G02B; G02B5/00; G02B5/20; G02B5/208; G02B5/22; G02B5/226; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/266; Y10T428/269; Y10T428/31504; Y10T428/31551; Y10T428/31627; Y10T428/3163
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
58 words
An article of manufacture comprising a glass sheet at a thickness suitable for glazing, used for windows and windshields of automotive vehicles, said glazing having a total luminous transmittance above 70% and a monochromatic transmittance which on the average value decreases from the long wavelengths to the short wavelengths in the visible spectrum from about 5 to 50%.
Claim 2
Dependent Claim
58 words
An article of manufacture comprising a glass sheet at a thickness suitable for glazing, used for windows and windshields of automotive vehicles, said glazing having a total luminous transmittance above 70% and a monochromatic transmittance which on the average value decreases from the long wavelengths to the short wavelengths in the visible spectrum from about 5 to 50%.
Claim 3
Dependent Claim
22 words
The article according to claim 1 wherein said monochromatic transmittance decreases very rapidly below the short wavelength end of the visible spectrum.
Claim 4
Dependent Claim
40 words
The article according to claim 1 wherein the increase in the average value of said transmittance from the range from 400 nm to 550 nm to the range from 550 nm to 750 nm is from about 5 to 15%.
Claim 5
Dependent Claim
30 words
The article according to claim 3 wherein said average transmittance is between 60 and 85% in the first named range and between 70 and 90% in the second named range.
Claim 6
Dependent Claim
36 words
The article according to claim 1 wherein the average of the monochromatic transmittance over the range from 550 nm to 580 nm is higher than the monochromatic transmittance at adjacent wavelengths above and below said range.
Claim 7
Dependent Claim
28 words
The article according to claim 1 wherein the monochromatic transmittance over the range from 500 nm to 550 nm is higher than at wavelength immediately below 500 nm.
Claim 8
Dependent Claim
27 words
The article according to claim 1 wherein the dominant wavelength is between 570 nm and 580 nm and the excitation purity thereof is between 2 and 6%.
Claim 9
Dependent Claim
68 words
The article according to claim 7 for use in windows of vehicles, said glass sheet having a 3 millimeter thickness thereof and for normally incident light from a source of illuminant C of the International Commission on Illumination, a total luminous transmittance Y between 76 and 79.5%, a dominant wavelength λ D between 574 nm and 580 nm, and a colorimetric purity P e between 2 and 5%.
Claim 10
Dependent Claim
37 words
The article according to claim 8 wherein the quantities Y, λ D and P e and the total solar energy transmittance T.S.E.T. of said glass have respectively substantially the following values: 78.7%, 579 nm, 2% and 77.6%.
Claim 11
Dependent Claim
37 words
The article according to claim 8 wherein the quantities Y, λ D and P e and the total solar energy transmittance T.S.E.T. of said glass have respectively substantially the following values: 77.5%, 578 nm, 2% and 75.2%.
Claim 12
Dependent Claim
37 words
The article according to claim 8 wherein the quantities Y, λ D and P e and the total solar energy transmittance T.S.E.T. of said glass have respectively substantially the following values: 77.7%, 574 nm, 3.7% and 70.9%.
Claim 13
Dependent Claim
37 words
The article according to claim 8 wherein the quantities Y, λ D and P e and the total solar energy transmittance T.S.E.T. of said glass have respectively substantially the following values: 78.7%, 575 nm, 4% and 72.3%.
Claim 14
Dependent Claim
19 words
The article according to claim 11 wherein said glass sheet has a thickness between 3 mm. and 5 mm.
Claim 15
Dependent Claim
19 words
The article according to claim 8 wherein said glass sheet has a thickness between 2 mm. and 3 mm.
Claim 16
Dependent Claim
43 words
The article according to claim 14 wherein the total luminous transmittance Y, the dominant wavelength λ D , the excitation purity P e , and the total solar energy transmittance T.S.E.T. have substantially the following values respectively: 74.8%, 572 nm, 4.6% and 64.3%.
Claim 17
Dependent Claim
43 words
The article according to claim 14 wherein the total luminous transmittance Y, the dominant wavelength λ D , the excitation purity P e , and the total solar energy transmittance T.S.E.T. have substantially the following values respectively: 75.8%, 573 nm, 5.3% and 65.3%.
Claim 18
Dependent Claim
16 words
The article according to claim 14, said window having a total solar energy transmittance below 66%.
Claim 19
Dependent Claim
20 words
The article of manufacture according to claim 1, comprising a glass sheet having a total solar energy transmittance below 66%.
Claim 20
Dependent Claim
18 words
The article according to claim 1 being comprised of a sheet of silicate glass tinted in the mass.
Claim 21
Dependent Claim
32 words
The article according to claim 19 being further comprised of a clear, untinted sheet of silicate glass, and a clear, untinted sheet of plastic between and adhesively bonded to said glass sheets.
References Cited (Backward Citations)
US2524719A
Cited
US2628927A
Cited
US2676117A
Cited
US2755212A
Cited
US2938808A
Cited
US2902377A
Cited
US2965503A
Cited
US3156577A
Cited
US3406085A
Cited
US3300323A
Cited
US3466180A
Cited
US3537944A
Cited
US3723142A
Cited
US3846152A
Cited
US3944440A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-17 | 1982-01-16 | 1982-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-17 | 1986-01-16 | 1986-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-17 | 1990-01-16 | 1990-07-18 | $7700.00 | Window Closed / Lapsed |