US5482780A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polypropylene film with cold seal release and cold seal receptive surfaces
Assignee: Applied Extrusion Technologies Inc
•
Filing: 1994-05-23
•
Granted: 1996-01-09
•
Expires: 2014-05-23
Abstract
Abstract An oriented polymeric alpha-olefin film having: an isotactic polypropylene homopolymer core; a cold seal release skin layer adherent to one side of the core; and a surface treated cold seal receptive layer or such treated layer with a cold seal cohesive composition over the surface treatment of said layer on the other side of the core. The cold seal release skin layer comprises a slip agent and a blend of two polymers, namely, an ethylene-propylene random copolymer containing about 2% to 8% of ethylene in such copolymer and an ethylene-butylene copolymer containing about 0.5% to 6% of ethylene in such copolymer. The cold seal receptive layer is of an ethylene-propylene random copolymer containing about 2 to 8% of ethylene.
Inventors
- 👤 Andrew F. Wilkie
- 👤 Michael D. Butler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 17:24
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B32B27/32; C; C08; C08L; C08L23/00; C08L23/02; C08L23/10; C08L23/12; C08L23/14; C08L23/142; B32B2307/00; B32B2307/50; B32B2307/514; B32B2307/518; B32B2323/00; B32B2323/04; B32B2323/043; B32B2323/10; B32B2439/00; C08L2205/00; C08L2205/03; C08L23/04; C08L23/06; C08L23/18; C08L23/20; C08L2312/00; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24893; Y10T428/25; Y10T428/259; Y10T428/28; Y10T428/2813; Y10T428/2817; Y10T428/2826; Y10T428/31504; Y10T428/31652; Y10T428/31663; Y10T428/31667; Y10T428/31855; Y10T428/31909; Y10T428/31913
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
175 words
A coextruded biaxially oriented polypropylene packaging film comprising: A. a 70 to 150 gauge core layer fabricated of isotactic polypropylene homopolymer; B. said core layer having on one side thereof: a 2 to 10 gauge cold seal release layer comprising a blend of (a) about 25% to 80% by weight of an ethylene-propylene random copolymer containing about 2% to 8% of ethylene (b) 20% to 75% by weight of an ethylene-butylene copolymer containing about 0.5% to 6% by weight of ethylene and about 94 to 99.5% of butylene and (c) a non-migratory slip agent in an amount sufficient to decrease the coefficient of friction of the release layer; and C. said core layer having on the other side thereof a 1 to 10 gauge cold seal receptive skin layer fabricated of an ethylene-propylene random copolymer containing from about 2% to 8% of ethylene and 92 to 98% of propylene, said cold seal receptive skin layer having an outer surface which has been surface modified to make it more receptive to a cold seal cohesive composition.
Claim 2
Dependent Claim
175 words
A coextruded biaxially oriented polypropylene packaging film comprising: A. a 70 to 150 gauge core layer fabricated of isotactic polypropylene homopolymer; B. said core layer having on one side thereof: a 2 to 10 gauge cold seal release layer comprising a blend of (a) about 25% to 80% by weight of an ethylene-propylene random copolymer containing about 2% to 8% of ethylene (b) 20% to 75% by weight of an ethylene-butylene copolymer containing about 0.5% to 6% by weight of ethylene and about 94 to 99.5% of butylene and (c) a non-migratory slip agent in an amount sufficient to decrease the coefficient of friction of the release layer; and C. said core layer having on the other side thereof a 1 to 10 gauge cold seal receptive skin layer fabricated of an ethylene-propylene random copolymer containing from about 2% to 8% of ethylene and 92 to 98% of propylene, said cold seal receptive skin layer having an outer surface which has been surface modified to make it more receptive to a cold seal cohesive composition.
Claim 3
Dependent Claim
48 words
The film of claim 1 wherein the slip agent comprises from about 1,000 to 10,000 parts per million by weight of cross-linked silicone having a particle size of about 1 to 4.5 microns and the quantity of ethylene in the ethylene-butylene copolymer is from about 0.5% to 3%.
Claim 4
Dependent Claim
40 words
The film of claim 2 wherein the cold seal release layer contains kaolin clay in a quantity sufficient to decrease the coefficient of friction and the quantity of ethylene in the ethylene-propylene random copolymer is from about 3% to 5%.
Claim 5
Dependent Claim
20 words
The film of claim 1 wherein the cold seal release layer includes up to about 3% of high density polyethylene.
Claim 6
Dependent Claim
23 words
The film of claim 1 wherein the cold seal release skin layer has its surface physically modified to be more receptive to ink.
Claim 7
Dependent Claim
13 words
The film of claim 5 wherein the surface modification is by corona treatment.
Claim 8
Dependent Claim
43 words
The film of claim 1 wherein the cold seal receptive skin layer has its outer surface modified by a method selected from the group consisting of flame spraying and corona treatment to make it receptive to adherence of the cold seal cohesive composition.
Claim 9
Dependent Claim
19 words
The film of claim 7 wherein the said receptive skin layer is coated with a cold seal cohesive composition.
Claim 10
Dependent Claim
162 words
An oriented composite polyolefin film comprising: A. a core layer of an alpha olefin containing at least 90% by weight of isotactic polypropylene homopolymer; B. a cold seal release skin layer on one side of the core said layer comprising a blend of (a) from about 25% to 80% by weight of an ethylene-propylene random copolymer containing from 2% to 8% by weight of ethylene (b) from about 20% to 75% by weight of an ethylene-butylene copolymer containing from about 0.5% to 6% of ethylene and (c) a non-migrating slip agent in an amount sufficient to provide to such layer a coefficient of friction of not greater than about 0.4; and C. a cold seal receptive skin layer of an ethylene-propylene random copolymer on the other side of the core, said random copolymer containing about 2% to 8% of ethylene and wherein the surface of the receptive layer has been physically modified so as to better adhere to a cold seal composition.
Claim 11
Dependent Claim
162 words
An oriented composite polyolefin film comprising: A. a core layer of an alpha olefin containing at least 90% by weight of isotactic polypropylene homopolymer; B. a cold seal release skin layer on one side of the core said layer comprising a blend of (a) from about 25% to 80% by weight of an ethylene-propylene random copolymer containing from 2% to 8% by weight of ethylene (b) from about 20% to 75% by weight of an ethylene-butylene copolymer containing from about 0.5% to 6% of ethylene and (c) a non-migrating slip agent in an amount sufficient to provide to such layer a coefficient of friction of not greater than about 0.4; and C. a cold seal receptive skin layer of an ethylene-propylene random copolymer on the other side of the core, said random copolymer containing about 2% to 8% of ethylene and wherein the surface of the receptive layer has been physically modified so as to better adhere to a cold seal composition.
Claim 12
Dependent Claim
20 words
The film of claim 9 wherein the surface of the receptive layer has been modified by flame or corona treatment.
Claim 13
Dependent Claim
17 words
The film of claim 10 wherein the surface of the receptive layer is modified by corona treatment.
Claim 14
Dependent Claim
18 words
The film of claim 9 wherein the core contains from about 0.5% to 5% of high density polyethylene.
Claim 15
Dependent Claim
51 words
The film of claim 9 wherein: the core contains at least 95% by weight of isotactic polypropylene homopolymer; the quantity of ethylene in the ethylene-butylene copolymer is from about 0.5% to 3%; and a cold seal cohesive composition is adhered to the physically modified surface of the cold seal receptive layer.
Claim 16
Dependent Claim
19 words
The film of claim 9 wherein the release layer contains from about 0.3 to 3% of high density polyethylene.
Claim 17
Dependent Claim
23 words
The film of claim 9 wherein the slip agent is cross linked silicone having a particle size of about 1 to 4.5 microns.
Claim 18
Dependent Claim
19 words
The film of claim 9 wherein the slip agent is a combination of cross linked silicone and kaolin clay.
Claim 19
Dependent Claim
27 words
The film of claim 9 wherein the core is fabricated of isotactic polypropylene homopolymer blended with an ethylene-propylene random copolymer, ethylene-propylene block copolymer, or high density polyethylene.
References Cited (Backward Citations)
US4230767A
Cited
US4293608A
Cited
US4357383A
Cited
US4777081A
Cited
US4692380A
Cited
US4758396A
Cited
US5318824A
Cited
US4741950A
Cited
US4883698A
Cited
US5026592A
Cited
US4888237A
Cited
US4944990A
Cited
US4997700A
Cited
US5176954A
Cited
US5091236A
Cited
US5326625A
Cited
US5209884A
Cited
US5194318A
Cited
US5134173A
Cited
US5318834A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-01-08 | 1999-07-10 | 2000-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-01-08 | 2003-07-10 | 2004-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-01-08 | 2007-07-10 | 2008-01-09 | $7700.00 | Window Closed / Lapsed |