Abstract
Abstract Filled, thermoplastic-modified thermosetting polyester resin formulations are provided as encapsulants for microelectronics devices. The polyester encapsulant formulations include either a low profile thermoplastic resin additive or a combination of polyethylene and a low shrink thermoplastic additive. In preferred embodiments the polyester encapsulant formulations are of low viscosity and can be utilized in various pressure molding protocols. The encapsulant matrix is characterized by a low coefficient of thermal expansion, very low shrinkage, low modulus, and good thermal conductivity. Microelectronics devices encapsulated with the polyester resin formulation exhibit good resistance to moisture related and stress-induced failure.
Inventors
- 👤 William L. Jamison
- 👤 William H. Jenson
- 👤 George E. Sears, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:50
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/42; H01B3/421; C; C08; C08K; C08K3/00; C08K3/01; C08K3/013; C08L; C08L67/00; C08L67/06
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
161 words
A thermosetting polyester resin formulation having molding properties suitable for use in manufacture of microelectronic devices with a low stress induced device failure rate said formulation comprising (a) about 20 to about 60 weight percent of a resin composition comprising (a-1) about 30 to about 60 weight percent of unsaturated polyester, (a-2) about 15 to about 35 weight percent of a low profile thermoplastic resin, or, in combination, polyethylene and a low shrink thermoplastic resin and (a-3) about 10 to about 40 weight percent of unsaturated monomer capable of cross linking the unsaturated polyester, (b) about 40 to about 80 weight percent of inert filler substantially free of mineral fibers, and (c) a free-radical initiating agent in a amount effective to polymerize the resin composition, said formulation having a molding viscosity of less than 8×10 6 centipoise and at ambient temperature and capable of thermosetting to a plastic matrix with a coefficient of thermal expansion of less than 30×10 -6 cm/cm/C.
Claim 2
Dependent Claim
161 words
A thermosetting polyester resin formulation having molding properties suitable for use in manufacture of microelectronic devices with a low stress induced device failure rate said formulation comprising (a) about 20 to about 60 weight percent of a resin composition comprising (a-1) about 30 to about 60 weight percent of unsaturated polyester, (a-2) about 15 to about 35 weight percent of a low profile thermoplastic resin, or, in combination, polyethylene and a low shrink thermoplastic resin and (a-3) about 10 to about 40 weight percent of unsaturated monomer capable of cross linking the unsaturated polyester, (b) about 40 to about 80 weight percent of inert filler substantially free of mineral fibers, and (c) a free-radical initiating agent in a amount effective to polymerize the resin composition, said formulation having a molding viscosity of less than 8×10 6 centipoise and at ambient temperature and capable of thermosetting to a plastic matrix with a coefficient of thermal expansion of less than 30×10 -6 cm/cm/C.
Claim 3
Dependent Claim
27 words
The polyester resin formulation of claim 1 wherein the inert filler comprises low aspect ratio mineral particulates having an average particle size of less than 15 microns.
Claim 4
Dependent Claim
24 words
The resin formulation of claim 2 wherein the inert filler is substantially free of mineral fillers having an aspect ratio of 3:1 or more.
Claim 5
Dependent Claim
39 words
The resin formulation of claim 1 having a molding viscosity of less than 8×10 6 centipoise at ambient temperature and capable of thermosetting to a plastic matrix having a coefficient of thermal expansion of less than 25×10 -6 cm/cm/°C.
Claim 6
Dependent Claim
12 words
The resin formulation of claim 1 substantially free of mold release agents.
Claim 7
Dependent Claim
16 words
The resin formulation of claim 1 wherein the thermoplastic resin is a low profile thermoplastic resin.
Claim 8
Dependent Claim
16 words
The resin formulation of claim 4 wherein the thermoplastic resin is a low profile thermoplastic resin.
Claim 9
Dependent Claim
41 words
The resin formulation of claim 7 having a molding viscosity of less than 3×10 6 centipoise and said formulation capable of thermosetting to a plastic matrix with a coefficient of thermal expansion of about 10×10 -6 to about 20×10 -6 cm/cm/°C.
Claim 10
Dependent Claim
18 words
The resin formulation of claim 7 wherein the thermoplastic resin has an acid number of less than 15.
Claim 11
Dependent Claim
14 words
The resin formulation of claim 1 wherein the thermoplastic resin comprises polyethylene and polystyrene.
Claim 12
Dependent Claim
23 words
The resin formulation of claim 2 wherein the inert filler further comprises thermoplastic fibers dispersible in but not soluble in the resin composition.
Claim 13
Dependent Claim
24 words
The resin formulation of claim 1 wherein the thermoplastic resin comprises a saturated polyester, a polyurethane, a urethane-polyester copolymer or a styrene butadiene rubber.
Claim 14
Dependent Claim
36 words
The resin formulation of claim 8 which is substantially free of conventional mold release agents, wherein the thermoplastic resin comprises a low profile thermoplastic resin, and wherein the inert filler comprises fused silica and alumina trihydrate.
Claim 15
Dependent Claim
168 words
A thermosetting injection moldable polyester resin formulation adapted for encapsulation of electronics devices with a low stress induced device failure rate, said formulation comprising about 25 to about 50 weight percent of a resin composition comprising about 35 to about 60 weight percent of unsaturated polyester, about 20 to about 30 weight percent of thermoplastic resin having an acid number less than 15, and about 10 to about 40 weight percent of unsaturated monomer capable of cross-linking the unsaturated polyester, about 50 to about 75 weight percent of an inert filler substantially free of mineral fibers and comprising low aspect ratio particulate mineral filler having an average particle size of less than 15 microns, and an organic peroxide curing agent in an amount effective to polymerize the resin composition, said resin formulation having a molding viscosity of less than 5×10 6 centipoise at ambient temperature and said formulation being capable of thermosetting to a plastic matrix having a coefficient of thermal expansion of less than 30×10 -6 cm/cm/°C.
Claim 16
Dependent Claim
168 words
A thermosetting injection moldable polyester resin formulation adapted for encapsulation of electronics devices with a low stress induced device failure rate, said formulation comprising about 25 to about 50 weight percent of a resin composition comprising about 35 to about 60 weight percent of unsaturated polyester, about 20 to about 30 weight percent of thermoplastic resin having an acid number less than 15, and about 10 to about 40 weight percent of unsaturated monomer capable of cross-linking the unsaturated polyester, about 50 to about 75 weight percent of an inert filler substantially free of mineral fibers and comprising low aspect ratio particulate mineral filler having an average particle size of less than 15 microns, and an organic peroxide curing agent in an amount effective to polymerize the resin composition, said resin formulation having a molding viscosity of less than 5×10 6 centipoise at ambient temperature and said formulation being capable of thermosetting to a plastic matrix having a coefficient of thermal expansion of less than 30×10 -6 cm/cm/°C.
Claim 17
Dependent Claim
16 words
The resin formulation of claim 14 wherein the thermoplastic resin comprises a low profile thermoplastic resin.
Claim 18
Dependent Claim
25 words
The resin formulation of claim 15 wherein the thermoplastic resin comprises polystyrene and polyethylene powder in a weight ratio of about 20:1 to about 2:1.
Claim 19
Dependent Claim
17 words
The resin formulation of claim 15 wherein the thermoplastic resin has an acid number less than 10.
Claim 20
Dependent Claim
18 words
The resin formulation of claim 16 where the inert filler consists essentially of fused silica and alumina trihydrate.
Claim 21
Dependent Claim
25 words
The resin formulation of claim 16 wherein the thermoplastic resin is selected from the group consisting of saturated polyesters, polyurethanes, urethane/polyester copolymers and styrenebutadiene rubbers.
Claim 22
Dependent Claim
18 words
The resin formulation of claim 16 wherein the inert filler consists essentially of fused silica and alumina trihydrate.
Claim 23
Dependent Claim
42 words
The resin formulation of claim 14 having a molding viscosity of less than 3×10 6 centipoise at ambient temperature and said formulation being capable of thermosetting to a plastic matrix with a coefficient of thermal expansion of less than 25×10 -6 cm/cm/°C.
Claim 24
Dependent Claim
11 words
The composition of claim 15 substantially free of mold release agents.
Claim 25
Independent Claim
179 words
A method for reducing the stress-induced failures of electronic devices encapsulated in a plastic matrix formed by thermosetting a resin formulation comprising a resin composition, a mineral filler, and a catalyst in amount effective to polymerize said resin formulation under thermosetting conditions for said resin composition, said method comprising the steps of forming the plastic matrix by injection molding and thermosetting a polyester resin formulation comprising about 20 to about 60 weight percent of a resin composition comprising about 30 to about 60 weight percent of unsaturated polyester, about 15 to about 35 weight percent of a low profile thermoplastic resin having an acid number less than 15, or in combination polyethylene and a low shrink thermoplastic resin, and about 10 to about 40 weight percent of unsaturated monomer capable of cross-linking the unsaturated polyester, about 40 to about 80 weight percent of an inert filler having an average particle size of less than 20 microns and substantially free of mineral fiber, said polyester resin formulation having a molding viscosity of less than 8×10 6 centipoise at ambient temperature.
Claim 26
Independent Claim
179 words
A method for reducing the stress-induced failures of electronic devices encapsulated in a plastic matrix formed by thermosetting a resin formulation comprising a resin composition, a mineral filler, and a catalyst in amount effective to polymerize said resin formulation under thermosetting conditions for said resin composition, said method comprising the steps of forming the plastic matrix by injection molding and thermosetting a polyester resin formulation comprising about 20 to about 60 weight percent of a resin composition comprising about 30 to about 60 weight percent of unsaturated polyester, about 15 to about 35 weight percent of a low profile thermoplastic resin having an acid number less than 15, or in combination polyethylene and a low shrink thermoplastic resin, and about 10 to about 40 weight percent of unsaturated monomer capable of cross-linking the unsaturated polyester, about 40 to about 80 weight percent of an inert filler having an average particle size of less than 20 microns and substantially free of mineral fiber, said polyester resin formulation having a molding viscosity of less than 8×10 6 centipoise at ambient temperature.
Claim 27
Dependent Claim
13 words
The method of claim 23 wherein the low shrink thermoplastic resin comprises polystyrene.
Claim 28
Dependent Claim
16 words
The method of claim 24 wherein the resin formulation is substantially free of mold release agents.
Claim 29
Dependent Claim
15 words
The method of claim 23 wherein the thermoplastic resin is a low profile thermoplastic resin.
Claim 30
Dependent Claim
20 words
The method of claim 26 wherein the resin formulation is substantially free of mold release agents and trialkoxyorgano-metal silane compounds.
Claim 31
Dependent Claim
151 words
A thermosetting polyester resin formulation comprising about 20 to about 60 weight percent of a resin composition comprising about 30 to about 60 weight percent of unsaturated polyester, about 15 to about 35 weight percent of thermoplastic resin, and about 10 to about 40 weight percent of unsaturated monomer capable of cross-linking the unsaturated polyester, about 40 to about 80 weight percent of inert filler substantially free of mineral fibers and consisting essentially of mineral particulates having an aspect ratio of less than 3:1 and an average particle size of less than 20 microns in their largest dimension and a free radical initiating agent in an amount effective to polymerize the resin composition at elevated temperature, said formulation having a molding viscosity of less than 8×10 6 centipoise at ambient temperature and capable of thermosetting to a plastic matrix having a coefficient of thermal expansion of less than 30×10 -6 cm/cm/°C.
Claim 32
Dependent Claim
151 words
A thermosetting polyester resin formulation comprising about 20 to about 60 weight percent of a resin composition comprising about 30 to about 60 weight percent of unsaturated polyester, about 15 to about 35 weight percent of thermoplastic resin, and about 10 to about 40 weight percent of unsaturated monomer capable of cross-linking the unsaturated polyester, about 40 to about 80 weight percent of inert filler substantially free of mineral fibers and consisting essentially of mineral particulates having an aspect ratio of less than 3:1 and an average particle size of less than 20 microns in their largest dimension and a free radical initiating agent in an amount effective to polymerize the resin composition at elevated temperature, said formulation having a molding viscosity of less than 8×10 6 centipoise at ambient temperature and capable of thermosetting to a plastic matrix having a coefficient of thermal expansion of less than 30×10 -6 cm/cm/°C.
Claim 33
Dependent Claim
30 words
The composition of claim 28 wherein the polyester resin formulation further comprises an effective amount of a coupling agent and has a molding viscosity of less than 5×10 6 centipoise.
Claim 34
Dependent Claim
30 words
The composition of claim 28 wherein the polyester formulation is capable of being thermoset to a plastic matrix having a coefficient of thermal expansion of less than 25×10 -6 cm/cm/°C.
Claim 35
Dependent Claim
15 words
The composition of claim 28 wherein the thermoplastic resin is a low profile thermoplastic resin.
Claim 36
Dependent Claim
17 words
The composition of claim 28 wherein the polyester resin formulation is substantially free of trialkoxyorgano-metal silane compounds.
Claim 37
Dependent Claim
17 words
The composition of claim 28 wherein the polyester resin formulation is substantially free of mold release agents.
Claim 38
Dependent Claim
15 words
The composition of claim 28 wherein the inert filler comprises alumina trihydrate and fused silica.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-12-11 | 1999-06-12 | 1999-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-12-11 | 2003-06-12 | 2003-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-12-11 | 2007-06-12 | 2007-12-12 | $7700.00 | Window Closed / Lapsed |