Method of fabricating a self-aligned contact using organic dielectric materials
Assignee: Texas Instruments Inc
•
Filing: 1994-08-23
•
Granted: 1996-01-09
•
Expires: 2014-08-23
Abstract
Abstract A semiconductor device and process for making the same are disclosed which incorporate organic dielectric materials to form self-aligned contacts (SACTs) reliably, even in deep, narrow gaps. In one embodiment, conductors 26 with insulating conductor caps 28 are formed over a silicon substrate 20 with a thin gate oxide 22. A conformal dielectric layer 30, preferably of thermally-grown oxide, is deposited over this structure, which is then covered with an organic-containing layer 32 and an inorganic cap layer 34 (e.g., CVD TEOS). An etch window 38 is patterned in photoresist layer 36 and used as a mask to etch cap window 39 through layer 34, using layer 32 as an etch stop. A second etch removes organic-containing layer 32 in contact window 41 (and preferably strips photoresist), using conformal layer 30 as an etch stop. A short anisotropic etch may be used to clear conformal layer 30 from gap bottom 43, after which conducting material 40 may be used to make electrical contact to the substrate.
Inventors
- 👤 Robert H. Havemann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:07
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/069
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
173 words
A method of fabricating a self-aligned contact on a semiconductor device comprising: (a) providing two separated conductors on a substrate; (b) forming a conformal dielectric layer over said conductors and said substrate, thereby creating an insulated gap having a first width between said conductors; (c) depositing an organic-containing dielectric layer over said conductors and said substrate to a depth sufficient to completely cover said conductors and fill said insulated gap; (d) depositing an inorganic cap layer over said organic-containing dielectric layer; (e) etching a cap window through said cap layer, said cap window substantially vertically aligned with said gap and having a second width greater than said first width; and (f) etching a contact window through said organic-containing dielectric layer, using said cap window as a mask for said contact window, and using an etchant which does not substantially affect said conformal dielectric layer, whereby a lower portion of said contact window is laterally confined to said insulated gap, and whereby said conformal dielectric layer is left substantially intact by said etching steps.
Claim 2
Independent Claim
173 words
A method of fabricating a self-aligned contact on a semiconductor device comprising: (a) providing two separated conductors on a substrate; (b) forming a conformal dielectric layer over said conductors and said substrate, thereby creating an insulated gap having a first width between said conductors; (c) depositing an organic-containing dielectric layer over said conductors and said substrate to a depth sufficient to completely cover said conductors and fill said insulated gap; (d) depositing an inorganic cap layer over said organic-containing dielectric layer; (e) etching a cap window through said cap layer, said cap window substantially vertically aligned with said gap and having a second width greater than said first width; and (f) etching a contact window through said organic-containing dielectric layer, using said cap window as a mask for said contact window, and using an etchant which does not substantially affect said conformal dielectric layer, whereby a lower portion of said contact window is laterally confined to said insulated gap, and whereby said conformal dielectric layer is left substantially intact by said etching steps.
Claim 3
Dependent Claim
14 words
The method of claim 1, wherein said conductors each contain an insulating conductor cap.
Claim 4
Dependent Claim
49 words
The method of claim 2, further comprising: anisotropically etching exposed portions of said conformal dielectric layer in said contact window to expose said substrate in at least a portion of said insulated gap; and depositing a conducting material in said contact window to provide electrical contact to said substrate.
Claim 5
Dependent Claim
61 words
The method of claim 1, wherein said forming a conformal dielectric layer step comprises: (a) depositing dielectric material conformally over said conductors and said substrate; (b) anisotropically etching said dielectric material such that said dielectric material is substantially removed from horizontal surfaces of said conductors and said substrate; and (c) depositing a conformal dielectric overlayer over said conductors and said substrate.
Claim 6
Dependent Claim
34 words
The method of claim 1, wherein said conformal dielectric layer is comprised of materials selected from the group consisting of thermally-grown oxide, CVD silicon dioxide, doped oxide, silicon nitride, silicon oxynitride, and combinations thereof.
Claim 7
Dependent Claim
46 words
The method of claim 1, wherein a patterned photoresist layer overlying said cap layer is used to facilitate said etching a cap window through said cap layer step, and wherein said etching a contact window through said organic-containing dielectric layer step simultaneously removes said photoresist layer.
Claim 8
Dependent Claim
26 words
The method of claim 1, wherein said organic-containing dielectric layer acts as an etch stop for said etching a contact window through said cap layer step.
Claim 9
Dependent Claim
19 words
The method of claim 1, wherein said organic-containing dielectric contains between 10 and 100 percent by weight organic material.
Claim 10
Dependent Claim
18 words
The method of claim 8, wherein said organic-containing dielectric consists essentially of said organic material and silicon dioxide.
Claim 11
Independent Claim
267 words
A method of fabricating a self-aligned contact on a semiconductor device comprising: (a) providing two separated conductors formed on a substrate, said conductors having insulating conductor caps; (b) forming a conformal dielectric layer over said conductors and said substrate, thereby creating an insulated gap between said conductors; (c) depositing an organic-containing dielectric layer over said conductors and said substrate to a depth sufficient to completely cover said conductors and fill said insulated gap; (d) depositing an inorganic cap layer over said organic-containing dielectric layer; (e) depositing a photoresist layer over said cap layer and patterning an etch window through said photoresist layer, said etch window being substantially vertically aligned with and being wider than said insulated gap; (f) etching a cap window through said cap layer, using said etch window as a mask for said cap window, and using said organic-containing dielectric layer as an etch stop; (g) etching a contact window through said organic-containing dielectric layer, using said cap window as a mask for said contact window, and using an etchant which does not substantially affect said conformal dielectric layer, said etching a contact window step also removing said photoresist layer; (h) anisotropically etching exposed portions of said conformal dielectric layer in said contact window to expose said substrate in at least a portion of said insulated gap; and (i) depositing a conducting material in said contact window to provide electrical contact to said substrate, whereby an electrical contact to said substrate is laterally positioned by said insulated gap, and whereby capacitive coupling between said conductors is decreased, as compared to a solid silicon dioxide dielectric.
Claim 12
Independent Claim
267 words
A method of fabricating a self-aligned contact on a semiconductor device comprising: (a) providing two separated conductors formed on a substrate, said conductors having insulating conductor caps; (b) forming a conformal dielectric layer over said conductors and said substrate, thereby creating an insulated gap between said conductors; (c) depositing an organic-containing dielectric layer over said conductors and said substrate to a depth sufficient to completely cover said conductors and fill said insulated gap; (d) depositing an inorganic cap layer over said organic-containing dielectric layer; (e) depositing a photoresist layer over said cap layer and patterning an etch window through said photoresist layer, said etch window being substantially vertically aligned with and being wider than said insulated gap; (f) etching a cap window through said cap layer, using said etch window as a mask for said cap window, and using said organic-containing dielectric layer as an etch stop; (g) etching a contact window through said organic-containing dielectric layer, using said cap window as a mask for said contact window, and using an etchant which does not substantially affect said conformal dielectric layer, said etching a contact window step also removing said photoresist layer; (h) anisotropically etching exposed portions of said conformal dielectric layer in said contact window to expose said substrate in at least a portion of said insulated gap; and (i) depositing a conducting material in said contact window to provide electrical contact to said substrate, whereby an electrical contact to said substrate is laterally positioned by said insulated gap, and whereby capacitive coupling between said conductors is decreased, as compared to a solid silicon dioxide dielectric.
Claim 13
Dependent Claim
23 words
The method of claim 10, further comprising, before said depositing an inorganic cap layer step, thinning said organic-containing layer with a blanket etchback.
References Cited (Backward Citations)
US4576900A
Cited
US4683024A
Cited
US4980316A
Cited
JPH03105923A
Cited
US5198298A
Cited
US5037777A
Cited
JPH04127454A
Cited
US5100838A
Cited
US5069747A
Cited
US5200358A
Cited
US5246883A
Cited
US5279989A
Cited
US5371047A
Cited
US5393712A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-01-08 | 1999-07-10 | 2000-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-01-08 | 2003-07-10 | 2004-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-01-08 | 2007-07-10 | 2008-01-09 | $7700.00 | Window Closed / Lapsed |