Method of forming insulating film
Assignee: Alcan Tech Co Inc
•
Filing: 1995-01-09
•
Granted: 1996-09-10
•
Expires: 2015-01-09
Abstract
Abstract The present invention relates to a film forming method of forming a silicon containing insulating film by plasma CVD. Objects of the present invention are to form, using a highly safe reaction gas, an insulating film which is dense, has excellent step coverage and is low in moisture and in organic residues such as carbon. The insulating film has good affinity for the silicon oxide film formed by the thermal CVD method. The invention also enables control of the refractive index and stress etc. of the insulating film formed. The mixed gas, including the organic compound having Si-H bonds and the oxidizing gas, is converted to a plasma and the silicon containing insulating film is formed on a deposition substrate from the plasma.
Inventors
- 👤 Kazuo Maeda
- 👤 Noboru Tokumasu
- 👤 Yoshiaki Yuyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:06
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/401; C23C16/402; H10P14/66; H10P14/662; H10P14/6922; H10P14/6927; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10P14/668; H10P14/6681; H10P14/6682; H10P14/6684; H10P14/6686
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
64 words
A method of forming a silicon device comprising: (a) forming a plasma from a gas containing at least one organic compound having Si-H bonds and an oxidizing gas; (b) contacting a deposition substrate with said plasma to form a silicon-containing insulating film as a backing layer on the substrate; and (c) coating said backing layer with a layer of silicon oxide by thermal CVD.
Claim 2
Independent Claim
64 words
A method of forming a silicon device comprising: (a) forming a plasma from a gas containing at least one organic compound having Si-H bonds and an oxidizing gas; (b) contacting a deposition substrate with said plasma to form a silicon-containing insulating film as a backing layer on the substrate; and (c) coating said backing layer with a layer of silicon oxide by thermal CVD.
Claim 3
Dependent Claim
30 words
The method of forming an insulating film according to claim 1, wherein said organic compound having Si-H bonds is selected from the group consisting of alkylsilanes, arylsilanes, alkoxysilanes and siloxanes.
Claim 4
Dependent Claim
46 words
The method of forming an insulating film according to claim 2, wherein said alkylsilanes and arylsilanes are represented by the general formula R n SiH 4-n (n=1 to 3), and said R is a member selected from the group consisting of alkyl, aryl and their derivatives.
Claim 5
Dependent Claim
45 words
The method of forming an insulating film according to claim 2, wherein said organic compound containing Si-H bonds is an alkoxysilane and said alkoxysilane is expressed by a general formula (RO) n SiH 4-n (n=1 to 3), wherein R is alkyl or a derivative thereof.
Claim 6
Dependent Claim
63 words
The method of forming an insulating film according to claim 2, wherein said organic compound having Si-H bonds is a chain siloxane expressed by the general formula R n H 3-n SiO(R k H 2-k SiO) m SiH 3-n R n (n=1, 2; k=0 to 2; m≧0), wherein R is a member selected from the group consisting of alkyl, aryl and their derivatives.
Claim 7
Dependent Claim
52 words
The method of forming an insulating film according to claim 5, wherein said organic compound having Si-H bonds is a chain siloxane derivative expressed by the general formula (RO) n H 3-n SiOSiH 3-n (OR) n (n=1, 2), wherein R is a member selected from the group consisting of alkyl and aryl.
Claim 8
Dependent Claim
51 words
The method of forming an insulating film according to claim 2, wherein said organic compound having Si-H bonds is a ring siloxane expressed by the general formula (R k H 2-k SiO) m (k=1; m≧2), wherein R is a member selected from the group consisting of alkyl, aryl and their derivatives.
Claim 9
Dependent Claim
43 words
A method of forming an insulating film according to claim 1, wherein said oxidizing gas includes at least one gas selected from the group consisting of O 2 , NO, N 2 O, NO 2 , CO, CO 2 and H 2 O.
Claim 10
Dependent Claim
40 words
A method in accordance with claim 1 further comprising: (d) repeating step (a) to form a second plasma; and (e) contacting said silicon oxide layer with said second plasma to form a silicon-containing insulating film covering said silicon oxide layer.
Claim 11
Dependent Claim
47 words
A method in accordance with claim 1 wherein said deposition substrate includes a plurality of spaced interconnection layers whereby said interconnection layers become coated with said insulating film in step (b) and spaces between said interconnection layers become filled by said silicon oxide layer in step (c).
Claim 12
Independent Claim
66 words
A method of forming a silicon device comprising: (a) providing a deposition substrate having one surface coated with a silicon oxide layer formed by thermal CVD; (b) forming a plasma from a gas containing at least one organic compound having Si-H bonds and an oxidizing gas; and (c) contacting said deposition substrate with said plasma to form a silicon-containing insulating film covering said silicon oxide layer.
Claim 13
Independent Claim
66 words
A method of forming a silicon device comprising: (a) providing a deposition substrate having one surface coated with a silicon oxide layer formed by thermal CVD; (b) forming a plasma from a gas containing at least one organic compound having Si-H bonds and an oxidizing gas; and (c) contacting said deposition substrate with said plasma to form a silicon-containing insulating film covering said silicon oxide layer.
Claim 14
Dependent Claim
41 words
A method in accordance with claim 11 wherein said deposition substrate includes a plurality of spaced interconnection layers, said interconnection layers being covered by said silicon oxide layer, with spaces between said interconnection layers being filled by said silicon oxide layer.
Claim 15
Dependent Claim
30 words
The method of forming an insulating film according to claim 11, wherein said organic compound having Si-H bonds is selected from the group consisting of alkylsilanes, arylsilanes, alkoxysilanes and siloxanes.
Claim 16
Dependent Claim
45 words
The method of forming an insulating film according to claim 13, wherein said alkylsilanes and arylsilanes are represented by the general formula R n SiH 4-n (n=1 to 3), wherein R is a member selected from the group consisting of alkyl, aryl and their derivatives.
Claim 17
Dependent Claim
45 words
The method of forming an insulating film according to claim 13, wherein said organic compound containing Si-H bonds is an alkoxysilane and said alkoxysilane is expressed by a general formula (RO) n SiH 4-n (n=1 to 3), wherein R is alkyl or a derivative thereof.
Claim 18
Dependent Claim
63 words
The method of forming an insulating film according to claim 13, wherein said organic compound having Si-H bonds is a chain siloxane expressed by the general formula R n H 3-n SiO(R k H 2-k SiO) m SiH 3-n R n (n=1, 2; k=0 to 2; m≧0), wherein R is a member selected from the group consisting of alkyl, aryl and their derivatives.
Claim 19
Dependent Claim
52 words
The method of forming an insulating film according to claim 16, wherein said organic compound having Si-H bonds is a chain siloxane derivative expressed by the general formula (RO) n H 3-n SiOSiH 3-n (OR) n (n=1, 2), wherein R is a member selected from the group consisting of alkyl and aryl.
Claim 20
Dependent Claim
51 words
The method of forming an insulating film according to claim 13, wherein said organic compound having Si-H bonds is a ring siloxane expressed by the general formula (R k H 2-k SiO) m (k=1; m≧2), wherein R is a member selected from the group consisting of alkyl, aryl and derivatives thereof.
Claim 21
Dependent Claim
43 words
A method of forming an insulating film according to claim 11, wherein said oxidizing gas includes at least one gas selected from the group consisting of O 2 , NO, N 2 O, NO 2 , CO, CO 2 and H 2 O.
References Cited (Backward Citations)
US4708884A
Cited
US5051380A
Cited
US5124014A
Cited
US5120680A
Cited
US5378510A
Cited
US5403630A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-09-10 | 2000-03-11 | 2000-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-09-10 | 2004-03-11 | 2004-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-09-10 | 2008-03-11 | 2008-09-10 | $7700.00 | Window Closed / Lapsed |