Coating composition for the surface treatment of a rubber article
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1994-12-23
•
Granted: 1996-06-18
•
Expires: 2014-12-23
Abstract
Abstract Disclosed is a silicone-based coating composition in the form of an aqueous dispersion of organopolysiloxanes suitable for the surface treatment of a rubber article to impart the surface with excellent lubricity and abrasion resistance so as to be useful for upgrading, for example, wind shields in automobiles. The coating composition comprises, as the effective ingredients, four organopolysiloxanes each in the form of an aqueous dispersion or solution including (a) an organopolysiloxane having a branched molecular structure consisting of two types of the siloxane units of the general formulas R12SiO and R1SiO1.5, in which R1 is a monovalent hydrocarbon group, (b) a hydrolysis-condensation product of an epoxy group-containing dialkoxy silane compound, (c) a hydrolysis-condensation product of an aminoalkyl group-containing dialkoxy silane compound and (d) cured silicone rubber particles in a specified proportion.
Inventors
- 👤 Yoshinori Inokuchi
- 👤 Satoshi Kuwata
- 👤 Toshikatu Kanehara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:37
CPC Classifications
C; C09; C09D; C09D183/00; C09D183/04; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; C08J7/046; C08J2321/00; C08J2483/00
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
400 words
A silicone-based coating composition for the surface treatment of a rubber article which is a uniform water-base mixture comprising: (a) an aqueous dispersion of a non-flowable organopolysiloxane having a branched molecular structure consisting essentially of the organosiloxane units represented by the general formulae R 1 2 SiO and R 1 SiO 1 .5, in which R 1 is a monovalent hydrocarbon group having 1 to 20 carbon atoms, as a first organopolysiloxane ingredient; (b) an aqueous dispersion of a hydrolysis-condensation product of an epoxy group-containing alkoxy silane compound represented by the general formula R 2 R 3 Si(OR 4 ) 2 , in which R 2 is a monovalent organic group substituted by an epoxy group and having 5 to 20 carbon atoms and R 3 and R 4 are each a monovalent hydrocarbon group having 1 to 6 carbon atoms, as a second organopolysiloxane ingredient; (c) a hydrolysis-condensation product of an amino-group containing alkoxy silane compound represented by the general formula R 5 R 6 N(CH 2 ) a [NR 7 (CH 2 ) b ] c --SiR 8 (OR 9 ) 2 , in which R 5 , R 6 and R 7 are each a hydrogen atom or a monovalent hydrocarbon group having 1 to 6 carbon atoms, R 8 and R 9 are each a monovalent hydrocarbon group having 1 to 6 carbon atoms, the subscripts a and b are each a positive integer not exceeding 6 and the subscript c is zero or a positive integer not exceeding 3, as a third organopolysiloxane ingredient; and (d) an aqueous dispersion of particles of a cured silicone rubber as a fourth organopolysiloxane ingredient, the component (c) being dissolved or dispersed in the blend of the components (a), (b) and (d), in such a blending proportion of the components (a), (b), (c) and (d) that the amount of the first organopolysiloxane in the component (a) is in the range from 10 to 90% by weight, the amount of the second organopolysiloxane in the component (b) is in the range from 1 to 50% by weight, the amount of the third organopolysiloxane as the component (c) is in the range from 1 to 50% by weight and the amount of the fourth organopolysiloxane in the component (d) is in the range from 1 to 70% by weight each based on the total amount of the first to fourth organopolysiloxanes.
Claim 2
Dependent Claim
400 words
A silicone-based coating composition for the surface treatment of a rubber article which is a uniform water-base mixture comprising: (a) an aqueous dispersion of a non-flowable organopolysiloxane having a branched molecular structure consisting essentially of the organosiloxane units represented by the general formulae R 1 2 SiO and R 1 SiO 1 .5, in which R 1 is a monovalent hydrocarbon group having 1 to 20 carbon atoms, as a first organopolysiloxane ingredient; (b) an aqueous dispersion of a hydrolysis-condensation product of an epoxy group-containing alkoxy silane compound represented by the general formula R 2 R 3 Si(OR 4 ) 2 , in which R 2 is a monovalent organic group substituted by an epoxy group and having 5 to 20 carbon atoms and R 3 and R 4 are each a monovalent hydrocarbon group having 1 to 6 carbon atoms, as a second organopolysiloxane ingredient; (c) a hydrolysis-condensation product of an amino-group containing alkoxy silane compound represented by the general formula R 5 R 6 N(CH 2 ) a [NR 7 (CH 2 ) b ] c --SiR 8 (OR 9 ) 2 , in which R 5 , R 6 and R 7 are each a hydrogen atom or a monovalent hydrocarbon group having 1 to 6 carbon atoms, R 8 and R 9 are each a monovalent hydrocarbon group having 1 to 6 carbon atoms, the subscripts a and b are each a positive integer not exceeding 6 and the subscript c is zero or a positive integer not exceeding 3, as a third organopolysiloxane ingredient; and (d) an aqueous dispersion of particles of a cured silicone rubber as a fourth organopolysiloxane ingredient, the component (c) being dissolved or dispersed in the blend of the components (a), (b) and (d), in such a blending proportion of the components (a), (b), (c) and (d) that the amount of the first organopolysiloxane in the component (a) is in the range from 10 to 90% by weight, the amount of the second organopolysiloxane in the component (b) is in the range from 1 to 50% by weight, the amount of the third organopolysiloxane as the component (c) is in the range from 1 to 50% by weight and the amount of the fourth organopolysiloxane in the component (d) is in the range from 1 to 70% by weight each based on the total amount of the first to fourth organopolysiloxanes.
Claim 3
Dependent Claim
125 words
The silicone-based coating composition for the surface treatment of a rubber article as claimed in claim I in which the blending proportion of the components (a), (b), (c) and (d) is such that the amount of the first organopolysiloxane in the component (a) is in the range from 20 to 70% by weight, the amount of the second organopolysiloxane in the component (b) is in the range from 5 to 20% by weight, the amount of the third organopolysiloxane as the component (c) is in the range from 5 to 20% by weight and the amount of the fourth organopolysiloxane in the component (d) is in the range from 5 to 50% by weight based on the total amount of the first to fourth organopolysiloxanes.
Claim 4
Dependent Claim
30 words
The silicone-based Coating composition for the surface treatment of a rubber article as claimed in claim 1 in which the epoxy group-containing alkoxy silane compound is 3-glycidyloxypropyl methyl diethoxy silane.
Claim 5
Dependent Claim
35 words
The silicone-based coating composition for the surface treatment of a rubber article as claimed in claim 1 in which the amino group-containing alkoxy silane compound is 3-(N-2-aminoethyl)aminopropyl methyl dimethoxy silane or 3-aminopropyl methyl dimethoxy silane.
Claim 6
Dependent Claim
46 words
The silicone-based coating composition for the surface treatment of a rubber article as claimed in claim 1 in which the cured silicone rubber is an alkenyl group-containing organopolysiloxane crosslinked with an organohydrogenpolysiloxane by the hydrosilation reaction in the presence of a platinum compound as a catalyst.
Claim 7
Independent Claim
454 words
A method for the improvement of the abrasion resistance and lubricity of the surface of a rubber article which comprises the steps of: (A) coating the surface of the rubber article with a silicone-based coating composition which is a uniform water-base mixture comprising: (a) an aqueous dispersion of a non-flowable organopolysiloxane having a branched molecular structure consisting essentially of the organosiloxane units represented by the general formulas R 1 2 SiO and R 1 SiO 1 .5, in which R 1 is a monovalent hydrocarbon group having 1 to 20 carbon atoms, as a first organopolysiloxane ingredient; (b) an aqueous dispersion of a hydrolysis-condensation product of an epoxy group-containing alkoxy silane compound represented by the general formula R 2 R 3 Si(OR 4 ) 2 , in which R 2 is a monovalent organic group substituted by an epoxy group and having 5 to 20 carbon atoms and R 3 and R 4 are each a monovalent hydrocarbon group having 1 to 6 carbon atoms, as a second organopolysiloxane ingredient; (c) a hydrolysis-condensation product of an amino-group containing alkoxy silane compound represented by the general formula R 5 R 6 N(CH 2 ) a [NR 7 (CH 2 ) b ] c --SiR 8 (OR 9 ) 2 , in which R 5 , R 6 and R 7 are each a hydrogen atom or a monovalent hydrocarbon group having 1 to 6 carbon atoms, R 8 and R 9 are each a monovalent hydrocarbon group having 1 to 6 carbon atoms, the subscripts a and b are each a positive integer not exceeding 6 and the subscript c is zero or a positive integer not exceeding 3, as a third organopolysiloxane ingredient; and (d) an aqueous dispersion of particles of a cured silicone rubber as a fourth organopolysiloxane ingredient, the component (c) being dissolved or dispersed in the blend of the components (a), (b) and (d), in such a blending proportion of the components (a), (b), (c) and (d) that the amount of the first organopolysiloxane in the component (a) is in the range from 10 to 90% by weight, the amount of the second organopolysiloxane in the component (b) is in the range from 1 to 50% by weight, the amount of the third organopolysiloxane as the component (c) is in the range from 1 to 50% by weight and the amount of the fourth organopolysiloxane in the component (d) is in the range from 1 to 70% by weight each based on the total amount of the first to fourth organopolysiloxanes; and (B) drying the coating film on the surface of the rubber article to effect curing of the organopolysiloxane ingredients in the coating composition to form a cured coating layer.
Claim 8
Independent Claim
454 words
A method for the improvement of the abrasion resistance and lubricity of the surface of a rubber article which comprises the steps of: (A) coating the surface of the rubber article with a silicone-based coating composition which is a uniform water-base mixture comprising: (a) an aqueous dispersion of a non-flowable organopolysiloxane having a branched molecular structure consisting essentially of the organosiloxane units represented by the general formulas R 1 2 SiO and R 1 SiO 1 .5, in which R 1 is a monovalent hydrocarbon group having 1 to 20 carbon atoms, as a first organopolysiloxane ingredient; (b) an aqueous dispersion of a hydrolysis-condensation product of an epoxy group-containing alkoxy silane compound represented by the general formula R 2 R 3 Si(OR 4 ) 2 , in which R 2 is a monovalent organic group substituted by an epoxy group and having 5 to 20 carbon atoms and R 3 and R 4 are each a monovalent hydrocarbon group having 1 to 6 carbon atoms, as a second organopolysiloxane ingredient; (c) a hydrolysis-condensation product of an amino-group containing alkoxy silane compound represented by the general formula R 5 R 6 N(CH 2 ) a [NR 7 (CH 2 ) b ] c --SiR 8 (OR 9 ) 2 , in which R 5 , R 6 and R 7 are each a hydrogen atom or a monovalent hydrocarbon group having 1 to 6 carbon atoms, R 8 and R 9 are each a monovalent hydrocarbon group having 1 to 6 carbon atoms, the subscripts a and b are each a positive integer not exceeding 6 and the subscript c is zero or a positive integer not exceeding 3, as a third organopolysiloxane ingredient; and (d) an aqueous dispersion of particles of a cured silicone rubber as a fourth organopolysiloxane ingredient, the component (c) being dissolved or dispersed in the blend of the components (a), (b) and (d), in such a blending proportion of the components (a), (b), (c) and (d) that the amount of the first organopolysiloxane in the component (a) is in the range from 10 to 90% by weight, the amount of the second organopolysiloxane in the component (b) is in the range from 1 to 50% by weight, the amount of the third organopolysiloxane as the component (c) is in the range from 1 to 50% by weight and the amount of the fourth organopolysiloxane in the component (d) is in the range from 1 to 70% by weight each based on the total amount of the first to fourth organopolysiloxanes; and (B) drying the coating film on the surface of the rubber article to effect curing of the organopolysiloxane ingredients in the coating composition to form a cured coating layer.
Claim 9
Dependent Claim
44 words
The method for the improvement of the abrasion resistance and lubricity of the surface of a rubber article as claimed in claim 6 in which the thickness of the coating layer as dried and cured is in the range from 0.1 to 10 μm.
Claim 10
Dependent Claim
24 words
The silicone-based coating composition of claim 1, wherein the first organopolysiloxane ingredient has a viscosity of at least 10 6 centistokes at 25° C.
Claim 11
Dependent Claim
50 words
The silicone-based coating composition of claim 1, wherein, in the first organopolysiloxane, each R 1 is, independently, an alkyl group, alkenyl group, phenyl group, tolyl group or cycloalkyl group of 1 to 20 carbon atoms, optionally, substituted with halogen atoms or organic groups containing an epoxy, carboxyl or amino group.
Claim 12
Dependent Claim
47 words
The silicone-based coating composition of claim 1, wherein, in the second organopolysiloxane, R 2 is 2-glycidyloxyethyl, 3-glycidyloxypropyl, 2-(3,4-epoxycyclohexyl)ethyl or 3-(3,4-epoxycyclohexyl)propyl, and R 3 and R 4 are, independently, an alkyl group, phenyl group or cycloalkyl group of 1 to 6 carbon atoms, optionally, substituted with halogen atoms.
Claim 13
Dependent Claim
72 words
The silicone-based coating composition of claim 1, wherein, in the third organopolysiloxane, R 5 , R 6 and R 7 are, independently, a hydrogen atom or an alkyl group, phenyl group or cycloalkyl group of 1 to 6 carbon atoms, optionally, substituted with halogen atoms and R 8 and R 9 are, independently, an alkyl group, phenyl group or cycloalkyl group of 1 to 6 carbon atoms, optionally, substituted with halogen atoms.
Claim 14
Dependent Claim
29 words
The silicone-based coating composition of claim 1, wherein, the particles of cured silicone rubber as the fourth organopolysiloxane ingredient have an average particle diameter of 0.1 to 100 μm.
References Cited (Backward Citations)
US4252933A
Cited
EP0186839A2
Cited
US4652618A
Cited
EP0467406A2
Cited
US5246995A
Cited
US5270110A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-06-18 | 1999-12-18 | 2000-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-06-18 | 2003-12-18 | 2004-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-06-18 | 2007-12-18 | 2008-06-18 | $7700.00 | Window Closed / Lapsed |