Patent US5545682A successfully refreshed from Google Patents.
US5545682A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Silicone compositions for the formation of cured release coatings
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1995-05-23
•
Granted: 1996-08-13
•
Expires: 2015-05-23
Abstract
Abstract The introduction of release coating-forming silicone compositions that yield cured release coatings that exhibit excellent release properties against tacky substances and do not impair the residual adhesion of tacky substances. Silicone composition for the formation of cured release coatings, that characteristically comprises (A) 100 weight parts of a cured coating-forming silicone composition into which there is admixed (B) 0.5 to 500 weight parts organosilicon polymer with the following average unit formula <IMAGE> wherein R represents C1 to C10 monovalent hydrocarbon groups that are free of aliphatic unsaturation; R1 represents organic groups selected from the group consisting essentially of C2 to C20 alkylene groups and organic groups with the formulas -R3(OR3)y- and -R3-(R2SiO)zR2Si-R3- (R is defined as above, R3 denotes C2 to C20 alkylene groups, which may be the same or different, y is an integer with a value of 1 or more, and z is zero or an integer with a value of 1 or more); R2 represents groups selected from the group consisting essentially of C1 to C10 monovalent hydrocarbon groups, the hydrogen atom, C1 to C10 alkoxy groups, and the hydroxyl group; n=3 to 20; x=1 to 13; and n>/=x.
Inventors
- 👤 Nobuo Kaiya
- 👤 Hideki Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 16:49
CPC Classifications
C; C09; C09D; C09D183/00; C09D183/04; C09D183/14
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
268 words
A silicone composition for the formation of cured release coatings, wherein said composition comprises (A) 100 weight parts of a cured coating-forming silicone composition selected from the group consisting of addition reaction-curing cured coating-forming silicone compositions, condensation reaction-curing cured coating-forming silicone compositions, organoperoxide-curing cured coating-forming silicone compositions, and cured coating-forming silicone compositions that are cured by exposure to high-energy radiation into which there is admixed (B) 0.5 to 500 weight parts organosilicon polymer having a viscosity of 10 to 10,000 centistokes with the following average unit formula ##STR34## wherein each R is independently a C 1 to C 10 monovalent hydrocarbon group that is free of aliphatic unsaturation; R 1 is an organic group selected from the group consisting of C 2 to C 20 alkylene groups, organic groups with the formula --R 3 (OR 3 ) y -- where each R 3 is independently a C 2 to C 20 alkylene group and y is an integer with a value of 1 or more, and organic groups with the formula --R 3 --(R 2 SiO) z R 2 Si--R 3 -- where R and R 3 are defined as above and z is an integer with a value of 1 or more; R 2 is selected from the group consisting of C 1 to C 10 monovalent hydrocarbon groups, the hydrogen atom, C 1 to C 10 alkoxy groups, and the hydroxyl group; n is an integer with a value of at least 3 but no greater than 20; x is an integer with a value of at least 1 but no greater than 13; and n≧x.
Claim 2
Dependent Claim
268 words
A silicone composition for the formation of cured release coatings, wherein said composition comprises (A) 100 weight parts of a cured coating-forming silicone composition selected from the group consisting of addition reaction-curing cured coating-forming silicone compositions, condensation reaction-curing cured coating-forming silicone compositions, organoperoxide-curing cured coating-forming silicone compositions, and cured coating-forming silicone compositions that are cured by exposure to high-energy radiation into which there is admixed (B) 0.5 to 500 weight parts organosilicon polymer having a viscosity of 10 to 10,000 centistokes with the following average unit formula ##STR34## wherein each R is independently a C 1 to C 10 monovalent hydrocarbon group that is free of aliphatic unsaturation; R 1 is an organic group selected from the group consisting of C 2 to C 20 alkylene groups, organic groups with the formula --R 3 (OR 3 ) y -- where each R 3 is independently a C 2 to C 20 alkylene group and y is an integer with a value of 1 or more, and organic groups with the formula --R 3 --(R 2 SiO) z R 2 Si--R 3 -- where R and R 3 are defined as above and z is an integer with a value of 1 or more; R 2 is selected from the group consisting of C 1 to C 10 monovalent hydrocarbon groups, the hydrogen atom, C 1 to C 10 alkoxy groups, and the hydroxyl group; n is an integer with a value of at least 3 but no greater than 20; x is an integer with a value of at least 1 but no greater than 13; and n≧x.
Claim 3
Dependent Claim
21 words
A silicone composition as claimed in claim 1 wherein there is 2 to 200 parts (B) per 100 parts of (A).
Claim 4
Dependent Claim
209 words
A silicone composition as claimed in claim 1 wherein component (B) is straight-chain organosilicon polymer whose main chain is comprised of repeat unit(s) with the following formula ##STR35## and whose terminals are selected from groups with the following formula ##STR36## wherein each R is independently selected from a C 1 to C 10 monovalent hydrocarbon group that is free of aliphatic unsaturation; R 1 is an organic group selected from the group consisting essentially of C 2 to C 20 alkylene groups, organic groups with the formula --R 3 (OR 3 ) y -- where each R 3 is independently a C 2 to C 20 alkylene group and Y is an integer with a value of 1 or more, and organic groups with the formula --R 3 --(R 2 SiO) z R 2 Si--R 3 -- where R and R 3 are defined as above and z is zero or an integer with a value of 1 or more; R 2 is selected from the group consisting essentially of C 1 to C 10 monovalent hydrocarbon groups, the hydrogen atom, C 1 to C 10 alkoxy groups, and the hydroxyl group; and n is an integer with a value of at least 3 but no greater than 20.
Claim 5
Dependent Claim
248 words
A silicone composition as claimed in claim 1 wherein component (B) is organosilicon polymer whose main chain is comprised of units with the following formula ##STR37## and whose terminals are selected from groups with the following formula ##STR38## wherein each R is independently selected from a C 1 to C 10 monovalent hydrocarbon group that is free of aliphatic unsaturation; R 1 is an organic group selected from the group consisting essentially of C 2 to C 20 alkylene groups, organic groups with the formula --R 3 (OR 3 ) y -- where each R 3 is independently a C 2 to C 20 alkylene group and y is an integer with a value of 1 or more, and organic groups with the formula --R 3 --(R 2 SiO) z R 2 Si--R 3 -- where R and R 3 are defined as above and z is zero or an integer with a value of 1 or more; R 2 is selected from the group consisting essentially of C 1 to C 10 monovalent hydrocarbon groups, the hydrogen atom, C 1 to C 10 alkoxy groups, and the hydroxyl group; and n is an integer with a value of at least 3 but no greater than 20 m is an integer with a value of at least 2 but no greater than 13; and n≧m; with the proviso that the organosilicon polymer contains in each molecule at least one ##STR39## unit in which m is at least 3.
Claim 6
Dependent Claim
30 words
A silicone composition as claimed in claim 3 wherein in the organosilicon polymer the repeat unit is of the formula ##STR40## and the terminals are groups with the formula ##STR41##
Claim 7
Dependent Claim
30 words
A silicone composition as claimed in claim 4 wherein in the organosilicon polymer the repeat unit is of the formulas ##STR42## and the terminals are groups with the formula ##STR43##
Claim 8
Dependent Claim
30 words
A silicone composition as claimed in claim 1 wherein in the organosilicon polymer the repeat unit is of the formulas ##STR44## and the terminals are groups with the formula ##STR45##
Claim 9
Dependent Claim
30 words
A silicone composition as claimed in claim 4 wherein in the organosilicon polymer the repeat unit is of the formulas ##STR46## and the terminals are groups with the formula ##STR47##
Claim 10
Dependent Claim
18 words
A silicone composition as claimed in claim 1 wherein in the organosilicon polymer is of the formula ##STR48##
Claim 11
Dependent Claim
30 words
A silicone composition as claimed in claim 3 wherein in the organosilicon polymer the repeat unit is of the formula ##STR49## and the terminals are groups of the formula ##STR50##
Claim 12
Dependent Claim
30 words
A silicone composition as claimed in claim 1 wherein in the organosilicon polymer the repeat unit is of the formulas ##STR51## and the terminals are groups of the formula ##STR52##
Claim 13
Dependent Claim
30 words
A silicone composition as claimed in claim 1 wherein in the organolsilicon polymer the repeat unit is of the formula ##STR53## and the terminals are groups with the formula ##STR54##
Claim 14
Dependent Claim
30 words
A silicone composition as claimed in claim 3 wherein in the organosilicon polymer the repeat unit is of the formula ##STR55## and the terminals are groups with the formula ##STR56##
Claim 15
Dependent Claim
30 words
A silicone composition as claimed in claim 1 wherein in the organolisicon polymer the repeat unit is of the formulas ##STR57## and the terminals are groups with the formula ##STR58##
Claim 16
Dependent Claim
19 words
A silicone composition as claimed in claim 1 wherein component (A) is an addition reaction-curing cured coating-forming silicone composition.
Claim 17
Dependent Claim
105 words
A silicone composition as claimed in claim 15 wherein addition reaction-curing cured coating-forming silicone composition comprises (a) 100 weight parts organopolysiloxane that contains at least 2 alkenyl groups in each molecule and that has a viscosity at 25° C. of at least 40 centipoise, (b) 0.5 to 90 weight parts organohydrogenpolysiloxane that contains at least 3 silicon-bonded hydrogen atoms in each molecule and that has a viscosity at 25° C. of 1 to 1,000 centipoise, and (c) platinum catalyst, in a quantity that provides 0.1 to 1,000 weight parts platinum metal for each 1,000,000 weight parts of the combined amount of components (a) and (b).
Claim 18
Dependent Claim
58 words
A silicone composition as claimed in claim 16 wherein the organopolysiloxane (a) is an organopolysiloxane with the average unit formula formula R 4 a SiO.sub.(4-a)/2 where R 4 is a monovalent hydrocarbon group and subscript a has a value of 1.95 to 2.05 and containing endblocking groups selected from the group consisting of trimethylsiloxy, dimethylvinylsiloxy, dimethylphenylsiloxy, and dimethylhydroxysiloxy.
Claim 19
Dependent Claim
67 words
A silicone composition as claimed in claim 16 wherein the organohydrogenpolysiloxane (b) is an organohydrogenpolysiloxane with the average unit formula R 5 b SiO.sub.(4-b)/2 where R 5 is selected from the group consisting of the hydrogen atom and monovalent hydrocarbon groups excluding alkenyl groups and subscript b ranges from 1.5 to 3.0 and containing endblocking groups selected from the group consisting of trimethylsiloxy, dimethylphenylsiloxy, dimethylhydrogensiloxy, and dimethylhydroxysiloxy.
Claim 20
Dependent Claim
48 words
A silicone composition as claimed in claim 16 wherein the platinum catalyst is selected from the group consisting of chloroplatinic acid, alcohol solutions of chloroplatinic acid, chloroplatinic acid/olefin complexes, chloroplatinic acid/vinylsiloxane complexes, chloroplatinic acid/ketone complexes, platinum supported on alumina micropowder, platinum supported on silica micropowder, and platinum black.
Claim 21
Dependent Claim
24 words
The silicone composition as claimed in claim 16 wherein there is additionally present in the addition reaction-curing cured coating-forming silicone composition a addition-reaction inhibitor.
Claim 22
Dependent Claim
19 words
A silicone composition as claimed in claim 1 wherein component (A) is a condensation reaction-curing cured coating-forming silicone composition.
Claim 23
Dependent Claim
89 words
A silicone composition as claimed in claim 21 wherein the condensation reaction-curing cured coating-forming silicone composition comprises (a') 100 weight parts organopolysiloxane that contains at least 2 silanol groups in each molecule and that has a viscosity at 25° C. of at least 40 centipoise, (b') 0.5 to 90 weight parts organohydrogenpolysiloxane that contains at least 2 silicon-bonded hydrogen atoms in each molecule and that has a viscosity at 25° C. of 1 to 1,000 centipoise, and (c') 0.01 to 20 weight parts metal salt of an organic acid.
Claim 24
Dependent Claim
65 words
A silicone composition as claimed in claim 22 wherein the organopolysiloxane (a') is an organopolysiloxane with the average unit formula R 6 c SiO.sub.(4-c)/2 where R 6 is selected from the group consisting of a monovalent hydrocarbon group and the hydroxyl group and subscript c has a value of 1.95 to 2.05 and contains endblocking groups selected from the group consisting of dimethylhydroxysiloxy and methylphenylhydroxysiloxy.
Claim 25
Dependent Claim
66 words
A silicone composition as claimed in claim 22 wherein the organohydrogenpolysiloxane (b') is selected from an organohydrogenpolysiloxane with the average unit formula R 7 d SiO.sub.(4-d)/2 where R 7 is selected from the group consisting of the hydrogen atom and monovalent hydrocarbon groups and subscript d ranges from 1.5 to 3.0 and containing endblocking groups selected from the group consisting of trimethylsiloxy, dimethylphenylsiloxy, dimethylhydrogensiloxy, and dimethylhydroxysiloxy.
Claim 26
Dependent Claim
37 words
A silicone composition as claimed in claim 22 wherein the metal salt of organic acid is selected from the group consisting of dibutyltin diacetate, dibutyltin dioctoate, dibutyltin dilaurate, dioctyltin dilaurate, tin octoate, zinc naphthoate, and iron octoate.
References Cited (Backward Citations)
US3527659A
Cited
US4123604A
Cited
EP0108208A2
Cited
EP0493841A2
Cited
US5334688A
Cited
EP0652257A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-08-13 | 2000-02-12 | 2000-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-08-13 | 2004-02-12 | 2004-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-08-13 | 2008-02-12 | 2008-08-13 | $7700.00 | Window Closed / Lapsed |