Method of fabricating a self-aligned contact using a liquid-phase oxide-deposition process
Assignee: United Microelectronics Corp
•
Filing: 1995-05-26
•
Granted: 1996-08-20
•
Expires: 2015-05-26
Abstract
Abstract This invention provides a method of fabricating a self-aligned contact of a semiconductor device using a liquid-phase oxide-deposition (LPD) process. A gate electrode and source/drain regions are formed on a semiconductor substrate. A layer of photoresist is coated and patterned overlying an area of the semiconductor substrate that will form a contact. Using the photoresist as a mask, an oxide layer is formed in self-aligned manner by a liquid-phase deposition process. The photoresist is removed to expose a contact portion of the source/drain regions. An interlevel conductive layer is formed on the semiconductor substrate, wherein the interlevel conductive layer is connected to the source/drain regions through the contact portion.
Inventors
- 👤 Jengping Lin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:46
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/01; H10D84/02; H10D84/03; H10D84/038; H10D64/00; H10D64/01; H10D64/011; H10D84/0123; H10D84/0126; H10D84/0149; H10P; H10P14/00; H10P14/60
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
114 words
A method for fabricating a self-aligned contact of a semiconductor device comprising the steps of: forming a gate electrode on a semiconductor substrate; forming source/drain regions on said semiconductor substrate; coating and patterning a layer of photoresist overlying an area of said semiconductor substrate that will form a contact portion of said source/drain regions; forming an oxide layer by a liquid-phase deposition process using said photoresist as a mask covering said contact portion of said source/drain regions; removing said photoresist to expose the contact portion of said source/drain regions; and forming an interlevel conductive layer on said semiconductor substrate, wherein said interlevel conductive layer is connected to said source/drain regions through said contact portion.
Claim 2
Independent Claim
114 words
A method for fabricating a self-aligned contact of a semiconductor device comprising the steps of: forming a gate electrode on a semiconductor substrate; forming source/drain regions on said semiconductor substrate; coating and patterning a layer of photoresist overlying an area of said semiconductor substrate that will form a contact portion of said source/drain regions; forming an oxide layer by a liquid-phase deposition process using said photoresist as a mask covering said contact portion of said source/drain regions; removing said photoresist to expose the contact portion of said source/drain regions; and forming an interlevel conductive layer on said semiconductor substrate, wherein said interlevel conductive layer is connected to said source/drain regions through said contact portion.
Claim 3
Dependent Claim
65 words
The method of claim 1, wherein the step of forming a gate electrode includes the steps of: successively forming a first oxide layer, a polysilicon layer, and a second oxide layer on said semiconductor substrate; anisotropically etching said second oxide layer, said polysilicon layer, and said second oxide layer to form a gate electrode; and forming a sidewall spacer on sidewalls of said gate electrode.
Claim 4
Dependent Claim
73 words
The method of claim 1, wherein the step of forming a gate electrode includes the steps of: successively forming a first oxide layer, a polysilicon layer, a metal silicide layer, and a second oxide layer on said semiconductor substrate; anisotropically etching said second oxide layer, said metal silicide layer, said polysilicon layer and said first oxide layer to form a gate electrode; and forming a sidewall spacer on sidewalls of said gate electrode.
Claim 5
Dependent Claim
29 words
The method of claim 1, wherein the step of forming source/drain regions includes the step of implanting impurities into said semiconductor substrate using said gate electrode as a mask.
Claim 6
Dependent Claim
37 words
The method of claim 1, wherein the step of forming an oxide layer includes the step of forming an oxide layer deposited to a thickness of between 100 Å to 3000 Å by said liquid-phase deposition process.
Claim 7
Dependent Claim
35 words
The method of claim 1, wherein the step of forming an interlevel conductive layer includes the step of forming an interlevel conductive layer made of polysilicon connected to said source/drain regions through said contact portion.
Claim 8
Dependent Claim
37 words
The method of claim 1, wherein the step of forming an interlevel conductive layer includes the step of forming an interlevel conductive layer made of polycide, metal silicide/polysilicon, connected to said source/drain regions through said contact portion.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-08-20 | 2000-02-19 | 2000-08-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-08-20 | 2004-02-19 | 2004-08-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-08-20 | 2008-02-19 | 2008-08-20 | $7700.00 | Window Closed / Lapsed |