Laser-machining polymers
Assignee: Tyco Electronics UK Ltd
•
Filing: 1989-02-03
•
Granted: 1996-01-30
•
Expires: 2009-02-03
Abstract
Abstract PCT No. PCT/GB89/00109 Sec. 371 Date Feb. 26, 1991 Sec. 102(e) Date Feb. 26, 1991 PCT Filed Feb. 3, 1989 PCT Pub. No. WO89/07337 PCT Pub. Date Aug. 10, 1989.Article and method of making same by laser-ablation-machining of (a) aromatic and/or amorphous polyamide material, or (b) polymeric material having repeating in its polymer backbone aromatic rings and aliphatic chains (with the proviso that the aliphatic chains have at least 4 carbon atoms when the material is a polyester, and preferably in all cases U.V. laser radiation is preferred, preferably at wavelengths greater than 248 nm from a KrF or XeCl excimer laser. The preferred polyamides, polyetheresters, and polyimides have superior machining performance and may be useful for making uniaxially electrically conductive articles by machining holes cleanly through laminar sheets of the preferred polymers, which sheets are subsequently metal plated.
Inventors
- 👤 Michael J. Ludden
- 👤 Richard J. Penneck
- 👤 Nicholas J. G. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:09
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/69; H05; H05K; H05K3/00; H05K3/0011; H05K3/0017; H05K3/0026; H05K3/0032; B; B23; B23K; B23K1/00; B23K1/0008; B23K1/0016; B23K20/00; B23K20/02; B23K20/023; B23K26/00; B23K26/36; B23K26/40; B23K31/00; B23K31/02; G; G03; G03F; G03F7/00; G03F7/20; G03F7/2051; G03F7/2053; H10W40/00; H10W40/20; H10W40/25; H10W40/257; H10W70/01; H10W70/05; H10W70/095; H10W70/62; H10W70/63; H10W70/635; H10W70/688; H10W70/695; H10W99/00; B23K2101/00; B23K2101/36; B23K2101/40; B23K2103/00; B23K2103/30; B23K2103/42; B23K2103/50; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/032; H05K1/0326; H05K1/0333; H05K1/0346; H05K1/0353; H05K1/036; H05K2201/00; H05K2201/01; H05K2201/0104; H05K2201/0116; H05K2201/0137; H05K2201/0154; H05K2201/10; H05K2201/10227; H05K2201/10378; H05K2203/00; H05K2203/10; H05K2203/107
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
111 words
A method of making an article of polymeric material comprising laser-ablation-machining a body of polymeric material at a laser wavelength, power density, and energy fluence sufficient to remove portions of the body, the body comprising low to zero-charring material selected from the group consisting of: (a) polyamide material which is aromatic or amorphous or both; (b) polymer having in its polymer backbone aromatic rings and aliphatic chains, the polymer being selected from the group consisting of polyetheresters and polyimides; and (c) polyester material other than polyetheresters having in its polymer backbone aromatic rings, ester carboxylate groups and aliphatic chains between the carboxylate groups, which chains having at least 4 carbon atoms.
Claim 2
Independent Claim
111 words
A method of making an article of polymeric material comprising laser-ablation-machining a body of polymeric material at a laser wavelength, power density, and energy fluence sufficient to remove portions of the body, the body comprising low to zero-charring material selected from the group consisting of: (a) polyamide material which is aromatic or amorphous or both; (b) polymer having in its polymer backbone aromatic rings and aliphatic chains, the polymer being selected from the group consisting of polyetheresters and polyimides; and (c) polyester material other than polyetheresters having in its polymer backbone aromatic rings, ester carboxylate groups and aliphatic chains between the carboxylate groups, which chains having at least 4 carbon atoms.
Claim 3
Dependent Claim
29 words
A method according to claim 1, wherein the polymeric material comprises a polyetherester block copolymer having ester blocks and having aromatic rings in the backbone of the ester blocks.
Claim 4
Dependent Claim
19 words
A method according to claim 2, the polyetherester also having aliphatic chains in the backbone of the ester blocks.
Claim 5
Dependent Claim
33 words
A method according to claim 1, the polyetherester being a poyetherester block copolymer of ether blocks and ester blocks having aliphatic chains and no aromatic rings in the backbone of the ether blocks.
Claim 6
Dependent Claim
24 words
A method according to claim 1 wherein at least some of the said aliphatic chains of polymer (b) contain at least four carbon atoms.
Claim 7
Dependent Claim
27 words
A method according to claim 2, wherein the polyetherester block copolymer comprises polyester blocks of repeat unit formula ##STR27## and polyether blocks of repeat unit formula ##STR28##
Claim 8
Dependent Claim
14 words
A method according to claim 1 wherein the polymeric material comprises an aromatic polyamide.
Claim 9
Dependent Claim
21 words
A method according to claim 7, wherein the aromatic polyamide has in its backbone aromatic rings derived from a phthalic acid.
Claim 10
Dependent Claim
129 words
A method according to claim 1, wherein the polymeric material comprises a polyamide (A) based on the condensation of terephthalic acid with trimethylhexamethylene diamine (preferably containing a mixture of 2,2,4- and 2,4,4-trimethylhexamethylene diamine isomers), or (B) formed from the condensation of one or more bis-aminomethylnorbornane isomers with one or more aliphatic, cycloaliphatic or aromatic dicarboxylic acids e.g. terephthalic acid and optionally including one or more amino acid or lactam e.g. gamma-caprolactam comopomers, or (C) based on units derived from laurinlactam, isophthalic acid and bis-(4-amino-3-methylcyclohexyl) methane, or (D) based on the condensation of 2,2-bis-(p-aminocyclohexyl) propane with adipic and azeleic acids, and polyamides based on the condensation of trans cyclohexane-1,4-dicarboxylic acid with the trimethylhexamethylene diamine isomers mentioned in (A) above, or (E) based on units derived from m-xylylenediamine and adipic acid.
Claim 11
Dependent Claim
22 words
A method according to claim 1, wherein the polymeric material comprises a polyimide having in its backbone aromatic rings derived from pyromellitimide.
Claim 12
Dependent Claim
25 words
A method according to claim 10, wherein the polymeric material comprises a polyimide having in its backbone aliphatic chains of at least 10 carbon atoms.
Claim 13
Dependent Claim
17 words
A method according to claim 10, wherein the polyimide is derived from 1,12-dodecamethylene pyromellitimide or 1,13-tridecamethylene pyromellitimide.
Claim 14
Dependent Claim
13 words
A method according to claim 1 wherein the laser-machined polymeric material is amorphous.
Claim 15
Dependent Claim
17 words
A method according to claim 1, including laser machining at a UV wavelength greater than 248 nanometers.
Claim 16
Dependent Claim
18 words
A method according to claim 14, including laser machining by means of an XeCl or KrF excimer laser.
Claim 17
Dependent Claim
22 words
A method according to claim 1, wherein the polymeric material is doped with an aromatic carbonyl compound to enhance the laser machining.
Claim 18
Dependent Claim
31 words
A method according to claim 1, wherein the laser-machined polymeric material comprises a laminar sheet having at least one layer of polyamide material and at least one layer of polyimide material.
Claim 19
Dependent Claim
22 words
A method according to claim 17, wherein the polyamide layer(s) comprise(s) a polyamide as specified in any of claims 7 to 9.
Claim 20
Dependent Claim
22 words
A method according to claim 17, wherein the polyimide layer(s) comprise(s) a polyimide as specified in any of claims 10 to 12.
Claim 21
Dependent Claim
21 words
A method according to claim 17 wherein the polyimide is derived from polymerization of 4,4'-biphenyl dianhydride and 4,4'-diaminobiphenyl, 4,4'-diaminobiphenylether, or phenylenediamine.
Claim 22
Dependent Claim
37 words
A method according to claim 17, wherein the polyimide material is capable of retaining at least 50% of its original elongation after immersion in water of pH10 at 100° C. for 4 days according to ASTM D882.
Claim 23
Dependent Claim
24 words
A method according to claim 1, wherein the polymeric material is in the form of a sheet and through-holes are laser-machined through the sheet.
Claim 24
Dependent Claim
17 words
A method according to claim 1, wherein the laser-machined polymeric material is spin-coated on a supporting substrate.
Claim 25
Dependent Claim
33 words
A method according to claim 1 wherein at least part of the polymeric material is cross-linkable and is cross-linked by exposure to laser light of lower power than that used for the laser-machining.
Claim 26
Dependent Claim
16 words
A method according to claim 1, wherein the laser-machined polymeric material is a polymeric photoresist layer.
Claim 27
Dependent Claim
19 words
A method according to claim 1, wherein the polymeric material has a C:H ratio of not more than 0.9.
References Cited (Backward Citations)
US3790744A
Cited
US4417948A
Cited
US4414059A
Cited
US4617085A
Cited
US5175043A
Cited
US4780177A
Cited
US4877644A
Cited
US4857382A
Cited
US4915981A
Cited
US5075195A
Cited
US5207955A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-01-29 | 1999-07-31 | 2000-01-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-01-29 | 2003-07-31 | 2004-01-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-01-29 | 2007-07-31 | 2008-01-30 | $7700.00 | Window Closed / Lapsed |