Method and apparatus for forming solder balls and solder columns
Assignee: Intel Corp
•
Filing: 1994-09-15
•
Granted: 1996-08-06
•
Expires: 2014-09-15
Abstract
Abstract A method for forming solder balls and an apparatus and method for forming solder columns on the electrical contact pads of an electronic package in order to establish a more reliable electrical and mechanical connection between an electronic package and a printed circuit board. In one embodiment, solder balls are formed on the electrical contact pads of a package by placing solder cylinders over the electrical contact pads and then passing the package through a reflow furnace where the solder cylinders take the form of spheres and are wetted onto the pads. In a second embodiment, a laminated solder column is formed that is resistant to collapse during the manufacturing process. The laminated solder column comprises a solder cylinder being clad on its top and bottom surfaces with a solder material having a lower melting temperature than that of the center solder cylinder. When attaching the solder column to a package or a printed circuit board reflow temperatures are maintained above the melting temperature of the cladding material but below the melting temperature of the center solder cylinder such that the cladding is wetted onto the electrical contact pads of the package or printed circuit board while the center solder cylinder maintains its solid form.
Inventors
- 👤 George W. Chiu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:11
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/341; H05K3/3431; H05K3/3436; B; B23; B23K; B23K35/00; B23K35/001; H10; H10W; H10W70/00; H10W70/099; H10W72/00; H10W72/01; H10W72/012; B23K35/22; B23K35/24; B23K35/26; H05K2201/00; H05K2201/10; H05K2201/10613; H05K2201/10954; H05K2201/10992; H05K2203/00; H05K2203/04; H05K2203/0415; H05K2203/043; H05K2203/0435; H10W72/20; H10W72/221; H10W72/222; H10W72/251; H10W72/252; Y; Y02; Y02P; Y02P70/00; Y02P70/50; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/4913; Y10T29/49144
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
90 words
A method of forming a solder ball on a package, said method comprising the steps of: a) positioning a solid solder member having at least one planar surface over an electrical contact pad having a second planar surface wherein said at least one planar surface is substantially parallel to said second planar surface; b) heating said solid solder member to a temperature that is above the melting temperature of said solid solder member such that said solid solder member becomes substantially spherical and is wetted onto said electrical contact pad.
Claim 2
Independent Claim
90 words
A method of forming a solder ball on a package, said method comprising the steps of: a) positioning a solid solder member having at least one planar surface over an electrical contact pad having a second planar surface wherein said at least one planar surface is substantially parallel to said second planar surface; b) heating said solid solder member to a temperature that is above the melting temperature of said solid solder member such that said solid solder member becomes substantially spherical and is wetted onto said electrical contact pad.
Claim 3
Dependent Claim
15 words
The method according to claim 1 wherein said solid solder member comprises a solder cylinder.
Claim 4
Dependent Claim
16 words
The method according to claim 1 wherein said solid solder member comprises a rectangular solder member.
Claim 5
Dependent Claim
14 words
The method according to claim 1 wherein said solid solder member comprises 60/40 Sn/Pb.
Claim 6
Dependent Claim
27 words
The method according to claim 4 wherein said heating step is performed at a temperature in the range of approximately 225° C. plus or minus 20° C.
Claim 7
Independent Claim
104 words
A method of forming a solder ball on a package, said method comprising the steps of: a) positioning a solid solder member having at least one planar surface over an electrical contact pad having a first planar surface such that said at least one planar surface is substantially parallel to said first planar surface, said electrical contact pad being located on a first surface of a substrate; b) placing said substrate into a reflow furnace having a temperature above the melting temperature of said solid solder member such that said solid solder member becomes substantially spherical and is wetted onto said electrical contact pad.
Claim 8
Independent Claim
104 words
A method of forming a solder ball on a package, said method comprising the steps of: a) positioning a solid solder member having at least one planar surface over an electrical contact pad having a first planar surface such that said at least one planar surface is substantially parallel to said first planar surface, said electrical contact pad being located on a first surface of a substrate; b) placing said substrate into a reflow furnace having a temperature above the melting temperature of said solid solder member such that said solid solder member becomes substantially spherical and is wetted onto said electrical contact pad.
Claim 9
Dependent Claim
33 words
The method according to claim 6 wherein prior to positioning said solid solder member over said electrical contact pad a flux is applied over said first planar surface of said electrical contact pad.
Claim 10
Dependent Claim
35 words
The method according to claim 6 wherein prior to positioning said solid solder member over said electrical contact pad a flux is applied over said at least one planar surface of said solid solder member.
Claim 11
Dependent Claim
45 words
The method according to claim 6 wherein prior to positioning said solid solder member over said electrical contact pad a flux is applied over said at least one planar surface of said solid solder member and said first planar surface of said electrical contact pad.
Claim 12
Dependent Claim
16 words
The method according to claim 7, 8 or 9 wherein said flux comprises a resin flux.
Claim 13
Dependent Claim
15 words
The method according to claim 6 wherein said solid solder member comprises a solder cylinder.
Claim 14
Dependent Claim
16 words
The method according to claim 6 wherein said solid solder member comprises a rectangular solder body.
Claim 15
Dependent Claim
14 words
The method according to claim 6 wherein said solid solder member comprises 60/40 Sn/Pb.
Claim 16
Dependent Claim
24 words
The method according to claim 13 wherein said reflow furnace temperature is in the range of approximately 225° C. plus or minus 20° C.
Claim 17
Independent Claim
105 words
A method of forming solder balls for attaching an electronic package to a motherboard, said method comprising the steps of: a) applying a flux over a plurality of electrical contact pads located on a first surface of a substrate; b) positioning a solid solder cylinder over each of said electrical contact pads such that said flux is disposed between said solid solder cylinders and said electrical contact pads; c) placing said substrate into a reflow furnace having a temperature above the melting temperature of said solid solder cylinders such that said solid solder cylinders become substantially spherical and are wetted onto said electrical contact pads.
Claim 18
Independent Claim
105 words
A method of forming solder balls for attaching an electronic package to a motherboard, said method comprising the steps of: a) applying a flux over a plurality of electrical contact pads located on a first surface of a substrate; b) positioning a solid solder cylinder over each of said electrical contact pads such that said flux is disposed between said solid solder cylinders and said electrical contact pads; c) placing said substrate into a reflow furnace having a temperature above the melting temperature of said solid solder cylinders such that said solid solder cylinders become substantially spherical and are wetted onto said electrical contact pads.
Claim 19
Dependent Claim
16 words
The method according to claim 15 wherein said flux is applied to said solid solder cylinders.
Claim 20
Dependent Claim
15 words
The method according to claim 15 or 16 wherein said flux comprises a resin flux.
Claim 21
Dependent Claim
14 words
The method according to claim 15 wherein said solid solder cylinders comprise 60/40 Sn/Pb.
Claim 22
Dependent Claim
24 words
The method according to claim 18 wherein said reflow furnace temperature is in the range of approximately 225° C. plus or minus 20° C.
Claim 23
Independent Claim
103 words
A method for attaching a laminated solder column to an electrical contact pad comprising the steps of: a) applying a flux over an electrical contact pad; b) positioning a laminated solder column having a first and second solder layer over said electrical contact pad such that said flux is disposed between said second solder layer and said electrical contact pad; c) placing said substrate into a reflow furnace having a temperature above the melting temperature of said second solder layer but below the melting temperature of said first solder layer such that said second solder layer is wetted onto said electrical contact pad.
Claim 24
Independent Claim
103 words
A method for attaching a laminated solder column to an electrical contact pad comprising the steps of: a) applying a flux over an electrical contact pad; b) positioning a laminated solder column having a first and second solder layer over said electrical contact pad such that said flux is disposed between said second solder layer and said electrical contact pad; c) placing said substrate into a reflow furnace having a temperature above the melting temperature of said second solder layer but below the melting temperature of said first solder layer such that said second solder layer is wetted onto said electrical contact pad.
Claim 25
Dependent Claim
21 words
The method according to claim 20 wherein said flux is applied to said second solder layer of said laminated solder column.
Claim 26
Dependent Claim
16 words
The method according to claim 20 wherein said first and second solder layers comprise solder cylinders.
Claim 27
Dependent Claim
17 words
The method according to claim 20 wherein said first and second solder layers comprise rectangular solder members.
Claim 28
Dependent Claim
14 words
The method according to claim 20 wherein said second solder layer comprises 60/40 Sn/Pb.
Claim 29
Dependent Claim
14 words
The method according to claim 20 wherein said first solder layer comprises 90/10 Pb/Sn.
Claim 30
Independent Claim
193 words
A method of forming a solder column on an electronic device, said method comprising the steps of: a) applying a first barrier to a first planar surface of a first solder body; b) applying a second barrier to a second planar surface of said first solder body; c) cladding said first planar surface of said first solder body with a second solder body having a third and fourth planar surface such that said first barrier is disposed between said first and third planar surfaces; d) cladding said second planar surface of said first solder body with a third solder body having a fifth and sixth planar surface such that said second barrier is disposed between said second and fifth planar surfaces; e) positioning said third solder body over an electrical contact pad having a seventh planar surface such that said sixth planar surface is parallel to said seventh planar surface; f) heating said third solder body to a temperature that is above the melting temperature of said third solder body but below the melting temperature of said first solder body such that said third solder body is wetted onto said electrical contact pad.
Claim 31
Independent Claim
193 words
A method of forming a solder column on an electronic device, said method comprising the steps of: a) applying a first barrier to a first planar surface of a first solder body; b) applying a second barrier to a second planar surface of said first solder body; c) cladding said first planar surface of said first solder body with a second solder body having a third and fourth planar surface such that said first barrier is disposed between said first and third planar surfaces; d) cladding said second planar surface of said first solder body with a third solder body having a fifth and sixth planar surface such that said second barrier is disposed between said second and fifth planar surfaces; e) positioning said third solder body over an electrical contact pad having a seventh planar surface such that said sixth planar surface is parallel to said seventh planar surface; f) heating said third solder body to a temperature that is above the melting temperature of said third solder body but below the melting temperature of said first solder body such that said third solder body is wetted onto said electrical contact pad.
Claim 32
Dependent Claim
17 words
The method according to claim 26 wherein said first, second, and third solder bodies comprise solder cylinders.
Claim 33
Dependent Claim
18 words
The method according to claim 26 wherein said first, second, and third solder bodies comprise rectangular solder members.
Claim 34
Dependent Claim
16 words
The method according to claim 26 wherein said first and third solder bodies comprise 60/40 Sn/Pb.
Claim 35
Dependent Claim
14 words
The method according to claim 26 wherein said second solder body comprises 90/10 Pb/Sn.
Claim 36
Dependent Claim
15 words
The method according to claim 26 wherein said first and second barrier layers comprise nickel.
Claim 37
Dependent Claim
14 words
The method according to claim 26 wherein said first and second barriers comprise palladium.
Claim 38
Independent Claim
90 words
A method of forming a solder bump on a package, said method comprising the steps of: a) positioning a solid solder member having at least one planar surface over an electrical contact pad having a second planar surface wherein said at least one planar surface is substantially parallel to said second planar surface; b) heating said solid solder member to a temperature that is above the melting temperature of said solid solder member such that said solid solder member becomes substantially rounded and is wetted onto said electrical contact pad.
Claim 39
Independent Claim
90 words
A method of forming a solder bump on a package, said method comprising the steps of: a) positioning a solid solder member having at least one planar surface over an electrical contact pad having a second planar surface wherein said at least one planar surface is substantially parallel to said second planar surface; b) heating said solid solder member to a temperature that is above the melting temperature of said solid solder member such that said solid solder member becomes substantially rounded and is wetted onto said electrical contact pad.
Claim 40
Dependent Claim
15 words
The method according to claim 33 wherein said solid solder member comprises a solder cylinder.
Claim 41
Dependent Claim
16 words
The method according to claim 33 wherein said solid solder member comprises a rectangular solder member.
Claim 42
Dependent Claim
14 words
The method according to claim 33 wherein said solid solder member comprises 60/40 Sn/Pb.
Claim 43
Dependent Claim
27 words
The method according to claim 36 wherein said heating step is performed at a temperature in the range of approximately 225° C. plus or minus 20° C.
References Cited (Backward Citations)
US3292240A
Cited
US3303393A
Cited
US3436818A
Cited
US3486223A
Cited
US3811186A
Cited
US3921285A
Cited
US4545610A
Cited
US4673772A
Cited
US4693770A
Cited
US4818728A
Cited
US4752027A
Cited
WO1989002653A1
Cited
US5075965A
Cited
US5186383A
Cited
US5269453A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-08-06 | 2000-02-05 | 2000-08-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-08-06 | 2004-02-05 | 2004-08-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-08-06 | 2008-02-05 | 2008-08-06 | $7700.00 | Window Closed / Lapsed |