US4245068A — Low profile additives for unsaturated polyester r…

Claim 1

Independent Claim 119 words

An improved process for preparing a thermoset polyester composition wherein a thermosettable composition of an unsaturated polyester and vinyl monomer capable of cross-linking the polyester is subjected to conditions sufficient to form a thermoset composition, the improvement comprising adding to the thermosettable composition an alkylene oxide polymer soluble in the thermosettable composition and substantially less soluble in the cured thermoset composition, said alkylene oxide polymer being present in an amount such that the alkylene oxide polymer and the thermosettable composition form a true solution and a portion of the alkylene oxide polymer in solution with the thermosettable composition is insoluble in the cured thermoset composition, said amount being sufficient to reduce the shrinkage in the thermosettable composition during cure.

Claim 2

Dependent Claim 119 words

An improved process for preparing a thermoset polyester composition wherein a thermosettable composition of an unsaturated polyester and vinyl monomer capable of cross-linking the polyester is subjected to conditions sufficient to form a thermoset composition, the improvement comprising adding to the thermosettable composition an alkylene oxide polymer soluble in the thermosettable composition and substantially less soluble in the cured thermoset composition, said alkylene oxide polymer being present in an amount such that the alkylene oxide polymer and the thermosettable composition form a true solution and a portion of the alkylene oxide polymer in solution with the thermosettable composition is insoluble in the cured thermoset composition, said amount being sufficient to reduce the shrinkage in the thermosettable composition during cure.

Claim 3

Dependent Claim 79 words

The improved process of claim 1 wherein the alkylene oxide polymer is soluble in the thermosettable composition at concentrations of at least 3 weight percent based on the total weight of the unsaturated polyester, vinyl monomer and alkylene oxide polymer and substantially less soluble in the cured thermoset composition such that at least about 2 weight percent of the alkylene oxide polymer based on the total weight of the unsaturated polyester, vinyl monomer and alkylene oxide polymer is insoluble.

Claim 4

Dependent Claim 89 words

The improved process of claim 2 wherein the alkylene oxide polymer comprises from about 3 to about 25 weight percent of the thermosettable composition based on the weight of the unsaturated polyester, vinyl monomer and alkylene oxide polymer, at least about 2 weight percent of the alkylene oxide polymer in solution with the thermosettable composition based on the total weight of the unsaturated polyester, vinyl monomer and alkylene oxide polymer is insoluble in the cured thermoset composition, and the shrinkage during cure is reduced by at least 40 percent.

Claim 5

Dependent Claim 84 words

The improved process of claim 3 wherein the alkylene oxide polymer is a poly(alkylene oxide) represented by the formula: ##STR9## wherein B is hydroxy or the residue of an organic active hydrogen initiator, R 1 and R 2 are hydrogen, methyl or ethyl provided when R 1 or R 2 is hydrogen, the other is methyl or ethyl and x and y are integers such that the poly(alkylene oxide) is soluble in the thermosettable composition and substantially less soluble in the cured thermoset composition.

Claim 6

Dependent Claim 31 words

The improved process of claim 4 wherein R 1 and R 2 are methyl and the poly(alkylene oxide) has a number average molecular weight (Mn) between about 800 and about 1600.

Claim 7

Dependent Claim 32 words

The improved process of claim 4 wherein the alkylene oxide polymer has a carbon to oxygen ratio between about 2.1 and about 4 and a Mn from about 6000 to about 400.

Claim 8

Dependent Claim 47 words

The improved process of claim 4 wherein R 1 is hydrogen; R 2 is methyl; x has an average value from about 5 to about 45, and y has an average value from about 10 to about 30 and a Mn between about 1500 and about 3000.

Claim 9

Dependent Claim 100 words

The improved process of claim 3 wherein the alkylene oxide polymer is represented by the formula: ##STR10## wherein B is hydrogen or the residue of an organic active hydrogen initiator as hereinbefore described; R 3 and R 4 are hydrogen, ethyl or methyl provided R 3 and R 4 are not all hydrogen or ethyl; each Z is independently hydrocarbylene; each Q 1 is independently ##STR11## each Q 2 is independently ##STR12## and d, e and f are independently integers such that the alkylene oxide copolymer is soluble in the thermosettable composition and substantially less soluble in the thermoset composition.

Claim 10

Dependent Claim 34 words

The improved process of claim 8 wherein the (Q 1 --Z--Q 2 ) is derived from the group consisting of toluene diisocyanate; 4,4'-diphenylmethane diisocyanate; trimellitic anhydride acid chloride; pyromellitic dianhydride; and 3,3',4,4'-benzophenone tetracarboxylic dianhydride.

Claim 11

Dependent Claim 54 words

The improved process of claim 8 wherein f is 1 or 2, R 3 and R 4 are independently hydrogen and methyl, with a ratio of hydrogen to methyl being from about 0.1 to about 10 and the alkylene oxide polymer has a number average molecular weight of from about 500 to about 6000.

Claim 12

Dependent Claim 54 words

The improved process of claim 8 wherein f is 1 or 2, R 3 and R 4 are independently hydrogen and ethyl, with a ratio of hydrogen to ethyl being from about 0.3 to about 15 and the alkylene oxide polymer has a number average molecular weight of from about 500 to about 6000.

Claim 13

Dependent Claim 36 words

The improved process of claim 8 wherein f is 1 or 2, R 3 and R 4 are methyl and the alkylene oxide polymer has a number average molecular weight of from about 600 to 2400.

Claim 14

Dependent Claim 91 words

A thermosettable composition comprising an unsaturated polyester, a vinyl monomer capable of cross-linking the unsaturated polyester, and a soluble alkylene oxide polymer which is substantially less soluble in a thermoset composition derived from the thermosettable composition, said alkylene oxide polymer being present in an amount such that the alkylene oxide polymer, vinyl monomer and unsaturated polyester form a true solution and a portion of the alkylene oxide polymer in solution is insoluble in the cured thermoset composition, said amount being sufficient to reduce the shrinkage of the thermosettable composition during cure.

Claim 15

Dependent Claim 91 words

A thermosettable composition comprising an unsaturated polyester, a vinyl monomer capable of cross-linking the unsaturated polyester, and a soluble alkylene oxide polymer which is substantially less soluble in a thermoset composition derived from the thermosettable composition, said alkylene oxide polymer being present in an amount such that the alkylene oxide polymer, vinyl monomer and unsaturated polyester form a true solution and a portion of the alkylene oxide polymer in solution is insoluble in the cured thermoset composition, said amount being sufficient to reduce the shrinkage of the thermosettable composition during cure.

Claim 16

Dependent Claim 67 words

The thermosettable composition of claim 13 comprising from about 3 to about 25 weight percent of the alkylene oxide polymer wherein at least about 2 weight percent of the soluble alkylene oxide polymer based on the total weight of the unsaturated polyester, vinyl monomer and alkylene oxide polymer is insoluble in the cured thermoset composition and the shrinkage is reduced by at least 40 percent during cure.

Claim 17

Dependent Claim 81 words

The thermosettable composition of claim 13 wherein the soluble alkylene oxide polymer is of the formula: ##STR13## wherein B is hydroxy or the residue of an organic active hydrogen initiator, R 1 and R 2 are hydrogen, methyl or ethyl provided when R 1 or R 2 is hydrogen, the other is methyl or ethyl and x and y are integers such that the alkylene oxide polymer is soluble in the thermosettable composition and substantially less soluble in the thermoset composition.

Claim 18

Dependent Claim 69 words

The thermosettable composition of claim 13 wherein the soluble alkylene oxide polymer is represented by the formula: ##STR14## wherein B is hydrogen or the residue of an organic active hydrogen initiator as hereinbefore described; R 3 and R 4 are hydrogen, ethyl or methyl; each Z is independently hydrocarbylene; each Q 1 is independently ##STR15## each Q 2 is independently ##STR16## and d, e and f are independently integers.

Claim 19

Dependent Claim 11 words

A thermoset composition derived from the thermosettable composition of claim 13.

Claim 20

Dependent Claim 11 words

A thermoset composition derived from the thermosettable composition of claim 15.

Claim 21

Dependent Claim 11 words

A thermoset composition derived from the thermosettable composition of claim 16.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1984-01-13	1984-07-14	1985-01-13	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1988-01-13	1988-07-14	1989-01-13	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1992-01-13	1992-07-14	1993-01-13	$7700.00	Window Closed / Lapsed

Low profile additives for unsaturated polyester resins

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag