US4888237A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for manufacturing a metallized polyolefin film and resulting film
Assignee: Mobil Oil AS
•
Filing: 1988-02-16
•
Granted: 1989-12-19
•
Expires: 2008-02-16
Abstract
Abstract A process for manufacturing a metallized polymeric film to provide a structure possessing high metal-to-film adhesion and little, if any, tendency toward metal fracture is disclosed. In one embodiment of the process, at least one polyolefin layer is provided to a film which includes a substantially isotactic polymer having a degree of atacticity of no more than about 6%. The isotactic component is preferably polypropylene homopolymer. Other components include up to about 34% of an adhesive-promoting component which can be a C 2 -C 4 polymer, including homo-, co-, and terpolymers having C 2 -C 4 carbon chains, and a second isotactic polymer having a degree of atacticity of from about 6% to about 15%. The surface of the polyolefin layer is subjected to flame treatment followed by vacuum metallization of this surface (preferably with aluminum).
Inventors
- 👤 Ricardo Balloni
- 👤 Jay K. Keung
- 👤 Eldridge M. Mount, III
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 00:26
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/20; B; B29; B29C; B29C59/00; B29C59/08; B29K; B29K2023/00; B29K2023/10; B29K2023/12; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10S428/913; Y10T; Y10T428/00; Y10T428/28; Y10T428/2813; Y10T428/2817; Y10T428/2826; Y10T428/2848; Y10T428/31504; Y10T428/31678; Y10T428/31692
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
66 words
A metallized flexible polymeric film comprising: at least one metal-receiving layer possessing a glossy metal-receiving, polyolefin surface treated by exposure to flame prior to metallization to significantly enhance the adhesion of subsequently applied metal to said surface, said polyolefin containing at least about 50 weight percent of a substantially isotactic homopolymer and possessing an average xylene soluble content of not more than about 10 weight percent.
Claim 2
Dependent Claim
66 words
A metallized flexible polymeric film comprising: at least one metal-receiving layer possessing a glossy metal-receiving, polyolefin surface treated by exposure to flame prior to metallization to significantly enhance the adhesion of subsequently applied metal to said surface, said polyolefin containing at least about 50 weight percent of a substantially isotactic homopolymer and possessing an average xylene soluble content of not more than about 10 weight percent.
Claim 3
Dependent Claim
41 words
The metallized film of claim 1 which further comprises a core layer having two sides, the first side of which is in direct contact with said metal-receiving layer, on the side of said metal-receiving layer not adhered to said metal layer.
Claim 4
Dependent Claim
24 words
The metallized film of claim 2 which further comprises a heat sealable layer in direct contact with the second side of said core layer.
Claim 5
Dependent Claim
25 words
The metallized film of claim 1 wherein said substantially isotactic homopolymer is polypropylene which has a degree of atacticity of not more than about 6%.
Claim 6
Dependent Claim
46 words
The metallized film of claim 4 wherein said metal-receiving layer further comprises a second substantially isotactic hompolymer having a degree of atacticity of from about 6% to about 15%, said second homopolymer present in an amount up to about 50% by weight of said metal-receiving layer.
Claim 7
Dependent Claim
51 words
The metallized film of claim 1 wherein said metal-receiving layer further comprises a C 2 -C 4 polymer which promotes adhesion of the metal to the surface of said metal-receiving layer, said adhesion promoting component included in an amount of not more than about 34% by weight of said metal-receiving layer.
Claim 8
Dependent Claim
25 words
The metallized film of claim 6 wherein said C 2 -C 4 polymer includes homo-, co- and terpolymers of C 2 -C 4 carbon chains.
Claim 9
Dependent Claim
88 words
The metallized film of claim 1 wherein said metal-receiving layer further comprises a C 2 -C 4 polymer which promotes adhesion of the metal to the surface of said metal-receiving layer, said adhesion-promoting component included in an amdount of not more than about 34% by weight of said metal-receiving layer, a second substantially isotactic homopolymer having a degree of atacticity of from about 6% to about 15%, provided that said at least one substantially isotactic homopolymer is present in an amount of at least about 50% by weight.
Claim 10
Dependent Claim
82 words
A metallized film prepared by a process for metallizing a flexible polymeric film comprising: (a) providing at least one polyolefin metal-receiving layer having at least 50 percent by weight of one substantially isotactic polymer having a degree of atacticity of no more than about 6%; (b) treating the metal-receiving polyolefin surface by exposure to flame to significantly enhance the adhesion of subsequently applied metal to the surface; and (c) applying metal to the flame treated metal-receiving film surface under vacuum metallizing conditions.
Claim 11
Dependent Claim
82 words
A metallized film prepared by a process for metallizing a flexible polymeric film comprising: (a) providing at least one polyolefin metal-receiving layer having at least 50 percent by weight of one substantially isotactic polymer having a degree of atacticity of no more than about 6%; (b) treating the metal-receiving polyolefin surface by exposure to flame to significantly enhance the adhesion of subsequently applied metal to the surface; and (c) applying metal to the flame treated metal-receiving film surface under vacuum metallizing conditions.
Claim 12
Dependent Claim
86 words
The metallized film of claim 9, wherein said polyolefin metal-receiving layer further comprises: a C 2 -C 4 polymer which promotes adhesion of metal to the surface by said metal-receiving layer, said adhesion-promoting component is included in an amount up to about 34% by weight of said layer. a second substantially isotactic polymer having a degree of atacticity of from about 6% to about 15%, provided that said at least one substantially isotactic polymer is present in an amount of at least about 50% by weight.
Claim 13
Dependent Claim
51 words
The metallized film of claim 9, wherein the polymeric film is a multilayer film structure in which the metal-receiving polyolefin layer constitutes the upper layer of the structure, substantially crystalline polypropylene homopolymer constitutes the core layer of the structure and a heat sealable resin constitutes the lower layer of the structure.
Claim 14
Dependent Claim
20 words
The metallized film of claim 9, wherein the polymeric film is oriented by stretching prior to step (b) and (c).
Claim 15
Dependent Claim
29 words
The metallized film of claim 9, wherein flame treating of the metal-receiving polyolefin film surface imparts an energy density of from about 30 to about 60 dynes/cm to this
Claim 16
Dependent Claim
12 words
The metallized film of claim 9, wherein the metal film is aluminum.
References Cited (Backward Citations)
US2632921A
Cited
US2648097A
Cited
US3028622A
Cited
US3255034A
Cited
US3375126A
Cited
US3431135A
Cited
US3347697A
Cited
US3674536A
Cited
US4211811A
Cited
US4239827A
Cited
US4345005A
Cited
US4357383A
Cited
US4508786A
Cited
US4522887A
Cited
US4604322A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-12-18 | 1993-06-19 | 1993-12-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-12-18 | 1997-06-19 | 1997-12-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-12-18 | 2001-06-19 | 2001-12-19 | $7700.00 | Window Closed / Lapsed |